JP7450538B2 - 防音材 - Google Patents
防音材 Download PDFInfo
- Publication number
- JP7450538B2 JP7450538B2 JP2020533499A JP2020533499A JP7450538B2 JP 7450538 B2 JP7450538 B2 JP 7450538B2 JP 2020533499 A JP2020533499 A JP 2020533499A JP 2020533499 A JP2020533499 A JP 2020533499A JP 7450538 B2 JP7450538 B2 JP 7450538B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- sound absorption
- soundproofing material
- bonding
- soundproofing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記繊維材は、1~10μmの平均繊維径および5~200cm3/cm2・secの通気量を有し、
前記接合層は、前記表皮層と前記裏面層とが対面している面全体に対して50~95%の接合面積率を有する防音材を提供する。
[防音材の構成]
図1は、本発明の一実施形態である防音材の構成を模式的に示す斜視図である。防音材10は、繊維材からなる表皮層11と、空隙が連通している多孔質材からなる裏面層13と、接合層12とを備えた積層構成を有する。防音材10は、例えば、輸送機器、建設機械・機器、電子・電気機器、家電などの発音体から発せられる音を吸音するための部材として用いられる。
接合層12は表皮層11と裏面層13とを接合するための層であり、表皮層11と裏面層13とが積層される際に、両層の間に接合材を使用して、後述する所定の接合面積率の範囲となるように形成する。上記接合材としては、形状及び寸法を容易、正確に実現することができて、連通した空隙を実質的に有しない材料を使用する。
上記表皮層11の繊維材は、1~10μmの範囲の平均繊維径および5~200cm3/cm2・secの範囲の通気量を有する。繊維材とは、繊維によってその形状が支持されており、繊維と繊維の間に空間を有し、気体がその空間を通過することができる材料をいう。繊維材は、好ましくはシート状である。不織布、織布及び編み物はここでいう繊維材に含まれる。反対に、樹脂発泡体又は樹脂フィルム材は、仮に通気性を有する材料であってもここでいう繊維材に含まれない。なお、ここでいう繊維の平均繊維径とは、顕微鏡で500倍の拡大写真を取り、その中からスケールで繊維の直径方向の長さを100本分測定し、その平均値を求め、小数点以下1桁を四捨五入したものを意味する。
上記裏面層13は、空隙が連通している多孔質材からなる。空隙が連通している多孔質材としては、吸音材として使用されるものであれば限定されるものではないが、フェルト、合成繊維からなる不織布(ニードルパンチによる合成繊維の混合品又は合成繊維100 %のフェルトを含む)等の繊維材や連続気泡を有するフォーム材等が挙げられる。
さらに、上記繊維材の目付は、50~1500g/m2の範囲が好ましく、100~300g/m2の範囲がより好ましく、200~280g/m2の範囲が特に好ましい。またさらに、上記繊維材の平均見かけ密度は、0.01~0.1g/cm3の範囲が好ましい。
本発明の防音材10は、繊維材からなる表皮層11と、空隙が連通している多孔質材からなる裏面層13とを接合層12により接合して得られる。表皮層11と裏面層13の結合方法としては、前述したように、該両層を、塗工された粘着剤又は両面粘着テープ(基材を有しない基材レス両面粘着テープも含む)を用いて、所定の接合面積率となるように貼り合わせる方法が好ましい。具体的には、表皮層11又は裏面層13のいずれか一方の面に、所定の幅にスリットされた両面粘着テープ(基材レス両面テープも含む)、パンチングされた両面テープ又は離型フィルムにストライプ状やドット状に粘着剤を塗工したシート等により接合層12を所定の接合面積率となるように貼り合わせ、又は転写した後、両層を圧着・接合すれば良い。表皮層11と裏面層13との圧着は、常温の環境下において、非加熱で行うことができる。しかしながら、必要に応じて加熱しながら圧着を行うこともできる。
に準拠して測定した垂直入射吸音率が、1/3オクターブバンドの中心周波数2000、2500、3150および4000Hzの全てにおいて55%以上であることが好ましく、1/3オクターブバンドの中心周波数1600、2000、2500、3150および4000Hzの全てにおいて55%以上であることがより好ましく、1/3オクターブバンドの中心周波数1250、1600、2000、2500、3150、4000Hzの全てにおいて55%以上であることが特に好ましい。
JIS A 1405-2に準拠した音響インピーダンス管(内径:29.0mm)を用いて、1/3オクターブバンド中心周波数1000~4000Hzの周波数範囲で垂直入射吸音率を測定した。具体的には、1000、1250、1600、2000、2500、3150,4000Hzの垂直入射吸音率を測定した。測定は、背後空気層を取らない剛壁密着で行った。防音材として実用上有効か否かについての判定を以下の基準に従い評価した。
