JP7074070B2 - 化粧材 - Google Patents
化粧材 Download PDFInfo
- Publication number
- JP7074070B2 JP7074070B2 JP2018558089A JP2018558089A JP7074070B2 JP 7074070 B2 JP7074070 B2 JP 7074070B2 JP 2018558089 A JP2018558089 A JP 2018558089A JP 2018558089 A JP2018558089 A JP 2018558089A JP 7074070 B2 JP7074070 B2 JP 7074070B2
- Authority
- JP
- Japan
- Prior art keywords
- adjusting layer
- gloss adjusting
- gloss
- layer
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
化粧材の表面に平面的な柄模様と併せて立体的な凹凸感を表現する手法としては、従来、様々な方法が考案され、目的に応じて使い分けられている。なかでも、化粧材の表面に実際に凹凸を形成するのではなく、凹部または凸部として表現したい部分の表面の艶状態(具体的には光沢度)を異ならせることにより、人間の目の錯覚を利用して視覚的に凹凸の立体感を表現する手法がある。この手法によれば、実際には凹凸形状が存在しなくても、人間の目には、相対的に艶の高い部分は凸部、艶の低い部分は凹部として認識される。
このような手法によれば、特殊な薬剤等を必要とすることなく、艶の異なる2種類の塗料を用意するだけで、いかなる基材に対しても、容易に立体的な凹凸感を付与することができる。しかも、艶の異なる合成塗料層の形成は、柄模様(柄インキ層)の形成に引き続きグラビア印刷法等の慣用の印刷法で行うことができるので、特殊設備は一切不要で生産能率も高く、柄模様との同調も容易である。また、合成塗料層の厚みは表現しようとする凹凸の高低差と比較すれば遥かに薄く済むので、樹脂の使用量を削減できるほか、可撓性の面でも有利であり、折り曲げ加工適性に優れた化粧材を容易に実現できる。また、化粧材の表面に大きな凹凸が無いので、凹部に汚染物が留まることも無いという利点もある。
一方、透明樹脂としてアクリル基やメタクリル基を有する電離放射線硬化樹脂は、比較的分子量が低いことと1分子あたりの官能基数が大きいことから架橋密度が高く、耐傷性を向上させやすい樹脂と言える。このような電離放射線硬化樹脂を透明樹脂として用いることにより、高度な耐傷性を有する化粧材を提供することが可能である。なお、耐傷性は主に化粧材最表面の強度に依存するため、最表面層の構成材料のみ、電離放射線硬化樹脂を積極的に用いれば良い。
上記課題を達成するべく、本発明の一態様は、基材上に設けられた第1の艶調整層と、第1の艶調整層上に部分的に設けられ、第1の艶調整層の艶と異なる艶を有する第2の艶調整層とを備え、第1の艶調整層を構成する樹脂成分は、ポリオールとイソシアネートとを有するウレタン系熱硬化樹脂と、アクリル基またはメタクリル基を有する電離放射線硬化樹脂との混合物であり、電離放射線硬化樹脂100質量部に対して、ウレタン系熱硬化樹脂を3質量部以上100質量部以下の範囲内で含む化粧材であることを要旨とする。
ここで、図面は模式的なものであり、厚みと平面寸法との関係、各層の厚みの比率等は現実のものとは異なる。また、以下に示す実施形態は、本発明の技術的思想を具体化するための構成を例示するものであって、本発明の技術的思想は、構成部品の材質、形状および構造等を下記のものに特定するものでない。本発明の技術的思想は、特許請求の範囲に記載された請求項が規定する技術的範囲内において、種々の変更を加えることができる。
図1に示すように、実施形態に係る化粧材1は、基材2上に設けられた第1の艶調整層5と、第1の艶調整層5上に部分的に設けられ、第1の艶調整層5の艶と異なる艶を有する第2の艶調整層6とを備えている。そして、これら第1、第2の艶調整層5、6のうち、第1の艶調整層5に用いる透明樹脂が、各種ポリオールとイソシアネートから成る2液のウレタン系熱硬化樹脂と、アクリル基またはメタクリル基を有する電離放射線硬化樹脂との混合物であり、熱硬化樹脂の混合割合が電離放射線硬化樹脂100質量部に対して、3質量部以上100質量部以下の範囲内であることが重要である。これにより、積層時の不具合を抑制しつつ、高度な耐傷性を発現可能な化粧材1を提供することができる。
なお、基材2と第1の艶調整層5との間には、後述するように下地ベタインキ層3、柄インキ層4および透明樹脂層(不図示)等、他の層を配置する構成としてもよい。
