JP6482222B2 - 樹脂組成物及びそれらを用いた成形体 - Google Patents
樹脂組成物及びそれらを用いた成形体 Download PDFInfo
- Publication number
- JP6482222B2 JP6482222B2 JP2014195943A JP2014195943A JP6482222B2 JP 6482222 B2 JP6482222 B2 JP 6482222B2 JP 2014195943 A JP2014195943 A JP 2014195943A JP 2014195943 A JP2014195943 A JP 2014195943A JP 6482222 B2 JP6482222 B2 JP 6482222B2
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- resin
- isophthalic acid
- modified polyethylene
- polyethylene terephthalate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
またポリ乳酸と耐熱性樹脂を混合した樹脂、エポキシ化合物、カルボジイミド化合物を溶融混合することで耐加水分解性、耐熱性、引張伸度を向上させた樹脂組成物も作製されている(特許文献2)。
特許文献2では、ポリ乳酸を含む樹脂組成物であるが、ポリ乳酸が生分解であるため、例えば40℃以上の高温環境下での長期保管において、樹脂が分解してしまうという問題が生じる。
前記エポキシ基を有するオレフィン系相溶化剤(B)がエチレン―グリシジルメタクリレート共重合体であることが好ましい。
前記イソフタル酸変性ポリエチレンテレフタレート(A)のイソフタル酸変性率が2〜30モル%であることが好ましい。
また、本発明は、基材の少なくとも片面に前記樹脂組成物からなる層が積層された積層体を提供する。
また、本発明は、共押出法によって少なくとも片方の表面層に前記樹脂組成物からなる層を形成したことを特徴とする多層フィルムまたは多層シートを提供する。
また、本発明は、内容物と直接接触する樹脂層が前記樹脂組成物からなることを特徴とする容器または成形品を提供する。
本実施形態の樹脂組成物は、以下の樹脂(A)、樹脂(B)、樹脂(C)からなり、樹脂(A)の分子両末端に樹脂(B)、樹脂(C)をそれぞれ化学結合させ、屈曲性と成形性を向上させ、かつ、高温環境下でも薬剤や化粧水などの有効成分が吸着しにくい樹脂組成物である。
樹脂(A):イソフタル酸変性ポリエチレンテレフタレート
樹脂(B):オレフィン系相溶化剤
樹脂(C):ポリカルボジイミド化合物
「I−PET」・・・イソフタル酸変性ポリエチレンテレフタレート(イソフタル酸変性率23モル%、極限粘度IV=0.68dl/g、ρ=1.34g/cm3、Tmなし)
「E−GMA(1)」・・・エチレン―グリシジルメタクリレート共重合体(Tm=87℃、MFR=380g/10分、GMA含有率19重量%)
「E−GMA(2)」・・・エチレン―グリシジルメタクリレート共重合体(Tm=105℃、MFR=3g/10分、GMA含有率6重量%)
「PCI」・・・ポリカルボジイミド(軟化温度55℃、製品名:カルボジライト(登録商標)LA−1、日清紡ケミカル(株)製)
(1)(溶融混合ペレット作製)
表1に示す組成により、各実施例および比較例の溶融混合ペレットを小型ストランドダイ押出機で作製した。
(2)(プレスシート)
続けて、溶融混合により作製したペレットを用いて、熱プレス機で1mmの厚さに成形する方法によりプレスシートを製造した。
(1)(メルトフローレート(MFR)測定)
メルトフローレート(MFR)は、220℃または240℃で、2.16kg荷重における値(g/10分)を測定した。MFR測定は、Tダイ押出成形時の成形加工性、ダイレクトブロー成形におけるドローダウンの指標になることから実施している。
1mmの厚さに成形したプレスシートを15mm(巾)×100mm(長さ)の大きさに切り、MIT耐折度試験機(テスター産業(株)製)を用いて、1.5kgf(14.7N)、角度135°で折り曲げ試験を実施し、破断するまでの折り曲げ回数を測定した。
有効成分として酢酸α−トコフェロール(ビタミンEアセテート)を含む市販の化粧水3mlを15mm(外径)×32mm(高さ)の遮光性ガラス瓶に入れ、同じガラス瓶に7mm(巾)×25mm(高さ)の大きさに切った厚さ1mmのプレスシートを入れ、蓋を閉め密閉し、40℃で1ヶ月保管した後に開封し、化粧水中の酢酸α−トコフェロールの残存量を高速液体クロマトグラフィ法で定量し、前記残存量をもとに有効成分の残存率を算出した。
小型Tダイ押出機を用いて厚さ50μmのフィルムを作製した。Tダイの幅は150mm、Tダイ―冷却ロール間の距離(エアギャップ)は50mm、押出機の設定温度、樹脂の押出量は実施例、比較例全て同じ条件で行ない、製膜したフィルム幅から計算式{(Tダイ幅)−(フィルム幅)}/2を用いて製膜時のネックインを算出した。
またフィルムのネックインにおいても本発明(実施例1)はI−PET単体(比較例1)よりもネックインが小さくなり、フィルムの加工性が向上することが確認できている。
I−PET、PCIの2種混合(比較例5,6)では、折曲試験における破断までの折曲回数はI−PETよりも低下するという結果が得られた。酢酸トコフェロールの残存率も1ヶ月後ではI−PET単体とほぼ同等レベルであるが、3ヶ月後ではPCIの配合比率が高くなることで残存率が低下するという結果も得られた(比較例6)。
Claims (8)
- イソフタル酸変性ポリエチレンテレフタレート(A)とエポキシ基を有するオレフィン系相溶化剤(B)およびポリカルボジイミド化合物(C)との溶融混合により得られる樹脂を含む樹脂組成物であって、前記イソフタル酸変性ポリエチレンテレフタレート(A)の分子両末端に、前記エポキシ基を有するオレフィン系相溶化剤(B)と前記ポリカルボジイミド化合物(C)を化学結合させた樹脂を含む樹脂組成物。
- 前記イソフタル酸変性ポリエチレンテレフタレート(A)と前記エポキシ基を有するオレフィン系相溶化剤(B)と前記ポリカルボジイミド化合物(C)との合計を100質量%とするうち、前記イソフタル酸変性ポリエチレンテレフタレート(A)が85〜98質量%、前記エポキシ基を有するオレフィン系相溶化剤(B)が1〜13質量%、前記ポリカルボジイミド化合物(C)が1〜9質量%の範囲内で含まれることを特徴とする請求項1に記載の樹脂組成物。
- 前記エポキシ基を有するオレフィン系相溶化剤(B)がエチレン―グリシジルメタクリレート共重合体である請求項1または2に記載の樹脂組成物。
- 前記イソフタル酸変性ポリエチレンテレフタレート(A)のイソフタル酸変性率が2〜30モル%である請求項1ないし3のいずれかに記載の樹脂組成物。
- 請求項1ないし4のいずれかに記載の樹脂組成物から形成されるフィルムまたはシート。
- 基材の少なくとも片面に請求項1ないし4のいずれかに記載の樹脂組成物からなる層が積層された積層体。
- 共押出法によって少なくとも片方の表面層に請求項1ないし4のいずれかに記載の樹脂組成物からなる層を形成したことを特徴とする多層フィルムまたは多層シート。
- 内容物と直接接触する樹脂層が請求項1ないし4のいずれかに記載の樹脂組成物からなることを特徴とする容器または成形品。