JP6654648B2 - 繊維強化ポリマー組成物 - Google Patents
繊維強化ポリマー組成物 Download PDFInfo
- Publication number
- JP6654648B2 JP6654648B2 JP2017555220A JP2017555220A JP6654648B2 JP 6654648 B2 JP6654648 B2 JP 6654648B2 JP 2017555220 A JP2017555220 A JP 2017555220A JP 2017555220 A JP2017555220 A JP 2017555220A JP 6654648 B2 JP6654648 B2 JP 6654648B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- polymer composition
- reinforced polymer
- fiber
- fiber reinforced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%のポリプロピレン(PP(
polypropylene)1)と、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の炭素繊維(CF:carbon fiber)と、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の、炭素繊維(CF)以外の繊維(F:fiber)と、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のカップリング剤としての極性変性ポリプロピレン(PMP:polar modified polypropylene)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と
を含む、繊維強化ポリマー組成物を目的とする。
(a)ISO1133にしたがって測定したメルトフローレートMFR2(230℃、2.16kg)が75g/10分以下であり、および/または
(b)融解温度Tmが158〜170℃の範囲内である。
(a)密度が1,200g/cm3以下であり、および/または
(b)ISO178にしたがった引張弾性率が少なくとも8200MPaであり、および/または
(c)ISO527‐2にしたがった引張強度が100〜150MPaの範囲内である。
本発明の繊維強化ポリマー組成物は、ポリプロピレン(PP)、炭素繊維(CF)、炭素繊維(CF)以外の繊維(F)、およびカップリング剤としての極性変性ポリプロピレン(PMP)を含む。
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%のポリプロピレン(PP1)と、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の炭素繊維(CF)と、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の、炭素繊維(CF)以外の繊維(F)と、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のカップリング剤としての極性変性ポリプロピレン(PMP)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と、
を含む。
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%のポリプロピレン(PP1)と、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の炭素繊維(CF)と、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の、炭素繊維(CF)以外の繊維(F)と、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のカップリング剤としての極性変性ポリプロピレン(PMP)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と、
(e)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%の、ISO1133にしたがって測定したメルトフローレートMFR2(230℃、2.16kg)が100g/10分より大きいポリプロピレン(PP2)と
を含むのが好ましい。
