JP5883262B2 - 湿式電子写真印刷用紙 - Google Patents
湿式電子写真印刷用紙 Download PDFInfo
- Publication number
- JP5883262B2 JP5883262B2 JP2011204816A JP2011204816A JP5883262B2 JP 5883262 B2 JP5883262 B2 JP 5883262B2 JP 2011204816 A JP2011204816 A JP 2011204816A JP 2011204816 A JP2011204816 A JP 2011204816A JP 5883262 B2 JP5883262 B2 JP 5883262B2
- Authority
- JP
- Japan
- Prior art keywords
- paper
- wet electrophotographic
- electrophotographic printing
- mass
- printing paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
JIS P 8140:1998年「紙及び板紙−吸水度試験方法−コッブ法」に準拠して測定した。なお、接触時間は30秒とした。コブ吸水度の値を表1に示す。コブ吸水度が、30g/m2以下を実用レベルとし、30g/m2を超えた場合を実用不可レベルとした。
JIS P8142:2005「紙及び板紙−75度鏡面光沢度の測定方法」に従って測定した75度鏡面光沢度」に従って、最上層の表面の75度鏡面光沢度を測定した。鏡面光沢度の値を表1に示す。75度光沢度が、60%以上を実用レベルとし、60%未満を実用不可レベルとした。
まず、A3判に切断した湿式電子写真印刷用紙に、湿式電子写真印刷機(HP Indigo5500 Digital Press:HP社製)を用いて画像を印刷後、折機(スタール:ハイデル社製)を用いて印刷面を谷折の二つ折りでA4判とし、これを10枚準備した。次に、糊丁合い機(全自動丁合い機:ミタニ社製)で糊付け及び丁合いして10枚重ねた。最後に、圧着加工後、背固め機(芳野社製)を用いて背固め加工したサンプルについて端面のずれ又は糊のはみ出しを視感評価し、貼合適性を評価した。
◎:端面のズレ又は糊のはみ出しは無く、非常にきれいにアルバム加工できる(実用レベル)。
○:端面のズレ又は糊のはみ出しはほぼ無く、きれいにアルバム加工できる(実用レベル)。
△:端面のズレ又は糊のはみ出しが多少あるが、アルバム加工できる(実用下限レベル)。
×:端面のズレ又は糊のはみ出しがあり、アルバム加工に難がある(実用不可レベル)。
貼合適性の評価で使用したサンプルを平置きとし、台からの浮き具合によって紙癖(反り)について評価した。
◎:各ページについて全く反りが無く、製本した状態でも各ページ間に全く隙間が無く良好である(実用レベル)。
○:各ページについて若干反りはあるが、製本した状態は各ページ間に全く隙間が無く良好である(実用レベル)。
△:各ページについてやや反りはあるが、製本した状態でも各ページ間に若干隙間がある程度で使用可能である(実用下限レベル)。
×:各ページについて反りが大きく、製本した状態でも各ページ間に隙間ができ、使用できない(実用不可レベル)。
得られた湿式電子写真印刷用紙のコックリングについて評価した。具体的には、糊付け加工後の印刷面を観察し、そのボコツキの程度を視感評価した。
◎:ボコツキが全く無く良好である(実用レベル)。
○:ボコツキが無く良好である(実用レベル)。
△:多少ボコツキがあるが、使用可能である(実用下限レベル)。
×:ボコツキが大きく使用できない(実用不可レベル)。
6000枚印刷後の転写ドラム上のトナーの残存状況を目視で評価した。
◎:転写ドラム上にトナーの汚れが無く、良好である(実用レベル)。
○:転写ドラム上にトナーの汚れがほとんど無く、良好である(実用レベル)。
△:転写ドラム上にトナーの汚れが多少あるが、実用上問題無い(実用下限レベル)。
×:転写ドラム上にトナーの汚れが酷い(実用不可レベル)。
印刷後、24時間経過した印刷サンプルの各色ベタ部にセロハン粘着テープ(セロテープ(登録商標)R:ニチバン社製)を貼り付け、180度剥離で約5mm/秒の速さで粘着テープを剥離した。剥離後の紙表面上の液体トナーの定着度合いを目視で評価した。
◎:粘着テープへの液体トナーの付着が無く、粘着テープの剥離跡の印刷濃度は変わらない(実用レベル)。
○:液体トナーが粘着テープに多少取られるが、粘着テープの剥離跡の印刷濃度はほとんど変わらない(実用レベル)。
△:液体トナーが粘着テープに取られ、粘着テープの剥離跡の印刷濃度がやや低下しているが、実用上問題無い(実用下限レベル)。