基材2は、化粧材1の原紙として用いられるものであれば、特に限定されるものではない。例えば、薄葉紙、樹脂混抄紙、チタン紙、樹脂含浸紙、難燃紙、無機質紙等の紙類、天然繊維または合成繊維からなる織布もしくは不織布、ホモまたはランダムポリプロピレン樹脂、ポリエチレン樹脂等のポリオレフィン樹脂、共重合ポリエステル樹脂、アモルファス状態の結晶性ポリエステル樹脂、ポリエチレンナフタレート樹脂、ポリブチレン樹脂、アクリル系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、フッ素系樹脂等の合成樹脂系基材、木材単板、突板、合板、集成材、パーティクルボード、中密度繊維板等の木質系基材、石膏板、セメント板、珪酸カルシウム板、陶磁器板等の無機系基材、鉄、銅、アルミニウム、ステンレス等の金属系基材、またはこれらの複合材、積層体等、従来公知の材料を用いることができる。また、基材2の形状としては、フィルム状、シート状、板状、異型成型体等を用いることができる。
下地ベタインキ層3は、基材2と柄インキ層4との間に設けられ、求められる意匠に応じて、基材2の第1の艶調整層5側の面の全面を被覆する層である。また、下地ベタインキ層3は、隠蔽性等、必要に応じて2層以上の多層としてもよい。さらに、柄インキ層4は、求められる意匠を表現するために必要な分版の数だけ積層して形成してもよい。このように、下地ベタインキ層3は、柄インキ層4との組合せによって求められる意匠、つまり、表現したい意匠に応じて様々な組み合わせとなるが、特に限定されるものではない。
下地ベタインキ層3、並びに後述する柄インキ層4および第1、第2の艶調整層5、6の各層は、グラビア印刷法、オフセット印刷法、スクリーン印刷法、静電印刷法、インクジェット印刷法等の各種印刷方法によって形成することができる。また、下地ベタインキ層3および第1の艶調整層5は、基材2の第1の艶調整層5側の面の全面を被覆しているため、ロールコート法、ナイフコート法、マイクログラビアコート法、ダイコート法等の各種コーティング方法によっても形成できる。これらの印刷方法、コーティング方法は、形成する層によって別々に選択してもよいし、同じ方法を選択して一括加工してもよい。
柄インキ層4は、基材2と第1の艶調整層5の間に設けられ、化粧材1に柄模様を付加するための層である。柄模様としては、木目模様、石目模様、砂目模様、タイル貼模様、煉瓦積模様、布目模様、皮絞模様、幾何学図形等を用いることができる。柄インキ層4の形成箇所は、第2の艶調整層6の直下の部分のみとなっている。すなわち、第2の艶調整層6が、柄インキ層4と重なる部分にのみ形成された構成となっている。また、柄インキ層4の柄模様は、第2の艶調整層6の艶と同調している。これにより、柄インキ層4による意匠性に、第2の艶調整層6による意匠性を付加することができる。それゆえ、天然木や天然石に近い高級感のある意匠表現を有した化粧材1を形成することができる。
柄インキ層4の構成材料は、特に限定されるものではない。例えば、下地ベタインキ層3と同様に、マトリックスと、染料、顔料等の着色剤とを溶剤中に溶解、分散してなる印刷インキやコーティング剤を用いることができる。また、柄インキ層4には、各種機能を付与するために、体質顔料、可塑剤、分散剤、界面活性剤、粘着付与剤、接着助剤、乾燥剤、硬化剤、硬化促進剤、および硬化遅延剤等の機能性添加剤を添加してもよい。
第1の艶調整層5は、下地ベタインキ層3および柄インキ層4の第1の艶調整層5側の面に設けられ、化粧材1表面の艶状態を調整するための層である。第1の艶調整層5の形成箇所は、下地ベタインキ層3および柄インキ層4の第1の艶調整層5側の面の全面となっており、基材2の第1の艶調整層5側の面の全面を被覆している。また、第2の艶調整層6は、第1の艶調整層5の第2の艶調整層6側の面に設けられ、第1の艶調整層5の艶と異なる艶を有し、化粧材1表面の艶状態を調整するための層である。第2の艶調整層6の形成箇所は、第1の艶調整層5の第2の艶調整層6側の面の一部となっている。そして、これら第1、第2の艶調整層5、6の艶の差により凹凸形状が表現可能となっている。
なお、相対的に艶の高い艶調整層においても、任意の艶消し剤を添加することが可能である。これらは最終的な凹凸感や意匠性に応じて適宜調整されるべきものである。また、第1、第2の艶調整層5、6に用いられる艶消し剤および樹脂組成物は、同じでも異なっていてもよい。これらは凹凸感および各種要求特性から自由に選択することができる。
上記の電離放射線硬化樹脂の数平均分子量を測定する方法は特に限定されないが、ゲル浸透クロマトグラフィー(GPC)を用いることが好ましい。そのGPCの測定装置については特に限定されるものではないが、GPCカラムの充填材はポリスチレンゲルが好ましく、溶離液としてはテトラヒドロフラン(THF)を用いることが好ましい。また、GPCの標準物質にはポリスチレンポリマーを用いればよい。なお、上記の多官能(メタ)アクリレートモノマーについては、単体で構成されているため、その構造が既知であれば、数平均分子量は、構造式から算出される値を用いてもよい。