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%のポリプロピレン(PP1)と、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の炭素繊維(CF)と、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の、炭素繊維(CF)以外の繊維(F:fiber)と、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のカップリング剤としての極性変性ポリプロピレン(PMP)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と、
(e)繊維強化ポリマー組成物の全重量に基づいて最大20重量%の少なくとも一つの添加剤と
を含む、繊維強化ポリマー組成物を目的とする。
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%のポリプロピレン(PP1)と、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の炭素繊維(CF)と、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の、炭素繊維(CF)以外の繊維(F:fiber)と、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のカップリング剤としての極性変性ポリプロピレン(PMP)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と、
(e)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%の、一つ以上のさらなる極性変性ポリプロピレン(PMP2)であって、
一つ以上のさらなる極性変性ポリプロピレン(PMP2)の全重量に基づいて0.5〜3重量%の量の、極性基から誘導される基を含む、
一つ以上のさらなる極性変性ポリプロピレン(PMP2)と
を含む、繊維強化ポリマー組成物を目的とする。
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%のポリプロピレン(PP1)と、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の炭素繊維(CF)と、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の、炭素繊維(CF)以外の繊維(F:fiber)と、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のカップリング剤としての極性変性ポリプロピレン(PMP)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と、
(e)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%の、ISO1133にしたがって測定したメルトフローレートMFR2(230℃、2.16kg)が100g/10分より大きいポリプロピレン(PP2)と、
(f)繊維強化ポリマー組成物の全重量に基づいて最大20重量%の少なくとも一つの添加剤と、
(g)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%の、一つ以上のさらなる極性変性ポリプロピレン(PMP2)であって、
一つ以上のさらなる極性変性ポリプロピレン(PMP2)の全重量に基づいて0.5〜3重量%の量の、極性基から誘導される基を含む、
一つ以上のさらなる極性変性ポリプロピレン(PMP2)と
を含む、繊維強化ポリマー組成物を目的とするのが好ましい。
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%、より好ましくは30〜80重量%、最も好ましくは50〜65重量%など、40〜70重量%のポリプロピレン(PP1)と、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%、より好ましくは5〜40重量%、最も好ましくは15〜25重量%など、10〜30重量%の炭素繊維(CF)と、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%、より好ましくは5〜40重量%、最も好ましくは5〜15重量%など、5〜20重量%の、炭素繊維(CF)以外の繊維(F:fiber)と、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%、より好ましくは2〜8重量%、最も好ましくは4〜5重量%など、3〜6重量%のカップリング剤としての極性変性ポリプロピレン(PMP)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と、
(e)繊維強化ポリマー組成物の全重量に基づいて最大20重量%の、より好ましくは0.1〜10重量%、最も好ましくは0.1〜2重量%など、0.1〜5重量%の少なくとも一つの添加剤と
