JPH0329595B2 - - Google Patents
Info
- Publication number
- JPH0329595B2 JPH0329595B2 JP61201235A JP20123586A JPH0329595B2 JP H0329595 B2 JPH0329595 B2 JP H0329595B2 JP 61201235 A JP61201235 A JP 61201235A JP 20123586 A JP20123586 A JP 20123586A JP H0329595 B2 JPH0329595 B2 JP H0329595B2
- Authority
- JP
- Japan
- Prior art keywords
- ink
- recording
- receiving layer
- recording sheet
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
<産業上の利用分野>
本発明はインクジエツトプリンターに好適な記
録シートに関する。更に詳しくは本発明は透光性
に優れ、その記録画像をオーバーヘツドプロジエ
クター(以下OHPと称す)等の光学機器により
透過して観察するのに適した記録シートに関す
る。
録シートに関する。更に詳しくは本発明は透光性
に優れ、その記録画像をオーバーヘツドプロジエ
クター(以下OHPと称す)等の光学機器により
透過して観察するのに適した記録シートに関す
る。
<従来の技術>
インクジエツトプリンターは、記録の鮮明さ、
音の静かさ、カラー化の容易なことなどの優れた
特徴により近年普及している。インクジエツトプ
リンターはジエツトノズルの詰まりを防ぐために
乾燥しにくいインクが用いられ、このインクの成
分はバインダー、染料、溶媒、添加剤などを水に
溶解したものが一般的である。従つてインクジエ
ツトプリンターで印刷記録を行う場合記録シート
は吸水性を有する必要があり、通常インクを十分
吸収する性能を付与すべく特別に設計された紙が
用いられている。
音の静かさ、カラー化の容易なことなどの優れた
特徴により近年普及している。インクジエツトプ
リンターはジエツトノズルの詰まりを防ぐために
乾燥しにくいインクが用いられ、このインクの成
分はバインダー、染料、溶媒、添加剤などを水に
溶解したものが一般的である。従つてインクジエ
ツトプリンターで印刷記録を行う場合記録シート
は吸水性を有する必要があり、通常インクを十分
吸収する性能を付与すべく特別に設計された紙が
用いられている。
一方インクジエツトプリンターのカラー化に伴
つて透明な被記録材料に記録を行い、OHP用記
録シートとして使用する要求が高まつている。し
かし、透明な記録シートは、通常プラスチツクフ
イルムよりなるが、このプラスチツクフイルムは
疎水性でインクジエツトプリンター用インクを全
く吸収しないので、その上に直接記録されたイン
クは容易に乾燥せず、指でこすつたり、重ね合わ
されたりすると記録部分が汚れて、実用にならな
い。
つて透明な被記録材料に記録を行い、OHP用記
録シートとして使用する要求が高まつている。し
かし、透明な記録シートは、通常プラスチツクフ
イルムよりなるが、このプラスチツクフイルムは
疎水性でインクジエツトプリンター用インクを全
く吸収しないので、その上に直接記録されたイン
クは容易に乾燥せず、指でこすつたり、重ね合わ
されたりすると記録部分が汚れて、実用にならな
い。
そこでこの対策として水性インクに対する受容
性すなわちインク吸収性を向上させるために、例
えばポリビニルアルコールを主体としてこれにグ
リセリン、塩化リチウム、でんぷん、ゼラチン、
