JP4895535B2 - 非クロメート系リン酸塩処理亜鉛めっき鋼板 - Google Patents
非クロメート系リン酸塩処理亜鉛めっき鋼板 Download PDFInfo
- Publication number
- JP4895535B2 JP4895535B2 JP2005186951A JP2005186951A JP4895535B2 JP 4895535 B2 JP4895535 B2 JP 4895535B2 JP 2005186951 A JP2005186951 A JP 2005186951A JP 2005186951 A JP2005186951 A JP 2005186951A JP 4895535 B2 JP4895535 B2 JP 4895535B2
- Authority
- JP
- Japan
- Prior art keywords
- chromate
- steel sheet
- phosphate
- galvanized steel
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(2)非クロメート薬剤が固形分として更にポリエステル樹脂を含有することを特徴とする前出(1)に記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
(3)非クロメート皮膜が、固形分として、タンニンまたはタンニン酸を2〜80g/l、シランカップリング剤を2〜80g/l、微粒シリカを1〜40g/l含有する非クロメート薬剤から形成した皮膜であることを特徴とする前出(1)または(2)に記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
(4)非クロメート皮膜が、固形分として更にポリエステル樹脂を1〜60g/l含有する非クロメート薬剤から形成した皮膜であることを特徴とする前出(2)または(3)記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
(5)非クロメート薬剤中のシランカップリング剤がグリシジルエーテル基を有することを特徴とする前出(1)乃至(4)の何れかに記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
(6)非クロメート皮膜の付着量が固形分にして10〜2000mg/m2であることを特徴とする前出(1)乃至(5)の何れかに記載の非クロメート系リン酸塩処理亜鉛めっき鋼板、である。
先ずベースとなる鋼板として、亜鉛付着量を各種変化させた電気亜鉛めっき鋼板(EG)にリン酸塩処理したもの(クロメートシーリング無し)を作製した。
使用したEGは以下の通りである。
EG03:板厚1.0mm、亜鉛付着量片面当たり3g/m2(両面めっき)
EG10:板厚1.0mm、亜鉛付着量片面当たり10g/m2(両面めっき)
EG20:板厚1.0mm、亜鉛付着量片面当たり20g/m2(両面めっき)
1.耐食性
各サンプルを50×100mmに切断し端面をシールしたもの及び、中央部に裏面から7mmエリクセン押し出し加工を施したものを作製し、テストピースとした。これらについてJIS K 5400の9.1記載の方法で塩水噴霧試験を実施した。試験時間は、EG03ベースは24時間、EG10ベースは48時間、EG20ベースは72時間とした。評価は、平面部エリクセン部ともに、それぞれの部分で錆の発生している面積の割合にて行った。平面部については、錆発生面積が1%未満の場合に◎、1%以上10%未満の場合に○、10%以上50%未満の場合に△、50%以上の場合に×と評価した。エリクセン部については、錆発生面積が10%未満の場合に◎、10%以上30%未満の場合に○、30%以上70%未満の場合に△、70%以上の場合に×と評価した。
各サンプルに、関西ペイント製アミラック#1000を乾燥膜厚で20μmバーコート塗装し、10分間セッティングの後120℃オーブンで20分間焼き付けた。評価は、1次(オーブンで焼き付けて室温まで冷却し、1日放置後に評価)及び、2次(沸騰水30分浸漬後1昼夜放置)で行った。密着性は、塗装面に1mm間隔100目の碁盤目を入れ、テープ剥離すること及び、エリクセンで7mm押し出し加工し、テープ剥離することにより評価した。碁盤目の入れ方、エリクセンの押し出し方法、テープ剥離の方法についてはJIS K 5400の8.2、及びJIS K 5400の8.5記載の方法に準じて実施した。碁盤目部あるいはエリクセン加工部のうち、テープ剥離で剥離した面積が1%未満の場合に◎、1%以上5%未満の場合に○、5%以上10%未満の場合に△、10%以上の場合に×と評価した。
各サンプルの平面部に指紋を押し付け、その前後での色差(ΔE)を測定し評価した。3名により評価し、評価点の平均をとった。ΔEが0.2未満が◎、ΔEが0.2以上0.5未満が○、ΔEが0.5以上1.0未満が△、ΔEが1.0以上が×と評価した。
上下電極としてCF型、アルミナ分散銅、13mmφ、先端径5mmのものを使用し、電極間距離25mm、加圧力250トン、シーケンス30サイクル、通電と保持時間の合計12サイクル、アップスロープ無しの条件にて、同一サンプルを2枚重ね合わせたものを溶接した。溶接電流を各種変化させて溶接し、溶接後に溶接部を引き剥がしてナゲット径を測定し、ナゲット系が4mmを下回らない限界点を溶接電流の下限、電極の溶着が発生しない限界点を溶接電流の上限としたとき、適正溶接電流範囲(上下限の差)が3kV以上であれば○、3kV未満であれば△、適正溶接電流範囲が存在しない場合は×と評価した。
各薬剤を40℃恒温漕中で各所定時間経時させた後に、それらを使ってリン酸塩処理亜鉛めっき鋼板を処理する。この処理板の塗装密着性を評価し、その評点が全項目について、経時無し薬剤を処理したサンプルと同等である限界の経時時間を記録した。
Claims (6)
- 亜鉛めっき鋼板の表面にリン酸塩処理皮膜を有し、その上に、固形分として、グアニジン化合物を含むことなく、タンニンまたはタンニン酸、シランカップリング剤、及び微粒シリカを含有する非クロメート薬剤から形成した非クロメート皮膜を有することを特徴とする非クロメート系リン酸塩処理亜鉛めっき鋼板。
- 非クロメート薬剤が固形分として更にポリエステル樹脂を含有することを特徴とする請求項1記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
- 非クロメート皮膜が、固形分として、タンニンまたはタンニン酸を2〜80g/l、シランカップリング剤を2〜80g/l、微粒シリカを1〜40g/l含有する非クロメート薬剤から形成した皮膜であることを特徴とする請求項1または請求項2記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
- 非クロメート皮膜が、固形分として更にポリエステル樹脂を1〜60g/l含有する非クロメート薬剤から形成した皮膜であることを特徴とする請求項2または請求項3記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
- 非クロメート薬剤中のシランカップリング剤がグリシジルエーテル基を有することを特徴とする請求項1乃至請求項4の何れかに記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。
- 非クロメート皮膜の付着量が固形分にして10〜2000mg/m2であることを特徴とする請求項1乃至請求項5の何れかに記載の非クロメート系リン酸塩処理亜鉛めっき鋼板。