JP6452273B2 - 吸水性樹脂の処理方法 - Google Patents
吸水性樹脂の処理方法 Download PDFInfo
- Publication number
- JP6452273B2 JP6452273B2 JP2013131690A JP2013131690A JP6452273B2 JP 6452273 B2 JP6452273 B2 JP 6452273B2 JP 2013131690 A JP2013131690 A JP 2013131690A JP 2013131690 A JP2013131690 A JP 2013131690A JP 6452273 B2 JP6452273 B2 JP 6452273B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- absorbent resin
- resin powder
- metal salt
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、使用後の吸収性物品が含有する吸水性樹脂の処理方法に関する。
高齢化により、介護用の大人用使い捨て紙おむつを使用する人が増加している。また、世界的にみても、子供用使い捨て紙おむつを使用する人口が増加している。近年、使い捨て紙おむつの使用量が急速に増大している。使用後の紙おむつは、汚物でよごれているため、再利用することなく廃棄される。廃棄された紙おむつは、通常、焼却処理されている。しかし、紙おむつの廃棄量の増大にともなって、環境保護の観点から、紙おむつを構成する材料を再利用することが検討されている。
特許文献１には、使用済み紙おむつをビニールとそれ以外に分離する使用済み紙おむつの分離方法であって、裁断又は破砕された使用済み紙おむつに水と脱水剤を加えて混合し、使用済み紙おむつに含まれる吸水ポリマーを脱水剤と反応させて脱水させる反応工程と、その脱水済みの混合物を回転ドラムに投入して溶解し、ビニール以外の溶解物を沈殿させて回転ドラム外に排出させ、ビニールを回転ドラム内に残留させる分離工程と、その残留したビニールを回転ドラム外に吸引して回収する回収工程とを有することを特徴とする、使用済み紙おむつの分離方法が開示されている。
特許文献２には、裁断された使用済紙おむつと処理用液体とを受け入れて攪拌し、前記紙おむつの母材分及び吸水性物質分を含む再生用物質と、プラスチック分と、を分離する攪拌分離槽と；前記攪拌分離槽から排出された前記再生用物質を含む前記処理用液体を受け入れる第１の回収槽と；前記攪拌分離槽から排出された前記再生用物質を含む前記処理用液体を受け入れる第２の回収槽であって、前記第１の回収槽とは別の第２の回収槽とを備える；使用済紙おむつの処理装置が開示されている。
特許文献３には、使用済み紙おむつを収容する回転ドラムと、この回転ドラムの少なくとも下端部分を収納して内部に水を溜める水槽部と、この水槽部内へ水を供給する水供給手段と、回転ドラムを回転駆動して水に浸漬した紙おむつを水溶物と不溶物と分離解体にする駆動手段と、分離解体された水溶物を汚水とともに下水処理施設側へ排出する排出手段と、を備えたことを特徴とする紙おむつ処理装置が開示されている。
特許文献４には、吸水してゲル状となっている吸水性樹脂を含有する汚れた衛生用品を粉砕し、この粉砕された衛生用品を消毒剤を含有する水中に分散させて、衛生用品に付着していた汚れの一部を前記衛生用品の粉砕物から分離することを特徴とする吸水してゲル状となっている吸水性樹脂を含有する汚れた衛生用品からのその素材の回収方法が開示されている。
特許文献５には、粉状プラスチック材料乾燥物及び吸水した吸水性樹脂から回収された吸水性樹脂を含有して１ミリメートル以上の粒度の粒状物に形成されていることを特徴とする粒状の排泄物処理材が開示されている。
