JP7363169B2 - 衛生薄葉紙用包装フィルム及び包装体 - Google Patents
衛生薄葉紙用包装フィルム及び包装体 Download PDFInfo
- Publication number
- JP7363169B2 JP7363169B2 JP2019141493A JP2019141493A JP7363169B2 JP 7363169 B2 JP7363169 B2 JP 7363169B2 JP 2019141493 A JP2019141493 A JP 2019141493A JP 2019141493 A JP2019141493 A JP 2019141493A JP 7363169 B2 JP7363169 B2 JP 7363169B2
- Authority
- JP
- Japan
- Prior art keywords
- vinyl acetate
- ethylene
- weight
- acetate copolymer
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
VAc80 - VAc50 = 30重量%
VAc80 - VAc25 = 55重量%
エチレン-酢酸ビニル共重合体(B)が、前記の2種以上の共重合体組成物である場合、各共重合体の酢酸ビニル含量の差を取った際に、各酢酸ビニル含量の差が全ての組合せにおいて70重量%以下であることが好ましい。これにより得られる組成物からなるフィルムの透明性がより向上する。全ての酢酸ビニル含量の差は、好ましくは60重量%以下である。
(1)メルトマスフローレート(MFR)
ポリ乳酸(A)およびエチレン-酢酸ビニル共重合体のMFRは、メルトインデクサー(宝工業製)にて190℃、2.16kg荷重の条件にて測定した。
(2)酢酸ビニル含有率
酢酸ビニル含有率は、JIS K6924-1に準拠して測定した。
(3)ヘーズ
成形したフィルムをヘーズメーター(日本電色工業製、NDH7000型)にて測定した。
(4)引張試験
成形したフィルムをJIS Z1702のダンベル状試験片に打ち抜き、テンシロン引張試験機(オリエンテック製、RTE-1210)にて、チャック間距離40mm、引張速度500mm/分の条件で測定した。試料が破断した点における強度と伸度(破断伸度[%]=破断に要した引張長さ[mm]/チャック間距離40mm)を計測とした。厚みは各実施例に記載したものである。また、計測はMD、TDの両方に関して行った。
(5)衝撃強度
成形したフィルムをパンクチャー衝撃試験機(東洋精機製、FT-M型)にて、試験容量3Jの条件にて測定した。
(6)ヒートシール
成形したフィルムを2枚重ね、ヒートシールテスター(テスター産業社製、TP-701型)にて160℃、0.2MPa、1秒の条件でシールした後、幅15mmに裁断してテンシロン引張試験機(オリエンテック製、RTE-1210)にて接着強度を測定し、シール性を評価した。シール強度が5N以上のものを「○」、5Nより低いものを「×」とした。
(7)保香性
30cm×30cmに裁断したフィルム上に、紙管に香料が塗布されたトイレットロール1つを置き、フィルムを2つ折りにしてロールを包み込み、重なったフィルム端部をヒートシールテスター(テスター産業社製、TP-701型)にて160℃、0.2MPa、1秒の条件でシールすることでトイレットロールを密封包装した。香りがフィルムの外に漏れだしていないか密封後1日目、2日目、10日間の時点で評価した。評価は密封包装のフィルムに鼻を近づけ匂いの有無を確認する官能的試験で行った。香り漏れがなかったものを「○」、香りが漏れ出たものを「×」とした。また、香り漏れの有無にかかわらず、評価後のフィルムを破って中のトイレットロールの香りを確認したが、いずれもトイレットロールに香りが残っていることを確認した。
生分解性ポリエステル樹脂(A)としてL体比率98.5%、D体比率1.5%、メルトマスフローレイト4g/10分であるポリ乳酸(A-1)(NatureWorks(株)社製、商品名Ingeo4032D)80重量%、エチレン-酢酸ビニル共重合体(B)として酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)20重量%をタンブラー混合機で予備ブレンドしておき、二軸押出機を用い180℃で溶融混練し生分解性ポリエステル樹脂組成物ペレットを得た。
上記生分解性ポリエステル樹脂組成物ペレットをインフレーション成形機(プラコー(株)製、スクリュー径50mmφ)へ供給し、温度200℃、ブローアップ比2.5、引取速度10m/分、フィルム厚み30μmの条件にて製膜することでフィルムを得た。得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
製膜条件を引取り速度30m/分、フィルム厚み10μmとした以外は実施例1と同様の手法によりフィルムを得た。得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)として酢酸ビニル含量80重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-80)(ランクセス(株)製 商品名レバプレン800)20重量%を用いた以外は、実施例2と同様の手法により厚み10μmのフィルムを得た。得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)として酢酸ビニル含量28重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体のケン化度30%の樹脂(B-28-OH)(東ソー(株)製 商品名メルセンH-3051)20重量%を用いた以外は、実施例2と同様の手法により厚み10μmのフィルムを得た。得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)20重量%を下記の組成とした以外は実施例2と同様の手法により厚み10μmのフィルムを得た。なお、2種類のエチレン-酢酸ビニル共重合体(B)は生分解性ポリエステル樹脂(A)とともに一緒にタンブラー混合機に投入して予備ブレンドを行った。以下の実施例も同様である。
・酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)10重量%
・酢酸ビニル含量50重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-50)(ランクセス(株)製 商品名レバプレン500)10重量%
得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)20重量%を下記の組成とした以外は実施例1と同様の手法により厚み30μmのフィルムを得た。
・酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)10重量%
・酢酸ビニル含量50重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-50)(ランクセス(株)製 商品名レバプレン500)5重量%
・酢酸ビニル含量80重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-80)(ランクセス(株)製 商品名レバプレン800)5重量%
得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)20重量%を下記の組成とした以外は実施例2と同様の手法により厚み10μmのフィルムを得た。
・酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)10重量%
・酢酸ビニル含量50重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-50)(ランクセス(株)製 商品名レバプレン500)5重量%
・酢酸ビニル含量80重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-80)(ランクセス(株)製 商品名レバプレン800)5重量%
得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)20重量%を下記の組成とした以外は実施例2と同様の手法により厚み10μmのフィルムを得た。
・酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)10重量%
・酢酸ビニル含量40重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-40)(ランクセス(株)製 商品名レバプレン400)2重量%
・酢酸ビニル含量50重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-50)(ランクセス(株)製 商品名レバプレン500)2重量%
・酢酸ビニル含量70重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-70)(ランクセス(株)製 商品名レバプレン700)2重量%
・酢酸ビニル含量80重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-80)(ランクセス(株)製 商品名レバプレン800)4重量%
得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)として架橋されたエチレン-酢酸ビニル共重合組成物(B-架橋)20重量%を用いた以外は実施例2と同様の手法により厚み10μmのフィルムを得た。但し、架橋されたエチレン-酢酸ビニル共重合組成物(B-架橋)は以下の方法により得た。
・酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)10重量%
・酢酸ビニル含量40重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-40)(ランクセス(株)製 商品名レバプレン400)2重量%
・酢酸ビニル含量50重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-50)(ランクセス(株)製 商品名レバプレン500)2重量%
・酢酸ビニル含量70重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-70)(ランクセス(株)製 商品名レバプレン700)2重量%
・酢酸ビニル含量80重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-80)(ランクセス(株)製 商品名レバプレン800)4重量%
得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
エチレン-酢酸ビニル共重合体(B)としてケン化処理されたエチレン-酢酸ビニル共重合組成物(B-ケン化)20重量%を用いた以外は実施例2と同様の手法により厚み10μmのフィルムを得た。但し、ケン化処理されたエチレン-酢酸ビニル共重合体(B-ケン化)は以下の方法により得た。
