JP6210681B2 - ガラス組成物およびガラス組成物から作製された繊維 - Google Patents
ガラス組成物およびガラス組成物から作製された繊維 Download PDFInfo
- Publication number
- JP6210681B2 JP6210681B2 JP2012523706A JP2012523706A JP6210681B2 JP 6210681 B2 JP6210681 B2 JP 6210681B2 JP 2012523706 A JP2012523706 A JP 2012523706A JP 2012523706 A JP2012523706 A JP 2012523706A JP 6210681 B2 JP6210681 B2 JP 6210681B2
- Authority
- JP
- Japan
- Prior art keywords
- weight percent
- glass
- glass composition
- weight
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本出願は、2009年8月3日に出願された通常出願第12/534,490号に対する優先権を主張し、この出願の全開示は参照として援用される。
本発明は、ガラス組成物、詳しくは繊維を形成するためのガラス組成物に関する。
ガラス連続繊維(E−ガラス型およびC−ガラス型)の大規模な商業生産は、結晶または実質的に結晶の性質の鉱物から主としてなるバッチ材料を溶融させることを含む。これらの結晶性原料をガラス状態に変換するには溶融プロセスにおいてかなりのエネルギーを投入する必要がある。結晶性材料に付随するかなりのエネルギー投資を考慮して、ガラス組成物の製造においてガラス状鉱物または非晶質鉱物が時に用いられてきた。ガラス構造または非晶質構造は、溶融プロセスにおいて消費されるエネルギーの量を低減することができる。例えば、ミネラルウールの製造のための原料のかなりの部分として、玄武岩および黒曜石などのガラス状鉱物が用いられてきた。
(項目1)
53〜64重量パーセントのSiO 2 、
8〜12重量パーセントのAl 2 O 3 、
8.5〜18重量パーセントのアルカリ酸化物成分(R 2 O)、および
金属酸化物(RO)成分
を含むガラス組成物であって、前記金属酸化物成分は、約0.15から約1.5の範囲のR 2 O/RO比を提供する量で存在するガラス組成物。
(項目2)
前記RO成分は、7重量パーセントから31重量パーセントの範囲の量で存在する、項目1に記載のガラス組成物。
(項目3)
前記RO成分は、金属酸化物の混合物を含む、項目1に記載のガラス組成物。
(項目4)
前記RO成分は、CaOとMgOとの混合物を含む、項目3に記載のガラス組成物。
(項目5)
前記RO成分は、7から26重量パーセントの範囲の量のCaOを含む、項目1に記載のガラス組成物。
(項目6)
前記RO成分は、最大5重量パーセントの量のMgOを含む、項目1に記載のガラス組成物。
(項目7)
前記R 2 O成分は、Na 2 O、K 2 OもしくはLi 2 O、またはそれらの混合物を含む、項目1に記載のガラス組成物。
(項目8)
前記R 2 Oは、6.5から16重量パーセントの範囲の量のNa 2 Oを含む、項目1に記載のガラス組成物。
(項目9)
R 2 Oは、2から4重量パーセントの範囲の量のK 2 Oを含む、項目1の項目に記載のガラス組成物。
(項目10)
R 2 Oは、最大2重量パーセントの量のLi 2 Oを含む、項目1の項目に記載のガラス組成物。
(項目11)
最大8重量パーセントの量のZrO 2 をさらに含む、項目1に記載のガラス組成物。
(項目12)
前記RO成分は、最大3重量パーセントの量のZnOを含む、項目1に記載のガラス組成物。
(項目13)
最大3重量パーセントの量のMnO 2 をさらに含む、項目1に記載のガラス組成物。
(項目14)
最大3重量パーセントの量のTiO 2 をさらに含む、項目1に記載のガラス組成物。
(項目15)
最大3重量パーセントの量のLa 2 O 3 をさらに含む、項目1に記載のガラス組成物。
(項目16)
約1120℃から約1300℃の範囲の繊維形成温度を有する、項目1に記載のガラス組成物。
(項目17)
前記ガラス組成物の形成温度と液相線温度との間の差は、少なくとも約65℃である、項目1に記載のガラス組成物。
(項目18)
