JP7524571B2 - 化粧材及び化粧材の製造方法 - Google Patents
化粧材及び化粧材の製造方法 Download PDFInfo
- Publication number
- JP7524571B2 JP7524571B2 JP2020053970A JP2020053970A JP7524571B2 JP 7524571 B2 JP7524571 B2 JP 7524571B2 JP 2020053970 A JP2020053970 A JP 2020053970A JP 2020053970 A JP2020053970 A JP 2020053970A JP 7524571 B2 JP7524571 B2 JP 7524571B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- nucleating agent
- decorative material
- base
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本開示は、このような問題に鑑みてなされたもので、その目的とするところは、耐傷性及び強度が高い化粧材及び化粧材の製造方法を提供することにある。
本開示の第一実施形態に係る化粧材について説明する。本実施形態に係る化粧材1は、例えば、建物の床材、特に土足で歩行される空間の床材上に施工される化粧材である。なお、以下の説明では、化粧材1の靴と接触する側を「上」とし、化粧材1が床面に接触する側を「下」として説明する場合がある。
図1は、本開示の実施形態に係る化粧材1の一構成例を説明するための断面図である。図1に示すように、化粧材1は、化粧シート10と、木質基材層31と、裏面接着剤層32と、を備えている。化粧シート10は、プライマー層11と、着色層12と、絵柄層13と、第一接着剤層14と、基材層15と、第二接着剤層16と、高耐傷性層17と、トップコート層18と、を備えている。化粧材1は、木質基材層31、裏面接着剤層32、プライマー層11、着色層12、絵柄層13、第一接着剤層14、基材層15、第二接着剤層16、高耐傷性層17及びトップコート層18がこの順に積層されて構成されている。
以下、各層について詳細に説明する。
木質基材層31の材料としては、例えば、木材単板、木材合板、集成材、パーティクルボード、中密度繊維板、硬質繊維板を採用することができる。また、木質基材層31は、耐水性を備えるMDF等も採用することができる。木質基材層31を有することにより、化粧材1全体としての強度が向上する。また、木質基材層31を有することにより、下地の凹凸の影響を受けにくくなる。
木質基材層31の厚さは、3mm以上6mm以下の範囲内であることが好ましい。木質基材層31の厚さが3mm以上である場合、化粧材1全体の強度がより向上する。また、木質基材層31の厚さが6mm以下である場合、化粧材1の曲げ性が必要以上に高くなりすぎず、施工性がより向上する。
木質基材層31は、表面硬度が必要とされる化粧シートと密着する空間にのみ木質基材を配置し、木質基材の下部に樹脂基材や合板等の基材を貼り合わせた複合基材としても良い。これにより、増し貼りする下地との接着がしやすくなり、床材のゆがみや反りを防止しやすくなる。
化粧シート10のプライマー層11と木質基材層31との間には裏面接着剤層32が形成されている。裏面接着剤層32は、木質基材層31の上に、裏面接着剤層32を形成するための組成物を塗布して形成してもよいし、プライマー層11の着色層12に対向する面と反対側の面上に、裏面接着剤層32を形成するための組成物を塗布して形成してもよい。裏面接着剤層32に含まれる接着剤は、着色層12に含まれる熱可塑性樹脂との組み合わせに応じて、例えば、ウレタン系、アクリル系、ポリエステル系等の中から任意に選択可能である。