ヒドロキシエチルセルロース、およびカルボキシ
メチルセルロース等、インクジエツトプリンター
用インキに対し湿潤性のある材料を含有した水性
のインク受容層を透明性基材に設けることが提案
されているが、従来のインク受容層はインク吸収
性を満足しているにしても、その一方で表面がベ
トついてシートを何枚も積層した場合ブロツキン
グを生じたり、又、材料によつては透明性が低下
したりする問題点を有するものであつた。
性すなわちインク吸収性を向上させるために、例
えばポリビニルアルコールを主体としてこれにグ
リセリン、塩化リチウム、でんぷん、ゼラチン、
ヒドロキシエチルセルロース、およびカルボキシ
メチルセルロース等、インクジエツトプリンター
用インキに対し湿潤性のある材料を含有した水性
のインク受容層を透明性基材に設けることが提案
されているが、従来のインク受容層はインク吸収
性を満足しているにしても、その一方で表面がベ
トついてシートを何枚も積層した場合ブロツキン
グを生じたり、又、材料によつては透明性が低下
したりする問題点を有するものであつた。
<発明が解決しようとする問題点>
本発明は上記の事情に鑑みてなされたものであ
り、透明な記録シートであつて、特に従来技術で
は不可能であつたインク吸収性が十分で、かつ透
明性に全く問題のない、しかもOHPに使用した
場合記録画像の透明性にすぐれたインクジエツト
記録用の記録シートを提供するものである。
り、透明な記録シートであつて、特に従来技術で
は不可能であつたインク吸収性が十分で、かつ透
明性に全く問題のない、しかもOHPに使用した
場合記録画像の透明性にすぐれたインクジエツト
記録用の記録シートを提供するものである。
<問題点を解決するための手段>
本発明は透明性を有する基材上に下記構造式(1)
を有するポリ(エチルオキサゾリン)を含有する
インク受容層を設けてなるインクジエト記録用シ
ートを提供するものである。
を有するポリ(エチルオキサゾリン)を含有する
インク受容層を設けてなるインクジエト記録用シ
ートを提供するものである。
(但し、nは正の整数)
本発明の記録シートを構成する基材としては、
透明性の優れた、例えばポリエチレンテレフタレ
ート、ジアセテート、トリアセテート、アクリル
系ポリマー、セロハン、セルロイド、ポリ塩化ビ
ニル、ポリカーボネート、ポリイミド等のプラス
チツクからなるフイルムもしくは板、ガラス板を
使用することができ、記録目的、記録画像の用途
あるいはその上部に設けられるインク受容層との
良好な密着性が得られるかどうかなどの諸条件に
応じて上記材料の中から適宜選択される。
透明性の優れた、例えばポリエチレンテレフタレ
ート、ジアセテート、トリアセテート、アクリル
系ポリマー、セロハン、セルロイド、ポリ塩化ビ
ニル、ポリカーボネート、ポリイミド等のプラス
チツクからなるフイルムもしくは板、ガラス板を
使用することができ、記録目的、記録画像の用途
あるいはその上部に設けられるインク受容層との
良好な密着性が得られるかどうかなどの諸条件に
応じて上記材料の中から適宜選択される。
又、本発明でいう基材は、水性インクの保持性
を向上させるために上記フイルムは板上にアルブ
ミン、ゼラチン、カゼイン、でんぷん、カチオン
でんぷん、アラビアゴム、アルギン酸ソーダ等の
天然樹脂やポリアミド、ポリアクリルアミド、ポ
リビニルピロリドン、四級化ポリビニルピロリド
ン、ポリエチレンイミン、ポリビニルポリジリウ
ムハライド、メラミン樹脂、ポリウレタン、カル
ボキシメチルセルロース、ポリビニルアルコー
ル、カチオン変性ポリビニルアルコール、ポリエ
ステル、ポリアクリル酸ソーダ等の合成樹脂の材
料から選ばれる親水性樹脂を主成分とするアンダ
ー層を設けたものであつてもよい。さらに又、該
