JPH03130208A - 歯科用セメント硬化液 - Google Patents
歯科用セメント硬化液Info
- Publication number
- JPH03130208A JPH03130208A JP1266238A JP26623889A JPH03130208A JP H03130208 A JPH03130208 A JP H03130208A JP 1266238 A JP1266238 A JP 1266238A JP 26623889 A JP26623889 A JP 26623889A JP H03130208 A JPH03130208 A JP H03130208A
- Authority
- JP
- Japan
- Prior art keywords
- acid
- weight
- meth
- polymer
- dental cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〈産業上の利用分野〉
本発明は、歯科用セメント硬化液に関し、更に詳細には
、特に歯質への接着性を著しく改善した新規な歯科用セ
メント硬化液に関する。
、特に歯質への接着性を著しく改善した新規な歯科用セ
メント硬化液に関する。
歯科用に供されるグラスアイオノマーセメントは、コン
ポジットレジンなどにくらべて特に歯髄為害作用が極め
て軽微で、しかもエナメル質、象牙質の何れの歯質に対
しても接着性を示し1辺縁封鎖性が良く、前歯部の修復
用と同時に補綴物の合着用、その他仮封用、裏装用、製
造用として有用なものである。
ポジットレジンなどにくらべて特に歯髄為害作用が極め
て軽微で、しかもエナメル質、象牙質の何れの歯質に対
しても接着性を示し1辺縁封鎖性が良く、前歯部の修復
用と同時に補綴物の合着用、その他仮封用、裏装用、製
造用として有用なものである。
〈従来の技術〉
歯科用セメント硬化液は、歯髄刺激性がほとんどなく、
しかも接着性を有する唯一のセメントである。従来より
該歯科用セメント硬化液に関する研究は種々なされてお
り、例えば特公昭54−21858号公報、特公昭55
−8019号公報又は特開昭54−149296号公報
には、所望の処理時間、硬化速度及び破砕抗力を向上さ
せるために、キレート化剤を添加した歯科用セメント組
成物が記載されている。
しかも接着性を有する唯一のセメントである。従来より
該歯科用セメント硬化液に関する研究は種々なされてお
り、例えば特公昭54−21858号公報、特公昭55
−8019号公報又は特開昭54−149296号公報
には、所望の処理時間、硬化速度及び破砕抗力を向上さ
せるために、キレート化剤を添加した歯科用セメント組
成物が記載されている。
しかしながら、前記組成物では、キレート化剤の添加量
をポリカルボン酸に対して、0.01〜10重量%、特
に好ましくは5重量%、即ち10重量%以下としている
ため、歯科用セメント硬化液として重要な接着性につい
ては、充分満足できるものではないのが実状である。
をポリカルボン酸に対して、0.01〜10重量%、特
に好ましくは5重量%、即ち10重量%以下としている
ため、歯科用セメント硬化液として重要な接着性につい
ては、充分満足できるものではないのが実状である。
また特公昭50−26573号公報には、歯科用カルボ
キシレートセメント硬化液が提案されており、操作性及
び破砕抗力が改善されてはいるものの、2塩基以上の有
機酸の添加量がポリカルボン酸に対して0.1〜5.0
重量%と10重量%以下であるため、前記組成物と同様
に充分満足できる接着性が得られない。
キシレートセメント硬化液が提案されており、操作性及
び破砕抗力が改善されてはいるものの、2塩基以上の有
機酸の添加量がポリカルボン酸に対して0.1〜5.0
重量%と10重量%以下であるため、前記組成物と同様
に充分満足できる接着性が得られない。
更に特公昭61−4826号公報には、トリメリット酸
エステルまたはその酸無水物と、エチレン性不飽和結合
を有する重合性化合物の少なくとも1種とで構成される
組成物が、金属、歯牙等に優れた接着性を有することが
提案されている。
エステルまたはその酸無水物と、エチレン性不飽和結合