また、第1、第2の艶調整層5、6の層厚は、任意の数値を選択できるが、前述の通り、艶消し剤の粒径は2μm以上15μm以下が好ましいため、1μm以上15μm以下とすることが好ましい。また、第1、第2の艶調整層5、6は、化粧材1の最表面となる層のため、化粧材1として必要な耐摩耗性、耐擦傷性、耐溶剤性、耐汚染性等の表面物性が求められる。なかでも、耐摩耗性や耐擦傷性は層厚による影響があり、層厚が厚い方が有利となる。したがって、第1、第2の艶調整層5、6のさらに好ましい層厚は2μm以上12μm以下となる。1μm未満の場合には、耐摩耗性および耐擦傷性が大幅に悪くなるため、化粧材1としての用途が限られる。また、15μmより大きい場合には、第1、第2の艶調整層5、6自体の可撓性が悪くなるため、化粧材1としての加工性が悪化する。
また、第1、第2の艶調整層5、6には、各種機能を付与するために、抗菌剤、防カビ剤等の機能性添加剤を添加してもよい。また、必要に応じて紫外線吸収剤、光安定化剤を添加してもよい。紫外線吸収剤としては、ベンゾトリアゾール系、ベンゾエート系、ベンゾフェノン系、トリアジン系を用いることができる。また、光安定化剤としては、ヒンダードアミン系を用いることができる。さらに、汚染防止性能やセロテープ(登録商標)離型性が求められる場合には、シリコーン骨格を持つ離型剤を添加することができる。この場合、離型剤の種類は特に限定されないが、樹脂組成物に対して反応性を有する末端官能基を持つシリコーン離型剤を用いることで、汚染防止性能やセロテープ離型性の耐久性を向上できる。
また、特に、化粧材1の特性として、耐摩耗性が要求される場合には、柄インキ層4と第1の艶調整層5の間に透明樹脂層(不図示)を設けることができる。透明樹脂層としては、例えば、オレフィン系樹脂を主成分とした樹脂組成物を用いることが好ましい。オレフィン系樹脂としては、ポリプロピレン、ポリエチレン、ポリブテン等の他に、αオレフィン(例えば、プロピレン、1-ブテン、1-ペンテン、1-ヘキセン、1-ヘプテン、1-オクテン、1-ノネン、1-デセン、1-ウンデセン、1-ドデセン、トリデセン、1-テトラデセン、1-ペンタデセン、1-ヘキサデセン、1-ヘプタデセン、1-オクタデセン、1-ノナデセン、1-エイコセン、3-メチル-1-ブテン、3-メチル-1-ペンテン、3-エチル-1-ペンテン、4-メチル-1-ペンテン、4-メチル-1-ヘキセン、4,4-ジメチル-1-ペンテン、4-エチル-1-ヘキセン、3-エチル-1-ヘキセン、9-メチル-1-デセン、11-メチル-1-ドデセン、12-エチル-1-テトラデセン等)を単独重合あるいは2種類以上共重合させたものや、エチレン・酢酸ビニル共重合体、エチレン・ビニルアルコール共重合体、エチレン・メチルメタクリレート共重合体、エチレン・エチルメタクリレート共重合体、エチレン・ブチルメタクリレート共重合体、エチレン・メチルアクリレート共重合体、エチレン・エチルアクリレート共重合体、エチレン・ブチルアクリレート共重合体等のように、エチレンまたはαオレフィンとそれ以外のモノマーとを共重合させたものを用いることができる。特に、表面強度の更なる向上を図る場合には、高結晶性のポリプロピレンを用いることが好ましい。
(1)以上のように、本実施形態の化粧材1では、第1の艶調整層5を構成する樹脂成分を、ポリオールとイソシアネートとを有するウレタン系熱硬化樹脂と、アクリル基またはメタクリル基を有する電離放射線硬化樹脂との混合物とし、第1の艶調整層5を構成する樹脂成分が、電離放射線硬化樹脂100質量部に対してウレタン系熱硬化樹脂を3質量部以上100質量部以下含むようにした。それゆえ、第1の艶調整層5の樹脂成分がウレタン系熱硬化樹脂と電離放射線硬化樹脂とを組合せてなるデュアル硬化方式の樹脂成分となり、ウレタン系熱硬化樹脂の添加量を最適な範囲とすることで、第2の艶調整層6の積層時に最低限の硬化状態を達成しつつ、化粧材1作製後に電離放射線硬化樹脂特有の高架橋を達成でき、高度な耐傷性を得ることができる。これにより、第2の艶調整層6の積層時に生じる不具合を抑制しつつ、高度な耐傷性を有する化粧材1を提供することができる。
(4)また、本実施形態の化粧材1では、アクリル基またはメタクリル基を有する電離放射線硬化樹脂の数平均分子量を300以上1500以下とした。それゆえ、電離放射線硬化樹脂の粘度を低下でき、艶調整層形成用インキを調製する際も、同粘度での固形分濃度を向上できるため、インキ自体の安定性や、塗布状態を向上することができる。
(1)なお、本実施形態では、第2の艶調整層6が柄インキ層4と重なる部分に形成され、柄インキ層4の柄模様と第2の艶調整層6の艶とが同調している例を示したが、他の構成を採用することもできる。例えば、図2に示すように、第2の艶調整層6が柄インキ層4の直上以外の部分に形成され、柄インキ層4の柄模様と第1の艶調整層5の艶とが同調していてもよい。これにより、柄インキ層4の柄模様に、露出している第1の艶調整層5の艶が付与され、柄インキ層4による意匠性に第1の艶調整層5による意匠性を付加できる。それゆえ、天然木等に近い高級感のある意匠表現を有した化粧材1を形成できる。また、第2の艶調整層6は、柄インキ層4の直上以外の部分と、柄インキ層4の直上部分の一部とに一体的に形成されていてもよい。この形態であっても、柄インキ層4の柄模様に、露出している第1の艶調整層5の艶が付与され、柄インキ層4による意匠性に第1の艶調整層5による意匠性を付加できる。