吸水性樹脂粉末が、吸水することにより凝集してなる吸水性樹脂の凝集物は、多量の水分を吸水し、さらに表面積が小さいために乾燥することが難しいという問題があった。特に、吸水して膨潤している吸水性樹脂に脱水剤（例えば、塩化カルシウム）を添加して脱水処理した場合にも、含水率は少し低下するものの、なお含水率が高く、吸水性樹脂の凝集物を乾燥することが困難であった。そのため、使い捨て紙おむつを再利用する場合に、吸水して凝集した吸水性樹脂の効率的な処理方法が求められている。
本発明は、前記事情に鑑みてなされたものであって、使用後の吸収性物品が含有する吸水性樹脂粉末を再利用するための処理方法を提供することを課題とする。
本発明は、前記事情に鑑みてなされたものであって、使用後の吸収性物品が含有する吸水性樹脂粉末を再利用するための処理方法を提供することを課題とする。
前記課題を解決する本発明の吸水性樹脂の処理方法は、吸水性樹脂粉末が、吸水することにより凝集してなる吸水性樹脂の凝集物に、弱酸のアルカリ金属塩を加えて混合することを特徴とする。
本発明者が鋭意検討した結果、脱水剤（例えば、塩化カルシウム）によって脱水処理した吸水性樹脂は、吸水性樹脂を構成するアクリル酸のカルボキシル基が、脱水剤の２価金属イオンによって、架橋構造を形成して、強い凝集力によって凝集していることを見い出した。そして、２価金属イオンによって架橋が形成されている吸水性樹脂粉末の凝集物に、弱酸のアルカリ金属塩を加えて混合することにより、脱水剤の２価金属イオンとアルカリ金属イオンとがイオン交換する。その結果、２価金属イオンによる架橋が切断される。金属架橋が切断されると、凝集力が低下するので、吸水性樹脂粉末の凝集物は、もとの粒状へと変化する。粒状の吸水性樹脂は、表面積が大きく容易に乾燥しやすい。
本発明によれば、使用後の吸収性物品が含有する吸水性樹脂粉末を再資源化することができる。得られた吸水性樹脂粉末は、土壌改良剤、固形燃料などとして好適に利用しうる。
本発明の吸水性樹脂の処理方法は、吸水性樹脂粉末が、吸水することにより凝集してなる吸水性樹脂粉末の凝集物に、弱酸のアルカリ金属塩を加えて混合することを特徴とする。
まず、吸収性物品の処理工程について図面を参照しながら説明するが、本発明は図面に示した処理工程に限定されない。図１には、吸収性物品の処理工程の一例を示した。第１工程は、汚物が付着した吸収性物品の洗浄工程である。まず、裁断した使用後の吸収性物品を、処理液体に投入する。処理液体としては、水が好適に用いられる。処理液体中で、撹拌処理することにより、吸収性物品に付着した汚物を洗浄することができる。また、吸収性物品を構成する材料の比重による分離が可能となる。
第２工程は、吸水性樹脂の脱水処理である。この脱水処理により、吸水性樹脂の吸水性が失われる。脱水剤としては、２価金属塩が好適に使用され、塩化カルシウムがより好適に使用される。２価金属塩で処理することによって、吸水性樹脂粉末を構成するアクリル酸のカルボキシル基が架橋される。その結果、吸水性樹脂粉末の凝集物の体積が縮小する。凝集物の体積変化により、凝集物から水が排出される。この脱水処理により、吸水性樹脂粉末の含水率が、約９８質量％から約７０質量％に低下する。
第３工程は、プラスチック成分回収工程である。吸収性物品に使用されていた不織布、フィルムなどのプラスチック成分が回収される。回収されたプラスチック成分は、さらに洗浄されて、油化・炭化原料などとして再利用されることが好ましい。第４工程は、パルプ回収工程である。第４工程では、吸収体を構成していたパルプが回収される。回収されたパルプは、さらに洗浄されて、再利用されることが好ましい。