を有する重合性化合物の少なくとも1種とで構成される
組成物が、金属、歯牙等に優れた接着性を有することが
提案されている。
しかしながら、前記組成物では、歯質に対して30重量
%リン酸水溶液によるエツチング操作が必要であり、従
って、操作が煩雑であり、更には重合性化合物をそのま
ま使用するため、歯髄に対して刺激を与えるという欠点
がある。
%リン酸水溶液によるエツチング操作が必要であり、従
って、操作が煩雑であり、更には重合性化合物をそのま
ま使用するため、歯髄に対して刺激を与えるという欠点
がある。
〈発明が解決しようとする課題〉
本発明の目的は、硬化速度の制御及び破砕抗力に優れ、
しかも特に優れた接着性を有する歯科用セメント硬化液
を提供することにある。
しかも特に優れた接着性を有する歯科用セメント硬化液
を提供することにある。
〈課題を解決するための手段〉
本発明によれば、カルボン酸基を含む重合体を、硬化液
中に40〜50重量%含み、多塩基酸を前記重合体10
0重量部に対し、11〜20重量部含有することを特徴
とする歯科用セメント硬化液が提供される。
中に40〜50重量%含み、多塩基酸を前記重合体10
0重量部に対し、11〜20重量部含有することを特徴
とする歯科用セメント硬化液が提供される。
以下本発明を更に詳細に説明する。
本発明の歯科用セメント硬化液は、特定量のカルボン酸
基を含む重合体と、特定量の多塩基酸とを含むことを特
徴とする。
基を含む重合体と、特定量の多塩基酸とを含むことを特
徴とする。
本発明に用いる重合体は、カルボン酸基を有する重合体
であれば特に限定されるものではなく、例えば(メタ)
アクリル酸、イタコン酸、マレイン酸、グルタコン酸、
アコニット酸、シトラコン酸、メサコン酸、フマル酸、
チグリン酸、クロトン酸、ムコン酸、イソクロトン酸、
3−ブテン酸、桂皮酸、アビエチン酸、無水マレイン酸
、無水イタコン酸又はこれらの置換体もしくは誘導体等
のカルボン酸基を有する不飽和単量体の単独重合体又は
共重合体、更には前記カルボン酸基を有する不飽和単量
体の1種又は2種以上と、例えばメチル(メタ)アクリ
レート、エチル(メタ)アクリレート、2−ヒドロキシ
エチル(メタ)アクリレート、n−プロピル(メタ)ア
クリレート、イソプロピル(メタ)アクリレート、n−
ブチル(メタ)アクリレート、イソブチル(メタ)アク
リレート、デシル(メタ)アクリレート、ラウリル(メ
タ)アクリレート、ステアリル(メタ)アクリレート、
グリシジル(メタ)アクリレート、ジメチルアミノエチ
ル(メタ)アクリレート、(メタ)アクリルアミド、N
、N−ジメチル(メタ)アクリルアミド、酢酸ビニル、
スチレン、α−メチルスチレン、(メタ)アクリロニト
リル、アクロレイン又はこれらの置換体若しくは誘導体
等カルボン酸基を有さない不飽和単量体との共重合体を
好ましく挙げることができる。
であれば特に限定されるものではなく、例えば(メタ)
アクリル酸、イタコン酸、マレイン酸、グルタコン酸、
アコニット酸、シトラコン酸、メサコン酸、フマル酸、
チグリン酸、クロトン酸、ムコン酸、イソクロトン酸、
3−ブテン酸、桂皮酸、アビエチン酸、無水マレイン酸
、無水イタコン酸又はこれらの置換体もしくは誘導体等
のカルボン酸基を有する不飽和単量体の単独重合体又は
共重合体、更には前記カルボン酸基を有する不飽和単量
体の1種又は2種以上と、例えばメチル(メタ)アクリ
レート、エチル(メタ)アクリレート、2−ヒドロキシ
エチル(メタ)アクリレート、n−プロピル(メタ)ア
クリレート、イソプロピル(メタ)アクリレート、n−
ブチル(メタ)アクリレート、イソブチル(メタ)アク
リレート、デシル(メタ)アクリレート、ラウリル(メ
タ)アクリレート、ステアリル(メタ)アクリレート、
グリシジル(メタ)アクリレート、ジメチルアミノエチ
ル(メタ)アクリレート、(メタ)アクリルアミド、N
、N−ジメチル(メタ)アクリルアミド、酢酸ビニル、
スチレン、α−メチルスチレン、(メタ)アクリロニト
リル、アクロレイン又はこれらの置換体若しくは誘導体
等カルボン酸基を有さない不飽和単量体との共重合体を
好ましく挙げることができる。