顕微鏡で500倍の拡大写真を取り、100本の繊維を任意に選び出し、その平均値を求め、小数点以下1桁を四捨五入し、平均繊維径を求めた。
JIS L 1096に準拠したフラジール形通気性試験機により測定した。フラジール形通気性試験機は、大栄科学精器製作所社製のDAP-360(製品型番)を使用した。測定条件は、差圧125Pa、測定孔径70mmとし、3箇所以上を測定し、その平均値で求めた。
JIS-L-1913-B法に準じて測定した。荷重に関しては、表皮層の場合は20kPa、裏面層の場合は0.02kPaの荷重とし、3箇所以上測定し、その平均値で求めた。
JIS-L-1913に準じて測定した。
ダイヤルゲージにて、測定子の径10mm、終圧0.8Nで3箇所以上測定し、その平均値で求めた。
接合層に用いた材料について、厚さ500μmの試料を準備し、株式会社日立ハイテクサイエンス社製の粘弾性測定装置DMA6100(製品名)を用いて、動的粘弾性を測定し、貯蔵弾性率を求めた。測定条件は、周波数1Hzのせん断ひずみを与えながら、昇温速度5℃/分とし、-80℃から80℃まで温度を変化させ、貯蔵弾性率(G’)を測定し、25℃における値を求めた。
(表皮層)
表皮層として、21cm3/cm2・secの通気量、20g/m2の目付、0.33g/cm3の平均見かけ密度及び0.06mmの厚さを有するポリエステル繊維材を準備した。このポリエステル繊維材は、繊維の平均繊維径が3μmであり、繊維が縦方向に配列している。
裏面層として、165cm3/cm2・secの通気量、200g/m2の目付、0.02g/cm3の平均見かけ密度及び10mmの厚さを有するポリエステル繊維フェルトを準備した。このポリエステル繊維フェルトの繊維の平均繊維径は19μmである。
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5938スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:0.5mm、片面セパ、粘着剤の貯蔵弾性率:3.5×105Pa)を幅5mmおよび幅6mmの棒状に裁断した。裏面層のフェルトを広げその表面に、棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン/スペース/ライン=6mm/5.9mm/5mm/5.9mm/6mmとなるように平行に配置・貼合した。
接合方法を下記とした以外は、実施例1と同様にして防音材を得た。
(接合方法)
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5938スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:0.5mm、片面セパ、粘着剤の貯蔵弾性率:3.5×105Pa)を幅4.8mmの棒状に裁断した。裏面層のフェルトを広げその表面に、棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン/スペース/ライン/スペース/ライン=4.8mm/2.4mm/4.8mm/4.8mm/4.8mm/2.4mm/4.8mmとなるように平行に配置・貼合した。
接合方法を下記とした以外は、実施例1と同様にして防音材を得た。
(接合方法)
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5938スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:0.5mm、片面セパ、粘着剤の貯蔵弾性率:3.5×105Pa)を幅4.8mmの棒状に裁断した。裏面層のフェルトを広げその表面に、棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン/スペース/ライン/スペース/ライン/スペース/ライン=4.8mm/1.2mm/4.8mm/1.2mm/4.8mm/1.2mm/4.8mm/1.2mm/4.8mmとなるように平行に配置・貼合した。
接合方法を下記とした以外は、実施例1と同様にして防音材を得た。
(接合方法)
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5938スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:0.5mm、片面セパ、粘着剤の貯蔵弾性率:3.5×105Pa)を幅6.3mmおよび幅13.6mmの棒状に裁断した。裏面層のフェルトを広げその表面に、棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン/スペース/ライン=6.3mm/1.3mm/13.6mm/1.3mm/6.3mmとなるように平行に配置・貼合した。
接合方法を下記とした以外は、実施例1と同様にして防音材を得た。
(接合方法)
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5938スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:0.5mm、片面セパ、粘着剤の貯蔵弾性率:3.5×105Pa)を幅13.85mmの棒状に裁断した。裏面層のフェルトを広げその表面に、棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン=13.85mm/1.1mm/13.85mmとなるように平行に配置・貼合した。