第５工程は、パルプ回収後の汚水の処理工程である。この汚水には、吸収性物品として使用されていた吸水性樹脂粉末が多く含まれ、パルプの残渣、し尿などが含まれている。汚水の沈降物や汚水の濃縮物は、汚泥として扱われる。汚泥には、吸水性樹脂粉末が凝集物として存在している。しかしながら、汚泥中には、吸水性樹脂粉末の凝集物が多量に含まれているため、汚泥を乾燥しにくいという問題がある。特に、そのまま乾燥しても、表面のみが乾燥され凝集物の内部は乾燥されないという問題がある。本発明の処理方法では、この汚泥に対して、弱酸のアルカリ金属塩を加える。弱酸のアルカリ金属塩は、汚泥中に含まれる吸水性樹脂粉末の凝集物に作用する。弱酸のアルカリ金属塩で処理することにより、２価金属イオンとアルカリ金属イオンとの間で、イオン交換反応が起こる。その結果、金属架橋が切断されることにより、吸水性樹脂粉末の凝集物を容易に粒状化することができる。粒状化された吸水性樹脂は、表面積が増加するので、容易に乾燥させることができる。
図２は、吸水性樹脂粉末の凝集状態の変化を示す図である。図２（ａ）は、吸水性樹脂粉末１の凝集物を示している。吸水性樹脂粉末１は、脱水剤の２価金属イオンにより金属架橋（−ＣＯＯ-・Ｍ２＋・-ＯＯＣ−）により凝集している。２価金属イオンＭ２＋とアルカリ金属イオンＭ＋とがイオン交換することによって、金属架橋が切断される（−ＣＯＯ-Ｍ+ Ｍ+-ＯＯＣ−）。その結果、吸収性樹脂粉末の凝集物は、粒状へと変化する（図２（ｂ））。
前記弱酸のアルカリ金属塩の添加量は、脱水剤で処理した含水状態の吸水性樹脂１００質量部に対して、１質量部以上が好ましく、３質量部以上がより好ましく、１００質量部以下が好ましく、３０質量部以下がより好ましい。
吸水した吸水性樹脂粉末の凝集物と、弱酸のアルカリ金属塩との混合は、特に限定されないが、たとえば愛知電機株式会社製ロッキングミキサーＢＨＲ型などを用いて行うことができる。前記混合は、特に限定されないが、５℃以上、１３０℃以下の温度範囲で、５分間〜６時間行うことが好ましい。混合するとともに、脱水を同時に行ってもよい。混合脱水は特に限定されないが８０℃以上、１３０℃以下の温度範囲で、５分間〜６時間行うことが好ましい。常圧、減圧、加圧いずれの条件で行ってもよい。
前記混合により、吸収樹脂粉末の凝集物は、粒状若しくは粉末状の吸収性樹脂に変化する。粒状若しくは粉末状の吸収性樹脂粉末は、表面積が大きいので、容易に乾燥させることができる。
前記弱酸のアルカリ金属塩の弱酸成分としては、吸水性樹脂粉末の構成成分であるアクリル酸と同じ程度若しくは弱い酸であることが好ましい。すなわち、弱酸成分として、アクリル酸の酸解離定数以上の酸解離定数を有する酸を用いることが好ましい。アクリル酸と同じ若しくは弱い酸の金属塩を使用することにより、脱水剤として使用する２価金属塩とのイオン交換反応が容易に起こりやすくなる。アクリル酸の水・２５℃での酸解離定数は、４．２６である。すわなち、本発明では、弱酸成分として、水・２５℃での酸解離定数が、４．２６以上の酸を用いることが好ましく、４．３０以上の酸を用いることがより好ましく、４．５０以上の酸を用いることがさらに好ましい。弱酸の酸解離定数の上限は、特に限定されないが、１２が好ましく、１０がより好ましい。例えば、酸解離定数が９．９５のフェノールでは、効果が認められるが、酸解離定数が１６のエタノールでは、効果が認められない。
酸（ＨｎＸｎ−）の酸解離定数ｐＫａは、以下の式で表される。
ｐＫａ＝−ｌｏｇ（１／Ｋａ）， Ｋａ＝［Ｈ+］ｎ・［Ｘｎ−］／［ＨｎＸｎ−］
酸（ＨｎＸｎ−）の酸解離定数ｐＫａは、以下の式で表される。
ｐＫａ＝−ｌｏｇ（１／Ｋａ）， Ｋａ＝［Ｈ+］ｎ・［Ｘｎ−］／［ＨｎＸｎ−］
