JP5028865B2 - 感光性樹脂凸版組成物およびそれからなる感光性樹脂凸版材 - Google Patents
感光性樹脂凸版組成物およびそれからなる感光性樹脂凸版材 Download PDFInfo
- Publication number
- JP5028865B2 JP5028865B2 JP2006152109A JP2006152109A JP5028865B2 JP 5028865 B2 JP5028865 B2 JP 5028865B2 JP 2006152109 A JP2006152109 A JP 2006152109A JP 2006152109 A JP2006152109 A JP 2006152109A JP 5028865 B2 JP5028865 B2 JP 5028865B2
- Authority
- JP
- Japan
- Prior art keywords
- photosensitive resin
- parts
- minutes
- meth
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
しかしなから、最近では感光性樹脂凸版材に対するユーザーの要求が、短い露光時間で微細なパターンを再現する方向へ進んでおり、最小細線保持は50μから30μ以下へと変化してきている。また、写真の印刷等に使用する最小ハイライトについても150線の3%からさらに細かな200線1%を要求されるようになっている。
それらの要求に対応する従来技術としては、感光樹脂層の紫外線透過率を特定の範囲にした感光性樹脂凸版材(特許文献4)や光透過率の異なる多層構造の感光性樹脂凸版材(特許文献5)などがあげられるが、性能とコストを満足するのではなかった。又、30μ細線と200線1%の網点を再現できる水現像型感光性フレキソ印刷用原版(特許文献6)も提案されているが、水性インキに限定されるために油性インキを用いる感光性樹脂凸版材には使用できるものではなかった。
(1)画像再現性:まず、感光層厚みが685μの感光性樹脂凸版原版に、画像として網点200線−1%〜95%、最小独立点直径50μm〜600μm、最小独立線幅が10μm〜150μm、600μ〜100μ幅の白抜けスリット、ベタ画像、スラップガイドを含む検査ネガを用い、200μmスリット幅の白抜け深度が少なくとも30μm以上となる最大露光時間を最適露光時間として、25W/m2のケミカルランプを用いて感光性樹脂表面より高さ5cmの距離から露光した。次にブラシ式ウォッシャー(120μmφナイロンブラシ、日本電子精機(株)制作JW-A2-PD型)で25℃の水道水を現像液にして行い、レリーフ画像を得ることができた。更に70℃で10分間、温風乾燥した後に超高圧水銀灯で30秒間後露光して得られたレリーフを評価した。画像再現性の評価は10倍のルーペを使い、肉眼で判定した。又、スリット深度については、ネガにおける白抜き線200μm巾が、レリーフにおいて何μmの深さとなって現れるかを評価するものである。
(2)最適露光時間:感光性樹脂層の厚みが685μの感光性樹脂凸版原版に、検査ネガを用いて200μmスリット幅の白抜け深度が30μm以上となる最大露光時間で露光し、その最大露光時間を最適露光時間とした。なお、深度が30μとは印刷時に200μmスリット幅の白抜け細線を再現するために必要な深度である。
(3)現像性:25℃の中性水を入れたブラシ式ウォッシャー(ブラシ:120 μφナイロンブラシ)で現像し、未露光部を除去するのに必要な時間を測定した。ブラシ式ウォッシャーは日本電子精機(株)のA2 サイズ用ウォッシャー(JW-A2- PD) を使用した。
N,N’−ビス(3−アミノプロピル)ピペラジン80部と2−メチルペンタメチレンジアミン20部をメタノール1000部に溶解した後、該ジアミン溶液にポリエチレングリコール(平均分子量600)600 部とヘキサメチレンジイソシアネート369部を反応させて得られた実質的に両末端にイソシアネート基を有するウレタンオリゴマー450部を、撹拌下徐々に添加した。両者の反応は約15分で完了した。この溶液をテフロン(登録商標)コートしたシャーレに取り、メタノールを蒸発除去後、減圧乾燥して得られた付加重合体は、ジアミン成分中に2−メチルペンタメチレンジアミンを20重量%、ポリエーテルセグメントを50.7重量%含有し、比粘度が1.75の水可溶性ポリマーであった。
N,N’−ビス(3−アミノプロピル)ピペラジン61部と2−メチルペンタメチレンジアミン33部をメタノール1000部に溶解した後、該ジアミン溶液にポリエチレングリコール(平均分子量600)600 部とヘキサメチレンジイソシアネート369部を反応させて得られた実質的に両末端にイソシアネート基を有するウレタンオリゴマー456部を、撹拌下徐々に添加した。両者の反応は約15分で完了した。この溶液をテフロン(登録商標)コートしたシャーレに取り、メタノールを蒸発除去後、減圧乾燥して得られた付加重合体は、ジアミン成分中に2−メチルペンタメチレンジアミンを35重量%、ポリエーテルセグメントを51.4重量%含有し、比粘度が1.73の水可溶性ポリマーであった。