からなる、繊維強化ポリマー組成物を特に目的とする。
(a)繊維強化ポリマー組成物の全重量に基づいて20〜89重量%、より好ましくは30〜80重量%、最も好ましくは50〜65重量%など、40〜70重量%のポリプロピレン(PP1)、
(b)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%、より好ましくは5〜40重量%、最も好ましくは15〜25重量%など、10〜30重量%の炭素繊維(CF)、
(c)繊維強化ポリマー組成物の全重量に基づいて5〜60重量%、より好ましくは5〜40重量%、最も好ましくは5〜15重量%など、5〜20重量%の炭素繊維(CF)以外の繊維(F:fiber)、
(d)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%、より好ましくは2〜8重量%、最も好ましくは4〜5重量%など、3〜6重量%のカップリング剤としての極性変性ポリプロピレン(PMP)であって、
極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)、および
(e)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%、より好ましくは2〜8重量%、最も好ましくは4〜6重量%など、4〜7重量%のISO1133にしたがって測定したメルトフローレートMFR2(230℃、2.16kg)が100g/10分より大きいポリプロピレン(PP2)、および/または
(f)繊維強化ポリマー組成物の全重量に基づいて最大20重量%、より好ましくは0.1〜10重量%、最も好ましくは0.1〜2重量%など、0.1〜5重量%の少なくとも一つの添加剤、および/または
(g)繊維強化ポリマー組成物の全重量に基づいて1〜10重量%、より好ましくは2〜8重量%、最も好ましくは4〜5重量%など、3〜6重量%の一つ以上のさらなる極性変性ポリプロピレン(PMP2)であって、
一つ以上のさらなる極性変性ポリプロピレン(PMP2)の全重量に基づいて0.5〜3重量%の量の、極性基から誘導される基を含む、
一つ以上のさらなる極性変性ポリプロピレン(PMP2)
からなる。
(i)モノカルボン酸およびポリカルボン酸の塩、例えば安息香酸ナトリウムまたはtert‐ブチル安息香酸アルミニウム、および
(ii)ジベンジリデンソルビトール(例えば1,3:2,4ジベンジリデンソルビトール)、およびメチルジベンジリデンソルビトール、エチルジベンジリデンソルビトールまたはジメチルジベンジリデンソルビトール等のC1〜C8‐アルキル置換ジベンジリデンソルビトール誘導体(例えば1,3:2,4ジ(メチルベンジリデン)ソルビトール)、または1,2,3‐トリデオキシ‐4,6:5,7‐ビス‐O‐[(4‐プロピルフェニル)メチレン]‐ノニトール等の置換ノニトール誘導体、および
(iii)リン酸のジエステルの塩類、例えばナトリウム2,2’‐メチレンビス(4,6‐ジ‐tert‐ブチルフェニル)ホスフェートまたはアルミニウム‐ヒドロキシ‐ビス[2,2’‐メチレン‐ビス(4,6‐ジ‐t‐ブチルフェニル)ホスフェート]、および
(iv)ビニルシクロアルカンポリマーおよびビニルアルカンポリマー、ならびに
(v)これらの混合物
からなる群より選択されるのが好ましい。
(a)密度が1.200g/cm3以下であり、より好ましくは0.800kg/m3〜1.200g/cm3の範囲内であり、最も好ましくは1.000g/cm3〜1.100g/cm3の範囲内など、0.900kg/m3〜1.100g/cm3の範囲内であり、および/または
(b)ISO527‐2にしたがった引張弾性率が少なくとも8200MPaであり、より好ましくは少なくとも9000MPaであり、最も好ましくは10000MPa〜13000MPaの範囲内など、少なくとも10000MPaであり、および/または
(c)ISO527‐2にしたがった引張強度が100〜150MPaの範囲内であり、より好ましくは110〜150MPaの範囲内であり、最も好ましくは130MPa〜150MPaの範囲内など、120〜150の範囲内である。
(a)密度が1.200g/cm3以下であり、より好ましくは0.800g/cm3〜1.200g/cm3の範囲内であり、最も好ましくは1.000g/cm3〜1.100g/cm3の範囲内など、0.900g/cm3〜1.100g/cm3の範囲内であり、または
(b)ISO527‐2にしたがった引張弾性率が少なくとも8200MPaであり、より好ましくは少なくとも9000MPaであり、最も好ましくは10000MPa〜13000MPaの範囲内など、少なくとも10000MPaであり、
(c)ISO527‐2にしたがった引張強度が100〜150MPaの範囲内であり、より好ましくは110〜150MPaの範囲内であり、最も好ましくは130MPa〜150MPaの範囲内など、120〜150の範囲内である。