多段で解離する酸の場合、すくなくとも１段の酸解離定数が、４．２６〜１２の範囲にあることが好ましく、４．３〜１１の範囲にあるこがより好ましく、４．５〜１０の範囲にあることがさらに好ましい。また、すべての段の解離定数が４．２６〜１２の範囲にあることが好ましく、４．３〜１１の範囲にあることがより好ましく、４．５〜１０の範囲にあることがさらに好ましい。
水・２５℃での酸解離定数が４．２６以上の酸の具体例としては、例えば、アジピン酸（４．２６）、アゼライン酸（４．３９）、ｐ−アニス酸（４．４８）、ｏ−アミノ安息香酸（２段目：４．９５）、ｐ−アミノ安息香酸（４．８５）、イソ吉草酸（４．５８）、イソニコチン酸（２段目：４．８７）、イソ酪酸（４．６３）、オクタン酸（４．８９）、吉草酸（４．６４）、キナルジン酸（２段目：４．７５）、クエン酸（２段目：４．３５）、クロトン酸（４．６９）、ケイ皮酸（ｔｒａｎｓ）（４．４４）、酢酸（４．５６）、シクロヘキサンカルボン酸（４．７０）、（Ｒ，Ｒ）−酒石酸（２段目：４．４４）、ｐ−ヒドロキシ安息香酸（４．５８）、ピメリン酸（４．３１）、２，６−ピリジンジカルボン酸（３段目：４．６８）、プロピオン酸（４．６７）、ヘキサン酸（４．６３）、ヘプタン酸（４．６６）、ｏ−ベンゼンジカルボン酸（２段目：４．９３）、マロン酸（２段目：５．２８）、酪酸（４．６３）、リンゴ酸（３．２４）、レブリン酸（４．４４）、炭酸（６．３５）などを挙げることができる。
前記アルカリ金属としては、リチウム、ナトリウム、カリウムなどを挙げることができる。前記弱酸のアルカリ金属塩の具体例としては、例えば、炭酸ナトリウム、炭酸水素ナトリウム、炭酸カリウム、炭酸水素カリウム、クエン酸アセテートナトリウム、および、コハク酸アセテートナトリウムなどを挙げることができる。また、前記弱酸のアルカリ金属塩は、固体状であることが好ましい。固体状の弱酸のアルカリ金属塩を加えて混合することにより、浸透圧により吸水性樹脂粉末の凝集物から水が排出されやすくなるからである。
前記処理方法により得られた粒状の吸水性樹脂を乾燥することにより、粒状の吸水性樹脂粉末を再生できる。再生した吸水性樹脂粉末は、吸収性能にも優れる。例えば、再生吸水性樹脂粉末の吸収倍率は、１５ｇ／ｇ以上である。
再生された吸水性樹脂粉末は、例えば、土壌改良剤として利用する、あるいは、固形燃料として利用することができる。そのため、本発明には、前記処理方法により得られた粒状の吸収性樹脂粉末を乾燥することを特徴とする再生吸水性樹脂粉末の製造方法、土壌改良剤の製造方法、および、固形燃料の製造方法が含まれる。
本発明の処理対象となる吸水性樹脂粉末は、特に限定されないが、アクリル酸を構成成分とする架橋重合体であって、そのカルボキシル基の少なくとも一部が中和されているものが好ましい。架橋重合体を構成するアクリル酸成分の含有率は、９０質量％以上が好ましく、９５質量％以上がより好ましく、９９質量％以下が好ましく、９７質量％以下がさらに好ましい。
架橋重合体のカルボキシル基の少なくとも一部を中和する陽イオンとしては、特に限定されないが、例えば、リチウム、ナトリウム、カリウム等のアルカリ金属イオン、マグネシウム、カルシウム等のアルカリ土類金属イオンなどを挙げることができる。これらの中でも、架橋重合体のカルボキシル基の少なくとも一部が、ナトリウムイオンで中和されていることが好ましい。なお、架橋重合体のカルボキシル基の中和は、重合して得られる架橋重合体のカルボキシル基を中和するようにしてもよいし、予め、中和された単量体を用いて架橋重合体を形成するようにしてもよい。
架橋重合体のカルボキシル基の中和度は、６０モル％以上が好ましく、６５モル％以上がより好ましい。中和度が低すぎると、得られる吸水性樹脂粉末の吸収性能が低下する場合があるからである。また、中和度の上限は、特に限定されず、カルボキシル基のすべてが中和されていてもよい。なお、中和度は、下記式で求められる。