アンダー層の強度補強および/または蓄材との密
着性を改善するために、必要に応じて、SBRラ
テツクス、NBRラテツクス、ポリビニルホルマ
ール、ポリメチルメタクリレート、ポリビニルブ
チラール、ポリアクリロニトリル、ポリ塩化ビニ
ル、ポリ酢酸ビニル、フエノール樹脂、アルキツ
ド樹脂等の樹脂をアンダー層に併用してもよい。
を向上させるために上記フイルムは板上にアルブ
ミン、ゼラチン、カゼイン、でんぷん、カチオン
でんぷん、アラビアゴム、アルギン酸ソーダ等の
天然樹脂やポリアミド、ポリアクリルアミド、ポ
リビニルピロリドン、四級化ポリビニルピロリド
ン、ポリエチレンイミン、ポリビニルポリジリウ
ムハライド、メラミン樹脂、ポリウレタン、カル
ボキシメチルセルロース、ポリビニルアルコー
ル、カチオン変性ポリビニルアルコール、ポリエ
ステル、ポリアクリル酸ソーダ等の合成樹脂の材
料から選ばれる親水性樹脂を主成分とするアンダ
ー層を設けたものであつてもよい。さらに又、該
アンダー層の強度補強および/または蓄材との密
着性を改善するために、必要に応じて、SBRラ
テツクス、NBRラテツクス、ポリビニルホルマ
ール、ポリメチルメタクリレート、ポリビニルブ
チラール、ポリアクリロニトリル、ポリ塩化ビニ
ル、ポリ酢酸ビニル、フエノール樹脂、アルキツ
ド樹脂等の樹脂をアンダー層に併用してもよい。
このようにして形成されるアンダー層の厚さ
は、インクを保持できる範囲であればよく、記録
するインクの量にもよるが、0.1μm以上あれば、
特に限定されるものではない。実用的には、0.5
〜15μmの範囲が好適である。
は、インクを保持できる範囲であればよく、記録
するインクの量にもよるが、0.1μm以上あれば、
特に限定されるものではない。実用的には、0.5
〜15μmの範囲が好適である。
本発明の記録シートを構成するインク受容層
は、記録時に記録装置や記録器具の記録手段から
インクを受容し、吸収して定着する部分である。
は、記録時に記録装置や記録器具の記録手段から
インクを受容し、吸収して定着する部分である。
該インク受容層に含有するポリ(エチルオキサ
ゾリン)は2−エチル−2−オキサゾリンのカチ
オン性開環重合によつて得られる下記構造式を有
するものが本発明に適用される。
ゾリン)は2−エチル−2−オキサゾリンのカチ
オン性開環重合によつて得られる下記構造式を有
するものが本発明に適用される。
上記ポリ(エチルオキサゾリン)の具体例とし
ては、例えば平均分子量5×104〜50×104、融点
範囲110〜120℃のダウケミカル社製商品番号
XAS−10874.01〜05が本発明に適用可能である。
ては、例えば平均分子量5×104〜50×104、融点
範囲110〜120℃のダウケミカル社製商品番号
XAS−10874.01〜05が本発明に適用可能である。
なお本発明においては、エチルオキサゾリンと
他のモノマー成分との共重合体であつても本発明
を構成するとができる。
他のモノマー成分との共重合体であつても本発明
を構成するとができる。
又、本発明でいうインク受容層には上記ポリ
(エチルオキサゾリン)以外に例えばポリエチレ
ンオキサイド、ポリプロピレンオキサイド等のポ
リアルキレンオキサイドもしくは該ポリアルキレ
ンオキサイドのイソシアネート変性物、スチレ
ン/アクリル酸エステル共重合体、スチレン/ア
クリロニトリル共重合体、アクリル系ホモコポリ
マー等の高分子材料を併用することも可能であ
る。
(エチルオキサゾリン)以外に例えばポリエチレ
ンオキサイド、ポリプロピレンオキサイド等のポ
リアルキレンオキサイドもしくは該ポリアルキレ
ンオキサイドのイソシアネート変性物、スチレ
