JPH03238629A - 光記録媒体 - Google Patents

光記録媒体

Info

Publication number
JPH03238629A
JPH03238629A JP2033782A JP3378290A JPH03238629A JP H03238629 A JPH03238629 A JP H03238629A JP 2033782 A JP2033782 A JP 2033782A JP 3378290 A JP3378290 A JP 3378290A JP H03238629 A JPH03238629 A JP H03238629A
Authority
JP
Japan
Prior art keywords
layer
recording
light
recording layer
optical recording
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2033782A
Other languages
English (en)
Inventor
Toru Yashiro
徹 八代
Yutaka Ueda
裕 上田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ricoh Co Ltd
Original Assignee
Ricoh Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ricoh Co Ltd filed Critical Ricoh Co Ltd
Priority to JP2033782A priority Critical patent/JPH03238629A/ja
Priority to US07/655,058 priority patent/US5242730A/en
Publication of JPH03238629A publication Critical patent/JPH03238629A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 ［産業上の利用分野］ 本発明は、光記録媒体に関する。
［従来の技術］ 従来、基板上に光反射吸収性色素記録膜を設け、この記
録膜に集光したレーザー光を照射することにより、照射
部の記録膜を除去し、孔、又は凹部を形成して光記録を
行う追記型の光記録媒体が、開発、実用化されている（
光デイスク用有機記録材料　ぶんしん出版　安倍）。
二のような媒体の構造は、空気中の異物等の記録層への
付着を防ぐために、２つの記録層を設けた透明基板、又
は、保護基板と記録層を設けた基板を、空隙を介して記
録層が内側になるように貼り合せた構造（エアーサンド
イッチ構造）となっている。
このような、光反射吸収性色素等を記録膜材料に用いて
、光照射により孔又は凹部を形成することにより記録を
行う従来の光記録媒体は、記録の際に形状変化（孔又は
凹）を伴うために、記録層上に密着した保護層を設けた
場合、記録感度が大きく低下してしまうという欠点があ
った。
又、保護層を設けない場合においても、特に高速、高密
度で記録をするためには、大きな記録レーザーパワーを
必要とし、記録レーザーパワーが低いと十分な反射率変
化が得られなかった。
更に孔又は凹部を形成する際に除去した記録膜の一部が
、他の記録膜表面に分解物や溶融物として飛散し、付着
するためにノイズやエラーの発生原因となっていた。
［発明が解決しようとする課題］ 本発明は上記問題点に鑑み、高速、高密度で記録する際
に低いレーザーパワーでも十分な反射率変化を得ること
が出来、除去した記録膜によるノイズやエラーの発生し
ない光記録媒体を提供するものである。
［課題を解決するための手段］ 本発明者らは、前記の課題を解決するため鋭意検討した
結果、基体上の記録層を特定材質の二種から構成するこ
とが有効であることを見出し、本発明に至った。
すなわち、本発明は、基板上に形成された記録層が光照
射により分解変形する第一の層と、第−層が分解変形す
ることにより変形する第二の層からなる光記録媒体にお
いて、前記第一の層が光吸収性有機化合物、前記第二の
層がアンチモンを５０ａｔ＊％以上含有する硫化物層２
−２からなることを特徴とする光記録媒体である。
本発明の光記録媒体の代表的な構成を第１図に示す。
本発明の光記録媒体の最も簡単な構成のものでは、（ａ
）に示すように、基板１上に記録層２−１　、２−２が
形成されていればよいが、（ｂ）　、　（ｃ）に示すよ
うに必要に応じて、基板１と記録層２−１．２−２との
間に下引き層４が、記録層２−１゜２−２上に保護層３
が形成されてもよい。
又、保護層３を設けない場合は、基板１上に光吸収性有
機化合物層２−ｌ、アンチモンを５０ａｔｍ％以上含有
する硫化物層２−２をｌ→２−１→２−２のように順次
積層するが、保護膜３を設けた場合は（ｂ）（ｃ）のよ
うに光吸収性有機化合物層２−１とアンチモンを５０ａ
ｔ１１％以上含有する硫化物層２−２の積層順序はｌ→
２−１→２−２→３でも１−２−２−２−１−３でもよ
い。
光照射による記録は、基板１側からが好ましいが、基板
の光透過性が低い場合は、記録層２−１．２−２側から
でもかまわない。
基板１の材料としては、透明プラスチック基板、ガラス
基板等を用いることができ、具体的には、例えば、ポリ
カーボネート樹脂、ポリオレフィン樹脂、アクリル樹脂
、エポキシ樹脂、石英ガラス等を挙げることができる。
なお、基板の表面には、トラッキング用案内溝や案内ピ
ット、更には、アドレス信号などのプリフォーマットが
形成されていてもよい。
記録層２−１の光吸収性有機化合物としては、光吸収性
色素、光吸収性色素と樹脂の化合物及び混合物、金属微
粒子を分散させた有機材料等を用いることが出来る。具
体的には、例えば光吸収性色素として、シアニン色素、
フタロシアニン色素、ナフタロシアニン色素、スクアリ
リウム色素、ナフトキノン色素、金属インドアニリン色
素、アズレニウム色素等を挙げることができ、混合、化
合する樹脂としては、ポリカーボネイト樹脂、アクリル
樹脂、ビニル樹脂、アルキル樹脂等を挙げることができ
、金属微粒子を分散させた有機材料としては、Ｔｅ／ア