生分解性ポリエステル樹脂(A)としてL体比率98.5%、D体比率1.5%、メルトマスフローレイト4g/10分であるポリ乳酸(A-1)(NatureWorks(株)社製 商品名Ingeo4032D)60重量%を用い、エチレン-酢酸ビニル共重合体(B)として酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)40重量%をタンブラー混合機で予備ブレンドしておき、二軸押出機を用い180℃で溶融混練し生分解性ポリエステル樹脂組成物ペレットを得た。
得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
生分解性ポリエステル樹脂(A)としてL体比率98.5%、D体比率1.5%、メルトマスフローレイト4g/10分であるポリ乳酸(A-1)(NatureWorks(株)社製 商品名Ingeo4032D)60重量%を用い、エチレン-酢酸ビニル共重合体(B)40重量%を下記の組成とした以外は実施例11と同様の手法により厚み20μmのフィルムを得た。
・酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)20重量%
・酢酸ビニル含量40重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-40)(ランクセス(株)製 商品名レバプレン400)4重量%
・酢酸ビニル含量50重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-50)(ランクセス(株)製 商品名レバプレン500)4重量%
・酢酸ビニル含量70重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-70)(ランクセス(株)製 商品名レバプレン700)4重量%
・酢酸ビニル含量80重量%、メルトマスフローレイト5g/10分であるエチレン-酢酸ビニル共重合体(B-80)(ランクセス(株)製 商品名レバプレン800)8重量%
得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
生分解性ポリエステル樹脂(A)としてL体比率98.5%、D体比率1.5%、メルトマスフローレイト4g/10分であるポリ乳酸(A-1)(NatureWorks(株)社製 商品名Ingeo4032D)40重量%を用い、エチレン-酢酸ビニル共重合体(B)として酢酸ビニル含量25重量%、メルトマスフローレイト3g/10分であるエチレン-酢酸ビニル共重合体(B-25)(東ソー(株)製 商品名ウルトラセン640)60重量%とした以外は実施例11と同様の手法により厚み20μmのフィルムを得た。得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
低密度ポリエチレン(LDPE)(東ソー(株)社製 商品名ペトロセン186)100重量%を用いた以外は実施例1と同様の手法により厚み20μmのフィルムを得た。得られたフィルムについて前記評価方法で測定した。評価の結果を表1に示す。
市販のポリエチレンテレフタレート(PET)フィルム 厚み:25μmについて前記評価方法で測定した。評価の結果を表1に示す。
Claims (11)
- ポリ乳酸(A)30重量%以上95重量%以下とエチレン-酢酸ビニル共重合体(B)5重量%以上70重量%以下(ここで(A)及び(B)の合計は100重量%とする)とを含む樹脂組成物からなる層を少なくとも一層含む衛生薄葉紙包装用フィルム。
- 前記エチレン-酢酸ビニル共重合体(B)が酢酸ビニル含有量の異なる2種以上のエチ
レン-酢酸ビニル共重合体を含む組成物である請求項1に記載の衛生薄葉紙包装用フィル
ム。 - 前記エチレン-酢酸ビニル共重合体(B)が酢酸ビニル含有量の異なる3種以上のエチ
レン-酢酸ビニル共重合体を含む組成物である請求項1または2いずれか一項に記載の衛
生薄葉紙包装用フィルム。 - 前記エチレン-酢酸ビニル共重合体(B)が、各共重合体の酢酸ビニル含量の差を取っ
た際に、少なくとも1組の共重合体の酢酸ビニル含量の差が40重量%以下となるエチレ
ンー酢酸ビニル共重合体組成物である請求項2または3に記載の衛生薄葉紙包装用フィル
ム。 - 前記エチレン-酢酸ビニル共重合体(B)が、架橋処理された2種以上のエチレン-酢
酸ビニル共重合体を含む組成物である請求項2乃至4いずれか一項に記載の衛生薄葉紙包
装用フィルム。 - 前記エチレン-酢酸ビニル共重合体(B)が、エチレン-酢酸ビニル共重合体(B)の加水分解物を含む請求項1乃至5いずれか一項に記載の衛生薄葉紙包装用フィルム。
- 前記ポリ乳酸(A)およびエチレン-酢酸ビニル共重合体(B)を含
有する樹脂組成物層の厚みが5μm以上50μm以下である請求項1乃至6いずれか一項
に記載の衛生薄葉紙包装用フィルム。 - 前記樹脂組成物層が、ポリ乳酸(A)を50重量%以上95重量%以下、エチレン-酢酸ビニル共重合体(B)を5重量%以上50重量%以下含む請求項1乃至7いずれか一項に記載の衛生薄葉紙包装用フィルム。
- 請求項1乃至8いずれか一項に記載の衛生薄葉紙包装用フィルムでトイレットロールが
包装されているトイレットロール包装体。 - トイレットロールが香り付きトイレットロールである請求項9に記載のトイレットロ
ール包装体。 - 請求項1乃至8のいずれか一項に記載の衛生薄葉紙包装用フィルムで箱入りティッシュ
ペーパーが包装されている箱入りティッシュペーパー包装体。