JP6699015B2 - ダイヤモンド基板の製造方法 - Google Patents
ダイヤモンド基板の製造方法 Download PDFInfo
- Publication number
- JP6699015B2 JP6699015B2 JP2016037183A JP2016037183A JP6699015B2 JP 6699015 B2 JP6699015 B2 JP 6699015B2 JP 2016037183 A JP2016037183 A JP 2016037183A JP 2016037183 A JP2016037183 A JP 2016037183A JP 6699015 B2 JP6699015 B2 JP 6699015B2
- Authority
- JP
- Japan
- Prior art keywords
- diamond
- substrate
- pattern
- patterned
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
下地表面にパターン状のダイヤモンドを設ける第一の工程と、該第一の工程で設けたパターン状のダイヤモンドの壁面に付着した異種付着物を除去する第二の工程と、前記第一の工程で設けたパターン状のダイヤモンドからダイヤモンドを成長させて、前記第一の工程で設けたパターン状のダイヤモンドにおけるパターン間隙にダイヤモンドを形成する第三の工程と、を含むことを特徴とするダイヤモンド基板の製造方法を提供する。
図2に示される方法で、ダイヤモンド基板を製造した。
図1に示される方法で、ダイヤモンド基板を製造した。
図2に示される方法で、ダイヤモンド基板を製造した。
まず、直径10.0mm、厚さ1.0mm、表面が(100)面となる両面研磨された単結晶シリコン(Si)基板を準備した。
Claims (6)
- ダイヤモンド基板の製造方法であって、
表面がダイヤモンドではない異種材料から構成される下地の前記表面にダイヤモンドを成長させて、該ダイヤモンドをパターン状に加工してパターン状のダイヤモンドを設け、該パターン状のダイヤモンドにおけるパターン間隙の底部を構成する材料を異種材料とする、又は、前記パターン間隙の底部の少なくとも一部を貫通させる第一の工程と、
該第一の工程で設けたパターン状のダイヤモンドの、パターンの側壁面に付着した、ダイヤモンドではない異種付着物を除去する第二の工程と、
前記第一の工程で設けたパターン状のダイヤモンドからダイヤモンドを成長させて、前記第一の工程で設けたパターン状のダイヤモンドにおけるパターン間隙にダイヤモンドを形成する第三の工程と、
を含むことを特徴とするダイヤモンド基板の製造方法。 - 前記第二の工程において、CF4プラズマを用いて前記ダイヤモンドの壁面に付着した前記異種付着物を除去することを特徴とする請求項1に記載のダイヤモンド基板の製造方法。
- 前記第一の工程において設けるパターン状のダイヤモンドにおけるパターン間隙の深さDと幅Wの比であるD/Wを、0.1以上とすることを特徴とする請求項1又は請求項2に記載のダイヤモンド基板の製造方法。
- 前記第一の工程において設けるパターン状のダイヤモンドにおけるパターン間隙の底部の少なくとも一部を、前記下地表面よりも下方に設けることを特徴とする請求項1に記載のダイヤモンド基板の製造方法。
- 前記第三の工程において、化学気相成長法を用いてダイヤモンドを成長させることを特徴とする請求項1から請求項4のいずれか一項に記載のダイヤモンド基板の製造方法。
- 前記第三の工程において成長させるダイヤモンドにボイドを形成することを特徴とする請求項1から請求項5のいずれか一項に記載のダイヤモンド基板の製造方法。