高耐傷性層17は、樹脂材料と樹脂材料の結晶化度を向上させる造核剤とを含む層である。本実施形態では、造核剤は、外膜で包含されてベシクル化された造核剤ベシクルの状態で樹脂材料に添加されている。
高耐傷性層17の厚さは、例えば70μm以上110μm以下であることが好ましく、85μm以上95μm以下であることがより好ましい。高耐傷性層17の厚さが70μm以上である場合、靴のかかとや小石等に対する高耐傷性層17の耐傷性が十分に高くなる。また、高耐傷性層17の厚さが110μm以下である場合、化粧材1の曲げ性が必要以上に高くなりすぎず、化粧材1を貼り付ける床材が平面でない場合にも床材に対して密着した状態で施工することができる。
高耐傷性層17を構成する樹脂材料としては、例えば熱可塑性樹脂により構成される。熱可塑性樹脂としては、特に制限はなく、従来の化粧シートで基材層等として用いられていた熱可塑性樹脂と同様の材料を用いることができる。熱可塑性樹脂としては、例えば、ポリエチレン、ポリプロピレン、ポリメチルペンテン、ポリブテン、エチレン-プロピレン共重合体、エチレン-α-オレフィン共重合体、プロピレン-α-オレフィン共重合体等のポリオレフィン樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリテトラメチレンテレフタレート、ポリエチレンナフタレート、ポリエチレンテレフタレート-イソフタレート共重合体、1,4-シクロヘキサンジメタノール共重合ポリエチレンテレフタレート、ポリアリレート、ポリカーボネート等のポリエステル系樹脂、エチレン-酢酸ビニル共重合体、エチレン-ビニルアルコール共重合体、エチレン-(メタ)アクリル酸(エステル)共重合体、エチレン-不飽和カルボン酸共重合体金属中和物(アイオノマー)等のオレフィン系共重合体樹脂等のポリオレフィン系樹脂、ポリ(メタ)アクリロニトリル、ポリメチル(メタ)アクリレート、ポリエチル(メタ)アクリレート、ポリブチル(メタ)アクリレート、ポリアクリルアミド等のアクリル系樹脂、6-ナイロン、6,6-ナイロン、6,10-ナイロン等のポリアミド系樹脂、ポリスチレン、AS樹脂、ABS樹脂等のスチレン系樹脂、ポリ塩化ビニル、ポリ酢酸ビニル、ポリビニルアルコール、ポリビニルアセタール、ポリビニルブチラール等のビニル系樹脂、ポリフッ化ビニル、ポリフッ化ビニリデン、ポリテトラフロロエチレン、エチレン-テトラフロロエチレン共重合体、エチレン-パーフロロアルキルビニルエーテル共重合体等のフッ素系樹脂等、或いはそれらの2種以上の混合物、共重合体、複合体、積層体等を使用できる。
高耐傷性層17はナノサイズの造核剤を含んでいる。ナノサイズの造核剤は、単層膜の外膜を具備するベシクルに内包された、造核剤ベシクルの形でポリプロピレン樹脂に添加されて使用されることが好ましい。また、本実施形態において、高耐傷性層17を構成する樹脂中の造核剤は、当該造核剤の一部を露出させた状態で、ベシクルに内包されていてもよい。高耐傷性層17は造核剤を含むため結晶化度を向上でき、化粧材1の耐擦傷性(耐傷性)を向上することができる。
ナノサイズの造核剤は、平均粒径が可視光の波長領域の1/2以下であることが好ましく、具体的には、可視光の波長領域が400nm以上750nm以下であるので、平均粒径が375nm以下であることが好ましい。
ここで、「主成分」とは、高耐傷性層17を構成する樹脂材料の50質量%以上を占める樹脂材料を示すものとする。
なお、造核剤ベシクルは、例えば、Bangham法、エクストルージョン法、水和法、界面活性剤透析法、逆相蒸発法、凍結融解法、超臨界逆相蒸発法などによって調製される。造核剤ベシクルは、その中でも特に超臨界逆相蒸発法を用いて調整されることが好ましい。
