JPH03244670A - 反応染料組成物ならびにそれを用いて繊維材料を染色または捺染する方法 - Google Patents
反応染料組成物ならびにそれを用いて繊維材料を染色または捺染する方法Info
- Publication number
- JPH03244670A JPH03244670A JP4356490A JP4356490A JPH03244670A JP H03244670 A JPH03244670 A JP H03244670A JP 4356490 A JP4356490 A JP 4356490A JP 4356490 A JP4356490 A JP 4356490A JP H03244670 A JPH03244670 A JP H03244670A
- Authority
- JP
- Japan
- Prior art keywords
- dyeing
- reactive dye
- parts
- formula
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〈産業上の利用分野〉
本発明はヒドロキシル基及び/又はアミド基を含有する
材料、特にセルロース繊維、天然又は合成ポリアミド繊
維、ポリウレタン繊維あるいは皮革等、更にはそれらの
混紡繊維を染色及び捺染するに適し、針先堅牢かつ耐湿
潤堅牢な染色を可能にする改良された反応染料組成物並
びにその適用に関する。
材料、特にセルロース繊維、天然又は合成ポリアミド繊
維、ポリウレタン繊維あるいは皮革等、更にはそれらの
混紡繊維を染色及び捺染するに適し、針先堅牢かつ耐湿
潤堅牢な染色を可能にする改良された反応染料組成物並
びにその適用に関する。
〈従来の技術〉
ヒドロキシル基及び/又はアミド基を含有する材料の染
色に用いられる反応染料として有用な化合物であり、ビ
ニルスルホン系反応基と色素母体がトリアジン環で連結
した化合物は、例えば、特開昭50−178号公報など
に記載されて公知である。
色に用いられる反応染料として有用な化合物であり、ビ
ニルスルホン系反応基と色素母体がトリアジン環で連結
した化合物は、例えば、特開昭50−178号公報など
に記載されて公知である。
〈発明が解決しようとする課題〉
基を表す。〕
従来、この種の反応染料は繊維材料の染色及び捺染の分
野に広く使用されている。しかし現在の技術水準は、特
定の染色法に対する適性に関する高い要求水準ならびに
染色物の堅牢性および染色性に関する要求の高度化の点
から十分に満足すべきものではない。
野に広く使用されている。しかし現在の技術水準は、特
定の染色法に対する適性に関する高い要求水準ならびに
染色物の堅牢性および染色性に関する要求の高度化の点
から十分に満足すべきものではない。
前記した公知の反応染料も、溶解性、経時安定性及び堅
牢性(例えば酸加水分解堅牢度)の面で更に改良される
ことが強く望まれている。
牢性(例えば酸加水分解堅牢度)の面で更に改良される
ことが強く望まれている。
本発明者らは、上述の公知染料を改良し、さらに染料に
対して要求される要件を広く満足できる新規な反応染料
を見い出す目的で鋭意検討した結果、本発明を完成した
。
対して要求される要件を広く満足できる新規な反応染料
を見い出す目的で鋭意検討した結果、本発明を完成した
。
〈課題を解決する為の手段〉
本発明は、遊離酸の形で下記一般式(I)〔式中、Zは
−[H=c)12又は−CH2CH2Z、を表し、Zl
はアルカリの作用で脱離する基を表す。〕で示される反
応染料と、該染料に対して10〜100重量%の、遊離
酸の形で下記一般式(n)〔式中、Z’ バーCH=C
Ha又1t −CH2CH2Z、を表し、Z2はアルカ
リの作用で脱離する基を表す。〕 で示される反応染料を含有することを特徴とする反応染
料組成物、およびそれを用いることを特徴とする繊維材
料を染色または捺染する方法を提供するものである。