ルキル樹脂、Ｂｉ／アルキル樹脂等を挙げることが出来
る。
好ましくは、光吸収性化合物としては、塗布による成膜
が容易であり高感度で光吸収による分解変形が可能な下
記一般式のシアニン色素を含む化合物が良い。
ＲＩ　　　　Ｒ２ Ｒ，Ｒ２ （式中、Ｒ１，Ｒ２及びＲ３は同じか又は異なっていて
もよくそれぞれはＣ１〜Ｃ６アルキルを表わし、Ｘはハ
ロゲン、過ハロゲン酸、四フッ化ホウ素、トルエンスル
ホン酸又はアルキル硫酸を表わし、Ａはベンゼン環又は
ナフチル環を表わしそしてそれぞれの環上には置換基と
してアルキル、アルコキシ、ヒドロキシ、カルボキシル
、ハロゲン、アリル又はアルキルカルボキシルがあって
もあるいはなくてもよく、モしてｎは０又は１〜３の整
数を表わす） 記録層２−１の膜厚は材料により異なるが１００〜３０
００　Ｋが好ましい。
記録層２−２はアンチモンを５０ａｔＩ１１％以上含有
する硫化物であり、記録層２−１の分解変形により記録
層側に凸形に変形する。
記録層２−２の他の成分元素としては、Ｉｎ。
Ａｕ、Ｓｎ、Ｃｕなどを用いるのが好ましい。
具体的な記録層２−２の材料としては、ＳＥ＋７０１　
ｎ１５ｓ！５＋　　５ｂ７０ｓｎ１５ｓ１５等を挙げる
ことができる。
記録層２−２のｓｂ含有量が５０ａｔＩｍ％未満になる
と膜が変形しにくく記録感度が低下する。
記録層２−２の膜厚は１００〜ａｏｏｏλであり、好ま
しくは、膜変形の容易な１０００λ以下の膜厚が良い。
記録層２−２を形成するには、抵抗加熱方式による真空
蒸着法（単源蒸着法、並びに、多源共蒸着法）によるの
が有利であるが、スパッタ法、ＥＢ蒸着法によってもか
まわない。
下引き層４は、（１）水又はガスなどのバリヤー層、（
２）記録層の保存安定性の確保、（３）反射率の向上、
（４〉プレグルーブの形成などの機能を光記録媒体に付
与するために設けられる。
そして下引き層４の材料としては、前記（１）　、　（
２）を重視すれば高分子材料（アクリル樹脂、エポキシ
樹脂など）、無機化合物（ＳｉＯｚ、ＺｎＳ、ＴｉＮ、
ＳｉＮ、　Ａｌ１２０３など）及び金属や半金属（Ａｕ
、Ｎｉ、Ｃｒ、Ｓｅなど）が使用でき、前記（３）を重
視すれば無機化合物（ＺｎＳ、５ｂｚＳｘ、ＳｎＳ、Ｉ
ｎＳなど）及び金属（ＡＩＩ、Ａｇ、Ａｕなど）が使用
でき、前記（４）を重視すれば各種の紫外線硬化樹脂、
熱硬化性樹脂及び熱可塑性樹脂が使用できる。
下引き層４の厚さは、材料の種類により異なるが、０．
１〜３０μ口くらいが適当である。
保護層３は（１）記録層２をキズ、ホコリ、汚れなどか
ら保護し、（２）記録層２の保存安定性を向上させ、〈
３）反射率を向上せしめる、などのために形成されるも
のである。保護層３の形成材料としては、下引き層４で
あげた材料をそのまま使用することができる。保護層３
の厚さは、下引き層４の場合と同様、材料の種類により
異なるが、０．１−１００μ量くらいが適当である。な
お、保護層３、下引き層４の形成手段としては、無機材
料を形成させる場合には真空成膜方法（蒸着法、スパッ
タ法など）、有機材料を形成させる場合には溶液塗工法
（スピンナーコーティング、スプレーコーティング、浸
漬コーティングなど）等の従来より知られている方法が
採用し得る。
本発明の光記録媒体は、記録層面に、集光したレーザー
ビームを照射することにより、記録層２−１が分解変形
し、この記録層２−１の′分解変形による圧力変化によ
って記録層２−２が記録層側に凸に変形することにより
記録することが出来る。
このとき、記録層２−１を光吸収性有機化合物（特にシ
アニン色素を含む化合物）、記録層２−２をｓｂを５０
ａｔｗ％以上含有する硫化物で構成することにより、従
来用いられている光反射、吸収性色素（シアニン色素な
ど）単層に比べ低記録パワーで大きな反射率変化を得る
ことが出来ることがわかった。
又、本発明の構成では、光吸収性有機化合物２−１の分
解物は、飛散することがないので飛散物によるノイズ増
加も発生しない。
［実施例］ 厚さ１．２關、直径１３０ｎφのポリメチルメタクリレ
ート（ＰＭＭＡ）板上に、アクリル系フォトポリマーに
よりトラッキング用のラセン状案内溝を設けた基板上に
、下記陽、１〜３に示す光吸収性化合物又は光吸収性化
合物と樹脂の混合物を１．２−ジクロルエタン溶液とし
てスピンコードすることにより厚さ約７００五の光吸収
性有機化合物層を形成した。
次に、これらの光吸収性有機化合物層上に抵抗加熱方式
の真空蒸着装置を用いて、Ｓ　ｂ　７０Ｓ　ｎ　＋ｓＳ
　ｌｓ＋　　Ｓ　ｂ　７０Ｉ　ｎ　＋ｓＳ　＋５＋Ｓ　
ｂ　８．Ｓ１５の組成の薄膜をｓｂと金属硫化物（Ｓｎ
Ｓ、ＩｎＳ、５ｂ２Ｓ３）の三原共蒸着により約４００
〜８００λの膜厚で形成し、７種類の本発明に係る光記
録媒体を作成した。
次に上記と同じ基板上に恥１〜３の光吸収性化合物の単
層のみを上記と同じ方法で作成したものを比較サンプル
として作成した。
これらの光記録媒体を光デイスクテスターに装着し、レ
ーザー光波長７８０ｒｖＳＮＡ　（レンズの開口数）　
０．５　、線速度１１．３■／ｓ　、記録レーザーパワ
ー６　ｍＷ、　　９　ａ＋Ｗ、再生レーザーパワー０．
５ｍＷの条件で７．５ＭＨｚ、３．７ＭＨｚの信号を記
録再生し、出力信号振幅をオシロスコープにより測定し
た。
結果は表−１のとおりであり本発明の光記録媒体はいず
れも比較サンプルに比べ大きな出力信号振幅が得られた
。
更にこれらの光記録媒体の記録ピットをＳＥＭにより観
察したところ、本発明の光記録媒体はどれも記録ピット
部の記録膜が記録層側に凸に変形し、記録膜表面には飛
散物がなかった。
これに対して比較例の光記録媒体はピット部の記録膜が
記録層側に凹に変形し、記録膜の分解物や溶融物が記録
膜表面に飛散しているのが認められた。
［発明の効果コ 以上説明したように、本発明の記録媒体は、従来の光反
射吸収性色素単層を記録層とした光記録媒体に比べ、低
いレーザーパワーで大きな反射率変化を得ることができ
、しかも、除去した記録膜によるノイズやエラーが発生
しない。
【図面の簡単な説明】
第１図（ａ）〜（Ｃ）は、本発明の光記録媒体の層構成
を説明する図。 ｌ・・・基板、 ２−１・・・光吸収性有機化合物層、 ２−２・・・アンチモンを５０ａｔｍ％以上含有する硫
化物層、 ３・・・保護層、 ４・・・下引層。 第１図＜ａ）

