JP7117809B1 - コンクリートスラッジ処理物の製造方法 - Google Patents
コンクリートスラッジ処理物の製造方法 Download PDFInfo
- Publication number
- JP7117809B1 JP7117809B1 JP2022045968A JP2022045968A JP7117809B1 JP 7117809 B1 JP7117809 B1 JP 7117809B1 JP 2022045968 A JP2022045968 A JP 2022045968A JP 2022045968 A JP2022045968 A JP 2022045968A JP 7117809 B1 JP7117809 B1 JP 7117809B1
- Authority
- JP
- Japan
- Prior art keywords
- concrete sludge
- mass
- sludge
- iron
- treated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
項1. コンクリートスラッジに、当該コンクリートスラッジの固形分に対して0.15質量%以上の量となる鉄を含む二価鉄化合物と、当該コンクリートスラッジの固形分に対して0.60質量%以上の量となるリン酸を含むリン酸化合物とを添加し、混合することでアルカリ性の混合物を得る工程、及び得られた混合物を少なくとも1時間保持する工程を含む、コンクリートスラッジ処理物の製造方法。
項2. 二価鉄化合物が、硫酸鉄(II)又は塩化鉄(II)である、項1に記載の製造方法。
項3. リン酸化合物が、オルトリン酸又はその塩である、項1又は2に記載の製造方法。
項4. 二価鉄化合物及びリン酸化合物が、液体に溶解した形態でコンクリートスラッジに添加される、項1~3のいずれか一項に記載の製造方法。
項5. 前記液体の添加量が、コンクリートスラッジ100 gに対して少なくとも1 mLである、項4に記載の製造方法。
項6. 前記液体の添加量が、コンクリートスラッジ100 gに対して1~10 mLである、項4又は5に記載の製造方法。
項7. 混合物が少なくとも24時間保持される、項1~6のいずれか一項に記載の製造方法。
項8. コンクリートスラッジ処理物が、乾燥質量1 g当たり少なくとも3 Lの硫化水素ガス吸着能を有し、かつコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、項1~7のいずれか一項に記載の製造方法。
項9. 濃度3 mg/Lのオゾンガスで10時間曝気した後のコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、項1~8のいずれか一項に記載の製造方法。
項10. 項1~9のいずれか一項に記載の方法により製造されたコンクリートスラッジ処理物で埋立廃棄物を被覆する工程を含む、埋立廃棄物からの硫化水素の放出を抑制するための方法。
項11. 二価鉄化合物及びリン酸化合物を含む、コンクリートスラッジ処理物を製造するためのキットであって、コンクリートスラッジ処理物が、乾燥質量1 g当たり少なくとも3 Lの硫化水素ガス吸着能を有し、かつコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、前記キット。
項12. 鉄に換算した濃度が1.5質量%以上である二価鉄化合物とリン酸に換算した濃度が6.0質量%以上であるリン酸化合物とを、液体に溶解した形態で含む、項11に記載のキット。
項13. 硫酸鉄(II)又は塩化鉄(II)とオルトリン酸とを溶解した液体を含む、項11又は12に記載のキット。
項14. 濃度3 mg/Lのオゾンガスで10時間曝気した後のコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、項11~13のいずれか一項に記載のキット。
項15. セメント水和物と、クロム及び鉄が結合したハイドロキシアパタイトとを含有する、覆土材。
項16. 乾燥質量1 g当たり少なくとも3 Lの硫化水素ガス吸着能を有し、かつ覆土材 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム溶出量が0.05 ppm以下である、項15に記載の覆土材。
項17. 濃度3 mg/Lのオゾンガスで10時間曝気した後の覆土材 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、項16に記載の覆土材。
(1)コンクリートスラッジ処理剤の調製
