JP7330365B2 - ネオジム鉄ホウ素磁石材料、製造方法、並びに応用 - Google Patents
ネオジム鉄ホウ素磁石材料、製造方法、並びに応用 Download PDFInfo
- Publication number
- JP7330365B2 JP7330365B2 JP2022513458A JP2022513458A JP7330365B2 JP 7330365 B2 JP7330365 B2 JP 7330365B2 JP 2022513458 A JP2022513458 A JP 2022513458A JP 2022513458 A JP2022513458 A JP 2022513458A JP 7330365 B2 JP7330365 B2 JP 7330365B2
- Authority
- JP
- Japan
- Prior art keywords
- magnet material
- boron magnet
- alloy
- neodymium
- mass percentage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
R:29.5~31.5wt.%、かつRH>1.5wt.%、
Cu:0.05~0.25wt.%、
Co:0.42~2.6wt.%、
Ga:0.20~0.3wt.%、
N:0.25~0.3wt.%、前記NはZr、Nb、Hf、およびTiのうちの1つまたは複数であり、
Al:0.46~0.6wt.%又はAl≦0.04wt.%、ただし、0wt.%ではなく、
B:0.98~1wt.%、
Fe:64~68wt.%、
ここで、前記Rは、希土類元素であり、前記Rには、少なくともNd及びRHが含まれ、前記RHは、重希土類元素であり、前記RHにはTbが含まれ、
前記Tbと前記Coとの質量比は15以下であるが、0ではない。
Nd:27~28wt.%、
Tb:2.8~4wt.%、
Cu:0.05~0.16wt.%、
Co:1.48~2.7wt.%、
Ga:0.2~0.26wt.%、
N:0.25~0.3wt.%、
Al:0.46~0.5wt.%又は0.02~0.04wt.%、
B:0.98~0.99wt.%、
Fe:64~66wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、
ここで、NはZr及び/又はTiであり、
前記Tbは前記Ndと前記Tbの総質量の9.7~13wt.%を占め、
前記Tbと前記Coとの質量比は、(1~15):1である。
Nd:27~28wt.%、
Tb:2.8~4wt.%、
Cu:0.05~0.16wt.%、
Co:1.48~2.7wt.%、
Ga:0.2~0.26wt.%、
N:0.25~0.3wt.%、
Al:0.46~0.5wt.%又は0.02~0.04wt.%、
B:0.98~0.99wt.%、
Fe:64~66wt.%、
Mn:0.01~0.035wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、
ここで、NはZr及び/又はTiであり、
前記Tbは前記Ndと前記Tbの総質量の9.7~13wt.%を占め、
前記Tbと前記Coとの質量比は、(1~15):1である。
Nd:27~28wt.%、
Tb:2.9~3.4wt.%、
Cu:0.05~0.16wt.%、
Co:1.48~2.7wt.%、
Ga:0.2~0.26wt.%、
N:0.26~0.3wt.%、
Al:0.46~0.5wt.%又は0.02~0.04wt.%、
B:0.98~0.99wt.%、
Fe:64~66wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、
ここで、NはZr及び/又はTiであり、
前記Tbは前記Ndと前記Tbの総質量の9.7~11wt.%を占め、
前記Tbと前記Coとの質量比は、(1~3):1である。
Nd:27~28wt.%、
Tb:2.9~3.4wt.%、
Cu:0.05~0.16wt.%、
Co:1.48~2.7wt.%、
Ga:0.2~0.26wt.%、
N:0.26~0.3wt.%、
Al:0.46~0.5wt.%又は0.02~0.04wt.%、
B:0.98~0.99wt.%、
Fe:64~66wt.%、
Mn:0.01~0.035wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、
ここで、NはZr及び/又はTiであり、
前記Tbは前記Ndと前記Tbの総質量の9.7~11wt.%を占め、
前記Tbと前記Coとの質量比は、(1~3):1である。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.15wt.%、