本明細書では、外膜がリン脂質のような生体脂質を含む物質から構成される造核剤ベシクルを、造核剤リポソームと称する。
外膜を構成するリン脂質としては、例えば、ホスファチジルコリン、ホスファチジルエタノールアミン、ホスファチジルセリン、ホスファチジン酸、ホスファチジルグリセロール、ホスファチジルイノシトール、カルジオピン、黄卵レシチン、水添黄卵レシチン、大豆レシチン、水添大豆レシチン等のグリセロリン脂質、スフィンゴミエリン、セラミドホスホリルエタノールアミン、セラミドホスホリルグリセロール等のスフィンゴリン脂質が挙げられる。
造核剤としては、樹脂が結晶化する際に結晶化の起点となる物質であれば特に限定するものではない。造核剤としては、例えば、リン酸エステル金属塩、安息香酸金属塩、ピメリン酸金属塩、ロジン金属塩、ベンジリデンソルビトール、キナクリドン、シアニンブルー及びタルク等が挙げられる。特に、ナノ化処理の効果を最大限に得るべく、非溶融型で良好な透明性が期待できるリン酸エステル金属塩、安息香酸金属塩、ピメリン酸金属塩、ロジン金属塩を用いることが好ましいが、ナノ化処理によって材料自体の透明化が可能な場合には、有色のキナクリドン、シアニンブルー、タルクなども用いることができる。また、非溶融型の造核剤に対して、溶融型のベンジリデンソルビトールを適宜混合して用いるようにしてもよい。
着色層12は、樹脂材料と、染料又は顔料等の着色剤とを含む層である。
着色層12の厚さは、所望の厚さとすることが可能であるが、例えば40μm以上70μm以下であることが好ましく、50μm以上60μm以下であることがより好ましい。着色層12の厚さが40μm以上である場合、顔料による着色効果が十分に発揮できる。また、着色層12の厚さが70μm以下の場合、樹脂材料及び顔料を必要以上に使用することなく着色層12を形成することができる。
着色層12を構成する樹脂材料としては、例えば熱可塑性樹脂により構成される。熱可塑性樹脂としては、特に制限はなく、従来の化粧シートで着色層として用いられていた熱可塑性樹脂と同様の材料を用いることができる。熱可塑性樹脂としては、高耐傷性層17に用いられるのと同様に、例えば、ポリエステル系樹脂、ポリオレフィン樹脂、オレフィン系共重合体樹脂等のポリオレフィン系樹脂、アクリル系樹脂、ポリアミド系樹脂、スチレン系樹脂、ビニル系樹脂、フッ素系樹脂等、或いはそれらの2種以上の混合物、共重合体、複合体、積層体等を使用できる。
着色層12を構成する着色剤としての無機顔料は、隠蔽性を付与するための酸化チタンに代表される公知の無機顔料を用いることができる。隠蔽性が低い場合、絵柄層13と床材の模様が混在し、好ましくない。無機顔料を含有することにより、隠蔽性が良好な化粧材1を得ることができる。
更に、分散性の向上や、押出適正を改善するために脂肪酸金属塩などの添加剤を加えても構わない。
絵柄層13は、着色層12の上面に形成され、例えば、木目模様、石目模様、砂目模様、タイル貼模様、煉瓦積模様、布目模様、皮絞模様、幾何学図形等の柄模様により形成されている。
絵柄層13の厚さは、3μm以上20μm以下の範囲内であることが好ましい。絵柄層13の厚さがこの数値範囲内である場合、印刷を明瞭にすることができるとともに、化粧材1を製造する際の印刷作業性が向上し、かつ製造コストを抑制することができる。
ここで、絵柄層13は、例えば、グラビア印刷法、オフセット印刷法、スクリーン印刷法、静電印刷法、インクジェット印刷法等の各種印刷方法によって形成することができる。これらの印刷方法は、形成する層によって別々に選択してもよいが、同じ方法を選択して一括加工することが効率的である。
基材層15は、樹脂材料、例えば熱可塑性樹脂により構成される。
