JP5113575B2 - 制振組成物 - Google Patents
制振組成物 Download PDFInfo
- Publication number
- JP5113575B2 JP5113575B2 JP2008078967A JP2008078967A JP5113575B2 JP 5113575 B2 JP5113575 B2 JP 5113575B2 JP 2008078967 A JP2008078967 A JP 2008078967A JP 2008078967 A JP2008078967 A JP 2008078967A JP 5113575 B2 JP5113575 B2 JP 5113575B2
- Authority
- JP
- Japan
- Prior art keywords
- polymer material
- vibration damping
- swellable mica
- mass
- mica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本実施形態における制振組成物には、高分子材料とその制振性を高めるための無機充填剤とが含有されている。無機充填剤は、膨潤性マイカと非膨潤性マイカとを含み、非膨潤性マイカのアスペクト比は50〜90の範囲である。
ゴム類としては、ウレタンゴム、シリコーンゴム、エチレン−プロピレンゴム、クロロプレンゴム、ブチルゴム、アクリロニトリル−ブタジエンゴム、スチレン−ブタジエンゴム、アクリルゴム、天然ゴム等が挙げられる。
高分子材料は、所定の温度領域(例えば20℃〜60℃)において制振性能をバランスよく発揮させるという観点から、20〜30℃の範囲のガラス転移点を有する第1の高分子材料と、45〜55℃の範囲のガラス転移点を有する第2の高分子材料とを含むことが好ましい。
制振組成物は、制振材料又は制振塗料として、振動エネルギーの抑制が要求される各種分野において利用することができる。制振組成物の適用分野としては、例えば自動車、壁材、床材、屋根材、フェンス等の建材、家電機器、産業機械等が挙げられる。なお、制振塗料として適用する際には、上記高分子材料をエマルションとして含有させることが好ましい。
(1)制振組成物には、膨潤性マイカと非膨潤性マイカとが含有されているとともに、非膨潤性マイカのアスペクト比は50〜90の範囲である。これにより、高分子材料中において、振動エネルギーが熱エネルギーへ変換される際に、それらマイカの振動特性が異なることから、エネルギー変換の効率が高まるものと推測される。その結果、優れた制振性能を発揮させることが容易な制振組成物が提供される。
(実施例1〜6、比較例1〜12)
表1に示されるように、高分子材料に対して膨潤性マイカ及び非膨潤性マイカの少なくとも一方を配合して混練機で加熱混練することで制振組成物を調製した。なお、表1の高分子材料の欄に示される“A”及び“B”は、いずれもアクリル系樹脂であって、“A”のガラス転移点(Tg)は30℃であるとともに、“B”のガラス転移点(Tg)は50℃である。
各例で得られた制振組成物をシート状に成形することによって、厚さ1mmのシート材を得た。各シート材を35mm×3mmの寸法に切断し、動的粘弾性測定用の試験片とした。動的粘弾性測定装置(RSA−II:レオメトリック社製)を用いて各試験片を加振しながら連続的に昇温した際の損失弾性率E″を測定した。測定条件は、加振の周波数10Hz、測定温度範囲−40℃〜+90℃、昇温速度5℃/分とした。各例のシート材について、損失弾性率E″のピーク値を表1に併記する。
Claims (2)
- 高分子材料とその制振性を高めるための無機充填剤とを含有する制振組成物であって、
前記高分子材料は20〜30℃の範囲のガラス転移点を有する第1の高分子材料と、45〜55℃の範囲のガラス転移点を有する第2の高分子材料とを含有し、
前記第1の高分子材料の質量(A)と前記第2の高分子材料の質量(B)との質量比(A/B)は1/15〜1/3の範囲であり、
前記無機充填剤は膨潤性マイカと非膨潤性マイカとを含み、同非膨潤性マイカのアスペクト比は70〜90の範囲であり、
前記非膨潤性マイカ及び前記膨潤性マイカの合計の含有量は、前記高分子材料100質量部に対して、45〜70質量部であり、
前記非膨潤性マイカの質量(a)と前記膨潤性マイカの質量(b)との質量比(a/b)が3〜10であることを特徴とする制振組成物。 - 前記第1の高分子材料と前記第2の高分子材料がいずれもアクリル系樹脂であることを特徴とする請求項1に記載の制振組成物。