JP5754229B2 - 練習用ゴルフボール - Google Patents
練習用ゴルフボール Download PDFInfo
- Publication number
- JP5754229B2 JP5754229B2 JP2011099862A JP2011099862A JP5754229B2 JP 5754229 B2 JP5754229 B2 JP 5754229B2 JP 2011099862 A JP2011099862 A JP 2011099862A JP 2011099862 A JP2011099862 A JP 2011099862A JP 5754229 B2 JP5754229 B2 JP 5754229B2
- Authority
- JP
- Japan
- Prior art keywords
- ball
- less
- mass
- core
- dimple
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
従って、ゲームボールと同様の打感であり、かつ低飛距離のボール性能が望まれている。
請求項1:
基材ゴム100質量部に対して、共架橋剤としてメタクリル酸を10〜40質量部、金属酸化物として酸化亜鉛を15〜30質量部、架橋開始剤を0.3〜5.0質量部をそれぞれ配合してなるゴム組成物にて形成されたコアとカバーとからなるゴルフボールであって、ボールを生産後30日後に最初に測定した時の、初期荷重98N(10kgf)から終荷重1,275N(130kgf)に負荷したときのボールのたわみ量をBH1(mm)、及び下記方法で測定した該ボ−ルの初速度をBV1(m/s)とすると共に、ボールを最初に測定してから350日放置した後、初期荷重98N(10kgf)から終荷重1,275N(130kgf)に負荷したときのボールのたわみ量をBH2(mm)、及び下記方法で測定した該ボ−ルの初速度をBV2(m/s)とするとき、BH2−BH1の差が0.2mm以内であり、且つBV2−BV1の差が0.3m/s以内であることを特徴とする練習用ゴルフボール。
[初速度の測定方法]
R&Aの承認するUSGAのドラム回転式の初速計と同方式の初速測定器を用い、サンプルを23±1℃の温度で3時間以上温度調節し、室温23±2℃の部屋でテストする。10個のサンプルを各々2回打撃して、6.28ft(1.91m)の間を通過する時間を計測し、初速を計算する。
請求項2:
カバーの樹脂成分がポリウレタンを主材とするものであり、カバーの厚さが0.3〜1.9mm、カバーの材料硬度がショアD硬度で30〜57である請求項1記載の練習用ゴルフボール。
請求項3:
ボールを最初に測定した時のボ−ルの初速度(BV1)が76m/s以下である請求項1又は2記載の練習用ゴルフボール。
請求項4:
ディンプルの縁に囲まれた平面から下方に形成されるディンプル空間体積の合計が、ボール表面にディンプルが存在しないと仮定した仮想球の体積に占める比率(VR)が0.8〜1.7である請求項1〜3のいずれか1項記載の練習用ゴルフボール。
請求項5:
表面に下記要件(1),(2)を満足するディンプルが形成されている請求項1〜4のいずれか1項記載のゴルフボール。
(1)周縁部に曲率半径(R)0.5〜2.5mmの丸みが設けられたディンプルを有する。
(2)直径(D)に対する上記曲率半径(R)の比率(R/D比率)が20%以上となるディンプルの合計個数(RA)のディンプル総数(N)に対する比率(ER)が15〜95%。
本発明の練習用ゴルフボールの構造は、例えば、図1に示されているように、コア1と、該コアを被覆するカバー2とからなるツーピースソリッドゴルフボールGである。なお、上記カバー2の表面には、通常、ディンプルDが多数形成されるものである。コア1及びカバー2は、図ではそれぞれ単層に形成されているが、コアを複数層で形成してもよく、また、カバーも複数層設けることができる。
本発明では、特に制限されるものではないが、カバーの樹脂成分がポリウレタンを主材とすることが好ましく、熱可塑性ポリウレタンエラストマーや熱硬化性ポリウレタン樹脂を使用することができ、特に熱可塑性ポリウレタンエラストマーを採用することが好適である。