中和度（モル％）＝１００×「架橋重合体の中和されているカルボキシル基のモル数」／「架橋重合体が有するカルボキシル基の総モル数（中和、未中和を含む）」
中和度（モル％）＝１００×「架橋重合体の中和されているカルボキシル基のモル数」／「架橋重合体が有するカルボキシル基の総モル数（中和、未中和を含む）」
本発明の処理対象となる吸収性物品は、吸水性樹脂粉末が使用されているものであれば特に限定されず、例えば、使い捨て紙おむつ、失禁パッド、軽失禁パッド、生理用ナプキン、母乳パッドなどを挙げることができる。これらの中でも、吸水性樹脂粉末の使用量が多い使い捨て紙おむつが好適である。
以下、本発明を実施例によって詳細に説明するが、本発明は、下記実施例によって限定されるものではなく、本発明の趣旨を逸脱しない範囲の変更、実施の態様は、いずれも本発明の範囲内に含まれる。
［処理例１〜１０］
使用後の市販の使い捨て紙おむつを破砕したものを、脱水剤として塩化カルシウムを含有する処理水に投入し、吸水性樹脂の脱水処理を行った。処理水中から、吸収性物品に使用されていた不織布、フィルムなどのプラスチック成分を分離回収し、次いで、パルプを分離回収した。分離回収後の汚水を脱水機で脱水して、汚泥（吸水性樹脂の凝集物）を回収した。
使用後の市販の使い捨て紙おむつを破砕したものを、脱水剤として塩化カルシウムを含有する処理水に投入し、吸水性樹脂の脱水処理を行った。処理水中から、吸収性物品に使用されていた不織布、フィルムなどのプラスチック成分を分離回収し、次いで、パルプを分離回収した。分離回収後の汚水を脱水機で脱水して、汚泥（吸水性樹脂の凝集物）を回収した。
［処理例１１〜１３］
フラッフパルプ１００質量部と吸水性樹脂粉末（サンダイヤポリマー社製アクアパールＤＳ５６０：アクリル酸を構成成分とする架橋重合体）６０質量部とを気流型混合装置（株式会社オーテック社製パッドフォーマー）で混合し、得られた混合物を目付約５００ｇ／ｍ２となるように均一にアクリル板（厚み４ｍｍ）上に積層し、５ｋｇ／ｃｍ２の圧力で３０秒間プレスし、吸収体を得た。この吸収体を１４ｃｍ×３６ｃｍの長方形に裁断し、各々の上下に吸収体と同じ大きさの吸水紙（目付１５．５ｇ／ｍ２、アドバンテック社製、フィルターペーパー２番）を配置し、さらにポリエチレンシート（タマポリ社製ポリエチレンフィルムＵＢ−１）を裏面に、不織布（目付２０ｇ／ｍ２、旭化成社製エルタスガード）を表面に配置することにより、吸収性物品を作製した。
フラッフパルプ１００質量部と吸水性樹脂粉末（サンダイヤポリマー社製アクアパールＤＳ５６０：アクリル酸を構成成分とする架橋重合体）６０質量部とを気流型混合装置（株式会社オーテック社製パッドフォーマー）で混合し、得られた混合物を目付約５００ｇ／ｍ２となるように均一にアクリル板（厚み４ｍｍ）上に積層し、５ｋｇ／ｃｍ２の圧力で３０秒間プレスし、吸収体を得た。この吸収体を１４ｃｍ×３６ｃｍの長方形に裁断し、各々の上下に吸収体と同じ大きさの吸水紙（目付１５．５ｇ／ｍ２、アドバンテック社製、フィルターペーパー２番）を配置し、さらにポリエチレンシート（タマポリ社製ポリエチレンフィルムＵＢ−１）を裏面に、不織布（目付２０ｇ／ｍ２、旭化成社製エルタスガード）を表面に配置することにより、吸収性物品を作製した。
生理的食塩水に前記吸収性物品を６０分間浸漬し、その後、６０分間金網の上に載せて水切りを行った。水切り後の吸収性物品を高速粉砕機ＲＳＣ−５００（株式会社リーイング）を用いて粉砕した。前記粉砕物を５質量％の塩化カルシウム液に浸漬して脱水処理を行った。脱水処理後、沈降物（吸水性樹脂の凝集物）を回収した。脱水処理前の吸水性樹脂の含水率は、９８質量％であり、沈降物（吸水性樹脂の凝集物）の含水率は、７２質量％であった。