裏面層を下記とした以外は、実施例1と同様にして防音材を得た。
(裏面層)
裏面層として、32cm3/cm2・secの通気量、250g/m2の目付、0.03g/cm3の平均見かけ密度および厚さ10mmの連続気泡を有するポリウレタン系フォーム材を準備した。
表皮層を下記とした以外は、実施例1と同様にして防音材を得た。
(表皮層)
表皮層として、10μmの平均繊維径、80cm3/cm2・secの通気量、94g/m2の目付、0.02g/cm3の平均見かけ密度及び4mmの厚さを有するアクリル/ポリエステル混合繊維材を準備した。このアクリル/ポリエステル混合繊維材は、アクリル繊維とポリエステル繊維の混合比率がアクリル繊維/ポリエステル繊維=63/37(質量比)であり、繊維の配列はランダムである。このアクリル/ポリエステル混合繊維材の繊維の平均繊維径は10μmであった。
表皮層を下記とした以外は、実施例2と同様にして防音材を得た。
(表皮層)
表皮層として、80cm3/cm2・secの通気量、94g/m2の目付、0.02g/cm3の平均見かけ密度及び4mmの厚さを有するアクリル/ポリエステル混合繊維材を準備した。このアクリル/ポリエステル混合繊維材は、アクリル繊維とポリエステル繊維の混合比率がアクリル繊維/ポリエステル繊維=63/37(質量比)であり、繊維の配列はランダムである。このアクリル/ポリエステル混合繊維材の繊維の平均繊維径は10μmであった。
表皮層を下記とした以外は、実施例3と同様にして防音材を得た。
(表皮層)
表皮層として、80cm3/cm2・secの通気量、94g/m2の目付、0.02g/cm3の平均見かけ密度及び4mmの厚さを有するアクリル/ポリエステル混合繊維材を準備した。このアクリル/ポリエステル混合繊維材は、アクリル繊維とポリエステル繊維の混合比率がアクリル繊維/ポリエステル繊維=63/37(質量比)であり、繊維の配列はランダムである。このアクリル/ポリエステル混合繊維材の繊維の平均繊維径は10μmであった。
裏面層を下記とした以外は、実施例3と同様にして防音材を得た。
(裏面層)
裏面層として、265cm3/cm2・secの通気量、100g/m2の目付、0.02g/cm3の平均見かけ密度及び5mmの厚さを有するポリエステル繊維フェルトを準備した。このポリエステル繊維フェルトの繊維の平均繊維径は19μmであった。
裏面層を下記とした以外は、実施例1と同様にして防音材を得た。
(裏面層)
裏面層として、113cm3/cm2・secの通気量、280g/m2の目付、0.02g/cm3の平均見かけ密度及び14mmの厚さを有するポリエステル繊維フェルトを準備した。このポリエステル繊維フェルトの繊維の平均繊維径は19μmであった。
裏面層を下記とした以外は、実施例2と同様にして防音材を得た。
(裏面層)
裏面層として、113cm3/cm2・secの通気量、280g/m2の目付、0.02g/cm3の平均見かけ密度及び14mmの厚さを有するポリエステル繊維フェルトを準備した。このポリエステル繊維フェルトの繊維の平均繊維径は19μmであった。
表皮層を下記とした以外は、実施例1と同様にして防音材を得た。
(表皮層)
表皮層として、9cm3/cm2・secの通気量、60g/m2の目付、0.12g/cm3の平均見かけ密度及び0.5mmの厚さを有するアクリル/ポリエステル混合繊維材を準備した。このアクリル/ポリエステル混合繊維材は、アクリル繊維とポリエステル繊維の混合比率がアクリル繊維/ポリエステル繊維=80/20(質量比)であり、繊維の配列はランダムである。このアクリル/ポリエステル混合繊維材の繊維の平均繊維径は6μmであった。
表皮層を下記とした以外は、実施例3と同様にして防音材を得た。
(表皮層)
表皮層として、190cm3/cm2・secの通気量、85g/m2の目付、0.14g/cm3の平均見かけ密度及び0.6mmの厚さを有するポリエステル繊維材を準備した。このポリエステル繊維材は、繊維の配列はランダムである。このポリエステル繊維材の繊維の平均繊維径は10μmであった。
接合方法を下記とした以外は、実施例2と同様にして防音材を得た。
(接合方法)
アクリル系粘着剤を使用した新タック化成社製基材レス両面粘着テープ「KF4#100」(商品名、基材:なし、粘着テープ厚さ:0.1mm、両面セパ付、粘着剤の貯蔵弾性率:1.1×105Pa)を幅4.8mmの棒状に裁断した。裏面層のフェルトを広げその表面に、軽剥離側のPETセパを剥がした棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン/スペース/ライン/スペース/ライン=4.8mm/2.4mm/4.8mm/4.8mm/4.8mm/2.4mm/4.8mmとなるように平行に配置・貼合した。
接合方法を下記とした以外は、実施例2と同様にして防音材を得た。
(接合方法)
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5933スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:3.0mm、片面セパ、粘着剤の貯蔵弾性率:3.6×105Pa)を幅4.8mmの棒状に裁断した。裏面層のフェルトを広げその表面に、棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン/スペース/ライン/スペース/ライン=4.8mm/2.4mm/4.8mm/4.8mm/4.8mm/2.4mm/4.8mmとなるように平行に配置・貼合した。