Co:1.49wt.%、
Ga:0.25wt.%、
Zr:0.27wt.%、
Al:0.46wt.%、
B:0.99wt.%、
Fe:65.72wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
Nd:27.13wt.%、
Tb:3.35wt.%、
Cu:0.15wt.%、
Co:1.49wt.%、
Ga:0.25wt.%、
Zr:0.26wt.%、
Al:0.45wt.%、
B:0.99wt.%、
Fe:65.74wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.15wt.%、
Co:1.49wt.%、
Ga:0.25wt.%、
Ti:0.27wt.%、
Al:0.46wt.%、
B:0.99wt.%、
Fe:65.70wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.15wt.%、
Co:1.49wt.%、
Ga:0.25wt.%、
Zr:0.27wt.%、
Al:0.46wt.%、
B:0.99wt.%、
Fe:65.72wt.%、
Mn:0.03wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.15wt.%、
Co:2.6wt.%、
Ga:0.25wt.%、
Zr:0.27wt.%、
Al:0.46wt.%、
B:0.99wt.%、
Fe:64.86wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味する。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.15wt.%、
Co:1.49wt.%、
Ga:0.25wt.%、
Zr:0.3wt.%、
Al:0.46wt.%、
B:0.99wt.%、
Fe:65.72wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.15wt.%、
Co:1.49wt.%、
Ga:0.25wt.%、
Zr:0.27wt.%、
Al:0.03wt.%、
B:0.99wt.%、
Fe:65.72wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.05wt.%、
Co:1.49wt.%、
Ga:0.25wt.%、
Zr:0.27wt.%、
Al:0.46wt.%、
B:0.99wt.%、
Fe:65.72wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
Nd:27.44wt.%、
Tb:2.98wt.%、
Cu:0.15wt.%、
Co:1.49wt.%、
Ga:0.2wt.%、
Zr:0.27wt.%、
Al:0.46wt.%、
B:0.99wt.%、
Fe:65.72wt.%、
パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、残部は不可避的不純物である。
本発明の積極的かつ進歩的な効果は以下の点にある。本出願の磁性体材料は、HcjとBrがいずれも高いとともに、BrとHcjの温度係数が低い。ここで、Hcjは13.39kOe以上に達することができ、Brは26.8kGs以上に達することができ、また、20~100℃のBrの温度係数|α|は0.092(Br)%/℃以下に達することができ、20~100℃のHcj温度係数|β|は0.46(Hcj)%/℃以下に達することができる。
1、本実施例においてネオジム鉄ホウ素磁性体材料の製造に使用された原料としては、主合金がNd28.46Fe66.73B0.99Tb1.2Co1.49Cu0.15Ga0.25Zr0.27Al0.46、副合金がNd20Fe60.36B0.99Tb16Co1.49Cu0.15Ga0.25Zr0.3Al0.46であり、ここで、下付き文字の数値は、各元素が前記主合金または副合金で占める質量百分率であり、ここで主合金と副合金の質量比は88:12であった。
注:100%未満は不可避的不純物である。
注:100%未満は不可避的不純物である。
(1)磁気特性検出
(1)磁気特性の評価:中国計量院のNIM-10000H型BH大塊希土類永久磁石非破壊測定システムを用いてネオジム鉄ホウ素磁石材料の磁気特性検出を行った。以下の表4は、磁気特性検出の結果を示している。
FE-EPMAによる検出:ネオジム鉄ホウ素磁石材料の垂直配向面を研磨し、電界放出電子プローブマイクロアナライザー(FE-EPMA)(日本電子株式会社(JEOL)、8530F)で検出した。まず、FE-EPMAで面走査することにより、磁石におけるTb、Co等の元素の分布を特定し、その後、FE-EPMAで単一点(シングルポイント)定量分析することにより、キー相におけるTb、Co等の元素の含有量を特定する。試験条件は、加速電圧15kv、プローブビーム50nAであった。