−[H=c)12又は−CH2CH2Z、を表し、Zl
はアルカリの作用で脱離する基を表す。〕で示される反
応染料と、該染料に対して10〜100重量%の、遊離
酸の形で下記一般式(n)〔式中、Z’ バーCH=C
Ha又1t −CH2CH2Z、を表し、Z2はアルカ
リの作用で脱離する基を表す。〕 で示される反応染料を含有することを特徴とする反応染
料組成物、およびそれを用いることを特徴とする繊維材
料を染色または捺染する方法を提供するものである。
本発明組成物における一般式(I)および(II>で示
される反応染料は、それぞれ遊離酸の形で、またはその
塩の形で存在し、特にアルカリ金属塩およびアルカリ土
類金属塩、中でもソーダ塩、カリ塩、リチウム塩が好ま
しい。
される反応染料は、それぞれ遊離酸の形で、またはその
塩の形で存在し、特にアルカリ金属塩およびアルカリ土
類金属塩、中でもソーダ塩、カリ塩、リチウム塩が好ま
しい。
一般式(1)および(If)で示される反応染料は特開
昭50−178号公報に記載された方法で製造すること
ができる。
昭50−178号公報に記載された方法で製造すること
ができる。
本発明の染料組成物は、前記一般式(I)おび(II)
で示されるモノアゾ反応染料を混合することによって得
られるが、−1式(II)で示される反応染料の混合量
は、一般式(I)の反応染料に対して、10〜100重
量%である。
で示されるモノアゾ反応染料を混合することによって得
られるが、−1式(II)で示される反応染料の混合量
は、一般式(I)の反応染料に対して、10〜100重
量%である。
本発明においては、前記一般式(1)および(■)で示
されるモノアゾ反応染料は、それぞれの合成時において
同時に合成されることで混合されていてもよく、又、別
々に合成されたのちに混合されてもよい。さらには、染
色時に混合されても差し支えない。
されるモノアゾ反応染料は、それぞれの合成時において
同時に合成されることで混合されていてもよく、又、別
々に合成されたのちに混合されてもよい。さらには、染
色時に混合されても差し支えない。
本発明組成物は、繊維反応性を有し、ヒドロシキ基含有
またはカルボンアミド基含有材料の染色又は捺染に使用
できる。材料は繊維材料の形で、あるいはその混紡材料
の形で使用されるのが好ましい。
またはカルボンアミド基含有材料の染色又は捺染に使用
できる。材料は繊維材料の形で、あるいはその混紡材料
の形で使用されるのが好ましい。
ヒドロキシ基含有材料は天然又は合成ヒドロキシ基含有
材料、たとえばセルロース繊維材料又はその再生生成物
及びポリビニアルコールなどである。セルロース繊維材
料は木綿、その他の植物繊維、たとえばリネン、麻、ジ
コート及びラミー繊維が好ましい。再生セルロース#a
維はたとえばビスコース・ステーブル及びフィラメント
ビスコースなどである。
材料、たとえばセルロース繊維材料又はその再生生成物
及びポリビニアルコールなどである。セルロース繊維材
料は木綿、その他の植物繊維、たとえばリネン、麻、ジ
コート及びラミー繊維が好ましい。再生セルロース#a
維はたとえばビスコース・ステーブル及びフィラメント
ビスコースなどである。
カルボンアミド基含有材料はたとえば台底及び天然のポ
リアミド及びポリウレタン、特に繊維の形で、たとえば
羊毛及びその他の動物毛、絹、皮革、ポリアミド−6,
6、ポリアミド−6、ポリアミド−11及びポリアミド
−4などである。
リアミド及びポリウレタン、特に繊維の形で、たとえば
羊毛及びその他の動物毛、絹、皮革、ポリアミド−6,
6、ポリアミド−6、ポリアミド−11及びポリアミド
−4などである。
本発明組成物は、上述の材料を、特に上述の繊維材料を
、物理的化学的性状に応じた方法で、染色又は捺染でき
る。
、物理的化学的性状に応じた方法で、染色又は捺染でき
る。
例えば、セルロースm維上に吸尽染色する場合、炭酸ソ
ーダ、第三燐酸ソーダ、苛性ソーダ等の酸結合剤の存在