(実施例1)
実施例1では、坪量50g/m2の含浸紙(GFR-506:興人(株)製)を基材2として用いた。そして、基材2の一方の面に、油性硝化綿樹脂系グラビア印刷インキ(PCNT(PCRNT)各色:東洋インキ(株)製)を使用して、下地ベタインキ層3と、柄インキ層4とをこの順に形成した。柄インキ層4の柄模様は、木目柄とした。
続いて、柄インキ層4を形成した基材2上に、第1の艶調整層5用のインキを基材2の一方の面の全面を被覆するように塗布(塗工)して、第1の艶調整層5を形成した。インキは、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)2.4質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)0.6質量部とを有する2液のウレタン系熱硬化樹脂(合計3質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。インキの塗布量は5g/m2とした。
実施例2では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)8質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)2質量部とを有する2液のウレタン系熱硬化樹脂(合計10質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
実施例3では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)16質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)4質量部とを有する2液のウレタン系熱硬化樹脂(合計20質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
実施例4では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)40質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)10質量部とを有する2液のウレタン系熱硬化樹脂(合計50質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
実施例5では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)80質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)20質量部とを有する2液のウレタン系熱硬化樹脂(合計100質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
実施例6では、第2の艶調整層6用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)20質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)5質量部とを有する2液のウレタン系熱硬化樹脂(合計25質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)5質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
実施例7では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)8質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)2質量部とを有する2液のウレタン系熱硬化樹脂(合計10質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例6と同様の構成とした。
実施例8では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)40質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)10質量部とを有する2液のウレタン系熱硬化樹脂(合計50質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例6と同様の構成とした。
実施例9では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)80質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)20質量部とを有する2液のウレタン系熱硬化樹脂(合計100質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例6と同様の構成とした。