Claims (11)
- ネオジム鉄ホウ素磁石材料が提供され、質量百分率で下記の成分を含み、
R:29.5~31.5wt.%、
Cu:0.05~0.25wt.%、
Co:0.42~2.6wt.%、
Ga:0.20~0.3wt.%、
N:0.25~0.3wt.%、前記NはZr、Nb、Hf、およびTiのうちの1つまたは複数であり、
Al:0.46~0.6wt.%、
B:0.98~1wt.%、
Fe:64~68wt.%、
ここで、前記Rは、希土類元素であり、前記Rは、軽希土類元素及びRHであり、前記軽希土類元素は、Ndであり、または、Nd及びPrであり、前記Ndの含有量は、27~28wt.%であり、前記RHは、重希土類元素であり、前記RHにはTbが含まれ、前記RHの含有量は、2.8~4wt.%であり、
前記Tbと前記Coとの質量比は15以下であるが、0ではなく、
前記Nは粒界に分布しており、
前記Coは、粒界三角領域に分布しており、
ネオジム鉄ホウ素磁石材料の粒界三角領域において、前記Tbの分布が前記Coの分布と重なっていない、
ことを特徴とするネオジム鉄ホウ素磁石材料。 - 前記Rの含有量は、30.15~31wt.%であり、および/または、
前記Rにおける前記RHの質量百分率は、9.7~13wt.%であり、および/または、
前記RHの含有量は、2.9~3.4wt.%であり、および/または、
前記Cuの含有量は、0.05~0.16wt.%であり、および/または、
前記Coの含有量は、1.48~2.6wt.%であり、および/または、
前記Gaの含有量は、0.2~0.26wt.%であり、および/または、
前記Nの含有量は、0.26~0.3wt.%であり、および/または、
前記Nの種類は、Zr、Nb、Hf及びTiのうちの1種又は複数種であり、および/または、
前記Alの含有量は、0.46~0.5wt.%であり、および/または、
前記Bの含有量は、0.98~0.99wt.%であり、および/または、
前記Feの含有量は、64~66wt.%であり、および/または、
前記Tbと前記Coの質量比は、(1~15):1であり、および/または、
前記ネオジム鉄ホウ素磁石材料には、Mnがさらに含まれ、および/または、
Tbは前記ネオジム鉄ホウ素磁石材料中の結晶粒の粒界と中心部分において分布する、
ことを特徴とする請求項1に記載のネオジム鉄ホウ素磁石材料。 - 前記Rの含有量は、30.1~30.6wt.%であり、および/または、
前記Rにおける前記RHの質量百分率は、9.7~11wt.%であり、および/または、
前記Coの含有量は、1.48~1.51wt.%であり、および/または、
前記Nの種類は、Zr及び/又はTiであり、および/または、
前記Tbと前記Coの質量比は、(1~3):1であり、および/または、
前記粒界に分布するTbの含有量は、前記結晶粒の中心部分に分布するTbの含有量よりも高い、
ことを特徴とする請求項2に記載のネオジム鉄ホウ素磁石材料。 - 前記Mnの含有量は、0.035wt.%以下であるが0wt.%ではない、
ことを特徴とする請求項2に記載のネオジム鉄ホウ素磁石材料。 - 前記ネオジム鉄ホウ素磁石材料は、質量百分率で下記の成分を含み、Nd:27~28wt.%、Tb:2.8~4wt.%、Cu:0.05~0.16wt.%、Co:1.48~2.6wt.%、Ga:0.2~0.26wt.%、N:0.25~0.3wt.%、Al:0.46~0.5wt.%、B:0.98~0.99wt.%、Fe:64~66wt.%、パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、ここで、NはZr及び/又はTiであり、前記Tbは前記Ndと前記Tbの総質量の9.7~13wt.%を占め、前記Tbと前記Coとの質量比は、(1~15):1である、
ことを特徴とする請求項1に記載のネオジム鉄ホウ素磁石材料。 - 前記ネオジム鉄ホウ素磁石材料は、質量百分率で下記の成分を含み、Nd:27~28wt.%、Tb:2.8~4wt.%、Cu:0.05~0.16wt.%、Co:1.48~2.6wt.%、Ga:0.2~0.26wt.%、N:0.25~0.3wt.%、Al:0.46~0.5wt.%、B:0.98~0.99wt.%、Fe:64~66wt.%、Mn:0.01~0.035wt.%、パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、ここで、NはZr及び/又はTiであり、前記Tbは前記Ndと前記Tbの総質量の9.7~13wt.%を占め、前記Tbと前記Coとの質量比は、(1~15):1であり、