基材層15の厚さは、160μm以上220μm以下の範囲内であることが好ましく、180μm以上190μm以下であることがより好ましい。基材層15の厚さが160μm以上である場合、下地となる床材の凹凸や段差などを吸収して化粧材1の施工仕上がりを良好にすることができる。また、基材層15の厚さが190μm以下である場合、基材層15を必要以上に厚く形成することがなく、化粧材1の製造コストを削減することができる。
また、基材層15は、高耐傷性層17と同様に造核剤又は造核剤ベシクルを含み、高結晶化されていても良い。
熱可塑性樹脂としては、特に制限はなく、従来の化粧シートで基材層として用いられていた熱可塑性樹脂と同様の材料を用いることができる。熱可塑性樹脂としては、高耐傷性層17に用いられるのと同様に、例えば、ポリエステル系樹脂、ポリオレフィン樹脂、オレフィン系共重合体樹脂等のポリオレフィン系樹脂、アクリル系樹脂、ポリアミド系樹脂、スチレン系樹脂、ビニル系樹脂、フッ素系樹脂等、或いはそれらの2種以上の混合物、共重合体、複合体、積層体等を使用できる。
トップコート層18は、樹脂材料により構成される。トップコート層18を構成する樹脂材料の主成分となる材料は、例えば、ポリウレタン系、アクリルシリコン系、フッ素系、エポキシ系、ビニル系、ポリエステル系、メラミン系、アミノアルキッド系、尿素系などの樹脂材料から適宜選択して用いられる。樹脂材料の形態は、水性、エマルジョン、溶剤系など特に限定されるものではない。樹脂材料の硬化法についても1液タイプ、2液タイプ、紫外線硬化法、熱硬化法、光硬化型など適宜選択して行うことができる。
第一接着剤層14は、基材層15と着色層12及び絵柄層13とを接着するために形成され、第二接着剤層16は、基材層15と高耐傷性層17とを接着するために形成される層である。第一接着剤層14及び第二接着剤層16を構成する材料は特に限定されるものではなく、接着する層間の相性を鑑みてウレタン系樹脂・変性シリコン系樹脂・エポキシ樹脂等の接着剤やポリエステル系樹脂等の粘着剤等公知の材料を適宜使用することができる。また、化粧材1の製造方法によっては第一接着剤層14及び第二接着剤層16は設けられていなくても良い。
プライマー層11としては、例えば、ポリエステル系樹脂、ポリウレタン系樹脂、これらの混合物等を使用することができる。更に、ポリオールとイソシアネートによる2液タイプにすることで、着色層12とプライマー層11との密着性及びプライマー層11自体の凝集力が向上する。ポリオールとしては、例えば、アクリルポリオール、ポリエステルポリオールなどが挙げられる。また、イソシアネートとしては、例えば、トリレンジイソシアネート、4,4’ジフェニルメタンジイソシアネート等の芳香族系、ヘキサメチレンジイソシアネート、イソホロンジイソシアネート、キシレンジイソシアネート等の脂肪族系が挙げられる。プライマー層11は、反応性の早さ、耐熱性の点で芳香族系のポリオールを用いることが好ましい。
プライマー層11の厚みは、1μm以上であることが好ましい。プライマー層11の厚みを1μm以上とすることにより、溶剤によって接着剤が溶解し、プライマー層11が消失して密着性が低下することを防止することができる。
化粧シート10の一製造例について説明する。
まず、着色層12となる着色フィルムを形成する。ポリプロピレン樹脂に無機顔料を添加した無機顔料含有ポリプロピレン樹脂を加熱溶融し、押し出し成形などによって、厚さが40μm以上70μm以下のシート状に成形して着色層12とする。この後、着色フィルム上に、所望の絵柄を印刷によって形成して絵柄層13を形成する。
次に、基材層15となる基材フィルムを形成する。ポリエステル樹脂を加熱溶融し、押し出し成形などによって、厚さが160μm以上220μm以下のシート状に成形して基材層15とする。