下、場合により中性塩、例えば芒硝又は食塩を加え、所
望によっては、溶解助剤、浸透剤又は均染剤を併用し、
比較的低い温度で行われる。染料の吸尽を促進する中性
塩は、本来の染色温度に達した後に初めて又はそれ以前
に、場合によっては分割して添加できる。
ーダ、第三燐酸ソーダ、苛性ソーダ等の酸結合剤の存在
下、場合により中性塩、例えば芒硝又は食塩を加え、所
望によっては、溶解助剤、浸透剤又は均染剤を併用し、
比較的低い温度で行われる。染料の吸尽を促進する中性
塩は、本来の染色温度に達した後に初めて又はそれ以前
に、場合によっては分割して添加できる。
バジング法に従ってセルロース繊維を染色する場合、室
温又は高められた温度でパッドし乾燥後、スチーミング
又は乾熱によって固着できる。
温又は高められた温度でパッドし乾燥後、スチーミング
又は乾熱によって固着できる。
セルロース繊維に対して捺染を行う場合、−相で、例え
ば重曹又はその他の酸縮合剤を含有する捺染ペーストで
捺染し、次いで100〜160℃でスチーミングするこ
とによって、あるいは二相で、例えば中性又は弱酸性捺
染ペーストで捺染し、これを熱い電解質含有アルカリ検
温に通過させ、又はアルカリ性電解質含有バジング液で
オーバーバジングし、スチーミング又は乾熱処理して実
施できる。
ば重曹又はその他の酸縮合剤を含有する捺染ペーストで
捺染し、次いで100〜160℃でスチーミングするこ
とによって、あるいは二相で、例えば中性又は弱酸性捺
染ペーストで捺染し、これを熱い電解質含有アルカリ検
温に通過させ、又はアルカリ性電解質含有バジング液で
オーバーバジングし、スチーミング又は乾熱処理して実
施できる。
捺染ペーストには、例えばアルギン酸ソーダ又は澱粉エ
ーテルのような糊剤又は乳化剤が、所望によっては、例
えば尿素のような通常の捺染助剤かつ(又は)分散剤と
併用して用いられる。
ーテルのような糊剤又は乳化剤が、所望によっては、例
えば尿素のような通常の捺染助剤かつ(又は)分散剤と
併用して用いられる。
セルロース繊維上に本発明の染料を固定させるに適した
酸結合剤は、例えばアルカリ金属又はアルカリ土類金属
と無機又は有機酸あるいは加熱状態でアルカリ遊離する
化合物との水溶性塩基性塩である。特にアルカリ金属の
水酸化物及び弱ないし中程度の強さの無機又は有機酸の
アルカリ金属塩が挙げられ、その内、特にソーダ塩及び
カリ塩が好ましい。このような酸結合剤として、例えば
苛性ソーダ、苛性カリ、重曹、炭酸ソーダ、蟻酸ソーダ
、炭酸カリ、第一、第二又は第三燐酸ソーダ、ケイ酸ソ
ーダ、トリクロロ酢酸ソーダ等が挙げられる。
酸結合剤は、例えばアルカリ金属又はアルカリ土類金属
と無機又は有機酸あるいは加熱状態でアルカリ遊離する
化合物との水溶性塩基性塩である。特にアルカリ金属の
水酸化物及び弱ないし中程度の強さの無機又は有機酸の
アルカリ金属塩が挙げられ、その内、特にソーダ塩及び
カリ塩が好ましい。このような酸結合剤として、例えば
苛性ソーダ、苛性カリ、重曹、炭酸ソーダ、蟻酸ソーダ
、炭酸カリ、第一、第二又は第三燐酸ソーダ、ケイ酸ソ
ーダ、トリクロロ酢酸ソーダ等が挙げられる。
台底及び天然のポリアミド及びポリウレタン繊維の染色
は、まず酸性ないし弱酸性の染浴からpH値の制御下に
吸尽させ、次に固着させるため中性、場合によりアルカ
リ性のpH値に変化させることによって行える。染色は
通常60〜120℃の温度で行えるが、均染性を達成す
るために通常の均染剤、例えば塩化シアヌルと3倍モル
のアミノベンゼンスルホン酸又はアミノナフタレンスル
ホン酸との縮合生成物あるいは例えばステアリルアミン
とエチレンオキサイドとの付加生成物を用いることもで
きる。
は、まず酸性ないし弱酸性の染浴からpH値の制御下に
吸尽させ、次に固着させるため中性、場合によりアルカ
リ性のpH値に変化させることによって行える。染色は
通常60〜120℃の温度で行えるが、均染性を達成す