(a)密度が1.200g/cm3以下であり、より好ましくは0.800g/cm3〜1.200g/cm3の範囲内であり、最も好ましくは1.000g/cm3〜1.100g/cm3の範囲内など、0.900g/cm3〜1.100g/cm3の範囲内であり、および
(b)ISO527‐2にしたがった引張弾性率が少なくとも8200MPaであり、より好ましくは少なくとも9000MPaであり、最も好ましくは10000MPa〜13000MPaの範囲内など、少なくとも10000MPaであり、および
(c)ISO527‐2にしたがった引張強度が100〜150MPaの範囲内であり、より好ましくは110〜150MPaの範囲内であり、最も好ましくは130MPa〜150MPaの範囲内など、120〜150の範囲内である。
(a)ポリプロピレン(PP1)と、
(b)炭素繊維(CF)と、
(c)炭素繊維(CF)以外の繊維(F)と、
(d)極性変性ポリプロピレン(PMP)と、
(e)任意のポリプロピレン(PP2)と、
(f)任意の少なくとも一つの添加剤と、
(g)任意の一つ以上のさらなる極性変性ポリプロピレン(PMP2)と
を押出機に加え、それらを押出して前記繊維強化ポリマー組成物を得るステップを含む。
繊維強化ポリマー組成物は、ポリマー成分を含まなければならない。軽量でありながら高い剛性および耐衝撃性をもつ等のバランスの良い機械的特性を達成するために、ポリマーは特定のポリプロピレンを含まなければならない。良好な剛性は、とりわけポリプロピレン(PP1)の存在により達成することができる。高分子量のポリプロピレン(PP1)であるのが好ましい。
(i)プロピレンと、
(ii)エチレンおよび/または少なくとも一つのC4〜C20α‐オレフィンであって、エチレン、1‐ブテン、1‐ペンテン、1‐ヘキセンおよび1‐オクテンからなる群より選択されるのが好ましく、エチレンおよび/または1‐ブテンであるのがより好ましく、エチレンであるのがなお好ましい、少なくとも一つのα‐オレフィンと
から誘導される単位を含むのが好ましく、これらから誘導される単位からなるのが好ましい。
a)ポリプロピレンマトリックス(M‐HECO)と、
b)弾性プロピレンコポリマー(E)と
を含むのが好ましい。
(i)プロピレンと、
(ii)エチレンおよび/または少なくとも一つのC4〜C8α‐オレフィンであって、エチレン、1‐ブテン、1‐ペンテン、1‐ヘキセンおよび1‐オクテンからなる群より選択されるのが好ましく、エチレンおよび/または1‐ブテンであるのがより好ましく、エチレンであるのがなお好ましい、少なくとも一つのα‐オレフィンと
から誘導される単位を含むのが好ましく、これらから誘導される単位からなるのが好ましい。
CH2=CH‐CHR3R4
であり、式中、R3およびR4は一緒になって5員または6員の飽和、不飽和または芳香環を形成するか、または独立して1〜4個の炭素原子を含むアルキル基を表し、変性された触媒が本発明によるポリプロピレン(PP1)の調製のために使用される。重合されたビニル化合物は、α核形成剤として作用する。触媒の変性ステップにおける固体触媒成分に対するビニル化合物の重量比は、最大5(5:1)であるのが好ましく、最大3(3:1)であるのが好ましく、0.5(1:2)〜2(2:1)であるのが最も好ましい。最も好ましいビニル化合物は、ビニルシクロヘキサン(VCH)である。
繊維強化ポリマー組成物は、高い剛性および高い耐衝撃性等のバランスの良い機械的性質を有すべきものと認められる。優れた剛性を確保するために、繊維強化ポリマー組成物は炭素繊維(CF)を含む。したがって、繊維強化ポリマー組成物の一つの必須成分は炭素繊維(CF)である。
本繊維強化ポリマー組成物は、良好な衝撃挙動を有するものと認められる。したがって、繊維強化ポリマー組成物の別の必須成分は、炭素繊維以外の繊維(F)である。
繊維強化ポリマー組成物においてマトリックスとして働くポリマー成分中の炭素繊維(CF)および炭素繊維(CF)以外の繊維(F)のより容易かつ均一な分散を達成するために、繊維強化ポリマー組成物は特定のカップリング剤を含む。
繊維強化ポリマー組成物は、さらなる任意成分を含みうる。加工性をさらに改善するために、メルトフローレートが高いさらなるポリマーを添加することが有利でありうる。したがって繊維強化ポリマー組成物は、ISO1133にしたがって測定したメルトフローレートMFR2(230℃、2.16kg)が100g/10分より大きく、100〜2000g/10分の範囲内であるのがより好ましく、100〜1500g/10分の範囲内であるのがなお好ましく、200〜1000g/10分の範囲内であるのがさらに好ましく、350〜800g/10分の範囲内であるのが最も好ましい追加のポリプロピレン(PP2)を含むのが好ましい。