ここで、着色フィルム及び基材フィルムは同時に形成されても良く、異なる順序で形成されても良い。
最後に、第二積層体の高耐傷性層17側面にトップコート層18を形成する。
以上により、化粧シート10を形成することができる。
上述した化粧材1は、表面が平坦である場合について説明したが、このような構成に限られない。例えば、図2に示すように、化粧材1は、化粧シート10のトップコート層18、又はトップコート層18及び高耐傷性層17の上面に凹凸を付与してより意匠性が高められていても良い。
以上のような化粧材1は、以下の効果を有する。
(1)本実施形態の化粧材1は、中密度繊維板である木質基材層31を有することが好ましい。
この構成によれば、床材の不陸の影響を受けにくくし、かつ化粧材1全体の強度を向上させることができる。
この構成によれば、プライマー層11と木質基材層31との間の密着性が向上させることができる。
この構成によれば、耐傷性に優れ、重歩行時における靴のかかとや小石による傷の発生を抑制可能な化粧材1を提供することができる。
この構成によれば、高耐傷性層17を構成する樹脂材料の結晶化度が十分に向上し、重歩行時に要求される耐傷性を十分に有する化粧材1を得ることができる。
この構成によれば、高耐傷性層17を構成する樹脂材料の結晶化度が十分に向上し、重歩行時に要求される耐傷性を十分に有する化粧材1を得ることができる。
この構成によれば、高耐傷性層17の主成分である樹脂材料とベシクルとの相溶性を良好なものとすることができる。
(7)本実施形態の化粧材1は、着色層12の一方の面に絵柄層13が設けられていることが好ましい。
この構成によれば、化粧材1の意匠性を向上させることができる。
以下、本開示の第二実施形態に係る化粧材について、図3を用いて説明する。
図3は、本開示の第二実施形態に係る化粧材2の一構成例を説明するための断面図である。本実施形態に係る化粧材2は、化粧材1と同様に、建物の床材、特に土足で歩行される空間の床材上に施工される化粧材である。
すなわち、化粧材2は、高耐傷性層17に代えて高耐傷性層27を備える点で、第一実施形態に係る化粧材1と相違する。
<高耐傷性層>
高耐傷性層27は、樹脂材料と無機材料とを含む層である。第一実施形態にかかる化粧材1では、造核剤を含む樹脂材料によって高い結晶性を有する高耐傷性樹脂シートを形成して高耐傷性層17とした。一方、第二実施形態にかかる化粧シート20及び化粧材2では、硬度の高い無機粒子を含む樹脂材料によって高い硬度を有する高耐傷性樹脂シートを形成して高耐傷性層27とすることで、高耐傷性を有する化粧シート20及び化粧材2を得る。
高耐傷性層27は、例えば、樹脂材料100質量部に対して0.05質量部以上0.5質量部以下の範囲内で無機粒子が添加された樹脂材料により形成される。
以上のような化粧材2は、第一実施形態の効果(5)に加えて以下の効果を有する。
(8)本実施形態の化粧材2は、樹脂材料と無機粒子とを含み、高硬度化された高耐傷性層27を有している。
この構成によれば、耐傷性に優れ、重歩行時における靴のかかとや小石による傷の発生を抑制可能な化粧材2を提供することができる。
以下、本開示の第三実施形態に係る化粧材について、図4を用いて説明する。
図4は、本開示の第三実施形態に係る化粧材3の一構成例を説明するための断面図である。本実施形態に係る化粧材3は、化粧材1と同様に、建物の床材、特に土足で歩行される空間の床材上に施工される化粧材である。
化粧材3は、第一実施形態に係る化粧材1又は第二実施形態に係る化粧材2の木質基材層31側の面に、離型シート41と粘着層42とを備えるタック層40を備えている点で、化粧材1、2と相違する。すなわち、化粧材3は、離型シート41、粘着層42、木質基材層31、裏面接着剤層32、プライマー層11、着色層12、絵柄層13、第一接着剤層14、基材層15、第二接着剤層16、高耐傷性層17又は高耐傷性層27、及びトップコート層18を備えている。