ン/アクリル酸エステル共重合体、スチレン/ア
クリロニトリル共重合体、アクリル系ホモコポリ
マー等の高分子材料を併用することも可能であ
る。
又、本発明でいうインク受容層には、記録シー
トの記録特性をより高めるためおよび耐ブロツキ
ング特性向上のために、記録シートの透明性を損
なわない程度に、例えばシリカ、クレー、タル
ク、ケイソウ土、炭酸カルシウム、硫酸カルシウ
ム、硫酸バリウム、ケイ酸アルミ、合成ゼオライ
ト、アルミナ、酸化亜鉛、リトポン、サチンホワ
イト等の充填剤をインク受容層に分散させても良
い。更に、記録シートの生産性、記録特性、ある
いは保存安定性等をより高めるために、分散剤、
蛍光染料、PH調整剤、消泡剤、潤滑剤、防腐剤
等の各種添加剤を混在させることもできる。これ
らの添加剤も記録シートの透明性を損なわない程
度に添加される。
トの記録特性をより高めるためおよび耐ブロツキ
ング特性向上のために、記録シートの透明性を損
なわない程度に、例えばシリカ、クレー、タル
ク、ケイソウ土、炭酸カルシウム、硫酸カルシウ
ム、硫酸バリウム、ケイ酸アルミ、合成ゼオライ
ト、アルミナ、酸化亜鉛、リトポン、サチンホワ
イト等の充填剤をインク受容層に分散させても良
い。更に、記録シートの生産性、記録特性、ある
いは保存安定性等をより高めるために、分散剤、
蛍光染料、PH調整剤、消泡剤、潤滑剤、防腐剤
等の各種添加剤を混在させることもできる。これ
らの添加剤も記録シートの透明性を損なわない程
度に添加される。
基材上にインク受容層を設けるには、インク受
容層を形成ることのできる材料を、適当な溶剤中
に溶解もしくは分散させて調整した塗工液をロー
ルコーテイング法、ブレードコーテイング法、ス
プレーコーテイング法、エアナイフコーテイング
法、ロツドコーテイング法等の方法により塗工
し、これを乾燥させる方法、また、前記のインク
受容層を形成することのできる材料を均一に混合
した混合物を前記透明性基材上にホツトメルトコ
ーテイング法、ラミネートコーテイング法等によ
り積層してインク受容層を形成する方法などを適
用することができる。
容層を形成ることのできる材料を、適当な溶剤中
に溶解もしくは分散させて調整した塗工液をロー
ルコーテイング法、ブレードコーテイング法、ス
プレーコーテイング法、エアナイフコーテイング
法、ロツドコーテイング法等の方法により塗工
し、これを乾燥させる方法、また、前記のインク
受容層を形成することのできる材料を均一に混合
した混合物を前記透明性基材上にホツトメルトコ
ーテイング法、ラミネートコーテイング法等によ
り積層してインク受容層を形成する方法などを適
用することができる。
本発明の記録シートの有するインク受容層の厚
さは、通常1〜20μm程度、好ましくは2〜10μ
m程度であるのが望ましい。インク受容層の厚み
が厚すぎる場合は、透明性(直線透過率)が低下
し、薄すぎる場合には、インク吸収性が低下する
ので好ましくない。
さは、通常1〜20μm程度、好ましくは2〜10μ
m程度であるのが望ましい。インク受容層の厚み
が厚すぎる場合は、透明性(直線透過率)が低下
し、薄すぎる場合には、インク吸収性が低下する
ので好ましくない。
なお本発明の記録シートは、すぐれた透明性を
有するので、その用途は単にOHPのみにとどま
ることなくスライド等OHP以外の光学機器によ
り記録画像をスクリーン等への投影観察に用いる
もの、カラー印刷のポジ版を作製する際の色分解
版、あるいは液晶等のカラーデイスプレーに用い
るCMF等、従来の表面画像観察用以外の用途に
も適用可能である。
有するので、その用途は単にOHPのみにとどま
ることなくスライド等OHP以外の光学機器によ
り記録画像をスクリーン等への投影観察に用いる