また、コア及びボールにおける初期荷重98N(10kgf)から終荷重1,275N(130kgf)に負荷したとき、それぞれのたわみ量を(CH)及び(BH1)とするとき、(CH)/(BH1)の値が0.95以上、好ましくは0.96以上、より好ましくは0.97以上であり、上限値として、1.1以下、好ましくは1.08以下、より好ましくは1.07以下である。(CH)/(BH1)の値が大き過ぎる場合、コアのたわみ量に対して、製品のたわみ量が非常に小さくなる。即ち、カバー硬度が硬くなるため、打感の低下や、長期使用における外観低下につながる場合がある。逆に、小さ過ぎる場合、カバーが非常に軟らかくなるため、割れ耐久が大きく低下してしまい、特にトップした時にカバーが割けてしまうことがある。また、スピンが非常に多くなってしまい、飛距離低下を招くことがある。一方、ボールを最初に測定した時のボールの反発性(BV1)は、65m/s以上、好ましくは68m/s以上、更に好ましくは71m/s以上、最も好ましくは73m/s以上、また、上限としては76m/s以下、より好ましくは75.7m/s以下、更に好ましくは75.4m/s以下である。この範囲を逸脱すると、極端に飛距離が低下したり、練習場において飛び過ぎて、ネットを超えてしまう不具合がある。
実施例及び比較例における練習用ゴルフボールを作製するに際し、下記表1に示す配合のゴム材料を用意する。このゴム組成物をニーダー又はロールにて適宜混練した後、表1中の温度及び時間の条件により加硫し、各例のソリッドコアを作成する。なお、下記表中の各材料の数字は質量部で表される。
(1)BR01: JSR製のNi触媒ブタジエンゴム:ムーニー粘度ML「46」
(2)IR2200: JSR製のイソプレンゴム:ムーニー粘度ML「82」
(3)BR730: JSR製のNd触媒ブタジエンゴム:ムーニー粘度ML「55」
(4)パーヘキサC−40: 日本油脂製の有機過酸化物
(5)パークミルD: 日本油脂製の有機過酸化物
(6)酸化亜鉛: 堺化学工業社製
(7)老化防止剤: 大内新興化学工業社製の「ノクラックNS−6」
(8)メタクリル酸: クラレ製
(9)メタクリル酸亜鉛: 浅田化学工業社製
(10)アクリル酸亜鉛: 日本蒸溜工業社製
商品名「ハイミラン」: 三井・デュポンポリケミカル製、アイオノマー樹脂
商品名「パンデックス」: 大日本インキ化学工業(株)製、熱可塑性ポリウレタンエラストマー
ステアリン酸マグネシウム: 日本油脂社製
二酸化チタン: 商品名「タイペークR550」石原産業社製
ポリエチレンワックス: 商品名「サンワックス161P」、三洋化成社製
このようにして得られた実施例及び比較例のコア、カバーの物性並びに練習用ボールの物性、飛距離、耐久性及び打感を下記の基準に従って評価する。その結果を表4に記す。
R:周縁部に設けられた丸みの曲率半径
R/D比率:直径(D)に対する曲率半径(R)の比率
N:ディンプル総数
RA:(R/D比率)が20%以上となるディンプルの合計個数
ER:(RA)のディンプル総数(N)に対する比率
DE:自己の直径(D)よりも大きい直径(D)のディンプルの曲率半径(R)が自己の曲率半径(R)以下になるディンプルと、最大の直径(D)を有する最大径ディンプルとの合計個数
DER:(DE)のディンプル総数(N)に対する比率
SR:ディンプルの縁に囲まれた平面で定義されるディンプル面積の合計が、ボール表面にディンプルが存在しないと仮定した仮想球の表面積に占める比率である表面占有率
VR:ディンプルの縁に囲まれた平面から下方に形成されるディンプル空間体積の合計が、ボール表面にディンプルが存在しないと仮定した仮想球の体積に占める比率
対象球体物であるコア及びボール製品について、インストロン・コーポレーション製「4204型」を用いて、10mm/minの速度で圧縮し、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量の差(mm)を測定する。
コアをファインカッターにてカットし、上記B〜Fの部分をJIS−C(JIS K6301−1975規格)に準じて、23±1℃に温調後、硬度測定実施。(N=5の各2箇所)