裏面層と接合層を下記とした以外は、実施例8と同様にして防音材を得た。
(裏面層)
裏面層として、110cm3/cm2・secの通気量、300g/m2の目付、0.02g/cm3の平均見かけ密度及び15mmの厚さを有するポリエステル繊維フェルトを準備した。このポリエステル繊維フェルトの繊維の平均繊維径19μmであった。
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5933スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:3.0mm、片面セパ、粘着剤の貯蔵弾性率:3.6×105Pa)を準備した。
表皮層および接合層を用いなかった以外は、実施例1と同様にして裏面層のみからなる防音材を得た。
表皮層を下記とした以外は、実施例3と同様にして防音材を得た。
(表皮層)
表皮層として、197cm3/cm2・secの通気量、85g/m2の目付、0.14g/cm3の平均見かけ密度及び0.6mmの厚さを有するポリエステル繊維材を準備した。このポリエステル繊維材の繊維の平均繊維径は17μmであった。
表皮層を下記とした以外は、実施例3と同様にして防音材を得た。
(表皮層)
表皮層として、0.2cm3/cm2・secの通気量、66g/m2の目付、0.03g/cm3の平均見かけ密度及び2mmの厚さを有する独立気泡タイプのポリエチレンフォーム材を準備した。
接合方法を下記とした以外は、実施例3と同様にして防音材を得た。
(接合方法)
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5938スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:0.5mm、片面セパ、粘着剤の貯蔵弾性率:3.5×105Pa)を100mm×100mmの大きさに裁断した。裏面層のフェルトを広げその表面に、上記粘着テープを配置・貼合した。
接合方法を下記とした以外は、実施例1と同様にして防音材を得た。
(接合方法)
ブチルゴム系粘着剤を使用したマクセル社製両面粘着テープ「No.5938スーパーブチルテープ」(商品名、基材:ポリエチレンネット、粘着テープ厚さ:0.5mm、片面セパ、粘着剤の貯蔵弾性率:3.5×105Pa)を幅4.8mmの棒状に裁断した。裏面層のフェルトを広げその表面に、棒状の粘着テープを、ライン(粘着テープ接合部)/スペース(開口部)/ライン/スペース/ライン=4.8mm/7.2mm/4.8mm/7.2mm/4.8mmとなるように平行に配置・貼合した。
実施例1で用いた表皮層と裏面層とを、粘着テープで接合せずに、単に重ね合わせたものを防音材とした。防音材の総厚さは、10.1mmであった。また、直径28.8mmの吸音率の測定試料において、接合面積率は0%であった。
11 表皮層
12 接合層
13 裏面層
14 通気性の開口部
Claims (13)
- 繊維材からなる表皮層と、表皮層に積層された、空隙が連通している多孔質材からなる裏面層と、該表皮層と裏面層との間に積層された、接合材からなる接合層とを、備えた防音材であって、
前記繊維材は、1~10μmの平均繊維径および5~200cm3/cm2・secの通気量を有し、
前記裏面層は32~300cm 3 /cm 2 ・secの通気量を有し、
前記接合層は、前記表皮層と前記裏面層とが対面する面全体に対して50~95%の接合面積率を有する防音材。 - 前記接合層は、前記表皮層と前記裏面層とが対面する面全体に対して60~95%の接合面積率を有する請求項1に記載の防音材。
- 前記接合材は、塗工された粘着剤又は両面粘着テープである請求項1又は2に記載の防音材。
- 前記塗工された粘着剤又は両面粘着テープの粘着剤は、25℃におけるせん断貯蔵弾性率が1.0×104~1.0×106Paの範囲である請求項3に記載の防音材。
- 前記接合層は、複数の棒状層を形成する請求項1に記載の防音材。
- 前記複数の棒状層は、縞模様を形成する請求項5に記載の防音材。
- 隣り合った棒状層同士の間隔は、1mm以上である請求項6に記載の防音材。
- 前記表皮層は、10~100cm3/cm2・secの通気量を有する請求項1~5のいずれか一項に記載の防音材。
- 前記裏面層は繊維材であって、前記繊維材の目付は、100~300g/m2である請求項1~8のいずれか一項に記載の防音材。
- 前記防音材の総厚さは、5~15mmである請求項1~9のいずれか一項に記載の防音材。
- 前記防音材は、JIS A1405-2に準拠して測定した垂直入射吸音率が、1/3オクターブバンドの中心周波数2000、2500、3150および4000Hzの全てにおいて55%以上である請求項1~10のいずれか一項に記載の防音材。
- 前記防音材は、JIS A1405-2に準拠して測定した垂直入射吸音率が、1/3オクターブバンドの中心周波数1600、2000、2500、3150および4000Hzの全てにおいて55%以上である請求項1~10のいずれか一項に記載の防音材。
- 前記防音材は、JIS A1405-2に準拠して測定した垂直入射吸音率が、1/3オクターブバンドの中心周波数1250、1600、2000、2500、3150、4000Hzの全てにおいて55%以上である請求項1~10のいずれか一項に記載の防音材。