N,N’−ビス(3−アミノプロピル)ピペラジン49部と2−メチルペンタメチレンジアミン40部をメタノール1000部に溶解した後、該ジアミン溶液にポリエチレングリコール(平均分子量600)600 部とヘキサメチレンジイソシアネート369部を反応させて得られた実質的に両末端にイソシアネート基を有するウレタンオリゴマー464部を、撹拌下徐々に添加した。両者の反応は約15分で完了した。この溶液をテフロン(登録商標)コートしたシャーレに取り、メタノールを蒸発除去後、減圧乾燥して得られた付加重合体は、ジアミン成分中に2−メチルペンタメチレンジアミンを45重量%、ポリエーテルセグメントを51.9重量%含有し、比粘度が1.74の水可溶性ポリマーであった。
N,N’−ビス(3−アミノプロピル)ピペラジン49部と2−メチルペンタメチレンジアミン40部をメタノール1000部に溶解した後、該ジアミン溶液にポリエチレングリコール(平均分子量600)600 部とヘキサメチレンジイソシアネート369部を反応させて得られた実質的に両末端にイソシアネート基を有するウレタンオリゴマー464部を、撹拌下徐々に添加した。両者の反応は約15分で完了した。この溶液をテフロン(登録商標)コートしたシャーレに取り、メタノールを蒸発除去後、減圧乾燥して得られた付加重合体は、ジアミン成分中に2−メチルペンタメチレンジアミンを45重量%、ポリエーテルセグメントを51.9重量%含有し、比粘度が1.74の水可溶性ポリマーであった。
実施例2と同様にしてジアミン成分中に2−メチルペンタメチレンジアミンを35重量%、主鎖にポリエーテルセグメントを51.4重量%含有し、比粘度が1.73の水可溶性ポリマーを得た。
実施例2と同様にしてジアミン成分中に2−メチルペンタメチレンジアミンを35重量%、主鎖にポリエーテルセグメントを51.4重量%含有し、比粘度が1.73の水可溶性ポリマーを得た。
N,N’−ビス(3−アミノプロピル)ピペラジン81部と2−メチルペンタメチレンジアミン14部をメタノール1000部に溶解した後、該ジアミン溶液にポリエチレングリコール(平均分子量600)600部の500部とヘキサメチレンジイソシアネート369部とを反応させて得られた実質的に両末端にイソシアネート基を有するウレタンオリゴマー454部を、撹拌下徐々に添加した。両者の反応は約15分で完了した。この溶液をテフロン(登録商標)コートしたシャーレに取り、メタノールを蒸発除去後、減圧乾燥して得られた付加重合体は、ジアミン成分中に2−メチルペンタメチレンジアミンを15重量%、ポリエーテルセグメントを51.1重量%含有し、比粘度が1.75の水可溶性ポリマーであった。
N,N’−ビス(3−アミノプロピル)ピペラジン38部と2−メチルペンタメチレンジアミン46部をメタノール1000部に溶解した後、該ジアミン溶液にポリエチレングリコールの平均分子量(平均分子量600)600部とヘキサメチレンジイソシアネート369部とを反応させて得られた実質的に両末端にイソシアネート基を有するウレタンオリゴマー466部を、撹拌下徐々に添加した。両者の反応は約15分で完了した。この溶液をテフロン(登録商標)コートしたシャーレに取り、メタノールを蒸発除去後、減圧乾燥して得られた付加重合体は、ジアミン成分中に2−メチルペンタメチレンジアミンを55重量%、ポリエーテルセグメントを52.5重量%含有し、比粘度が1.74の水可溶性ポリマーであった。
実施例2と同様にしてジアミン成分中に2−メチルペンタメチレンジアミンを35重量%、主鎖にポリエーテルセグメントを51.4重量%含有し、比粘度が1.73の水可溶性ポリマーを得た。
N,N’−ビス(3−アミノプロピル)ピペラジン86部と分岐していないジアミンとして1,9−ノナンジアミン22部をメタノール1000部に溶解した後、該ジアミン溶液にポリエチレングリコールの平均分子量(平均分子量600)600部とヘキサメチレンジイソシアネート369部とを反応させて得られた実質的に両末端にイソシアネート基を有するウレタンオリゴマー442部を、撹拌下徐々に添加した。両者の反応は約15分で完了した。この溶液をテフロン(登録商標)コートしたシャーレに取り、メタノールを蒸発除去後、減圧乾燥して得られた付加重合体は、ジアミン成分中に1,9−ノナンジアミンを20重量%、ポリエーテルセグメントを58.7重量%含有し、比粘度が1.70の水可溶性ポリマーであった。
Claims (2)
- 少なくとも可溶性合成高分子化合物、光重合性不飽和化合物、光重合開始剤を基本成分とする感光性樹脂凸版組成物であって、該可溶性高分子化合物が、(A) 2−メチルペンタメチレンジアミン、(B)ピペラジン環を有するジアミン及び(C) ポリオキシエチレングリコールとを反応させて得られる両末端にイソシアネート基を有するジイソシアネート化合物との反応で得られる付加重合体であり、(A)成分を全ジアミン量[(A)+(B)]に対して25〜45重量%を有する感光性樹脂組成物から得られた感光性樹脂凸版用印刷原版が、網点解像力が200線で網点1%、かつ最小独立線が幅20μmまで画像再現することを特徴とする印刷原版用感光性樹脂凸版組成物。
- 請求項1に記載の感光性樹脂凸版組成物から得られる感光性樹脂凸版材。