本発明は、本発明による繊維強化ポリマー組成物を含む物品も目的とする。物品は、本発明による繊維強化ポリマー組成物を80〜99.9重量%など、少なくとも80重量%含むのが好ましく、90〜99.9重量%など、少なくとも90重量%含むのがより好ましく、95〜99.9重量%など、少なくとも95重量%含むのがなお好ましい。一実施形態では、物品は、本発明による繊維強化ポリマー組成物からなる。
別段の定めがない限り、本発明の上述の一般的説明にも以下の実施例にも以下の用語の定義および決定方法が当てはまる。
定量的核磁気共鳴(NMR:nuclear‐magnetic resonance)分光法を用いて、ポリプロピレンホモポリマーのアイソタクティシティおよびレギオ規則性を定量する。
[mmmm]%=100*(mmmm/すべてのペンタッドの合計)
17.7および17.2ppmの二つのメチル部位の存在によって2,1エリスロレギオ欠陥の存在が示され、他の特徴的部位によって確認された。他のタイプのレギオ欠陥に対応する特徴的シグナルは、観察されなかった(Resconi,L.,Cavallo,L.,Fait,A.,Piemontesi,F.,Chem.Rev.2000,100,1253)。
P21e=(Ie6+Ie8)/2
P12=ICH3+P12e
プロペンの総量を、一次挿入プロペンおよび他のすべての存在するレギオ欠陥の合計として定量した:
Ptotal=P12+P21e
すべてのプロペンに対して2,1エリスロレギオ欠陥のモルパーセントを定量した:
[21e]mol.%=100*(P21e/Ptotal)
コモノマー取り込みの重量パーセントを、モル分率から計算した。
MFR2(230℃)は、ISO1133(230℃、2.16kg荷重)にしたがって測定する。
MFR2(190℃)は、ISO1133(190℃、2.16kg荷重)にしたがって測定する。
MFR(170℃)は、ISO1133(170℃、1.2kg荷重)の一般的定義に則して測定する。
固有粘度は、DIN ISO1628/1、1999年10月にしたがって(デカリン中135℃で)測定する。
使用化学物質:
2‐エチルヘキサノール、Amphochem提供
3‐ブトキシ‐2‐プロパノール‐(DOWANOL(商標)PnB)、Dow提供
シトラコン酸ビス(2‐エチルヘキシル)、SynphaBase提供
TiCl4、Millenium Chemicals提供
トルエン、Aspokem提供
Viscoplex(登録商標)1‐254、Evonik提供
ヘプタン、Chevron提供
洗浄2:30mlのTiCl4と1mlのドナーとの混合物で洗浄を行った。
洗浄3:100mlのトルエンで洗浄を行った。
洗浄4:60mlのヘプタンで洗浄を行った。
以下の本発明の実施例IE1ならびに比較実施例CE1およびCE2は、同方向回転二軸スクリュ押出機(CoperionのZSK40)でのコンパウンディングにより調製した。以下のプロセスパラメータを用いた:
‐ スループット100kg/時
‐ スクリュ速度100〜150rpm
‐ バレル温度250℃フラット
‐ 3つの穴を開けた5mm穴のダイプレート
「PP‐1」は、プロピレンブロックコポリマーであり、20℃の温度および54バールの圧力で液体充填して運転した45dm3の容積の撹拌槽型反応器で調製されている。反応器にプロピレンを反応器内の平均滞留時間が0.36時間となるような量で、0.98g/時の水素、70g/時のエチレン、および4.3g/時の上述の触媒調製にしたがって調製され、トリエチルアルミニウム(TEA:triethyl alminium)を助触媒とし、ジシクロペンチルジメトキシシラン(DCPDMS:dicyclopentyldimethoxysilane)を外部ドナーとし、TEA/Tiのモル比が約76mol/molであり、TEA/DCPDMSが8mol/molとした重合触媒とともに供給した。この予備重合反応器からのスラリーを、プロピレンに対する水素のモル比が0.044mol/kmolとなるように170kg/時のプロピレンおよび水素とともに150dm3の容積のループ反応器に導いた。ループ反応器は、80℃の温度および51バールの圧力で運転した。プロピレンコポリマーの生産速度は29kg/時であり、メルトフローレートMFR2は0.12g/10分であった。
「PP‐2」は、メルトフローレートMFR2(230℃)が75g/10分であり、融解温度が130〜170℃であるBorealis AGの市販のプロピレンホモポリマーHJ120UBである。
「繊維1」は、生産前の呼び径が10μmであり平均長が4.5mmであるNEGのガラス繊維ECS 03 T‐480Hである。
「繊維2」は、呼び径が17μmであるPPGのガラス繊維TufRov 4599であり、生産前にはエンドレス粗糸であり、ペレタイジング後には長さが約10mmである。
「炭素繊維」は、80重量%の炭素繊維を含む不織布であり、ニードルパンチにより生産されている。炭素繊維は、平均直径が7μmである。