(離型シート)
離型シート41は、従来公知の離型フィルム、セパレート紙、セパレートフィルム、セパ紙、剥離フィルム、剥離紙等の各種形態のものを適宜使用できる。例えば、上質紙、コート紙、含浸紙、プラスチックフィルム等の片面又は両面に離型層を形成したものを用いてもよい。離型層としては、離型性を有する材料であれば、特に限定されないが、例えば、シリコーン樹脂、有機樹脂変性シリコーン樹脂、フッ素樹脂、アミノアルキド樹脂、メラミン系樹脂、アクリル系樹脂、ポリエステル樹脂等を挙げることができる。
粘着層42は、離型シート41及びプライマー層11の双方との親和性が高い材料であれば特に限定されない。粘着層42は、例えば、ポリエステル系、アクリル系、ウレタン系接着剤及び酢酸ビニル系接着剤等を挙げることができる。
粘着層42は、貼り付け面(床材)に対する化粧材3の密着強度が10N/inch以上であることが好ましく、15N/inch以上であることがより好ましく、20N/inch以上であることがさらに好ましい。ここで、本実施形態において、貼り付け面(床材)に対する化粧材3の密着強度は、JISZ0237に準拠した剥離試験を行った場合の剥離強度よって示される。なお、粘着層42と床材との間の密着が得られにくい場合、床材上に粘着層42との密着性が向上するプライマー等を塗布してから化粧材3を貼り合せることが好ましい。
以上のような化粧材3は、第一、第二実施形態の効果(1)~(5)又は(5)及び(6)に加えて、以下の効果を有する。
(9)本実施形態の化粧材3は、化粧材3の下面側に離型シート41と粘着層42とを有するタック層40を有している。
この構成によれば、耐傷性に優れ、重歩行時における靴のかかとや小石による傷の発生を抑制可能な化粧材3の床材への施工性を向上させることができる。
この構成によれば、施工時に床材上に接着剤を塗布して化粧材3を圧着していく施工作業を効率化することができる。
実施例では、第三実施形態で説明した構成のタック層付き化粧シートを作製し、床材上に貼り合せて化粧シートの評価を行った。
厚さ55μmの着色シート(リケンテクノス社製)を着色層として用い、着色シートの一方の表面に、グラビア印刷によりウレタンインキ(東洋インキ株式会社製ラミスター)を用いて木目柄を印刷して絵柄層とした。
また、着色シートの絵柄層形成側面とは反対側の面に、グラビア印刷により2液ウレタン系樹脂を用いて固形分量が1g/m2となるようにして塗工してプライマー層とした。
次に、着色シートの絵柄層形成側面に、基材シートである厚さ190μmの透明ポリエステルフィルムをアクリル系接着剤(東洋モートン株式会社製)を用いてドライラミネートにより貼り合わせた。この後、着色シートと基材シートとを、十分な養生期間を設けてしっかり接着させた。
続いて、高耐傷性層の表面に、紫外線硬化型樹脂(DICグラフィック社製アクリルウレタン樹脂)をコーティングしてトップコート層を形成して、化粧シートを作製した。
造核剤ベシクルではなく無機粒子をポリプロピレン樹脂に混合して高耐傷性層を形成した以外は実施例1と同様にして実施例2の化粧材を形成した。
基材層を設けなかった以外は実施例1と同様にして実施例3の化粧材を形成した。
アクリル系粘着剤として、JISZ0237に準拠した剥離試験を行った場合の値が10N/inch未満の粘着強度がある粘着剤Bを用いた以外は、実施例と同様にして実施例4の化粧材を形成した。
高耐傷性層を設けなかった以外は実施例1と同様にして比較例1の化粧材を形成した。