×:液体トナーが粘着テープに多く付着し、粘着テープの剥離跡に白く抜けた部分が発生している(実用不可レベル)。
オフセット印刷機として、「リスロン40(L−40)」(小森社製)を使用し、墨、藍、紅及び黄インキにて4色印刷を8500枚/時の印刷速度で印刷し、耐刷力を評価した。
◎:ブランケットの汚れがほとんど無く、良好である(実用レベル)。
○:ブランケットの汚れが多少あるが、画線部の抜けがほとんど無く、良好である(実用レベル)。
△:ブランケットの汚れが多く、画線部の抜けが有る(実用下限レベル)。
×:ブランケットの汚れが酷く、画線部の抜けも多い(実用不可レベル)。
耐刷力評価と同様の方法で印刷し、5000枚重ねて一日放置した後のインク裏移りを観察し、次のように4段階で評価した。
◎:下積み1〜1000枚において4色重ねベタ部で全く裏移りが無い(実用レベル)。
○:下積み1〜1000枚において4色重ねベタ部で多少裏移りがあるが、3色重ねベタ部では裏移りが無い(実用レベル)。
△:下積み1〜1000枚において4色重ねベタ部と3色重ねベタ部で多少裏移りがあるが、2色重ねベタ部では裏移りが無い(実用下限レベル)。
×:下積み1〜1000枚において単色ベタ部でも裏移りがある(実用不可レベル)。
<基紙の形成>
フリーネスをCSF450mlに調整した広葉樹さらしクラフトパルプ(LBKP)からなるパルプスラリーに、該パルプスラリー中の絶乾パルプ100部に対して、タルク(NTL:日本タルク社製)5部と、硫酸バンド1部と、カチオン化でんぷん(ケート308:日本NSC社製)0.5部と、酸性ロジンサイズ剤(AL1212:星光PMC製)0.5部とを配合して調製した紙料を各々長網抄紙機にて抄紙し、表層40g/m2、中層70g/m2及び裏層40g/m2の3層抄き合わせし、坪量150g/m2の基紙を得た。
酸化澱粉(王子エースA:王子コーンスターチ社製)糊液をサイズ液とし、基紙の両面に乾燥塗工量が片面当たり1g/m2となるようにサイズプレスで塗布し、シリンダードライヤーで乾燥した。次いで、スチールカレンダーを用いて線圧40kg/cm、25℃、2ニップ1パスの条件で表面処理を行った。
顔料としてカオリンクレー(ハイドラスパース:ヒューバー社製)50部及び湿式重質炭酸カルシウム(ハイドロカーブ60:備北粉化工業社製)50部と、接着剤としてスチレン‐ブタジエン共重合ラテックス(0613:JSR社製)15部及び燐酸エステル化澱粉(MS#4600:日本食品加工社製)3質量部とを配合し、固形分濃度65%の下塗層形成用塗工液を調製した。下塗層形成用塗工液を、ブレードコーターを用いて基紙の両面に、片面当たりの乾燥塗工量が10g/m2となるように塗工及び乾燥し、坪量170g/m2の塗工紙を得た。
顔料としてカオリンクレー(コンツァーエクストリーム:イメリス社製、シェイプエンジニアードカオリン、アスペクト比1:35)65部、柱状軽質炭酸カルシウム(TP123CS:奥多摩工業社製、アスペクト比1:6)10部及び有機顔料(L‐8900:旭化成ケミカルズ社製、スチレン系プラスチックピグメント、平均粒子径350nm、密実タイプ、ポリスチレン比率100%)25部と、接着剤としてスチレン‐ブタジエン共重合ラテックス(0613:JSR社製)10部及び燐酸エステル化澱粉(MS#4600:日本食品加工社製)1部とを配合し、固形分濃度が45%の最上層形成用塗工液を調製した。最上層形成用塗工液を、エアーナイフコーターを用いて、下塗層を形成した塗工紙の両面に、片面当たり乾燥塗工量が10g/m2となるように塗工及び乾燥した。次いで、ラスタープレスを用いて線圧100kN/m、温度80℃で平坦化処理を行い、坪量190g/m2、用紙全体の厚さが167μmの湿式電子写真印刷用紙を得た。
基紙の形成で紙料に配合する酸性ロジンサイズ剤の配合量を0.25部に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合するカオリンクレーの配合量を80部に変更し、かつ、柱状軽質炭酸カルシウムの配合量を5部に変更し、かつ、有機顔料の配合量を15部に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合するカオリンクレーの配合量を45部に変更し、かつ、柱状軽質炭酸カルシウムの配合量を20部に変更し、かつ、有機顔料の配合量を35部に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合する柱状軽質炭酸カルシウムの配合量を20部に変更し、かつ、有機顔料の配合量を15部に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合する炭酸カルシウムを湿式重質炭酸カルシウム(ハイドロカーブ60