JP6709309B2 - 多層管 - Google Patents
多層管 Download PDFInfo
- Publication number
- JP6709309B2 JP6709309B2 JP2019082924A JP2019082924A JP6709309B2 JP 6709309 B2 JP6709309 B2 JP 6709309B2 JP 2019082924 A JP2019082924 A JP 2019082924A JP 2019082924 A JP2019082924 A JP 2019082924A JP 6709309 B2 JP6709309 B2 JP 6709309B2
- Authority
- JP
- Japan
- Prior art keywords
- polyolefin resin
- layer
- glass fiber
- weight
- gas barrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
上記ポリオレフィン樹脂層(上記第1,第2のポリオレフィン樹脂層)及び上記ポリオレフィン樹脂/ガラス繊維層に含まれている各ポリオレフィン樹脂は特に限定されない。上記ポリオレフィン樹脂として従来公知のポリオレフィン樹脂を用いることができる。上記ポリオレフィン樹脂は、1種のみが用いられてもよく、2種以上が併用されてもよい。
上記ポリオレフィン樹脂/ガラス繊維層は、ガラス繊維を含む。上記ポリオレフィン樹脂層(上記第1,第2のポリオレフィン樹脂層)は、少量であればガラス繊維を含んでいてもよく、ガラス繊維を含んでいなくてもよい。上記ポリオレフィン樹脂/ガラス繊維層がポリオレフィン樹脂100重量部に対してガラス繊維を10重量部以上含む場合に、上記ポリオレフィン樹脂層は、ポリオレフィン樹脂100重量部に対してガラス繊維を10重量部未満で含むことが好ましい。この場合に、上記ポリオレフィン樹脂/ガラス繊維層と上記ポリオレフィン樹脂層とは異なる。多層管の耐衝撃強度をより一層高める観点からは、上記ポリオレフィン樹脂層において、ガラス繊維の含有量は少ないほどよい。上記ポリオレフィン樹脂層において、ポリオレフィン樹脂100重量部に対するガラス繊維の含有量はより好ましくは10重量部以下、更に好ましくは5重量部以下、最も好ましくは0重量部(未使用)である。
多層管の耐衝撃強度、寸法安定性及びガスバリア性を効果的に高める観点からは、上記ポリオレフィン樹脂/ガラス繊維層は相溶化剤を含むことが好ましい。上記相溶化剤は、1種のみが用いられてもよく、2種以上が併用されてもよい。
上記ガスバリア層はガスバリア性を有していればよく、ガスバリア性を発現する適宜の材料により形成される。上記ガスバリア層の材料としては、エチレン−ビニルアルコール樹脂、ポリビニルアルコール、ポリアミド及びポリエチレンテレフタレート等が挙げられる。上記ガスバリア層の材料は1種のみが用いられてもよく、2種以上が併用されてもよい。
上記接着層は積層される層を接着する性質を有していればよく、接着性を発現する適宜の材料により形成される。
上記ポリオレフィン樹脂層(上記第1,第2のポリオレフィン樹脂層)及び上記ポリオレフィン樹脂/ガラス繊維層はそれぞれ、上記ポリオレフィン樹脂以外の熱可塑性樹脂を含んでいてもよい。但し、上記ポリオレフィン樹脂以外の熱可塑性樹脂を用いる場合には、層における上記ポリオレフィン樹脂以外の熱可塑性樹脂の含有量は、層における上記ポリオレフィン樹脂の含有量よりも少ないことが好ましい。
実施例1では、図2に示す積層構造を有する多層管を作製した。
第1,第2のポリオレフィン樹脂層の厚みを2mmに変更したこと、並びに、ポリオレフィン樹脂/ガラス繊維層の厚みを2mmに変更したこと以外は実施例1と同様にして、多層管を得た。
ポリオレフィン樹脂/ガラス繊維層を形成するために、ポリオレフィン樹脂(ポリエチレン、密度:0.95g/cm3)100重量部(55重量%)と、ガラス繊維(繊維長3mm、繊維径13μm、アミノシラン表面処理)72.7重量部(40重量%)と、相溶化剤(変性ポリエチレン、密度:0.95g/cm3)9.1重量部(5重量%)とを混合した組成物を用いた。
ポリオレフィン樹脂/ガラス繊維層を形成するために、ポリオレフィン樹脂(ポリエチレン、密度:0.95g/cm3)100重量部(55重量%)と、ガラス繊維(繊維長3mm、繊維径13μm、アミノシラン表面処理)72.7重量部(40重量%)と、相溶化剤(変性ポリエチレン、密度:0.95g/cm3)9.1重量部(5重量%)とを混合した組成物を用いた。
ポリオレフィン樹脂(ポリエチレン、密度:0.95g/cm3)を用いて、厚みが6mmである単層管を得た。
寸法安定性:
得られた多層管において、寸法安定性を評価するために、熱線膨張係数を測定した。熱機械分析(TMA)装置を用いて、昇温速度5℃/min、測定範囲−20℃から120℃の条件で測定した。
2…ポリオレフィン樹脂/ガラス繊維層
3…ポリオレフィン樹脂層
4…接着層
5…ガスバリア層
11,11A…多層管
Claims (6)
- 管状の複数の層を備える多層管であって、
管状であり、かつポリオレフィン樹脂を含む第1のポリオレフィン樹脂層(但し、ポリブテンが含まれている層を除く)と、
管状であり、かつポリオレフィン樹脂とガラス繊維とを含むポリオレフィン樹脂/ガラス繊維層(但し、前記ガラス繊維が、シート状繊維複合体として含まれている層を除く)と、
管状であり、かつポリオレフィン樹脂を含む第2のポリオレフィン樹脂層と、
を備え、
前記第1のポリオレフィン樹脂層の外側に、前記ポリオレフィン樹脂/ガラス繊維層が配置されており、
前記ポリオレフィン樹脂/ガラス繊維層の外側に、前記第2のポリオレフィン樹脂層が配置されており、
前記ガラス繊維の繊維長が、0.05mm以上、5mm以下である、多層管。 - 前記ガラス繊維の繊維径が、1μm以上、20μm以下である、請求項1に記載の多層管。
- 前記ガラス繊維が、シランカップリング剤により表面処理されている、請求項1又は2に記載の多層管。
- 前記ガラス繊維が、アミノシランにより表面処理されている、請求項3に記載の多層管。
- 前記第1のポリオレフィン樹脂層に含まれている前記ポリオレフィン樹脂が、ポリプロピレンであり、
前記ポリオレフィン樹脂/ガラス繊維層に含まれている前記ポリオレフィン樹脂が、ポリプロピレンであり、
前記第2のポリオレフィン樹脂層に含まれている前記ポリオレフィン樹脂が、ポリプロピレンである、請求項1〜4のいずれか1項に記載の多層管。 - 前記ポリオレフィン樹脂/ガラス繊維層が、相溶化剤をさらに含む、請求項1〜5のいずれか1項に記載の多層管。