もの、カラー印刷のポジ版を作製する際の色分解
版、あるいは液晶等のカラーデイスプレーに用い
るCMF等、従来の表面画像観察用以外の用途に
も適用可能である。
さらに、又、OHP用であつてもインクジエツ
トプリンター以外の記録手段、例えば電子写真法
によるPPC製版や手書き等も本発明の用途に包
含されるものである。
トプリンター以外の記録手段、例えば電子写真法
によるPPC製版や手書き等も本発明の用途に包
含されるものである。
<実施例>
以下、実施例に従つて本発明を詳述する。な
お、文中、部とあるのは重量基準である。
お、文中、部とあるのは重量基準である。
実施例 1
厚さ100μmのポリエチレンテレフタレート、
フイルムの片面に下記組成の塗液を乾燥後の塗布
厚が2〜3μmとなるように塗工乾燥してアンダ
ー層を形成し、透明性基材を作製した。
フイルムの片面に下記組成の塗液を乾燥後の塗布
厚が2〜3μmとなるように塗工乾燥してアンダ
ー層を形成し、透明性基材を作製した。
[ポリビニルピロリドン(K−90 G.A.F社製)
5部 メタノール 95部] しかるのち下記組成のインク受容層用塗液を乾
燥後の塗布厚が3〜4μmとなるように塗布乾燥
してインク受容層を形成し、本発明の記録シート
を得た。
5部 メタノール 95部] しかるのち下記組成のインク受容層用塗液を乾
燥後の塗布厚が3〜4μmとなるように塗布乾燥
してインク受容層を形成し、本発明の記録シート
を得た。
[ポリ(エチルオキサゾリン) 30部
(ダウケミカル社製XAS−10874−05の
MEK10%溶液) イソシアネート変性ポリエチレンオキサイド (明成化学工業社製アクアプレンL−713のト
リクレン15%溶液) 30部 トルエン 15部 MEK 15部 微粉末シリカ 0.01部 (徳山ソーダ社製フアインシールX−37)] 上記の記録シートのオンデマンド型インクジエ
ツト記録装置(インクジエツトカラーイメージプ
リンター型式10−0700、シヤープ社製)に適用し
た黄、赤、青および黒色の4種のインクを使用し
カラー記録をおこなつた。
MEK10%溶液) イソシアネート変性ポリエチレンオキサイド (明成化学工業社製アクアプレンL−713のト
リクレン15%溶液) 30部 トルエン 15部 MEK 15部 微粉末シリカ 0.01部 (徳山ソーダ社製フアインシールX−37)] 上記の記録シートのオンデマンド型インクジエ
ツト記録装置(インクジエツトカラーイメージプ
リンター型式10−0700、シヤープ社製)に適用し
た黄、赤、青および黒色の4種のインクを使用し
カラー記録をおこなつた。
その結果、記録数分後に触媒してもインクが指
に付着することがなく本発明の記録シートのイン
ク受容層がすぐれた吸収性を有することが確認さ
れた。
に付着することがなく本発明の記録シートのイン
ク受容層がすぐれた吸収性を有することが確認さ
れた。
次にカラー記録が施された本発明の記録シート
を市販のOHP装置(リコーOHP Wide、リコー
社製)にセツトし、スクリーンに画像を投影した
ところ鮮明なカラー画像が投影された。
を市販のOHP装置(リコーOHP Wide、リコー
社製)にセツトし、スクリーンに画像を投影した
ところ鮮明なカラー画像が投影された。
実施例 2
実施例1の透明性基材上に下記組成のインク受
容層塗液を塗布したことを除いて全て実施例1と
同要領にて本発明の記録シートを得た。
容層塗液を塗布したことを除いて全て実施例1と
同要領にて本発明の記録シートを得た。
[ポリ(エチルオキサゾリン) 30部
(ダウケミカル社製XAS−10874−05の
MEK10%溶液) イソシアネート変性ポリエチレンオキサイド (明成化学工業社製アクアプレンL−713のト
