JP5240189B2 - 多層ポリエステル容器及びその製造方法 - Google Patents
多層ポリエステル容器及びその製造方法 Download PDFInfo
- Publication number
- JP5240189B2 JP5240189B2 JP2009509279A JP2009509279A JP5240189B2 JP 5240189 B2 JP5240189 B2 JP 5240189B2 JP 2009509279 A JP2009509279 A JP 2009509279A JP 2009509279 A JP2009509279 A JP 2009509279A JP 5240189 B2 JP5240189 B2 JP 5240189B2
- Authority
- JP
- Japan
- Prior art keywords
- polyamide resin
- layer
- clay
- multilayer
- crystallinity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
特に、ポリアミド樹脂にクレイを分散させて成る機能性樹脂組成物から成る中間層を有する多層ポリエステル容器においては、延伸時に高負荷が生じやすいという延伸特性を有するため、中間層中にボイドを生じ、成形当初から白化する傾向がある。
本発明の多層ポリエステル容器においては、
1.ポリアミド樹脂から成る中間層の結晶化に伴う発熱ピークが9J/g以下であること、
2.ポリアミド樹脂が、ポリメタキシレンアジパミドであること、
3.クレイが、ポリアミド樹脂100重量部当り1乃至10重量部の量で含有されていること、
が好適である。
また本発明の多層ポリエステル容器の製造方法によれば、耐熱性ポリエステル容器の製造方法における熱固定工程を要することなく、容器胴部におけるクレイ配合ポリアミド樹脂組成物から成る中間層のDSC測定による発熱ピークの開始温度が96℃以上にすることができ、効率的に経時白化が防止された多層ポリエステル容器を製造することが可能となる。
前述したとおり、ポリアミド樹脂にクレイを配合して成るクレイ配合ポリアミド樹脂組成物は、延伸時の負荷が大きいという特性を有しており、その結果、通常のポリエステル容器の製法と同じ方法で、多層ポリエステル容器を成形した場合、成形当初から白化する傾向があり、経時保管によりさらに白化が進行し、透明性が損なわれるという問題があった。
すなわち、本発明における、多層ポリエステル容器のクレイ配合ポリアミド樹脂組成物から成る中間層における示差走査熱量計測定による結晶化に伴う発熱ピークの開始温度が上記値以上であるということは、多層ポリエステル容器の中間層の結晶化が促進されており、その後の環境条件によって結晶化し得る非晶質部分が少なく、結晶化しにくい構造であることを意味する。従って本発明の多層ポリエステル容器においては、経時保管による中間層の結晶化が抑制されており、その結果長期にわたって成形当初の透明性を維持することが可能となるのである。
すなわち、クレイ配合ポリアミド樹脂組成物から成る中間層のDSCによる発熱ピークの開始温度が上記値以上である本発明の多層ポリエステル容器においては、50℃、80%RH、72時間の促進経時実験において、容器のヘイズが減少するか、または上昇が抑制され、透明性が維持されているのに対して(実施例1〜5)、DSCによる発熱ピークの開始温度が上記値未満である多層ポリエステル容器においては、ヘイズが増加して、透明性が損なわれているのである(比較例1〜3、5)。
尚、本発明における内層及び外層のポリエステル樹脂の結晶化度Xcは、密度法により測定される。すなわち、下記式
Xc=[dc(d−da)/d(dc−da)]×100
ここで、daは完全非晶性ポリエステル樹脂の密度、dcは理論上の完全結晶化ポリエステル樹脂の密度、dは試料密度である、
により算出することができる。
すなわち、後述する実施例の結果からも明らかなように、プリフォームを上記温度範囲で加熱して二軸延伸ブロー成形してなる本発明の多層ポリエステル容器においては、クレイ配合ポリアミド樹脂組成物から成る内層の示差走査熱量計測定による結晶化に伴う発熱ピークの開始温度が上記値以上であるのに対して(実施例1〜5)、プリフォームの加熱温度が110℃未満である、従来の多層ポリエステル容器の製法で、二軸延伸ブロー成形を行った場合には、クレイ配合ポリアミド樹脂組成物から成る中間層の示差走査熱量計測定による結晶化に伴う発熱ピークの開始温度が上記値未満であり、結果として上述したように、経時保管によって透明性が損なわれているのである(比較例1、3、5)。