前記ガラス組成物の形成温度と液相線温度との間の差は、約45℃から約165℃の範囲である、項目1に記載のガラス組成物。
(項目19)
少なくとも50重量パーセントのガラス状鉱物であって、少なくとも80重量パーセントの量のSiO 2 とAl 2 O 3 との組み合わせを含むガラス状鉱物、および
少なくとも5重量パーセントのナトリウム源
を含むバッチ組成物から形成されるガラス組成物。
(項目20)
前記バッチは、少なくとも60重量パーセントの前記ガラス状鉱物を含む、項目19に記載のガラス組成物。
(項目21)
前記バッチは、少なくとも65重量パーセントの前記ガラス状鉱物を含む、項目19に記載のガラス組成物。
(項目22)
前記バッチは、少なくとも10重量パーセントの前記ナトリウム源を含む、項目19に記載のガラス組成物。
(項目23)
前記ガラス状鉱物は、パーライト、軽石、またはそれらの混合物を含む、項目19に記載のガラス組成物。
(項目24)
少なくとも50重量パーセントのガラス状鉱物および少なくとも5重量パーセントのナトリウム源を含むバッチ組成物を提供するステップであって、前記ガラス状鉱物は、少なくとも80重量パーセントの量のSiO 2 とAl 2 O 3 との組み合わせを含むステップ、および
前記バッチを加熱して前記ガラス組成物の溶融物を形成させるステップ
を含む、ガラス組成物を製造する方法。
(項目25)
前記バッチ組成物は、約1120℃から約1300℃の範囲の繊維形成温度に加熱される、項目24に記載の方法。
(項目26)
前記ガラス組成物を繊維化するステップをさらに含む、項目25に記載の方法。
(項目27)
56〜63重量パーセントのSiO 2 、
9〜12重量パーセントのAl 2 O 3 、
12〜17重量パーセントのRO(CaO+MgO)、
12〜14重量パーセントのR 2 O(Na 2 O+K 2 O)、
0〜2重量パーセントのLi 2 O、
0〜3重量パーセントのZnO、
0〜3重量パーセントのZrO 2 、
0〜3重量パーセントのMnO 2 、および
0〜3重量パーセントのLa 2 O 3
を含むガラス組成物。
(項目28)
60〜64重量パーセントのSiO 2 、
9〜12重量パーセントのAl 2 O 3 、
7〜15重量パーセントのRO(CaO+MgO)、および
13〜15.5重量パーセントのR 2 O(Na 2 O+K 2 O)、
0〜2重量パーセントのLi 2 O、
0〜3重量パーセントのZnO、
0〜3重量パーセントのZrO 2 、
0〜3重量パーセントのMnO 2 、および
0〜3重量パーセントのLa 2 O 3
を含むガラス組成物。
(項目29)
54〜63重量パーセントのSiO 2 、
9〜14重量パーセントのAl 2 O 3 、
11〜16.5重量パーセントのRO(CaO+MgO)、および
14〜17重量パーセントのR 2 O(Na 2 O+K 2 O)、
0〜2重量パーセントのLi 2 O、
0〜3重量パーセントのZnO、
0〜3重量パーセントのZrO 2 、
0〜3重量パーセントのMnO 2 、および
0〜3重量パーセントのLa 2 O 3
を含むガラス組成物。
(項目30)
前記ガラス組成物は、0.7重量パーセント未満のFe 2 O 3 を含む、項目27から29のいずれか1項に記載のガラス組成物。
(項目31)
53〜64重量パーセントのSiO 2 、
8〜12重量パーセントのAl 2 O 3 、
8.5〜18重量パーセントのアルカリ酸化物(R 2 O)成分、および
金属酸化物(RO)成分
を含み、
前記金属酸化物成分は、約0.15から約1.5の範囲のR 2 O/ROの質量比を提供する量で存在するガラス繊維。
(項目32)
ポリマー材料、および
前記ポリマー材料の中にある少なくとも1つのガラス繊維であって、
53〜64重量パーセントのSiO 2 、
8〜12重量パーセントのAl 2 O 3 、
8.5〜18重量パーセントのアルカリ酸化物(R 2 O)成分、および
金属酸化物(RO)成分
を含むガラス繊維
を含み、前記金属酸化物成分は、約0.15から約1.5の範囲のR 2 O/ROの質量比を提供する量で存在するポリマー複合体。
要旨
一局面において、本発明は、パーライトおよび/または軽石を含む、顕著な量の1つ以上のガラス状鉱物を含むバッチ組成物から形成されるガラス組成物を提供する。別の局面において、本発明は、本明細書に記載されているガラス組成物から形成されるガラス繊維を提供する。
*精製にSb2O3を用いた