本発明に用いる前記重合体の配合割合は、硬化液中に4
0〜50重量%の範囲である。配合割合が40重量%未
満の場合には、破砕抗力の低下が著しく、50重量%を
超えると、練和性が非常に悪くなりセメント粉末との混
合が困難となるので前記範囲とする必要がある。また前
記重合体の平均分子量(重合平均)は小さいほど水性分
散液の粘度が下がり練和操作性に適するが、1000未
満ではグラスアイオノマーにおける重合体の特徴が失わ
れ、5oooooを超えると硬化液の粘度が上がり練和
操作性が悪くなるため、1000〜500000の範囲
が好ましく、特に2000〜200000の範囲が望ま
しい。
0〜50重量%の範囲である。配合割合が40重量%未
満の場合には、破砕抗力の低下が著しく、50重量%を
超えると、練和性が非常に悪くなりセメント粉末との混
合が困難となるので前記範囲とする必要がある。また前
記重合体の平均分子量(重合平均)は小さいほど水性分
散液の粘度が下がり練和操作性に適するが、1000未
満ではグラスアイオノマーにおける重合体の特徴が失わ
れ、5oooooを超えると硬化液の粘度が上がり練和
操作性が悪くなるため、1000〜500000の範囲
が好ましく、特に2000〜200000の範囲が望ま
しい。
本発明において、前記重合体を調製するには、公知のラ
ジカル重合、イオン重合又は光重合等により行なうこと
ができる。前記重合反応は公知の方法で行なえばよく、
特に限定されるものではない。例えばラジカル重合にお
いては、反応温度0〜200’C,反応時間1〜20時
間で行なうのが好ましい、温度が0℃未満では反応が遅
延し、高分子量体が得られず、また200℃を超えると
、副反応が発生して、望ましい物性の重合体が得られな
いので好ましくない。反応時間が1時間未満では重合反
応が充分に進まず、モノマーの残留が生じ、収率が低下
するので好ましくない。
ジカル重合、イオン重合又は光重合等により行なうこと
ができる。前記重合反応は公知の方法で行なえばよく、
特に限定されるものではない。例えばラジカル重合にお
いては、反応温度0〜200’C,反応時間1〜20時
間で行なうのが好ましい、温度が0℃未満では反応が遅
延し、高分子量体が得られず、また200℃を超えると
、副反応が発生して、望ましい物性の重合体が得られな
いので好ましくない。反応時間が1時間未満では重合反
応が充分に進まず、モノマーの残留が生じ、収率が低下
するので好ましくない。
本発明に用いる多塩基酸としては、例えば酒石酸、クエ
ン酸、リンゴ酸、マロン酸、マレイン酸。
ン酸、リンゴ酸、マロン酸、マレイン酸。
フマル酸、フタル酸、ピメリン酸、ニコチン酸。
シュウ酸、コハク酸、グルタル酸、グルタミン酸。
グルタチオン酸、オキサロ酢酸、アゼライン酸、アスパ
ラギン酸、アジピン酸、イタコン酸、アコニット酸、メ
サコン酸、ムコン酸、グルタコン酸。
ラギン酸、アジピン酸、イタコン酸、アコニット酸、メ
サコン酸、ムコン酸、グルタコン酸。
シトラコン酸、トリメリット酸、ピロメリット酸等の分
子内に2つ以上のカルボキシル基を有する有機酸又は正
リン酸、ピロリン酸、トリポリリン酸等の無機酸等を好
ましく挙げることができ、使用に際しては、単独若しく
は混合物として用いることができる。
子内に2つ以上のカルボキシル基を有する有機酸又は正
リン酸、ピロリン酸、トリポリリン酸等の無機酸等を好
ましく挙げることができ、使用に際しては、単独若しく
は混合物として用いることができる。
本発明において、前記多塩基酸の配合割合は、前記重合
体100重量部に対して、11〜20重量部の範囲であ
り、好ましくは15〜20重量部の範囲である。配合割
合が11重量部未満では。
体100重量部に対して、11〜20重量部の範囲であ
り、好ましくは15〜20重量部の範囲である。配合割
合が11重量部未満では。
接着性の向上が充分でなく、また20重量部を超える場
合には、崩壊率の低下が著しいので前記範囲とする必要
がある。
合には、崩壊率の低下が著しいので前記範囲とする必要
がある。
本発明の歯科用セメント硬化液を調製するには、前記カ
ルボン酸基を含む重合体と、多塩基酸とを前記特定の含
有割合で水に溶解させることにより得ることができる。