「PMP」は、MFI(170℃)が71g/10分、無水マレイン酸含有量が2.2〜2.4重量%の、ドイツBYK Co.Ltdの(無水マレイン酸で官能化された)エチレンポリプロピレンコポリマー「TSPP3598GB」であり、さらにこのエチレンポリプロピレンコポリマーは、エチレン含有量が5.6重量%である。
「PMP2」は、MFR2(190℃)が80g/10分超、無水マレイン酸含有量が1.4重量%の、ドイツBYK Co.Ltdの(無水マレイン酸で官能化された)エチレンポリプロピレンコポリマー「TPPP8112FA」である。
Claims (19)
- (a)繊維強化ポリマー組成物の全重量に基づいて30〜80重量%のポリプロピレン(PP1)と、
(b)前記繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の炭素繊維(CF)と、
(c)前記繊維強化ポリマー組成物の全重量に基づいて5〜60重量%の、炭素繊維(CF)以外の繊維(F)と、
(d)前記繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のカップリング剤としての極性変性ポリプロピレン(PMP)と、
(e)前記繊維強化ポリマー組成物の全重量に基づいて1〜10重量%のポリプロピレン(PP2)であって、
前記ポリプロピレン(PP1)は、ISO1133にしたがって測定したメルトフローレートMFR2(230℃、2.16kg)が100g/10分以下であり、
前記ポリプロピレン(PP2)は、ISO1133にしたがって測定したメルトフローレートMFR2(230℃、2.16kg)が100g/10分より大きく、
前記極性変性ポリプロピレン(PMP)の全重量に基づいて1〜5重量%の量の、極性基から誘導される基を含む、
極性変性ポリプロピレン(PMP)と
を含む、繊維強化ポリマー組成物。 - 前記ポリプロピレン(PP1)は、融解温度Tmが158〜170℃の範囲内である、請求項1に記載の繊維強化ポリマー組成物。
- 前記ポリプロピレン(PP1)は、プロピレンホモポリマー(H‐PP1)である、請求項1または2に記載の繊維強化ポリマー組成物。
- 前記炭素繊維(CF)は、不織布の形態である、請求項1〜3のいずれか一項に記載の繊維強化ポリマー組成物。
- 前記不織布は、前記不織布の全重量に基づいて少なくとも50重量%の炭素繊維(CF)を含む、請求項4に記載の繊維強化ポリマー組成物。
- 前記繊維(F)は、ガラス繊維、金属繊維、鉱物繊維、セラミック繊維およびこれらの混合物を含む群より選択される、請求項1〜5のいずれか一項に記載の繊維強化ポリマー組成物。
- 前記炭素繊維(CF)および/または前記繊維(F)はサイジング剤を含む、請求項1〜6のいずれか一項に記載の繊維強化ポリマー組成物。
- 前記極性変性ポリプロピレン(PMP)は、酸無水物、カルボン酸、カルボン酸誘導体、一級および二級アミン、ヒドロキシル化合物、オキサゾリンならびにエポキシドからなる群より選択される極性基、さらにイオン性化合物から誘導される基を含む、請求項1〜7のいずれか一項に記載の繊維強化ポリマー組成物。
- 前記極性変性ポリプロピレン(PMP)は、無水マレイン酸によりグラフトされたプロピレンポリマーである、請求項1〜8のいずれか一項に記載の繊維強化ポリマー組成物。
- 前記極性変性ポリプロピレン(PMP)は、無水マレイン酸によりグラフトされたプロピレンコポリマーである、請求項9に記載の繊維強化ポリマー組成物。
- 前記無水マレイン酸によりグラフトされたプロピレンコポリマーは、コモノマー単位としてエチレンを含む、請求項10に記載の繊維強化ポリマー組成物。
- 前記繊維強化ポリマー組成物は、前記繊維強化ポリマー組成物の全重量に基づいて最大20重量%の量の少なくとも一つの添加剤をさらに含む、請求項1〜11のいずれか一項に記載の繊維強化ポリマー組成物。
- 前記繊維強化ポリマー組成物は、
(a)密度が1,200g/cm3以下であり、および/または
(b)ISO527‐2にしたがった引張弾性率が少なくとも8200MPaであり、および/または
(c)ISO527‐2にしたがった引張強度が100〜150MPaの範囲内である、
請求項1〜12のいずれか一項に記載の繊維強化ポリマー組成物。 - 請求項1〜13のいずれか一項に記載の繊維強化ポリマー組成物を含む物品。
- 前記物品は成形物品である、請求項14に記載の物品。
- 前記物品は、射出成形物品または発泡物品である、請求項14または15に記載の物品。
- 前記物品は、洗濯機もしくは食洗機の一部であるか、または自動車用物品である、請求項14〜16のいずれか一項に記載の物品。
- 前記自動車用物品は、車の内装品および外装品である、請求項17に記載の物品。
- 前記自動車用物品は、器械キャリア、シュラウド、構造キャリア、バンパ、サイドトリム、ステップ補助、ボティパネル、スポイラ、ダッシュボード、内装トリムである、請求項17または18に記載の物品。