または、前記ネオジム鉄ホウ素磁石材料は、質量百分率で下記の成分を含み、Nd:27~28wt.%、Tb:2.9~3.4wt.%、Cu:0.05~0.16wt.%、Co:1.48~2.6wt.%、Ga:0.2~0.26wt.%、N:0.26~0.3wt.%、Al:0.46~0.5wt.%、B:0.98~0.99wt.%、Fe:64~66wt.%、パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、ここで、NはZr及び/又はTiであり、前記Tbは前記Ndと前記Tbの総質量の9.7~11wt.%を占め、前記Tbと前記Coとの質量比は、(1~3):1であり、
または、前記ネオジム鉄ホウ素磁石材料は、質量百分率で下記の成分を含み、Nd:27~28wt.%、Tb:2.9~3.4wt.%、Cu:0.05~0.16wt.%、Co:1.48~2.6wt.%、Ga:0.2~0.26wt.%、N:0.26~0.3wt.%、Al:0.46~0.5wt.%、B:0.98~0.99wt.%、Fe:64~66wt.%、Mn:0.01~0.035wt.%、パーセントとは、前記ネオジム鉄ホウ素磁石材料における質量百分率を意味し、ここで、NはZr及び/又はTiであり、前記Tbは前記Ndと前記Tbの総質量の9.7~11wt.%を占め、前記Tbと前記Coとの質量比は、(1~3):1である、
ことを特徴とする請求項5に記載のネオジム鉄ホウ素磁石材料。 - ネオジム鉄ホウ素磁石材料を製造するための主合金であって、前記主合金の組成は、Nda-Feb-Bc-Tbd-Coe-Cuf-Gag-Alx-Mny-Nhであり、ここで、a、b、c、d、e、f、g、h、x、及びyは、各元素が前記主合金に占める質量分率であり、aは26~30wt.%であり、bは64~68wt.%であり、cは0.96~1.1wt.%であり、dは0.5~5wt.%であり、eは0.5~2.6wt.%であり、fは0.05~0.3wt.%であり、gは0.05~0.3wt.%であり、xは0.46~0.6wt.%であり、yは0~0.04wt.%であり、hは0.2~0.5wt.%であり、パーセントとは、前記主合金における質量百分率を意味し、前記Nの種類は、Zr、Nb、Hf及びTiのうちの1種又は複数種である、
ことを特徴とする請求項1~6のいずれかの1項に記載のネオジム鉄ホウ素磁石材料を製造するための主合金。 - ネオジム鉄ホウ素磁石材料を製造するための副合金であって、前記副合金の組成は、Ndi-Fej-Bk-Tbl-Com-Cun-Gao-Alr-Mnt-Npであり、ここで、i、j、k、l、m、n、o、p、r及びtは、各元素が前記副合金に占める質量分率であり、iは5~30wt.%であり、jは59~65wt.%であり、kは0.98~1wt.%であり、lは5~25wt.%であり、mは0.5~2.7wt.%であり、nは0.05~0.3wt.%であり、oは0.05~0.3wt.%であり、rは0.46~0.6wt.%であり、tは0~0.04wt.%であり、pは0~0.5wt.%であり、パーセントとは、前記副合金における質量百分率を意味し、前記Nの種類は、Zr、Nb、Hf及びTiのうちの1種又は複数種である、
ことを特徴とする請求項1~6のいずれかの1項に記載のネオジム鉄ホウ素磁石材料を製造するための副合金。 - ネオジム鉄ホウ素磁石材料の製造方法であって、請求項7に記載の前記主合金及び請求項8に記載の前記副合金を用いて二元系合金方法により製造され、前記主合金と前記副合金の質量比は(9~30):1である、
ことを特徴とするネオジム鉄ホウ素磁石材料の製造方法。 - 前記二元系合金方法による製造工程は、主合金と副合金を均一に混合した後に混合合金粉末を得、前記混合合金粉末を順序的に焼結、時効処理を実行させ、
前記した均一に混合することは、主合金と副合金を混合した後、水素破砕とジェットミリング処理を経て均一に混合したり、又は前記主合金と副合金をそれぞれ水素破砕とジェットミリング処理した後、均一に混合することである、
ことを特徴とする請求項9に記載のネオジム鉄ホウ素磁石材料の製造方法。 - 前記水素破砕は、0.067~0.098MPaの水素ガス圧力下で水素飽和吸蔵させ、480℃~530℃内で脱水素させ、
および/または、ジェットミリング処理後の粉体の粒径は3.7~4.2μmであり、
および/または、前記焼結の温度は、1050~1085℃であり、前記焼結時間は4~7時間であり、
および/または、前記時効処理の温度は、460~520℃であり、前記時効処理の時間は、4~10時間である、
ことを特徴とする請求項10に記載のネオジム鉄ホウ素磁石材料の製造方法。