表IVに提示されている本発明のガラス組成物の実施例20から37を、68〜73重量パーセントのパーライト、0〜13重量パーセントのドロマイト、4〜16重量パーセントの石灰岩および12〜17重量パーセントのソーダを含む成分の混合物を提供することによって調製した。実施例20から37を製造するために用いられたパーライト、石灰岩、ソーダおよび/またはドロマイトの特定の量を、各ガラス組成物の所望の組成パラメータに関して各鉱物の組成パラメータを参照して決定した。続いて、鉱物の混合物を約1400℃の温度に加熱して溶融ガラス組成物を得た。溶融ガラス組成物を冷却して実施例20から37のガラス組成物を提供した。
**1重量%Na2Oおよび1重量%CaOの代りにZnOを使用し、Sb2O3を除去した
表Vに提示されている実施例38のガラス組成物を、1重量%のNa2Oの代わりに1重量%のLi2Oを用いたことおよび精製時に用いられたSb2O3をすべて除去したことを除き、上記の実施例12のガラス組成物に従って調製した。表Vの実施例39のガラス組成物を、1重量%のNa2Oおよび1重量%のCaOの代わりにZnOを用いたことおよび精製時に用いられたSb2O3をすべて除去したことを除き、上記の実施例12のガラス組成物に従って調製した。
実施例1から71のいくつかのガラス組成物の溶融特性を検討した。本発明のガラス組成物の溶融特性の検討は、さまざまな組成パラメータがガラス組成物の形成温度(TF)および液相線(TL)温度を含む加工上考慮すべきことにどのように影響を及ぼすかを定める助けとなった。
logη=a*log(tgk)+b
の形で溶融粘度と相関し、ここで、a(1.09)およびb(0.87)は、NIST標準ガラス(710A)を用いるセル較正から求められた定数であった。粘度を定める際の相対誤差は、2.5<logη<3.5の粘度範囲で3%以内、logη<2.5およびlogη>3.5の範囲で4〜6%以内であった。
II.酸およびアルカリ腐食抵抗性
実験室内において単一チップブッシング装置を用いて本発明のガラス組成物から形成される繊維が作られた。同じ試験条件下の市販ガラス繊維腐食抵抗性と比較するために、AR−、C−、ECR−およびE−のガラス繊維もカレットを用いる同じ方法を用いて作られた。
2C−ガラス(重量%):66 SiO2、5.5 Al2O3、10.4 CaO、3.6 MgO、0.3 Fe2O3、0.2 K2O、12.5 Na2O、0.5F、および0.2 SO3。
3AR−ガラス(重量%):57 SiO2、3.2 Al2O3、15 ZrO2、4.2 CaO、0.1 MgO、0.1 Fe2O3、0.1 K2O、12 Na2O、0.5 F、および0.23 SO3。
III.機械的試験
実験室において単一チップブッシングから10μmの直径の繊維を引くことによって、本発明の実施例37のガラス組成物から形成された繊維の引張り強度を測定した。続いて、繊維を繊維形成の同じ日のうちに繊維に両端から引張り力を加えることによって試験した。図9は、57の試料サイズの場合について、平均約3050MPaおよび標準誤差22.4MPaを用いる繊維強度のワイブル統計解析のまとめである。テール部分を除くと、強度は単一ワイブル分布と適合し、単一破壊モードが繊維破壊(fiber failure)を支配していることを明らかに示唆した。
Claims (21)
- 53〜64重量パーセントのSiO2、
9〜12重量パーセントのAl2O3 、
12重量パーセントよりも多く18重量パーセントまでのアルカリ酸化物成分(R2O)、
1重量パーセント未満のFe2O3、および
金属酸化物(RO)成分
を含むガラス繊維の製造に使用するためのガラス組成物であって、
前記金属酸化物成分は、0.15から1.5の範囲のR2O/RO比を提供する量で存在し、前記RO成分は、7から26重量パーセントの範囲の量のCaOを含み、ここで、前記アルカリ酸化物成分(R 2 O)は、2〜4重量パーセントの範囲の量のK 2 Oを含み、そして前記ガラス組成物は、0〜3重量パーセントのZnOを含む、ガラス繊維の製造に使用するためのガラス組成物。 - 前記RO成分は、7重量パーセントから31重量パーセントの範囲の量で存在する、請求項1に記載のガラス組成物。
- 前記RO成分は、金属酸化物の混合物を含む、請求項1に記載のガラス組成物。
- 前記RO成分は、CaOとMgOとの混合物を含む、請求項3に記載のガラス組成物。
- 前記RO成分は、最大5重量パーセントの量のMgOを含む、請求項1に記載のガラス組成物。
- 前記R2 Oは、Na2O、K2OもしくはLi2O、またはそれらの混合物を含む、請求項1に記載のガラス組成物。