るために通常の均染剤、例えば塩化シアヌルと3倍モル
のアミノベンゼンスルホン酸又はアミノナフタレンスル
ホン酸との縮合生成物あるいは例えばステアリルアミン
とエチレンオキサイドとの付加生成物を用いることもで
きる。
本発明の組成物は繊維材料に対する染色及び捺染におい
て優れた性能を発揮する点に特徴がある。
て優れた性能を発揮する点に特徴がある。
特にセルロース繊維材料の染色に好適であり、良好な耐
光性と耐汗日光性、耐湿潤性、たとえば耐洗濯性、耐過
酸化洗濯性、耐汗性、耐塩素性、耐酸加水分解性及び耐
アルカリ性、更に良好な耐摩擦性と耐アイロン性を有す
る。
光性と耐汗日光性、耐湿潤性、たとえば耐洗濯性、耐過
酸化洗濯性、耐汗性、耐塩素性、耐酸加水分解性及び耐
アルカリ性、更に良好な耐摩擦性と耐アイロン性を有す
る。
また優れたビルドアツプ性、溶解性、均染性及びウオツ
シュオフ性、さらに良好な吸尽・固着性を有する点、染
色温度や染浴比の変動による影響を受けにくく安定した
品質の染色物が得られる点において特徴を有する。
シュオフ性、さらに良好な吸尽・固着性を有する点、染
色温度や染浴比の変動による影響を受けにくく安定した
品質の染色物が得られる点において特徴を有する。
また、得られた染色物のフィックス処理時や樹脂加工時
における変色が少なく、保存時の塩基性物質との接触に
よる変化が少ないことも特徴である。
における変色が少なく、保存時の塩基性物質との接触に
よる変化が少ないことも特徴である。
以下、実施例により本発明の詳細な説明する。
例中、部および%は夫々重量部および重量%を表す。
実施例 1
遊離酸の形で下記構造式(i)
で示されるモノアゾ反応染料100部と遊離酸の形で下
記構造式(u) で示されるモノアゾ反応染料10部とを配合して染料組
成物を得た。この組成物0.1.0.3および0.6部
を、各々水200部に溶解し、芒硝10部と木綿10部
を加え、60℃に昇温し、炭酸ソーダ4部を加えて、1
時間染色した。水洗、ンービング、水洗そして乾燥を行
ない、それぞれ諸堅牢度に優れ、良好なビルドアツプ性
を有する赤色の染色物が得られた。
記構造式(u) で示されるモノアゾ反応染料10部とを配合して染料組
成物を得た。この組成物0.1.0.3および0.6部
を、各々水200部に溶解し、芒硝10部と木綿10部
を加え、60℃に昇温し、炭酸ソーダ4部を加えて、1
時間染色した。水洗、ンービング、水洗そして乾燥を行
ない、それぞれ諸堅牢度に優れ、良好なビルドアツプ性
を有する赤色の染色物が得られた。
実施例 2
実施例1で用いた、構造式(i)で示されるモノアゾ反
応染料100部と実施例1で用いた、構造式(ii)で
示されるモノアゾ反応染料50部とを配合して染料組成
物を得、この0.1.0.3および0.6部を、各々水
200部に溶解し、芒硝10部と木綿10部を加え、6
0℃に昇温し、炭酸ソーダ4部を加えて、1時間染色し
た。水洗、ソーピング、水洗そして乾燥を行ない、それ
ぞれ諸堅牢度に優れ、良好なビルドアツプ性を有する赤
色の染色物が得られた。
応染料100部と実施例1で用いた、構造式(ii)で
示されるモノアゾ反応染料50部とを配合して染料組成
物を得、この0.1.0.3および0.6部を、各々水
200部に溶解し、芒硝10部と木綿10部を加え、6
0℃に昇温し、炭酸ソーダ4部を加えて、1時間染色し
た。水洗、ソーピング、水洗そして乾燥を行ない、それ
ぞれ諸堅牢度に優れ、良好なビルドアツプ性を有する赤
色の染色物が得られた。
実施例 3
実施例1で用いた、構造式(1)で示されるモノアゾ反
応染IF4100部と実施例1で用いた、構造式〈u)
で示されるモノアゾ反応染料100部とを配合して染料
組成物を得、この0.1.0.3および0.6部を、各
々水200部に溶解し、芒硝10部と木綿10部を加え
、60℃に昇温し、炭酸ソーダ4部を加えて、1時間染
色した。水洗、ソーピング、水洗そして乾燥を行ない、
