JP6275206B2 - 向上した品質の多スペクトル硫化亜鉛 - Google Patents
向上した品質の多スペクトル硫化亜鉛 Download PDFInfo
- Publication number
- JP6275206B2 JP6275206B2 JP2016134952A JP2016134952A JP6275206B2 JP 6275206 B2 JP6275206 B2 JP 6275206B2 JP 2016134952 A JP2016134952 A JP 2016134952A JP 2016134952 A JP2016134952 A JP 2016134952A JP 6275206 B2 JP6275206 B2 JP 6275206B2
- Authority
- JP
- Japan
- Prior art keywords
- zinc sulfide
- acid
- solution
- typically
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
カリフォルニア州ロサンゼルスのナショナルダイヤモンドラボラトリーからの0.16cmのコーティングされていないダイヤモンド深さ、平均のコーティングされていないダイヤモンドグリッドサイズ240および濃度100(72カラット/in3)の樹脂結合ホイールを有するブランチャードグラインダーにおいて硫化亜鉛プレートを創成する(機械加工する)ことにより、25cm×25cm×1cmの寸法を有する化学蒸着硫化亜鉛の5枚のプレートが準備される。研磨パッドは硫化亜鉛プレートとブランチャードグラインダーのチャックとの間に配置される。この研磨パッドは、20%〜30%の多孔度および1.2g/cm3の密度を有するポリウレタン含浸ポリエステルパッドである。機械加工は20kHzの速度で5分間行われる。次いで、この硫化亜鉛プレートはソニコア(商標)SC超音波クリーナーにおいて、水で15:1(体積)に希釈されたソニコア(商標)205過酷な苛性アルカリ溶液を用いてクリーニングされる。このクリーニング液は室温に維持される。この硫化亜鉛プレートは超音波クリーナーから取り出され、シュアワイプス(商標)で拭い乾かされる。
従来のCVDチャンバーのレトルト内に、固体としての塩化マグネシウムが入れられる。気体のマグネシウム金属元素を生じさせるために、このレトルトは950℃に加熱される。蒸気圧は8〜10Torrの範囲である。
固体としてのAlCl3がCVDチャンバーのレトルトに入れられる。このレトルトは700℃の温度に加熱される。AlCl3の蒸気圧は5Torr〜6Torrの範囲である。
CVDチャンバーの外側のソースから元素酸素が提供され、従来の装置を用いて炉内にポンプ移送される。
チャックは97%アセトンでまずクリーニングされ、次いで70%メチルアルコールでクリーニングされ、次いでマイクロダイン(MicroDyn(商標))反応性スパッタリングドラムコーターに搭載される。このチャック上に、堆積速度200Å/分でアルミナを堆積させるために、2つのスパッタリングソースおよび2つのマイクロ波プラズマ源が同時に使用される。ターゲット材料は99.99%純度のアルミニウムであり、それはこのチャックから12cmの距離にある。このチャックが搭載されるドラムは1回転/秒の速度で回転させられる。このコーティングチャンバーは堆積前に、10−6Torrの圧力までポンプ減圧される。二原子酸素とアルゴンとの混合物がこの堆積チャンバー内に導入される。二原子酸素およびアルゴンの流量は、それぞれ、50sccmおよび100sccmである。チャンバー内の全圧力は0.004Torrである。マイクロ波出力は3kWで周波数2.54GHzである。マイクロ波はこのマイクロ波源の近くでプラズマを発生させる。
研磨パッドが、40%〜50%の多孔度および0.3g/cm3の密度を有するポリウレタン含浸ポリエステルパッドであること以外は、実施例1に記載される方法が繰り返される。硫化亜鉛プレートは酢酸の水溶液でクリーニングされる。10%酢酸水溶液は、氷酢酸(テキサス州ラポルテのリオンデルバーゼルアセチルズ(LyondellBasell Acetyls)から市販)のストック溶液から調製される。各プレートは、pH2〜3を有する酢酸の10%水溶液中に15分間浸漬される。クリーニングの際に、この酢酸溶液は室温に維持される。クリーニング後、プレートは取り出され、脱イオン水で2分間すすがれる。次いで、プレートはシュアワイプス(商標)で拭って乾燥させられる。次いで、これらは高グレードのアセトンで1分間すすがれ、室温で空気乾燥される。
Claims (1)
- a)創成チャックをポリウレタン含浸ポリエステルパッドで被覆し;
b)被覆された創成チャックに硫化亜鉛基体を保持し;並びに、
c)被覆された創成チャックにおいて硫化亜鉛基体を創成する;
ことを含む方法。