JP6075987B2 - 高性能ドライタイヤのトレッド用ゴム組成物及び高性能ドライタイヤ - Google Patents
高性能ドライタイヤのトレッド用ゴム組成物及び高性能ドライタイヤ Download PDFInfo
- Publication number
- JP6075987B2 JP6075987B2 JP2012164011A JP2012164011A JP6075987B2 JP 6075987 B2 JP6075987 B2 JP 6075987B2 JP 2012164011 A JP2012164011 A JP 2012164011A JP 2012164011 A JP2012164011 A JP 2012164011A JP 6075987 B2 JP6075987 B2 JP 6075987B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- carbon black
- parts
- rubber
- rubber composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
0.6<結晶化カーボンブラック及び非結晶化カーボンブラックの合計含有量/可塑剤成分の含有量<1.4
なお、本明細書において、カーボンブラック(結晶化カーボンブラック、後述の非結晶化カーボンブラック)のNSAは、ASTM D6556の測定方法によって求められる。
なお、本明細書において、カーボンブラック(結晶化カーボンブラック、後述の非結晶化カーボンブラック)のオイル吸収量(DBP吸油量(OAN))は、ASTM D2414の測定方法によって求められる。
結晶化カーボンブラックのpHは、好ましくは12.0以下、より好ましくは11.0以下である。12.0を超えると、ゴムの加硫反応に悪影響を与える可能性がある。
結晶化カーボンブラックのpHは、JIS K6221(1982)に記載の方法で測定される値である。
なお、本明細書において、重量平均分子量(Mw)は、ゲルパーミエーションクロマトグラフ(GPC)(東ソー(株)製GPC−8000シリーズ、検出器:示差屈折計、カラム:東ソー(株)製のTSKGEL SUPERMALTPORE HZ−M)による測定値を基に標準ポリスチレン換算により求めた値である。
なお、芳香族系石油樹脂の軟化点は、JIS K 6220−1:2001に規定される軟化点を環球式軟化点測定装置で測定し、球が降下した温度である。
0.6<結晶化カーボンブラック及び非結晶化カーボンブラックの合計含有量/可塑剤成分の含有量<1.4
すなわち、前記成分を配合したゴム組成物を、未加硫の段階でトレッドなどの各タイヤ部材の形状にあわせて押出し加工し、他のタイヤ部材とともに、タイヤ成型機上にて通常の方法で成形することにより、未加硫タイヤを形成する。この未加硫タイヤを加硫機中で加熱加圧することによりタイヤを得る。
なお、本明細書における高性能ドライタイヤとは、ドライ路面でのグリップ性能に特に優れたタイヤであり、競技車両に使用する競技用タイヤをも含む概念である。
SBR:日本ゼオン(株)製のNipol9548(E−SBR、スチレン含有量:35質量%、ゴム固形分100質量部に対してオイル分37.5質量部含有)
カーボンブラック1:東海カーボン(株)製のシースト9SAF(非結晶化カーボンブラック、NSA:142m2/g、OAN:116cm3/100g)
カーボンブラック2:東海カーボン(株)製のシースト6ISAF(非結晶化カーボンブラック、NSA:114m2/g、OAN:114cm3/100g)
結晶化カーボンブラック:三菱化学(株)製の#4000(NSA:100m2/g、OAN:102cm3/100g、pH:10.0)
液状SBR:サートマー社製のRICON100(Mw:5000)
オイル:出光興産(株)製のダイアナプロセスAH−24
樹脂:日塗化学(株)製のエスクロンG90(クマロンインデン樹脂、軟化点:90℃)
酸化亜鉛:三井金属鉱業(株)製の酸化亜鉛
ステアリン酸:日油(株)製のステアリン酸「椿」
老化防止剤:住友化学(株)製のアンチゲン6C(N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン)
ワックス:大内新興化学工業(株)製のサンノックN
硫黄:軽井沢硫黄(株)製の粉末硫黄