リクレン15%溶液) 30部 ポリエステル樹脂(東洋紡社製バイロン
5500MEK10%溶液) 15部 トルエン 30部 MEK 30部 微粉末シリカ 0.015部] 上記の記録シートについて実施例1と同じ手順
で評価をおこなつたところ、インク吸収性、
OHPによる投影画像の鮮明性においてすぐれた
特性を有することが認められた。
MEK10%溶液) イソシアネート変性ポリエチレンオキサイド (明成化学工業社製アクアプレンL−713のト
リクレン15%溶液) 30部 ポリエステル樹脂(東洋紡社製バイロン
5500MEK10%溶液) 15部 トルエン 30部 MEK 30部 微粉末シリカ 0.015部] 上記の記録シートについて実施例1と同じ手順
で評価をおこなつたところ、インク吸収性、
OHPによる投影画像の鮮明性においてすぐれた
特性を有することが認められた。
実施例 3
厚さ100μmのポリエチレンテレフタレートフ
イルムかななる透明性基材の上に下記組成のイン
ク受容層用塗液を乾燥後の塗布厚が5〜6μmに
なるよう塗布乾燥してインク受容層を形成し本発
明の記録シートを得た。
イルムかななる透明性基材の上に下記組成のイン
ク受容層用塗液を乾燥後の塗布厚が5〜6μmに
なるよう塗布乾燥してインク受容層を形成し本発
明の記録シートを得た。
[ポリ(エチルオキサゾリン) 15部
(ダウケミカル社製XAS−10874−05の
MEK10%溶液) イソシアネート変性ポリエチレンオキサイド (明成化学工業社製アクアプレンL−713のト
リクレン15%溶液) 45部 トルエン 15部 MEK 15部 微粉末シリカ 0.1部 (徳山ソーダ社製フアインシールX−37)] 以上の記録シートについて実施例1と同じ手順
で評価をおこなつたところ、インク吸収性、
OHPによる投影画像の鮮明性について全く問題
がなく実用上十分耐えうるものであることを確認
した。
MEK10%溶液) イソシアネート変性ポリエチレンオキサイド (明成化学工業社製アクアプレンL−713のト
リクレン15%溶液) 45部 トルエン 15部 MEK 15部 微粉末シリカ 0.1部 (徳山ソーダ社製フアインシールX−37)] 以上の記録シートについて実施例1と同じ手順
で評価をおこなつたところ、インク吸収性、
OHPによる投影画像の鮮明性について全く問題
がなく実用上十分耐えうるものであることを確認
した。
比較例
ポリ(エチルオキサゾリン)を添加しなかつた
ことを除き、実施例1と同様な方法により比較用
の記録シートを得た。この記録シートに対して実
施例1と同様なインクジエツト記録したところ、
30分以上経過しても触指による指へのインク付着
が生じインク受容層のインク吸収性および乾燥性
がきわめて不良であつた。
ことを除き、実施例1と同様な方法により比較用
の記録シートを得た。この記録シートに対して実
施例1と同様なインクジエツト記録したところ、
30分以上経過しても触指による指へのインク付着
が生じインク受容層のインク吸収性および乾燥性
がきわめて不良であつた。
<発明の効果>
本発明は上記のごとき構成であるので、インク
ジエツトプリンターの水性インクに対する吸収
性、乾燥性がすぐれ、又、透明性においても全く
問題のないすぐれた透明性記録シートを得ること
ができる。
ジエツトプリンターの水性インクに対する吸収
性、乾燥性がすぐれ、又、透明性においても全く
問題のないすぐれた透明性記録シートを得ること
ができる。
Claims (1)
- 【特許請求の範囲】 1 透明性を有する基材上に下記構造式(1)を有す
るポリ(エチルオキサゾリン)を含有するインク
受容層を設けてなることを特徴とする記録シー
ト。 (但し、nは正の整数)