:備北粉化工業社製、アスペクト比1:1)に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合するカオリンクレーをカピムDG(シェイプエンジニアードカオリン、イメリス社製:アスペクト比1:13)に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合するカオリンクレーをコンツァー1500(シェイプエンジニアードカオリン、イメリス社製:アスペクト比1:58)に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合する有機顔料を変性スチレン系共重合体のプラスチックピグメント(L‐8999:旭化成ケミカルズ社製、平均粒子径200nm、密実タイプ、ポリスチレン比率100%)に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合する有機顔料を変性スチレン系共重合体のプラスチックピグメント(L‐8801:旭化成ケミカルズ社製、平均粒子径500nm、密実タイプ、ポリスチレン比率100%)に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
下塗層を設けなかった以外は、実施例1と同様に湿式電子写真印刷用紙を得た。坪量120g/m2、用紙全体の厚さが110μmの湿式電子写真印刷用紙を得た。
基紙の形成で、パルプスラリーに配合する酸性ロジンサイズ剤の配合量を1.0部に変更して用紙のコブ吸水度を5g/m2とした以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
表層を30g/m2に、中層を40g/m2に、裏層を30g/m2に変更して、これらを3層抄き合わせして基紙の坪量を100g/m2に変更し、用紙全体の坪量を140g/m2、用紙全体の厚さを125μmとした以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
表層を60g/m2に、中層を80g/m2に、裏層を60g/m2に変更して、これらを3層抄き合わせして基紙の坪量を200g/m2に変更し、用紙全体の坪量を240g/m2、用紙全体の厚さを213μmとした以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合するカオリンクレーの配合量を75部に変更し、かつ、柱状軽質炭酸カルシウムの配合量を0部(無添加)に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合する有機顔料の配合量を0部(無添加)に変更し、かつ、柱状軽質炭酸カルシウムの配合量を5部に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
最上層に配合するカオリンクレーの配合量を0部(無添加)に変更し、かつ、柱状軽質炭酸カルシウムの配合量50部に変更し、かつ、有機顔料の配合量を50部に変更した以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
基紙の形成でパルプスラリーに配合する酸性サイズ剤の配合量を0.1部に変更して、用紙のコブ吸水度を40g/m2とした以外は、実施例1と同様に湿式電子写真印刷用紙を得た。
Claims (6)
- 基紙の両面に顔料及び接着剤を主体とする1層以上の塗工層を設けた湿式電子写真印刷用紙において、
前記塗工層の最上層が、両面共に顔料としてカオリンクレー、炭酸カルシウム及び密実のプラスチックピグメントを含有し、
該密実のプラスチックピグメントの含有量が、前記最上層中の全顔料100質量部に対して10質量部以上40質量部以下であり、
JIS P8140:1998に従って測定したコブ吸水度(接触時間30秒)が、30g/m2以下であり、
前記最上層の表面をJIS P8142:2005に従って測定した75度鏡面光沢度が、60%以上であることを特徴とする湿式電子写真印刷用紙。 - 用紙全体の厚さが、130μm以上210μm以下であることを特徴とする請求項1に記載の湿式電子写真印刷用紙。
- 前記カオリンクレーのアスペクト比が1:12〜1:60であることを特徴とする請求項1又は2に記載の湿式電子写真印刷用紙。
- 前記炭酸カルシウムが、柱状の軽質炭酸カルシウムであることを特徴とする請求項1〜3のいずれかひとつに記載の湿式電子写真印刷用紙。
- アルバム用であることを特徴とする請求項1〜4のいずれか一つに記載の湿式電子写真印刷用紙。
- 前記密実のプラスチックピグメントの平均粒子径が、200nm以上500nm以下であることを特徴とする請求項1〜5のいずれか一つに記載の湿式電子写真印刷用紙。