本発明のポリエステル容器の中間層は、ポリアミド樹脂にクレイを分散して成るクレイ配合ポリアミド樹脂組成物を用いる。
すなわち、ポリアミド樹脂は、ガスバリア性に優れている一方、延伸応力が大きく、延伸により透明性及びガスバリア性等の機能が損なわれやすいという特徴を有し、更にかかるポリアミド樹脂にクレイを分散させた場合には、ポリアミド樹脂単独よりも延伸応力が大きくなるため、ボイドの発生による透明性及びガスバリア性等の機能が損なわれやすいため、特に本発明による改善が望まれるものである。
本発明においては特に、延伸時の応力が大きく、優れたガスバリア性を有するポリメタキシリレンアジパミド、ポリメタキシレンセバカミドを用いる場合に、その優れた作用効果を顕著に発現することができる。
本発明で用いるクレイは、クレイを有機化剤で膨潤化処理したものであることが、特にガスバリア性の点で好適である。この場合、上記クレイの中でも、モンモリロナイトは高膨潤性を有し、有機化剤の浸透による膨潤が起こり層間が広がりやすいため特に好ましい。
有機化剤としては、第4級アンモニウム塩が好ましく使用できるが、より好ましくは、炭素数12以上のアルキル基を少なくとも一つ以上有する第4級アンモニウム塩、具体的には、トリメチルドデシルアンモニウム塩、トリメチルテトラデシルアンモニウム塩等が用いられる。
クレイ含有ポリアミド樹脂組成物においては、クレイをポリアミド樹脂100重量部当たり1乃至10重量部、特に1乃至8重量部の割合で配合することが好ましい。上記範囲よりもクレイの量が少ない場合には、クレイを配合することにより得られるガスバリア性を上記範囲にある場合に比して充分に得ることができず、一方上記範囲よりもクレイの量が多い場合には、上記範囲にある場合に比して成形性に劣るようになるので好ましくない。
酸化性有機成分としては、側鎖または末端に官能基を有し且つ酸化可能なもの、具体的には、ブタジエン、無水マレイン酸変性ブタジエン等の酸乃至酸無水物で変性されたポリエンオリゴマー乃至ポリマーを挙げることができ、また遷移金属触媒としては、鉄、コバルト、ニッケル等の周期律表第VIII族金属成分が使用されるが、勿論、これらの例に限定されない。
酸化性有機成分の配合量は、ポリアミド樹脂100重量部当たり2乃至10重量部の量で配合されていることが好ましく、また遷移金属触媒は、金属換算で少なくとも300ppm配合されていることが好ましい。
本発明の内外層に用いるポリエステル樹脂は、従来公知のジカルボン酸成分及びジオール成分から成るポリエステル樹脂を用いることができる。
ジカルボン酸成分としては、ジカルボン酸成分の50%以上、特に80%以上がテレフタル酸であることが機械的性質や熱的性質から好ましいが、テレフタル酸以外のカルボン酸成分を含有することも勿論できる。テレフタル酸以外のカルボン酸成分としては、イソフタル酸、ナフタレンジカルボン酸、p−β−オキシエトキシ安息香酸、ビフェニル−4,4’−ジカルボン酸、ジフェノキシエタン−4,4’−ジカルボン酸、5−ナトリウムスルホイソフタル酸、ヘキサヒドロテレフタル酸、アジピン酸、セバシン酸等を挙げることができる。
また上記ジカルボン酸成分及びジオール成分には、三官能以上の多塩基酸及び多価アルコールを含んでいてもよく、例えば、トリメリット酸、ピロメリット酸、ヘミメリット酸,1,1,2,2−エタンテトラカルボン酸、1,1,2−エタントリカルボン酸、1,3,5−ペンタントリカルボン酸、1,2,3,4−シクロペンタンテトラカルボン酸、ビフェニル−3,4,3’,4’−テトラカルボン酸等の多塩基酸や、ペンタエリスリトール、グリセロール、トリメチロールプロパン、1,2,6−ヘキサントリオール、ソルビトール、1,1,4,4−テトラキス(ヒドロキシメチル)シクロヘキサン等の多価アルコールが挙げられる。
本発明の内外層に用いるポリエステル樹脂には、それ自体公知の樹脂用配合剤、例えば着色剤、抗酸化剤、安定剤、各種帯電防止剤、離型剤、滑剤、核剤等を最終成形品の品質を損なわない範囲で公知の処方に従って配合することができる。
本発明の多層ポリエステル容器は、ポリエステル樹脂から成る内外層、クレイ配合ポリアミド樹脂組成物から成る中間層を少なくとも1層有する限り種々の層構成を採用することができ、図1に示すように、ポリエステル樹脂から成る内層1及び外層2の間にクレイ配合ポリアミド樹脂組成物から成る中間層3を有する層構成のものでもよいし、図2に示すように、ポリエステル樹脂から成る内層1及び外層2に、ポリエステル樹脂からなる内層1とポリエステル樹脂から成る中間層4の間及びポリエステル樹脂から成る外層2及びポリエステル樹脂から成る中間層4の間に、クレイ配合ポリアミド樹脂組成物から成る中間層3a,3bが2つ形成された層構成等であってもよい。