実施例10では、第2の艶調整層6用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)2.4質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)0.6質量部とを有する2液のウレタン系熱硬化樹脂(合計3質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)5質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
実施例11では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)8質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)2質量部とを有する2液のウレタン系熱硬化樹脂(合計10質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例10と同様の構成とした。
実施例12では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)40質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)10質量部とを有する2液のウレタン系熱硬化樹脂(合計50質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例10と同様の構成とした。
実施例13では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)80質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)20質量部とを有する2液のウレタン系熱硬化樹脂(合計100質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例10と同様の構成とした。
実施例14では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)40質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)10質量部とを有する2液のウレタン系熱硬化樹脂(合計50質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。また、第2の艶調整層6用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)24質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)6質量部とを有する2液のウレタン系熱硬化樹脂(合計30質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)5質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
比較例1では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)0.8質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)0.2質量部とを有する2液のウレタン系熱硬化樹脂(合計1質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
比較例2では、第1の艶調整層5用のインキとして、電離放射線硬化樹脂(ジペンタエリスリトールヘキサアクリレート)100質量部に対して、アクリルポリオール(6KW-700:大成ファインケミカル(株)製)120質量部とポリイソシアネート(UR190B硬化剤:東洋インキ(株)製)30質量部とを有する2液のウレタン系熱硬化樹脂(合計150質量部)、シリカ系艶消し剤(ミズカシルP-803:水澤化学工業(株)製)10質量部、紫外線ラジカル開始剤(IRGACURE 184:BASF製)5質量部から構成した。それ以外は実施例1と同様の構成とした。
以上の実施例1~14、比較例1~2について、第1、第2の艶調整層5、6の連続塗工時の不具合の発生状態と、耐傷性の評価を行った。
(連続塗工時の不具合)
第2の艶調整層6の積層時の状況および作製後の化粧材1の外観から、第2の艶調整層6の積層時の不具合の有無を目視観察によって評価した。そして、不具合がない無い場合を「○」、第1の艶調整層5に僅かに溶解や削れを確認でき、僅かに不具合がある場合を「△」、第1の艶調整層5に溶解や削れを確認でき、不具合がある場合を「×」とした。