加硫促進剤TOT−N:大内新興化学工業(株)製のノクセラーTOT−N(テトラキス(2-エチルヘキシル)チウラムジスルフィド)
加硫促進剤DM:大内新興化学工業(株)製のノクセラーDM(ジ−2−ベンゾチアゾリルジスルフィド)
表1に示す配合処方にしたがい、1.7Lのバンバリーミキサーを用いて、硫黄および加硫促進剤以外のものを150℃で5分間混練りした。次に、オープンロールを用いて、得られた混練り物に硫黄および加硫促進剤を添加して80℃で5分間練り込み、未加硫ゴム組成物を得た。得られた未加硫ゴム組成物を150℃の条件下で30分間プレス加硫し、加硫ゴム組成物を得た。
また、得られた未加硫ゴム組成物をトレッドの形状に成形し、タイヤ成型機上で他のタイヤ部材とともに貼り合わせ、150℃の条件下で30分間プレス加硫し、試験用タイヤ(タイヤサイズ:215/45R17)を得た。
上記試験用タイヤを排気量2000ccの国産FR車に装着し、ドライアスファルト路面のテストコースにて10周の実車走行を行なった。その際における、操舵時のコントロールの安定性をテストドライバーが評価し、比較例1を100として指数表示をした。数値が大きいほどドライ路面におけるグリップ性能に優れることを示す。
上記試験用タイヤを排気量2000ccの国産FR車に装着し、ドライアスファルト路面のテストコースにて実車走行を行なった。その際におけるタイヤトレッドゴムの残溝量を計測し(新品時15mm)、耐摩耗性として評価した。残溝量が多いほど、耐摩耗性に優れる。比較例1の残溝量を100として指数表示した。数値が大きいほど、耐摩耗性に優れることを示す。
上記試験用タイヤを排気量2000ccの国産FR車に装着し、ドライアスファルト路面のテストコースにて10周の実車走行を行なった。その際における、ベストラップと最終ラップの操舵時のコントロールの安定性をテストドライバーが比較評価し、比較例1を100として指数表示をした。数値が大きいほどドライ路面におけるグリップ性能の持続性に優れることを示す。
上記試験用タイヤを排気量2000ccの国産FR車に装着し、ドライアスファルト路面のテストコースにて実車走行を行なった。その際におけるタイヤトレッドゴムの表面に付着したゴムをスクレイパーで剥ぎ取り、その重量を測定した。比較例1の付着ゴム量を100として指数表示した。数値が小さいほど、ゴムカス量(トレッド表面に付着したタイヤカス量)が少ないことを示す。
得られた加硫ゴム組成物を用いて、フレクソメーター(レオ・ラボ(株)製)にて、繰り返し圧縮変形を与えて、ゴムを自己発熱させることによってブローアウトするまでの時間を測定した。試験条件は以下のとおりである。結果は、比較例1のゴム組成物のブローアウトタイムを100として指数化した。指数が大きいほど、ブローアウト時間が向上されており、耐ブローアウト性に優れることを示す。
試験条件:繰り返し圧縮歪 20% 周波数 10Hz
Claims (9)
- ゴム成分100質量部に対して、結晶化された結晶化カーボンブラックを1〜25質量部含み、更に、液状ジエン系重合体を含む高性能ドライタイヤのトレッド用ゴム組成物。
- クマロンインデン樹脂を含む請求項1に記載の高性能ドライタイヤのトレッド用ゴム組成物。
- チウラム系加硫促進剤を含む請求項1又は2記載の高性能ドライタイヤのトレッド用ゴム組成物。
- 結晶化カーボンブラックは、窒素吸着比表面積(NSA)が80〜120m2/g、オイル吸収量(OAN)が50〜115cm3/100gである請求項1〜3のいずれかに記載の高性能ドライタイヤのトレッド用ゴム組成物。
- 結晶化カーボンブラックは、pHが6.0〜12.0である請求項1〜4のいずれかに記載の高性能ドライタイヤのトレッド用ゴム組成物。
- 結晶化カーボンブラック及び非結晶化カーボンブラックの合計含有量がゴム成分100質量部に対して、50〜200質量部である請求項1〜5のいずれかに記載の高性能ドライタイヤのトレッド用ゴム組成物。
- 結晶化カーボンブラック及び非結晶化カーボンブラックの合計含有量と、可塑剤成分の含有量が以下の式を満たす請求項1〜6のいずれかに記載の高性能ドライタイヤのトレッド用ゴム組成物。
0.6<結晶化カーボンブラック及び非結晶化カーボンブラックの合計含有量/可塑剤成分の含有量<1.4 - チアゾール系加硫促進剤を含む請求項1〜7のいずれかに記載の高性能ドライタイヤのトレッド用ゴム組成物。
- 請求項1〜8のいずれかに記載のゴム組成物を用いた高性能ドライタイヤ。