中間層であるクレイ配合ポリアミド樹脂組成物から成る層の厚みは20μm未満であることが容器の透明性の点から重要であり、特に5乃至15μmの範囲にあることが好ましく、中間層が胴部の全厚みの3乃至10%の範囲にあることが好ましい。
またクレイ配合ポリアミド樹脂組成物から成る中間層を複数存在させるときは、一つの中間層の厚みが20μm未満、特に5乃至15μmの範囲にあることが好ましく、中間層全体として胴部の全厚みの3乃至20%の範囲にあることが好ましい。
本発明の多層ポリエステル容器は、上記多層構造を有するプリフォームを成形し、このプリフォームを110乃至120℃、特に112乃至118℃の高温に加熱して、このプリフォームを軸方向に引っ張り延伸すると共に周方向にブロー延伸し、必要により熱固定することにより製造することができる。
多層プリフォームの製造は、それ自体公知の成形法で行うことができ、例えばクレイ配合ポリアミド樹脂組成物とポリエステル樹脂とを共押出する共押出成形法:クレイ配合ポリアミド樹脂組成物とポリエステル樹脂とを金型内に同時に射出する同時射出成形法:ポリエステル樹脂、クレイ配合ポリアミド樹脂組成物、ポリエステル樹脂を金型内に逐次射出する逐次射出法:クレイ配合ポリアミド樹脂組成物とポリエステル樹脂との共押出物をコア型とキャビティ型とで圧縮成形する圧縮成形法で製造することができる。
これら何れの方式による場合にも、形成されるプリフォームは過冷却状態、即ち非晶質状態にあるべきであり、またクレイ配合ポリアミド樹脂組成物から成る中間層は、熱可塑性ポリエステルの内外層中に内封されていることが好ましい。
延伸ブロー成形に先立って、プリフォームを熱風、赤外線ヒーター、高周波誘導加熱等の手段で延伸温度まで予備加熱するが、本発明においては、特に110乃至120℃、特に112乃至118℃の通常の延伸ブロー成形よりも高温に加熱して延伸ブローすることが重要である。すなわち上記温度よりもプリフォームの温度が低い場合には、クレイ配合ポリアミド樹脂組成物から成る中間層の延伸応力が大きくなり、延伸配向による結晶化の促進を望めず、経時保管による透明性の低下を抑制することができず、またボイドが発生し易くなって、得られる多層容器の透明性に劣るようになる。一方上記範囲よりも大きい場合には、プリフォームが軟化して延伸ブロー成形時に芯ズレを生じて成形性が悪化して、得られる多層容器の肉厚分布が不均一になったり、プリフォームが延伸ブロー成形前に結晶化してしまい、成形が不可能となる。
すなわち、上記温度範囲に加熱されたプリフォームを二軸延伸ブロー成形するに際して、プリフォーム内部に高温に加熱された加熱体が挿入されて内部加熱されていること及び/又は高温の熱風が圧入されていることにより、プリフォーム内部の温度がより高温になると共に、延伸ブロー成形時においてプリフォーム内部の温度が高温に保たれるため、歪の緩和が促進され、延伸応力の高いクレイ配合ポリアミド樹脂組成物から成る中間層の歪も緩和されるため、ボイドの形成が抑制され、透明性及びガスバリア性等の機能を損なうことがないのである。
内部加熱の加熱時間は、プリフォームの予備加熱温度及び内部加熱に用いる加熱体の設定温度によって変化させることが好ましく、好適には、8乃至20秒、特に10乃至15秒の範囲で加熱を行うことが望ましい。また、延伸ブロー成形する際に用いられるホットエアーは金型内にセットされたプリフォーム内部に2乃至3秒間圧入されることが望ましい。
延伸ブロー成形されたボトルは、耐熱用途に用いる場合には、それ自体公知の手段で熱固定することもできる。熱固定は、ワンモールド法で、ブロー成形金型中で行うこともできるし、また、ツーモールド法で、ブロー成形金型とは別個の熱固定用金型で行うこともできる。熱固定の温度は100乃至200℃の範囲が適当である。
本発明においては、かかる二段延伸ブロー成形においても、一次ブローの際にプリフォームの加熱温度を110乃至120℃の高温に加熱することが重要である。
[発熱ピーク開始温度および発熱ピークの測定]
作成した多層容器の胴部中央及び肩部から、クレイ配合ポリアミド樹脂組成物から成る中間層を剥がし取り、約8mgを精秤し、装置規定のアルミパンに封入した。アルミパンを示差走査熱量計[DSC7示差走査カロリメーター:PERKIN ELMER社製]により、20℃から280℃まで毎分10℃で昇温し、結晶化に伴う発熱ピークを示すチャートを得た。チャートから発熱ピーク開始温度を読みとり、またそのピーク面積から発熱ピーク(J/g)を求めた。
