JP6882965B2 - 車両用の樹脂製複合モジュール及びその製造方法 - Google Patents
車両用の樹脂製複合モジュール及びその製造方法 Download PDFInfo
- Publication number
- JP6882965B2 JP6882965B2 JP2017181452A JP2017181452A JP6882965B2 JP 6882965 B2 JP6882965 B2 JP 6882965B2 JP 2017181452 A JP2017181452 A JP 2017181452A JP 2017181452 A JP2017181452 A JP 2017181452A JP 6882965 B2 JP6882965 B2 JP 6882965B2
- Authority
- JP
- Japan
- Prior art keywords
- light source
- hard coat
- module
- resin
- ultraviolet rays
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
そこで本発明は、意匠性と、耐擦傷性を備える車両用の樹脂製複合モジュールとその製造方法を提供することを目的とする。
車両ウィンドウを有し、三次元形状の表面を有する車両用の樹脂製複合モジュールの製造方法であって、
前記樹脂製複合モジュールは、
樹脂製モジュール基体と、
前記樹脂製モジュール基体の上に形成されたシリコーン系ポリマーのハードコートと、を備え、
樹脂製モジュール基体の上にシリコーン系ポリマーを塗布してハードコートを形成する工程と、
前記ハードコートの表面の少なくとも一部に、その硬度がナノインデンテーション法による評価で0.8GPa以上となるように、紫外線を照射する工程とを有し、
前記紫外線を照射する工程において、少なくとも光源を有し出射面から波長360nm以下の紫外線を出射する光源ユニットを用いて、前記出射面から前記ハードコートの表面までの距離が10mm以下となるように、例えば不活性ガス雰囲気で前記ハードコートの表面に紫外線を照射する。
車両のウィンドウを有し、三次元形状の表面を有する車両用の樹脂製複合モジュールであって、
樹脂製モジュール基体と、
前記樹脂製モジュール基体の上に形成されたシリコーン系ポリマーのハードコートと、を備え、
前記ハードコートの表面の少なくとも一部に波長360nm以下の紫外線が照射されてその硬度がナノインデンテーション法による評価で0.8GPa以上とされている。
まず、本発明の第一の実施形態について説明する。本実施形態の樹脂製複合モジュールは、三次元形状のリアモジュールである。図1は、本発明の第一の実施形態に係るリアモジュール10を搭載した車両の断面模式図である。このリアモジュール10は、リアコンビネーションランプ14のアウタレンズ11とリアウィンドウ12とを一体に有する。また、リアモジュール10の一部はスポイラーも構成している。このようなリアモジュール10では、リアコンビネーションランプ14の周辺部分が複雑な凹凸形状であることが多い。
続いて、本発明の第二の実施形態について説明する。図6は、第二の実施形態においてハードコートの表面13に紫外線を照射する様子を示す模式図である。本実施形態は、光源ユニット120が異なる以外は第一の実施形態と同様である。光源ユニット120は、光源121と、光源121から表面13まで光源121から出射された光を導くレンズ部品124と、を有する。レンズ部品124は、ハードコートの表面13に対応する形状の出射面125を有する。光源ユニット120は、レンズ部品124の出射面125から波長360nm以下の紫外線を表面13に照射する。当該光源121としては、第一の実施形態で挙げたものを用いることができる。レンズ部品124としては、紫外線の減衰を抑制しつつ、光源121から出射面125に紫外線を導くことのできるものであれば特に限定されるものではないが、石英ガラス等を用いることができる。