硫酸鉄(II)7水和物10 gを水で溶解して100 mLとした硫酸鉄(II)水溶液、85%リン酸水溶液(H3PO4、和光純薬)10 gに水を加えて100 mLとしたリン酸水溶液、及び硫酸鉄(II)水溶液とリン酸水溶液を等量混合した硫酸鉄(II)+リン酸水溶液をそれぞれ調製した。硫酸鉄(II)水溶液は2.00質量%の鉄を含有し、リン酸水溶液は8.24質量%のリン酸を含有し、硫酸鉄(II)+リン酸水溶液は、1.00質量%の鉄及び4.12質量%のリン酸を含有する。
上記(1)で調製した硫酸鉄(II)水溶液及びリン酸水溶液を二液型の処理剤として、二液剤を構成するそれぞれの水溶液を等量混合した硫酸鉄(II)+リン酸水溶液を一液型の処理剤として用いて、以下のようにコンクリートスラッジ処理物を調製した。
上記(2)で得られた処理物に等量の水を添加、混合した。静置後、上澄みを採取し、ADVANTEC社製ろ紙5種A(保留粒子径7μm)でろ過した。ろ液を、ADVANTEC社製DISMICシリンジフィルター(孔径0.8μm,セルロースアセテート)を用いて加圧ろ過し、得られたろ液を分析試料として、パックテスト(登録商標)Cr6+(共立化学研究所)により六価クロム濃度を測定し、コンクリートスラッジ処理物からの六価クロムの溶出を評価した。
(1)コンクリートスラッジ処理物の製造
リン酸(H3PO4、和光純薬)10 gに水を加えて200 mLとしたリン酸水溶液に硫酸鉄(II)10 gを溶解して得た硫酸鉄(II)+リン酸水溶液を、一液型の処理剤として用いた。実施例1で調製したクロム添加コンクリートスラッジ200 gに対して、スラッジ質量の0.2、0.5、1.0、1.5、2.0、2.5、3.0、3.5、4、又は4.5質量%相当量の処理剤を添加し、混合して、室温で24時間静置することでコンクリートスラッジ処理物を調製した。スラッジ固形分の質量に対する、添加された処理剤中の鉄及びリン酸の量の割合を表1に示す。
実施例1の(3)と同様にして、上記(2)で得られた処理物から分析試料を調製した。分析試料50 mLを比色管に採取し、硫酸を加えてpHを9以下にした後、ジフェニルカルバジド溶液(10 g/L)を1 mL添加して静置した。5分後、分光光度計(OPTIMA製SP-300)を用いて波長540 nmでの吸光度を測定し、コンクリートスラッジ処理物から溶出した六価クロムの濃度(ppm)を算出した。結果を表1及び図2に示す。
上記(2)の分析試料のpHを測定した。最も多い4.5質量%量の処理剤を添加した処理物であっても、pHは12-13と強アルカリ性を示した。
リン酸(H3PO4、和光純薬)10 gに水を加えて200 mLとしたリン酸水溶液に硫酸鉄(II)10 gを溶解して得た硫酸鉄(II)+リン酸水溶液を、一液型の処理剤として用いた。コンクリートスラッジに酸化クロム(VI)(富士フィルム和光純薬)を添加して、コンクリートスラッジ中の六価クロム濃度を0.2 ppm~10 ppmに調整した。さらに、この10ppmクロム添加コンクリートスラッジにクロム低含有のコンクリートスラッジを添加混合し、六価クロム濃度0.2 ppm~8 ppmのコンクリートスラッジを調製した。これらのクロム添加コンクリートスラッジ(含水率43%)200 gに対して、スラッジ質量の1、2、又は4質量%相当量の処理剤を添加し、混合して、室温で24時間静置することでコンクリートスラッジ処理物を調製した。得られたコンクリートスラッジ処理物について、実施例2(2)と同様にして、コンクリートスラッジ処理物から溶出した六価クロムの濃度(ppm)を算出した。結果を表2及び図3に示す。
実施例1で調製した、硫酸鉄(II)水溶液とリン酸水溶液を等量混合した硫酸鉄(II)+リン酸水溶液を、一液型の処理剤として用いた。コンクリートスラッジ(含水率43%)1000 gに3000 mLの水を加え、酸化クロム(VI)(富士フィルム和光純薬)を添加して六価クロム濃度が4 ppmとなるように調整した後、大きな沈殿物を入れずに上部2500 mLを採取し、スラリー状のクロム添加コンクリートスラッジ(含水率85.7%)とした。
リン酸(H3PO4、和光純薬)10 gに水を加えて200 mLとしたリン酸水溶液に硫酸鉄(II)10 gを溶解して得た硫酸鉄(II)+リン酸水溶液を、一液型の処理剤として用いた。コンクリートスラッジ(含水率43%)200 gに対して、スラッジ質量の1質量%相当量の処理剤を添加し、混合して、室温で7日間静置することでコンクリートスラッジ処理物を調製した。処理剤添加後のコンクリートの外観を図6に示す。処理剤添加前のスラッジは粘土状であったが(図6左上)、処理剤を添加混合するとただちにスラリー状になった(図6中央上)。処理剤添加の1日後、スラッジの形状は粘土状に戻り(図6右上)、その後は徐々に水分が減って、処理剤添加の4日後には砕くと粉状になるまで水分が減少した(図6右下)。このことから、含水率が低いコンクリートスラッジであっても、1質量%相当量の処理剤を添加することで、スラッジ中の水和物から水が溶出することでスラリー状の形状となり、処理剤を容易に混合することができることが示された。