作成した多層ボトルの胴部中央から幅5mm、長さ5mmの試験片を切り出した。試験片から内側のポリエステル層と外側のポリエステル層をそれぞれ剥がし取り、試料を水−硝酸カルシウム系密度勾配管に20℃で2時間浸積した後の試料位置を読みとり、試験片の密度d(g/cm3)を求めた。得られた密度から、下記式により結晶化度χc(%)を求めた。
χc=[1.455×(d−1.335)/(d×(1.455−1.335))]×100
ここで、1.335は完全非晶性ポリエチレンテレフタレート樹脂の密度、1.455は理論上の完全結晶化ポリエチレンテレフタレート樹脂の密度である。
成形直後の多層ボトル及び50℃80%RHの環境下に72時間保管した後の多層ボトルの胴部中央から幅30mm、長さ40mmの試験片をそれぞれ切り出した。試験片を多層のまま、カラーコンピューター[S&M COLOUR COMPUTER MODEL SM−4 : スガ試験機(株)製]にてヘイズ(%)を測定した。
内外層PET用射出機(a)、中間層PET用射出機(b)、クレイ配合ポリアミド樹脂組成物用射出機(c)の3台の射出機を備えた共射出成形機を用い、射出機(a)及び(b)には150℃で4時間乾燥処理を行ったポリエチレンテレフタレート(PET)樹脂[BK6180(日本ユニペット(株)製)]、射出機(c)には、ポリメタキシリレンアジパミド樹脂(MXD6)[T620(日本ユニペット(株)製]と膨潤化処理を行った天然モンモリロナイト3重量%を二軸押出機にて溶融混練して得られたクレイ配合ポリアミド樹脂組成物を用いて、内外層及び中間層がPET層、それらの間がクレイ配合ポリアミド樹脂組成物から成る中間層である2種5層(a/c/b/c/a)、重量33gの多層プリフォームを逐次射出成形により作成した。
このプリフォームを、クオーツヒーター用いて外部から表面温度119℃まで予備加熱して、延伸倍率が縦3.0倍、横3.0倍に2軸延伸ブロー成形を行い、内容積516ml、胴部における各層の厚みが、内PET層(110μm)/内クレイ配合ポリアミド樹脂組成物層(18μm)/中間PET層(80μm)/外クレイ配合ポリアミド樹脂組成物層(17μm)/外PET層(140μm)の多層ボトルを作成した。
得られたボトルから、前記内クレイ配合ポリアミド樹脂組成物層の発熱ピーク開始温度と発熱ピーク、内PET層、外PET層の結晶化度及びヘイズを測定した。
多層プリフォームを111℃に予備加熱し、胴部における各層の厚みが、内PET層(100μm)/内クレイ配合ポリアミド樹脂組成物層(9μm)/中間PET層(110μm)/外クレイ配合ポリアミド樹脂組成物層(11μm)/外PET層(130μm)である以外は実施例1と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
多層プリフォームを113℃に予備加熱し、胴部における各層の厚みが、内PET層(110μm)/内クレイ配合ポリアミド樹脂組成物層(17μm)/中間PET層(80μm)/外クレイ配合ポリアミド樹脂組成物層(15μm)/外PET層(140μm)である以外は実施例1と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
多層プリフォームを116℃に予備加熱し、胴部における各層の厚みが、内PET層(100μm)/内クレイ配合ポリアミド樹脂組成物層(10μm)/中間PET層(110μm)/外クレイ配合ポリアミド樹脂組成物層(10μm)/外PET層(130μm)である以外は実施例1と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
多層プリフォームを117℃に予備加熱し、胴部における各層の厚みが、内PET層(100μm)/内クレイ配合ポリアミド樹脂組成物層(7μm)/中間PET層(110μm)/外クレイ配合ポリアミド樹脂組成物層(6μm)/外PET層(130μm)である以外は実施例1と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
多層プリフォームを109℃に予備加熱し、胴部における各層の厚みが、内PET層(100μm)/内クレイ配合ポリアミド樹脂組成物層(15μm)/中間PET層(100μm)/外クレイ配合ポリアミド樹脂組成物層(14μm)/外PET層(130μm)である以外は実施例1と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