続いて、本発明の第三の実施形態について説明する。図7は、第三の実施形態においてハードコートの表面13に紫外線を照射する様子を示す模式図である。本実施形態は、光源ユニット220が異なる以外は第一の実施形態と同様である。光源ユニット220は、光源221と、光源221から表面13まで光源221から出射された光を導く光ファイバ222と、を有する。光源ユニット220は、光ファイバ222の端面223から紫外線を表面13に照射する。当該光源221及び光ファイバ222としては、第一の実施形態で挙げたものを用いることができる。
続いて、本発明の第四の実施形態について説明する。図8は、第四の実施形態においてハードコートの表面13に紫外線を照射する様子を示す模式図である。本実施形態は、光源ユニット320が異なる以外は第一の実施形態と同様である。光源ユニット320は、光源321と、出射面325を有するレンズ部品324とを有する。光源ユニット320は、三次元形状の凹部の表面13からレンズ部品324の出射面325までの距離が10mm以下である位置まで、リアモジュール10に近づくことができる程度に小型である。光源ユニット320は、出射面325から紫外線を表面13に照射する。光源321としては、第一の実施形態で挙げたものを用いることができる。レンズ部品324としては、紫外線を透過することのできるものであれば特に限定されない。また、光源ユニット320自体が、第一の実施形態で挙げた光源であってもよい。
以上、本発明の実施形態について説明をしたが、本発明の技術的範囲が本実施形態の説明によって限定的に解釈されるべきではないのは言うまでもない。本実施形態は単なる例示であって、特許請求の範囲に記載された発明の範囲内において、様々な実施形態の変更が可能であることが当業者によって理解されるところである。本発明の技術的範囲は特許請求の範囲に記載された発明及びその均等の範囲に基づいて定められるべきである。
Claims (8)
- 車両ウィンドウを有し、三次元形状の表面を有する車両用の樹脂製複合モジュールの製造方法であって、
前記樹脂製複合モジュールは、
樹脂製モジュール基体と、
前記樹脂製モジュール基体の上に形成されたシリコーン系ポリマーのハードコートと、を備え、
樹脂製モジュール基体の上にシリコーン系ポリマーを塗布してハードコートを形成する工程と、
前記ハードコートの表面の少なくとも一部に、その硬度がナノインデンテーション法による評価で0.8GPa以上となるように、紫外線を照射する工程とを有し、
前記紫外線を照射する工程において、少なくとも光源を有し出射面から波長360nm以下の紫外線を出射する光源ユニットを用いて、前記出射面から前記ハードコートの表面までの距離が10mm以下となるように、前記ハードコートの表面に紫外線を照射する、車両用の樹脂製複合モジュールの製造方法。 - 前記光源ユニットは、
前記光源と、
前記光源から前記ハードコートの表面まで前記光源から出射された光を導く光ファイバを有し、
前記出射面は前記光ファイバの端面である、請求項1に記載の車両用の樹脂製複合モジュールの製造方法。 - 前記光ファイバの前記端面を前記ハードコートの表面に沿って動かす、請求項2に記載の車両用の樹脂製複合モジュールの製造方法。
- 複数の前記光ファイバの前記端面を前記ハードコートの表面に沿って配列する、請求項2に記載の車両用の樹脂製複合モジュールの製造方法。
- 前記光源ユニットは、
前記光源と、
前記ハードコートの表面に対応する形状の前記出射面を有し、前記光源から前記ハードコートの表面まで前記光源から出射された光を導くレンズ部品を有する、請求項1に記載の車両用の樹脂製複合モジュールの製造方法。 - 前記光源ユニットは、
前記光源と、
前記出射面を有するレンズ部品を有し、
前記出射面が前記ハードコートの表面に沿うように前記光源ユニットを動かす、請求項1に記載の車両用の樹脂製複合モジュールの製造方法。 - 紫外線照射領域における酸素の濃度が0.1〜10%である雰囲気である、請求項1〜6のいずれか一項に記載の車両用の樹脂製複合モジュールの製造方法。
- 車両のウィンドウを有し、三次元形状の表面を有する車両用の樹脂製複合モジュールであって、
樹脂製モジュール基体と、
前記樹脂製モジュール基体の上に形成されたシリコーン系ポリマーのハードコートと、を備え、
前記ハードコートの表面の少なくとも一部に波長360nm以下の紫外線が照射されてその硬度がナノインデンテーション法による評価で0.8GPa以上とされている、車両用の樹脂製複合モジュール。