それぞれ諸堅牢度に優れ、良好なビルドアツプ性を有す
る赤色の染色物が得られた。
応染IF4100部と実施例1で用いた、構造式〈u)
で示されるモノアゾ反応染料100部とを配合して染料
組成物を得、この0.1.0.3および0.6部を、各
々水200部に溶解し、芒硝10部と木綿10部を加え
、60℃に昇温し、炭酸ソーダ4部を加えて、1時間染
色した。水洗、ソーピング、水洗そして乾燥を行ない、
それぞれ諸堅牢度に優れ、良好なビルドアツプ性を有す
る赤色の染色物が得られた。
実施例 4
遊離酸の形で下記構造式(iii )
で示されるモノアゾ反応染料100部と遊離酸の形で下
記構造式(iv) で示されるモノアゾ反応染料10部とを配合して染料組
成物を得、この0.1,0.3および0.6部を、各々
水200部に溶解し、芒硝10部と木綿10部を加え、
60℃に昇温し、炭酸ソーダ4部を加えて、1時間染色
した。水洗、ソーピング、水洗そして乾燥を行ない、そ
れぞれ諸堅牢度に優れ、良好なビルドアツプ性を有する
赤色の染色物が得られた。
記構造式(iv) で示されるモノアゾ反応染料10部とを配合して染料組
成物を得、この0.1,0.3および0.6部を、各々
水200部に溶解し、芒硝10部と木綿10部を加え、
60℃に昇温し、炭酸ソーダ4部を加えて、1時間染色
した。水洗、ソーピング、水洗そして乾燥を行ない、そ
れぞれ諸堅牢度に優れ、良好なビルドアツプ性を有する
赤色の染色物が得られた。
実施例 5
遊離酸の形で上記構造式(1)で示されるモノアゾ反応
染料100部と遊離酸の形で上記構造式(iv)で示さ
れるモノアゾ反応染料20部とを配合して染料組成物を
得、この0.1.0.3および0.6部を、各々水20
0部に溶解し、芒硝10部と木綿10部を加え、60℃
に昇温し、炭酸ソーダ4部を加えて、1時間染色した。
染料100部と遊離酸の形で上記構造式(iv)で示さ
れるモノアゾ反応染料20部とを配合して染料組成物を
得、この0.1.0.3および0.6部を、各々水20
0部に溶解し、芒硝10部と木綿10部を加え、60℃
に昇温し、炭酸ソーダ4部を加えて、1時間染色した。
水洗、ソーピング、水洗そして乾燥を行ない、それぞれ
諸堅牢度に優れ、良好なビルドアツプ性を有する赤色の
染色物が得られた。
諸堅牢度に優れ、良好なビルドアツプ性を有する赤色の
染色物が得られた。
実施例 6
実施例1で得られた反応染料組成物を用いて、以下の組
成を持つ、色糊を作った。
成を持つ、色糊を作った。
反応染料組成物 5部尿素
5部アルギン酸ソーダ〈5%〉
元糊 50部熱?lk
25部重曹 2部バラ
ンス 13部この色糊をシル
ケット加工線ブロード上に印捺し、中間乾燥後、100
℃で5分間スチーミングを行い、湯洗い、ソーピング、
湯洗いそして乾燥した。得られた染色物は、諸堅牢度に
優れ、良好なビルドアツプ性を有していた。
5部アルギン酸ソーダ〈5%〉
元糊 50部熱?lk
25部重曹 2部バラ
ンス 13部この色糊をシル
ケット加工線ブロード上に印捺し、中間乾燥後、100
℃で5分間スチーミングを行い、湯洗い、ソーピング、
湯洗いそして乾燥した。得られた染色物は、諸堅牢度に
優れ、良好なビルドアツプ性を有していた。
(以下余白)
Claims (2)
- (1)遊離酸の形で下記一般式 ▲数式、化学式、表等があります▼ 〔式中、Zは−CH=CH_2又は−CH_2CH_2
Z_1を表し、Z_1はアルカリの作用で脱離する基を
表す。〕で示される反応染料と、該染料に対して10〜
100重量%の、遊離酸の形で下記一般式 ▲数式、化学式、表等があります▼ 〔式中、Z′は−CH=CH_2又は−CH_2CH_
2Z_2をあらわし、Z_2はアルカリの作用で脱離す
る基を表す。〕 で示される反応染料を含有することを特徴とする反応染
料組成物。 - (2)請求項1に記載の反応染料組成物を用いることを
特徴とする繊維材料の染色または捺染方法。