Claims (2)

    【特許請求の範囲】
  1. （１）基板上に形成された記録層が光照射により分解変
    形する第一の層と、第一の層が分解変形することにより
    変形する第二の層から成る光記録媒体において、前記第
    一の層が光吸収性有機化合物、前記第二の層がアンチモ
    ンを５０ａｔｍ％以上含有する硫化物から成ることを特
    徴とする光記録媒体。
  2. （２）上記光吸収性有機化合物が下記一般式で表わされ
    るシアニン色素を含むことを特徴とする請求項（１）記
    載の光記録媒体。 ▲数式、化学式、表等があります▼ （式中、Ｒ＿１、Ｒ＿２及びＲ＿３は同じか又は異なっ
    ていてもよくそれぞれはＣ＿１〜Ｃ＿６アルキルを表わ
    し、Ｘはハロゲン、過ハロゲン酸、四フッ化ホウ素、ト
    ルエンスルホン酸又はアルキル硫酸を表わし、Ａはベン
    ゼン環又はナフチル環を表わしそしてそれぞれの環上に
    は置換基としてアルキル、アルコキシ、ヒドロキシ、カ
    ルボキシル、ハロゲン、アリル又はアルキルカルボキシ
    ルがあってもあるいはなくてもよく、そしてｎは０又は
    １〜３の整数を表わす）
JP2033782A 1990-02-16 1990-02-16 光記録媒体 Pending JPH03238629A (ja)