ルボン酸基を含む重合体と、多塩基酸とを前記特定の含
有割合で水に溶解させることにより得ることができる。
本発明において、歯科用セメント硬化液の使用方法は、
例えば本発明の歯科用セメント硬化液と。
例えば本発明の歯科用セメント硬化液と。
公知のセメント粉末とを重量比で1=1〜3:1の範囲
で混合するのが好ましい、前記セメント粉末は、特に限
定されるものではなく、例えばケイ酸塩25〜35重量
%、水酸化物10〜20重量%、金属酸化物2〜15重
量%、フッ化物25〜35重量%、リン酸塩5〜15重
量%及び炭酸塩2〜8重量%の混合物等を使用すること
ができ5酸化亜鉛と、酸化マグネシウムとからなる混合
成分を焼成することにより得られるリン酸亜鉛セメント
用粉末を混合して用いることもできる。前記セメント粉
末の粒径は、100ミクロン以下、好ましくは0.1〜
10ミクロンの粒径範囲が望ましい。また前記セメント
粉末の、粉液比は、充填稠度で練和できれば特に限定さ
れるものではなく、セメント粉末の好ましい表面特性に
よっては、高粉液比のセメント粉末混合物を用いること
ができる。
で混合するのが好ましい、前記セメント粉末は、特に限
定されるものではなく、例えばケイ酸塩25〜35重量
%、水酸化物10〜20重量%、金属酸化物2〜15重
量%、フッ化物25〜35重量%、リン酸塩5〜15重
量%及び炭酸塩2〜8重量%の混合物等を使用すること
ができ5酸化亜鉛と、酸化マグネシウムとからなる混合
成分を焼成することにより得られるリン酸亜鉛セメント
用粉末を混合して用いることもできる。前記セメント粉
末の粒径は、100ミクロン以下、好ましくは0.1〜
10ミクロンの粒径範囲が望ましい。また前記セメント
粉末の、粉液比は、充填稠度で練和できれば特に限定さ
れるものではなく、セメント粉末の好ましい表面特性に
よっては、高粉液比のセメント粉末混合物を用いること
ができる。
〈発明の効果〉
本発明の歯科用セメント硬化液は、カルボン酸基を有す
る重合体と、特定量の多塩基酸とを有するので、特に優
れた接着性及び口内での崩壊率を歯科用セメントに付与
することができる。
る重合体と、特定量の多塩基酸とを有するので、特に優
れた接着性及び口内での崩壊率を歯科用セメントに付与
することができる。
〈実施例〉
次に実施例及び比較例によって具体的に説明する。尚、
例中の分子量はGPc法(ゲルパーミ工−シ巨ンクロマ
トグラフ法)による重量平均分子量を表わす。
例中の分子量はGPc法(ゲルパーミ工−シ巨ンクロマ
トグラフ法)による重量平均分子量を表わす。
大五五よ二重
表1に示す重合体及び多塩基酸を蒸留水に分散させ、歯
科用セメント硬化液を調製した。次いで得られた硬化液
1.0部と、表2に示す歯科セメント用粉末1.8部と
を約30〜60秒間練和し、グラスアイオノマーセメン
トを製造した。次に該グラスアイオノマーセメントを用
いて、牛前歯の象牙質研磨面に、歯科用コバルト・クロ
ム合金棒を合着し、24時間37℃の水中に浸漬した後
、圧縮せん断接着強さを測定した。その結果を表3に示
す。
科用セメント硬化液を調製した。次いで得られた硬化液
1.0部と、表2に示す歯科セメント用粉末1.8部と
を約30〜60秒間練和し、グラスアイオノマーセメン
トを製造した。次に該グラスアイオノマーセメントを用
いて、牛前歯の象牙質研磨面に、歯科用コバルト・クロ
ム合金棒を合着し、24時間37℃の水中に浸漬した後
、圧縮せん断接着強さを測定した。その結果を表3に示
す。
よ較叢土ニュ
歯科用セメント硬化液の組成及び配合量、特に多塩基酸
の量を表1に示すとおり代えた以外は、実施例1〜6と
同様にグラスアイオノマーセメントを調製し、接着強さ
を測定した。その結果を表3に示す。
の量を表1に示すとおり代えた以外は、実施例1〜6と
同様にグラスアイオノマーセメントを調製し、接着強さ
を測定した。その結果を表3に示す。
(以下余白)
表
1
手続補正書、。え。
平成 1年1.0月25日
Claims (1)
- カルボン酸基を含む重合体を、硬化液中に40〜50重
量%含み、多塩基酸を前記重合体100重量部に対し、
11〜20重量部含有することを特徴とする歯科用セメ
ント硬化液。