アクリル粘着剤として粘着剤Bを用いた。また、木質基材層を設けなかった。それ以外は実施例1と同様にして比較例2の化粧材を形成した。
(a)表面凹凸評価
実施例1~4及び比較例1,2の化粧材を表面に凹凸のある床上に貼り合わせ、化粧材の表面を指で触り、表面の凹凸の状態をA、B、C、Dの4段階で評価した。
(b)耐傷性の評価1(摩耗試験)
実施例1~4及び比較例1,2の化粧材をビニル床上に貼り合せ、フローリングの日本農林規格(JAS:Japanese Agricultural Standards)に規定された摩耗A試験を3000回クリアできるか否かを確認した。
実施例1~4及び比較例1,2の化粧材のそれぞれの表面を10円硬貨で強く引っ掻き、連続的な傷跡が生じるか否かを確認した。この試験では、3か所を硬貨で引っ掻き、傷跡が生じた本数を確認した。
実施例1~4及び比較例1,2の化粧材をビニル床上に貼り合せ、貼り合せ30日後においてビニル床に対する化粧材の接着性を目視にて確認した。
ここで、表面凹凸評価において、「A」は表面に凹凸が全くなく、平滑であるように感じる場合を示し、「B」は表面の凹凸をほぼ感じない場合を示し、「C」は表面の一部分に凹凸を感じる場合を示し、「D」は床の凹凸形状に沿って凹凸を感じる場合を示した。
摩耗試験において、「A」は摩耗A試験を3000回以上クリアした場合を示し、「B」は摩耗A試験を2000回以上クリアした場合を示し、「C」は摩耗A試験を1000回以上クリアした場合を示し、「D」は摩耗A試験を1000回以上クリアできなかった場合を示す。
また、スクラッチ試験において、「A」は傷が0本の場合を示し、「B」は傷が1本の場合を示し、「C」は傷が2本の場合を示し、「D」は傷が3本の場合を示す。
また、床材への接着性において、「A」は化粧材の剥がれがない場合を示し、「B」は化粧材の端部に微量の剥がれがある場合を示し、「C」は化粧材の端部に大きな剥がれがある場合を示し、「D」は化粧材が完全に剥がれた場合を示す。
一方、比較例1の化粧材は、摩耗試験を2000回転以上クリアすることができたものの、スクラッチ試験では傷が3本生じてしまった。
また、比較例2の化粧材は、摩耗A試験を3000回以上クリアでき、スクラッチ試験においても1か所のみ傷が生じた。また、比較例2の化粧材は、表面凹凸評価において表面の一部分に凹凸が感じられた。
また、以上の評価結果から、木質基材層を設けつつJISZ0237に準拠した剥離試験を行った場合の剥離強度が10N/inch以上の粘着剤を用いて形成した粘着層を有する化粧シートは、床材への接着性が30日経過後でも良好であることが確認された。
また、以上の評価結果から、造核剤ベシクルを含む高耐傷性層を形成した実施例1の化粧材は、無機粒子を含む高耐傷性層を形成した実施例2の化粧材と比較して、スクラッチ試験での評価が高く、局所的な引っ掻き等に対して高い効果を有することが確認された。
また、以上の評価結果から、木質基材層を有する実施例1の化粧材は、木質基材層を有さない比較例2の化粧材と比較してスクラッチ試験での評価が高く、また高い耐傷性を有することが確認された。
また、以上の評価結果から、木質基材層を有する実施例1の化粧材は、木質基材層を有さない比較例2の化粧材と比較して表面凹凸評価が高く、床材の不陸の影響を受けにくいことが確認された。
10,20 化粧シート
11 プライマー層
12 着色層
13 絵柄層
14 第一接着剤層
15 基材層
16 第二接着剤層
17,27 高耐傷性層
18 トップコート層
31 木質基材層
32 裏面接着剤層
40 タック層
41 離型シート
42 粘着層
Claims (17)
- 樹脂材料で構成された基材層と、
前記基材層の一方の面側に設けられ、樹脂材料と造核剤又は無機粒子とを含む高耐傷性層と、