＜吸水した吸水性樹脂の凝集物の処理＞
得られた汚泥または沈降物（吸水性樹脂粉末の凝集物）１０ｇに所定量の処理剤を２００ｍＬビーカーに入れて、薬さじを用いて６０分間混合した。得られた混合物をアルミ標準バット（幅：２７６ｍｍ、奥行：２１１ｍｍ、高さ：３５ｍｍ）に均一に敷き詰めた。アルミ標準バットを、送風恒温器（ヤマト科学株式会社ＤＫＭ６００）に１００℃×３０分入れて、混合物を乾燥させた。得られた結果を表１にまとめた。表中の乾燥性において、「○」は、乾燥が容易にできたことを意味し、「×」は、表面のみ乾燥し、内部は未乾燥であったことを意味する。吸収倍率は、乾燥した吸収性樹脂粉末を取り出し、２５０μｍ〜５００μｍの粒度に調整して吸収倍率を測定した。吸収倍率は、以下の方法により測定した。
＜吸水した吸水性樹脂の凝集物の処理＞
得られた汚泥または沈降物（吸水性樹脂粉末の凝集物）１０ｇに所定量の処理剤を２００ｍＬビーカーに入れて、薬さじを用いて６０分間混合した。得られた混合物をアルミ標準バット（幅：２７６ｍｍ、奥行：２１１ｍｍ、高さ：３５ｍｍ）に均一に敷き詰めた。アルミ標準バットを、送風恒温器（ヤマト科学株式会社ＤＫＭ６００）に１００℃×３０分入れて、混合物を乾燥させた。得られた結果を表１にまとめた。表中の乾燥性において、「○」は、乾燥が容易にできたことを意味し、「×」は、表面のみ乾燥し、内部は未乾燥であったことを意味する。吸収倍率は、乾燥した吸収性樹脂粉末を取り出し、２５０μｍ〜５００μｍの粒度に調整して吸収倍率を測定した。吸収倍率は、以下の方法により測定した。
（吸収倍率の測定方法）
吸収倍率の測定は、ＪＩＳ Ｋ ７２２３（１９９６）に準拠して行う。目開き６３μｍのナイロン網（ＪＩＳ Ｚ８８０１−１：２０００）を幅１０ｃｍ、長さ４０ｃｍの長方形に切断して長手方向中央で二つ折りにし、両端をヒートシールして幅１０ｃｍ（内寸９ｃｍ）、長さ２０ｃｍのナイロン袋を作製する。測定試料１．００ｇを精秤し、作製したナイロン袋の底部に均一になるように入れる。試料の入ったナイロン袋を、生理食塩水に浸漬させる。浸漬開始から６０分後にナイロン袋を生理食塩水から取り出し、１時間垂直状態に吊るして水切りした後、試料の質量（Ｆ１）を測定する。また、試料を用いないで同様の操作を行い、そのときの質量Ｆ０（ｇ）を測定する。そして、これら質量Ｆ１、Ｆ０および試料の質量から、次式に従って、目的とする吸収倍率を算出する。
吸収倍率（ｇ／ｇ）＝（Ｆ１−Ｆ０）／試料の質量
吸収倍率の測定は、ＪＩＳ Ｋ ７２２３（１９９６）に準拠して行う。目開き６３μｍのナイロン網（ＪＩＳ Ｚ８８０１−１：２０００）を幅１０ｃｍ、長さ４０ｃｍの長方形に切断して長手方向中央で二つ折りにし、両端をヒートシールして幅１０ｃｍ（内寸９ｃｍ）、長さ２０ｃｍのナイロン袋を作製する。測定試料１．００ｇを精秤し、作製したナイロン袋の底部に均一になるように入れる。試料の入ったナイロン袋を、生理食塩水に浸漬させる。浸漬開始から６０分後にナイロン袋を生理食塩水から取り出し、１時間垂直状態に吊るして水切りした後、試料の質量（Ｆ１）を測定する。また、試料を用いないで同様の操作を行い、そのときの質量Ｆ０（ｇ）を測定する。そして、これら質量Ｆ１、Ｆ０および試料の質量から、次式に従って、目的とする吸収倍率を算出する。
吸収倍率（ｇ／ｇ）＝（Ｆ１−Ｆ０）／試料の質量
表１の結果から、明らかなように、吸水性樹脂粉末が、吸水することにより凝集してなる吸水性樹脂粉末の凝集物に、弱酸のアルカリ金属塩を加えて混合すると、吸水性樹脂粉末の凝集物が粒状になる。そして、粒状の吸水性樹脂粉末は、含水率を約３質量％以下に乾燥し得ることが分かる。一方、ゲル状の吸水性樹脂は、表面のみ乾燥するが、内部は未乾燥のままであった。