(1)コンクリートスラッジ処理物の調製
塩化鉄(II)四水和物(和光純薬)10 gを水で溶解して100 mLとした塩化鉄(II)水溶液と実施例1で調製したリン酸水溶液を、二液型の処理剤として用いた。塩化鉄(II)水溶液は2.81質量%の鉄を含有する。
試験に用いた装置の構成を、図7を参照しながら説明する。1質量%の硫化ナトリウム九水和物(和光純薬)の水溶液200 mLをムエンケ式洗浄瓶11に入れ、チューブを介してマイクロピペット12及びカラム13に接続した。カラム13は、直径65 mm、上部直径100 mm、長さ165 mmの円筒形カラムであり、その下部に綿15を詰め、その上部に穴を設けてガス検知器14(キューレイ2・吸引式/PGM-2400P)を接続した。マイクロピペット12から塩酸を滴下すると、洗浄瓶11内に硫化水素ガスが発生し、カラム13を通してガス検知器14に吸引される。
2 オゾン発生チューブ
3 エアーポンプ
4 スターラー
5 試料
6 エアーストーン
11 ムエンケ式洗浄瓶
12 マイクロピペット
13 ガラス製カラム
14 ガス検知器
15 綿栓
16 試験物
17 ゴム栓
Claims (16)
- コンクリートスラッジに、当該コンクリートスラッジの固形分に対して0.15質量%以上の量となる鉄を含む二価鉄化合物と、当該コンクリートスラッジの固形分に対して0.60質量%以上の量となるリン酸を含むリン酸化合物とを同時に添加し、混合することでpH 12~13の混合物を得る工程、及び得られた混合物を少なくとも1時間保持する工程を含む、コンクリートスラッジ処理物の製造方法。
- 二価鉄化合物が、硫酸鉄(II)又は塩化鉄(II)である、請求項1に記載の製造方法。
- リン酸化合物が、オルトリン酸又はその塩である、請求項1又は2に記載の製造方法。
- 二価鉄化合物及びリン酸化合物が、液体に溶解した形態でコンクリートスラッジに添加される、請求項1~3のいずれか一項に記載の製造方法。
- 前記液体の添加量が、コンクリートスラッジ100 gに対して少なくとも1 mLである、請求項4に記載の製造方法。
- 前記液体の添加量が、コンクリートスラッジ100 gに対して1~10 mLである、請求項4又は5に記載の製造方法。
- 混合物が少なくとも24時間保持される、請求項1~6のいずれか一項に記載の製造方法。
- コンクリートスラッジ処理物が、乾燥質量1 g当たり少なくとも3 Lの硫化水素ガス吸着能を有し、かつコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、請求項1~7のいずれか一項に記載の製造方法。
- 濃度3 mg/Lのオゾンガスで10時間曝気した後のコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、請求項1~8のいずれか一項に記載の製造方法。
- 請求項1~9のいずれか一項に記載の方法により製造されたコンクリートスラッジ処理物で埋立廃棄物を被覆する工程を含む、埋立廃棄物からの硫化水素の放出を抑制するための方法。
- 請求項1~9のいずれか一項に記載の方法により製造されたコンクリートスラッジ処理物を用いて覆土する工程を含む、覆土方法。
- 請求項1~9のいずれか一項に記載の方法により製造されたコンクリートスラッジ処理物を用いて掘削された地盤を埋め戻す工程を含む、埋戻し方法。
- 鉄に換算した濃度が1.5質量%以上である二価鉄化合物とリン酸に換算した濃度が6.0質量%以上であるリン酸化合物とを溶解した液体を含む、請求項1~9のいずれか一項に記載の方法に使用するためのキットであって、
コンクリートスラッジ処理物が、乾燥質量1 g当たり少なくとも3 Lの硫化水素ガス吸着能を有し、かつコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下であり、
コンクリートスラッジに対して、コンクリートスラッジとの混合物のpHが12~13となる量の前記液体を添加することで用いられる、前記キット。 - 二価鉄化合物が、硫酸鉄(II)又は塩化鉄(II)である、請求項13に記載のキット。
- リン酸化合物が、オルトリン酸又はその塩である、請求項13又は14に記載のキット。
- 濃度3 mg/Lのオゾンガスで10時間曝気した後のコンクリートスラッジ処理物 1質量部を水 10質量部と混合して得た液体の上清中の六価クロム含有量が0.05 mg/L以下である、請求項13~15のいずれか一項に記載のキット。