- 前記R2Oは、6.5から16重量パーセントの範囲の量のNa2Oを含む、請求項1に記載のガラス組成物。
- 前記R2Oは、最大2重量パーセントの量のLi2Oを含む、請求項1の請求項に記載のガラス組成物。
- 最大8重量パーセントの量のZrO2をさらに含む、請求項1に記載のガラス組成物。
- 最大3重量パーセントの量のMnO2をさらに含む、請求項1に記載のガラス組成物。
- 最大3重量パーセントの量のTiO2をさらに含む、請求項1に記載のガラス組成物。
- 最大3重量パーセントの量のLa2O3をさらに含む、請求項1に記載のガラス組成物。
- 1120℃から1300℃の範囲の繊維形成温度を有する、請求項1に記載のガラス組成物。
- 前記ガラス組成物の形成温度と液相線温度との間の差は、少なくとも65℃である、請求項1に記載のガラス組成物。
- 前記ガラス組成物の形成温度と液相線温度との間の差は、45℃から165℃の範囲である、請求項1に記載のガラス組成物。
- 56〜63重量パーセントのSiO2、
9〜12重量パーセントのAl2O3 、
12〜17重量パーセントのRO(CaO+MgO)、ここでCaO含有量は少なくとも7重量パーセントである、
12重量パーセントよりも多く14重量パーセントまでのR2O(Na2O+K2O)、ここでK 2 O含有量は2〜4重量パーセントである、
0〜2重量パーセントのLi2O、
0〜3重量パーセントのZnO、
0〜3重量パーセントのZrO2、
0〜3重量パーセントのMnO2、
0〜3重量パーセントのLa2O3、および
1重量パーセント未満のFe2O3
を含むガラス繊維の製造に使用するためのガラス組成物。 - 60〜64重量パーセントのSiO2、
9〜12重量パーセントのAl2O3、
7〜15重量パーセントのRO(CaO+MgO)、ここでCaO含有量は少なくとも7重量パーセントである、
13〜15.5重量パーセントのR2O(Na2O+K2O)、
0〜2重量パーセントのLi2O、
0〜3重量パーセントのZnO、
0〜3重量パーセントのZrO2、
0〜3重量パーセントのMnO2、
0〜3重量パーセントのLa2O3、および
1重量パーセント未満のFe2O3
を含むガラス繊維の製造に使用するためのガラス組成物。 - 54〜63重量パーセントのSiO2、
9〜14重量パーセントのAl2O3 、
12〜16.5重量パーセントのRO(CaO+MgO)、ここでCaO含有量は少なくとも7重量パーセントである、
14〜17重量パーセントのR2O(Na2O+K2O)、ここでK 2 O含有量は2〜4重量パーセントである、
0〜2重量パーセントのLi2O、
0〜3重量パーセントのZnO、
0〜3重量パーセントのZrO2、
0〜3重量パーセントのMnO2、
0〜3重量パーセントのLa2O3、および
1重量パーセント未満のFe2O3
を含むガラス繊維の製造に使用するためのガラス組成物。 - 前記ガラス組成物は、0.7重量パーセント未満のFe2O3を含む、請求項16から18のいずれか1項に記載のガラス組成物。
- 53〜64重量パーセントのSiO2、
8〜12重量パーセントのAl2O3 、
12重量パーセントよりも多く18重量パーセントまでのアルカリ酸化物(R2O)成分、
1重量パーセント未満のFe2O3、および
金属酸化物(RO)成分
を含むガラス連続繊維であって、
前記金属酸化物成分は、0.15から1.5の範囲のR2O/ROの質量比を提供する量で存在し、そして前記金属酸化物(RO)成分は、7から26重量パーセントの範囲の量のCaOを含み、ここで、前記アルカリ酸化物(R 2 O)成分は、2〜4重量パーセントの範囲の量のK 2 Oを含み、そして前記ガラス連続繊維は、0〜3重量パーセントのZnOを含む、ガラス連続繊維。 - ポリマー材料、および
前記ポリマー材料の中にある少なくとも1つのガラス繊維であって、
53〜64重量パーセントのSiO2、
9〜12重量パーセントのAl2O3、
12重量パーセントよりも多く18重量パーセントまでのアルカリ酸化物(R2O)成分、
1重量パーセント未満のFe2O3、および
金属酸化物(RO)成分
を含むガラス繊維
を含むポリマー複合体であって、
前記金属酸化物成分は、0.15から1.5の範囲のR2O/ROの質量比を提供する量で存在し、そして前記金属酸化物(RO)成分は、7から26重量パーセントの範囲の量のCaOを含み、そして前記ガラス繊維は、0〜3重量パーセントのZnOを含む、ポリマー複合体。