図３は、脱水処理後の沈降物（吸水性樹脂の凝集物）を表す図面代用写真である。図４は、脱水処理後の沈降物（吸水性樹脂の凝集物）を、弱酸のアルカリ金属塩として、炭酸水素ナトリウムで処理した例を示している。図５は、脱水処理後の沈降物（吸水性樹脂の凝集物）を、塩化カリウムを用いて処理した例を示している。図４から、明らかなように、弱酸のアルカリ金属塩を用いた場合、吸水性樹脂の凝集物は、粒状になっていることがわかる。一方、図５のように塩化カリウムを用いた場合、浸透圧により、吸水性樹脂から水が排出しているが、凝集物のままであり乾燥が困難であった。
本発明の吸収体は、例えば、人体から排出される体液を吸収するために用いられる吸収性物品に好適に使用でき、特に失禁パッド、使い捨ておむつ、生理用ナプキン、母乳パッドなどの吸収性物品に好適に利用できる。
１：吸水性樹脂粉末
Claims (10)
- 吸水性樹脂粉末が吸水することにより凝集してなる吸水性樹脂粉末の凝集物であって、脱水剤として、２価金属塩を用いて脱水処理されている吸水性樹脂粉末の凝集物に、水・２５℃の酸解離定数が４．２６以上の弱酸のアルカリ金属塩を加えて混合し、吸水性樹脂粉末の凝集物を粒状に変化させ、得られた粒状の吸水性樹脂を乾燥することを特徴とする吸水性樹脂の処理方法。
- 前記吸水性樹脂粉末は、アクリル酸を主たる構成成分とする吸水性樹脂粉末である請求項１に記載の吸水性樹脂の処理方法。
- 前記２価金属塩は、塩化カルシウムである請求項１または２に記載の吸水性樹脂の処理方法。
- 前記水・２５℃の酸解離定数が４．２６以上の弱酸のアルカリ金属塩として、固体状のものを加える請求項１〜３のいずれか一項に記載の吸水性樹脂の処理方法。
- 前記水・２５℃の酸解離定数が４．２６以上の弱酸のアルカリ金属塩は、炭酸ナトリウム、炭酸水素ナトリウム、炭酸カリウム、炭酸水素カリウム、クエン酸アセテートナトリウム、および、コハク酸アセテートナトリウムよりなる群から選択される少なくとも１種である請求項１〜４のいずれかに記載の吸水性樹脂の処理方法。
- 前記水・２５℃の酸解離定数が４．２６以上の弱酸のアルカリ金属塩の添加量は、前記２価金属塩で処理した含水状態の吸水性樹脂１００質量部に対して、１質量部〜１００質量部である請求項１〜５のいずれか一項に記載の吸水性樹脂の処理方法。
- 前記吸水性樹脂粉末は、吸収性物品として使用されていたものである請求項１〜６のいずれか一項に記載の吸水性樹脂の処理方法。
- 吸水性樹脂粉末が吸水することにより凝集してなる吸水性樹脂粉末の凝集物であって、脱水剤として、２価金属塩を用いて脱水処理されている吸水性樹脂粉末の凝集物に、水・２５℃の酸解離定数が４．２６以上の弱酸のアルカリ金属塩を加えて混合し、吸水性樹脂粉末の凝集物を粒状に変化させ、得られた粒状の吸水性樹脂を乾燥することを特徴とする再生吸水性樹脂粉末の製造方法。
- 吸水性樹脂粉末が吸水することにより凝集してなる吸水性樹脂粉末の凝集物であって、脱水剤として、２価金属塩を用いて脱水処理されている吸水性樹脂粉末の凝集物に、水・２５℃の酸解離定数が４．２６以上の弱酸のアルカリ金属塩を加えて混合し、吸水性樹脂粉末の凝集物を粒状に変化させ、得られた粒状の吸水性樹脂を乾燥することを特徴とする土壌改良材の製造方法。
- 吸水性樹脂粉末が吸水することにより凝集してなる吸水性樹脂粉末の凝集物であって、脱水剤として、２価金属塩を用いて脱水処理されている吸水性樹脂粉末の凝集物に、水・２５℃の酸解離定数が４．２６以上の弱酸のアルカリ金属塩を加えて混合し、吸水性樹脂粉末の凝集物を粒状に変化させ、得られた粒状の吸水性樹脂を乾燥することを特徴とする固形燃料の製造方法。