前記基材層の前記高耐傷性層に対向する面と反対側の面に設けられた裏面接着剤層と、
前記裏面接着剤層の前記基材層に対向する面と反対側の面に設けられた木質基材層と、
前記基材層と前記裏面接着剤層との間に備えられ、前記基材層の他方の面に設けられた絵柄層と、
前記絵柄層の前記基材層に対向する面と反対側の面に設けられた着色層と、
前記木質基材層の前記絵柄層形成面と反対側の面に設けられたプライマー層と、
前記プライマー層の前記木質基材層に対向する面と反対側の面に設けられた粘着層と、
前記粘着層の前記プライマー層に対向する面と反対側の面に設けられた離型シートと、
を備える化粧材。 - 樹脂材料で構成された基材層と、
前記基材層の一方の面側に設けられ、樹脂材料と造核剤又は無機粒子とを含む高耐傷性層と、
前記基材層の前記高耐傷性層に対向する面と反対側の面に設けられた裏面接着剤層と、
前記裏面接着剤層の前記基材層に対向する面と反対側の面に設けられた木質基材層と、
を備え、
前記裏面接着剤層の塗布量が、3g/m 2 以上20g/m 2 以下である
化粧材。 - 樹脂材料で構成された基材層と、
前記基材層の一方の面側に設けられ、樹脂材料と造核剤又は無機粒子とを含む高耐傷性層と、
前記基材層の前記高耐傷性層に対向する面と反対側の面に設けられた裏面接着剤層と、
前記裏面接着剤層の前記基材層に対向する面と反対側の面に設けられた木質基材層と、
を備え、
フローリングの日本農林規格に規定された摩耗A試験の基準を3000回以上満たす
化粧材。 - 前記木質基材層が中密度繊維板である
請求項1から3のいずれか1項に記載の化粧材。 - 前記木質基材層の厚さは、3mm以上6mm以下である
請求項1から4のいずれか1項に記載の化粧材。 - 前記高耐傷性層は、単層膜の外膜を具備するベシクルに造核剤が内包された造核剤ベシクルを含む、
請求項1から5のいずれか1項に記載の化粧材。 - 前記造核剤ベシクルは、リン脂質からなる外膜を備える造核剤リポソームである
請求項6に記載の化粧材。 - 前記造核剤ベシクルは、超臨界逆相蒸発法によって単層膜を具備するベシクルに前記造核剤を内包させてベシクル化されている
請求項6又は7に記載の化粧材。 - 前記高耐傷性層は、前記樹脂材料100質量部に対して、0.05質量部以上0.5質量部以下の範囲内で前記造核剤が添加された樹脂材料により形成される
請求項6から8のいずれか1項に記載の化粧材。 - 前記高耐傷性層は、前記無機粒子として、シリカ、ガラス、アルミナ、チタニア、ジルコニア、炭酸カルシウム及び硫酸バリウムの少なくとも一種を含む
請求項1から5のいずれか1項に記載の化粧材。 - 前記高耐傷性層は、前記樹脂材料100質量部に対して、0.05質量部以上0.5質量部以下の範囲内で前記無機粒子が添加された樹脂材料により形成される
請求項10に記載の化粧材。 - 前記高耐傷性層の厚さは、70μm以上110μm以下である
請求項1から11のいずれか1項に記載の化粧材。 - 前記基材層の厚さは、160μm以上220μm以下である
請求項1から12のいずれか1項に記載の化粧材。 - 前記高耐傷性層の前記基材層に対向する面と反対側の面に設けられたトップコート層を備える
請求項1から13のいずれか1項に記載の化粧材。 - 前記粘着層の厚さは、50μm以上100μm以下である
請求項1に記載の化粧材。 - 前記粘着層の密着強度は、10N/inch以上である
請求項1又は15に記載の化粧材。 - 請求項1から16のいずれか1項に記載の化粧材の製造方法であって、
ベシクルに造核剤を内包させて、該造核剤をベシクル化してなる造核剤ベシクルを生成し、
第一樹脂材料を用いて形成された前記基材層の一方の面に、前記造核剤ベシクルを含む第二樹脂材料を用いて前記高耐傷性層を形成する
化粧材の製造方法。