胴部における各層の厚みが、内PET層(100μm)/内クレイ配合ポリアミド樹脂組成物層(22μm)/中間PET層(80μm)/外クレイ配合ポリアミド樹脂組成物層(24μm)/外PET層(100μm)である以外は実施例1と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
多層プリフォームを106℃に予備加熱し、胴部における各層の厚みが、内PET層(100μm)/内クレイ配合ポリアミド樹脂組成物層(10μm)/中間PET層(110μm)/外クレイ配合ポリアミド樹脂組成物層(8μm)/外PET層(130μm)である以外は実施例1と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
多層プリフォームを123℃に予備加熱し、実施例1と同様に多層ボトルを成形したが、プリフォームの結晶化により成形が困難であった。
内外層PET用射出機(a)、クレイ配合ポリアミド用射出機(b)の2台の射出機を備えた共射出成形機を用い、射出機(a)には150℃で4時間乾燥処理を行ったポリエチレンテレフタレート(PET)樹脂[BK6180(日本ユニペット(株)製)]、射出機(b)には、ポリメタキシリレンアジパミド樹脂(MXD6)[T620(日本ユニペット(株)製]と膨潤化処理を行った天然モンモリロナイト3重量%を二軸押出機にて溶融混練して得られたクレイ配合ポリアミド樹脂組成物を用いて、内外層がPET層、それらの間がクレイ配合ポリアミド樹脂組成物から成る中間層である2種3層(a/b/a)、重量28gの多層プリフォームを逐次射出成形により作成した。
このプリフォームを、クオーツヒーター用いて外部から表面温度105℃まで予備加熱して、延伸倍率が縦2.0倍、横3.1倍に2軸延伸ブロー成形を行い、内容積523ml、胴部における各層の厚みが、内PET層(200μm)/クレイ配合ポリアミド樹脂組成物層(25μm)/外PET層(180μm)の多層ボトルを作成した。
得られたボトルから、前記クレイ配合ポリアミド樹脂組成物層の発熱ピーク開始温度と発熱ピーク、内PET層、外PET層の結晶化度及びヘイズを測定した。
ポリメタキシリレンアジパミド樹脂(MXD6)[T620(日本ユニペット(株)製)]にクレイを配合せず、胴部における各層の厚みが、内PET層(100μm)/内MXD6層(12μm)/中間PET層(100μm)/外MXD6層(12μm)/外PET層(120μm)である以外は実施例3と同様に多層ボトルを成形し、結晶化ピーク、結晶化度、ヘイズの測定を行った。
Claims (5)
- ポリエステル樹脂から成る内外層及びポリアミド樹脂から成る少なくとも1層の中間層から成る多層ポリエステル容器において、
容器胴部における、前記ポリアミド樹脂から成る中間層の示差走査熱量計測定による結晶化に伴う発熱ピークの開始温度が96℃以上であり、前記ポリアミド樹脂中にクレイが分散されており、前記ポリアミドからなる中間層の厚みが20μm未満であり、前記ポリエステル樹脂から成る内層の結晶化度が23%以上29.5%以下及び外層の結晶化度が18%以上25.0%以下であると共に、該内層の結晶化度及び外層の結晶化度の平均値が24%以上26.4%以下であることを特徴とする多層ポリエステル容器。 - 前記ポリアミド樹脂から成る中間層の結晶化に伴う発熱ピークが9J/g以下である請求項1記載の多層ポリエステル容器。
- 前記ポリアミド樹脂が、ポリメタキシレンアジパミドである請求項1又は2記載の多層ポリエステル容器。
- 前記クレイが、ポリアミド樹脂100重量部当り1乃至10重量部の量で含有されている請求項1〜3の何れかに記載の多層ポリエステル容器。
- ポリエステル樹脂から成る内外層及びポリアミド樹脂から成る少なくとも1層の中間層から成り、該ポリアミド樹脂中にクレイが分散されている多層プリフォームを二軸延伸ブロー成形して成る多層ポリエステル容器の製造方法において、
多層プリフォームを110乃至120℃の温度に加熱して二軸延伸ブロー成形すると共に熱固定を行うことなく、ポリアミド樹脂から成る中間層の示差走査熱量計測定による結晶化に伴う発熱ピークの開始温度が96℃以上であり、前記ポリエステル樹脂から成る内層の結晶化度が23%以上29.5%以下及び外層の結晶化度が18%以上25.0%以下であると共に、該内層の結晶化度及び外層の結晶化度の平均値が24%以上26.4%以下である多層ポリエステル容器を成形することを特徴とする多層ポリエステル容器の製造方法。