コア表面をJIS−C(JIS K6301−1975規格)に準じて、23±1℃に温調後、硬度測定実施。(N=5の各2箇所)
初速は、R&Aの承認する装置であるUSGAのドラム回転式の初速計と同方式の初速測定器を用いて測定した。サンプルとしてのコア及びボールは23±1℃の温度で3時間以上温度調節し、室温23±2℃の部屋でテストされた。10個のサンプルを各々2回打撃して、6.28ft(1.91m)の間を通過する時間を計測し、初速を計算する。
カバーシートを作製し、ショアD(ASTM D−2240)に準じて、23±1℃に温調後の硬度を測定する。
ヘッドスピード(HS)=38m/s、9番アイアン(ブリヂストンスポーツ社製X−BLADE GR)のリーディングエッジでボールの同じ箇所を5回打撃後(トップ打撃)、入射速度43m/sで壁に繰返し衝突させた時のN=3個の割れ回数平均値を求める。
内容量8リットルの磁性のボールミルにゴルフボールを10個とバンカー用の砂3リットルを入れ、144時間ミキシングし、砂磨耗による、マークの欠け具合、表面の傷付き度合い、光沢減少の度合い、及び砂の付着の度合いを目視により調べた。ボール外観を良(○)、普通(△)、及び悪(×)の基準で評価する。
土手部(Y): ディンプル間の中心位置の土手部分のクリア塗装の厚さを計測する。
エッジ部分(Z): ディンプルエッジ部分のクリア塗装の厚さを計測する。
ボール2個を各々3箇所ずつ計測し、その平均値を計算する。
ドライバー(W#1)として、ブリヂストンスポーツ社製TourStage X−DRIVE701(ロフト角:9°)を打撃ロボットに取り付け、ヘッドスピード(HS)45m/sにて、ボールを打撃した直後のボールのスピン量及びトータル飛距離を測定する。
また、上記のマーク耐久実施後のボールのトータル飛距離を測定する。
2 カバー
D ディンプル
G ゴルフボール
Claims (5)
- 基材ゴム100質量部に対して、共架橋剤としてメタクリル酸を10〜40質量部、金属酸化物として酸化亜鉛を15〜30質量部、架橋開始剤を0.3〜5.0質量部をそれぞれ配合してなるゴム組成物にて形成されたコアとカバーとからなるゴルフボールであって、ボールを生産後30日後に最初に測定した時の、初期荷重98N(10kgf)から終荷重1,275N(130kgf)に負荷したときのボールのたわみ量をBH1(mm)、及び下記方法で測定した該ボ−ルの初速度をBV1(m/s)とすると共に、ボールを最初に測定してから350日放置した後、初期荷重98N(10kgf)から終荷重1,275N(130kgf)に負荷したときのボールのたわみ量をBH2(mm)、及び下記方法で測定した該ボ−ルの初速度をBV2(m/s)とするとき、BH2−BH1の差が0.2mm以内であり、且つBV2−BV1の差が0.3m/s以内であることを特徴とする練習用ゴルフボール。
[初速度の測定方法]
R&Aの承認するUSGAのドラム回転式の初速計と同方式の初速測定器を用い、サンプルを23±1℃の温度で3時間以上温度調節し、室温23±2℃の部屋でテストする。10個のサンプルを各々2回打撃して、6.28ft(1.91m)の間を通過する時間を計測し、初速を計算する。 - カバーの樹脂成分がポリウレタンを主材とするものであり、カバーの厚さが0.3〜1.9mm、カバーの材料硬度がショアD硬度で30〜57である請求項1記載の練習用ゴルフボール。
- ボールを最初に測定した時のボ−ルの初速度(BV1)が76m/s以下である請求項1又は2記載の練習用ゴルフボール。
- ディンプルの縁に囲まれた平面から下方に形成されるディンプル空間体積の合計が、ボール表面にディンプルが存在しないと仮定した仮想球の体積に占める比率(VR)が0.8〜1.7である請求項1〜3のいずれか1項記載の練習用ゴルフボール。
- 表面に下記要件(1),(2)を満足するディンプルが形成されている請求項1〜4のいずれか1項記載のゴルフボール。
(1)周縁部に曲率半径(R)0.5〜2.5mmの丸みが設けられたディンプルを有する。
(2)直径(D)に対する上記曲率半径(R)の比率(R/D比率)が20%以上となるディンプルの合計個数(RA)のディンプル総数(N)に対する比率(ER)が15〜95%。