化粧材1に対して、スチールウール(#0000)を用いて荷重500[g/cm2]、10回往復の耐傷性試験を実施した後、化粧材1の表面の傷や光沢度変化の有無を目視観察によって評価した。そして、傷や光沢度変化が見られない場合を「○」、傷や光沢度変化が僅かに見える場合を「△」、大きな傷や光沢度変化が見える場合を「×」とした。
これらの評価結果を表1に示す。なお、各評価が「○」又は「△」であれば、各機能を十分に備えており、製品として十分に使用することができる。
なお、本発明の化粧材1は、上記の実施形態および実施例に限定されるものではなく、発明の特徴を損なわない範囲において種々の変更が可能である。
Claims (12)
- 基材上に設けられた第1の艶調整層と、前記第1の艶調整層上に部分的に設けられ、前記第1の艶調整層の艶と異なる艶を有する第2の艶調整層とを備え、
前記第1の艶調整層を構成する樹脂成分は、ポリオールとイソシアネートとを有するウレタン系熱硬化樹脂と、アクリル基またはメタクリル基を有する電離放射線硬化樹脂との混合物であり、該電離放射線硬化樹脂100質量部に対して、該ウレタン系熱硬化樹脂を3質量部以上100質量部以下の範囲内で含み、
前記第2の艶調整層を構成する樹脂成分は、ポリオールとイソシアネートとを有するウレタン系熱硬化樹脂と、アクリル基またはメタクリル基を有する電離放射線硬化樹脂との混合物であり、該電離放射線硬化樹脂100質量部に対して、該ウレタン系熱硬化樹脂を0質量部を超えて25質量部以下の範囲内で含み、
前記第1の艶調整層および前記第2の艶調整層は、それぞれ艶消し剤を含むことを特徴とする化粧材。 - 基材上に設けられた第1の艶調整層と、前記第1の艶調整層上に部分的に設けられ、前記第1の艶調整層の艶と異なる艶を有する第2の艶調整層とを備え、
前記第1の艶調整層を構成する樹脂成分は、ポリオールとイソシアネートとを有するウレタン系熱硬化樹脂と、アクリル基またはメタクリル基を有する電離放射線硬化樹脂との混合物であり、該電離放射線硬化樹脂100質量部に対して、該ウレタン系熱硬化樹脂を3質量部以上100質量部以下の範囲内で含み、
前記第2の艶調整層を構成する樹脂成分は、アクリル基またはメタクリル基を有する電離放射線硬化樹脂のみであり、
前記第1の艶調整層および前記第2の艶調整層は、それぞれ艶消し剤を含むことを特徴とする化粧材。 - 前記アクリル基またはメタクリル基を有する電離放射線硬化樹脂は、数平均分子量が300以上5000以下の範囲内であることを特徴とする請求項1または2に記載の化粧材。
- 前記アクリル基またはメタクリル基を有する電離放射線硬化樹脂は、数平均分子量が300以上1500以下の範囲内であることを特徴とする請求項3に記載の化粧材。
- 前記基材と前記第1の艶調整層との間に設けられた柄インキ層を更に備え、
前記第2の艶調整層は、前記柄インキ層と重なる部分に形成され、前記柄インキ層の柄模様と前記第2の艶調整層の艶とが同調していることを特徴とする請求項1から4のいずれか1項に記載の化粧材。 - 前記基材と前記第1の艶調整層との間に設けられた柄インキ層を更に備え、
前記第1の艶調整層は、前記基材の前記第1の艶調整層側の面の全面を被覆しており、
前記第2の艶調整層は、前記柄インキ層の直上以外の部分に形成され、前記柄インキ層の柄模様と前記第1の艶調整層の艶とが同調していることを特徴とする請求項1から4のいずれか1項に記載の化粧材。 - 前記基材と前記第1の艶調整層との間に設けられた柄インキ層を更に備え、
前記第2の艶調整層は、前記柄インキ層と少なくとも一部が重なるように形成され、前記柄インキ層の柄模様と前記第2の艶調整層の艶とが同調していることを特徴とする請求項1から4のいずれか1項に記載の化粧材。 - 前記基材と前記第1の艶調整層との間に設けられた柄インキ層を更に備え、
前記第2の艶調整層は、前記柄インキ層の直上部分と、前記柄インキ層の直上以外の部分の一部とに一体的に形成され、前記柄インキ層の柄模様と前記第2の艶調整層の艶とが同調していることを特徴とする請求項1から4のいずれか1項に記載の化粧材。 - 前記基材と前記第1の艶調整層との間に設けられた柄インキ層を更に備え、
前記第1の艶調整層は、前記基材の前記第1の艶調整層側の面の全面を被覆しており、
前記第2の艶調整層は、前記柄インキ層の直上以外の部分と、前記柄インキ層の直上部分の一部とに一体的に形成され、前記柄インキ層の柄模様と前記第1の艶調整層の艶とが同調していることを特徴とする請求項1から4のいずれか1項に記載の化粧材。 - 前記艶消し剤は、無機材料を含むことを特徴とする請求項1から9のいずれか1項に記載の化粧材。
- 前記艶消し剤は、1次粒子が2次凝集してなる艶消し剤であることを特徴とする請求項1から10のいずれか1項に記載の化粧材。
- 前記第1の艶調整層を構成する前記ウレタン系熱硬化樹脂の、前記第1の艶調整層を構成する前記電離放射線硬化樹脂100質量部に対する含有量は、前記第2の艶調整層を構成する前記ウレタン系熱硬化樹脂の、前記第2の艶調整層を構成する前記電離放射線硬化樹脂100質量部に対する含有量よりも多いことを特徴とする請求項1に記載の化粧材。