JP4863315B2 - 高速増殖炉用核燃料ペレットの製造方法 - Google Patents
高速増殖炉用核燃料ペレットの製造方法 Download PDFInfo
- Publication number
- JP4863315B2 JP4863315B2 JP2009035145A JP2009035145A JP4863315B2 JP 4863315 B2 JP4863315 B2 JP 4863315B2 JP 2009035145 A JP2009035145 A JP 2009035145A JP 2009035145 A JP2009035145 A JP 2009035145A JP 4863315 B2 JP4863315 B2 JP 4863315B2
- Authority
- JP
- Japan
- Prior art keywords
- powder
- nuclear fuel
- container
- ratio
- fast breeder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
この試験は、上述のバッチ方式の加熱炉とロータリーキルン方式の加熱炉についてそれぞれ行った。その結果、両者とも焙焼条件が650 ℃以上、1時間で焙焼でき、還元条件が650 ℃以上、水素当量3倍以上で安定した還元ができ、このような条件の下で、O/Uが2.0から2.2の焙焼還元粉が得られた。しかし、本発明では脱硝粉末の取扱いの観点からこれまで実績のあるバッチ方式の加熱炉を採用した。
101 Pu-U溶液混合工程
102 マイクロ波脱硝工程
103 焙焼還元工程
104 造粒工程
105 ペレット成型工程
106 焼結(O/M調整)工程
107 ペレット製品化工程
20 造粒装置
30 ダイ
Claims (1)
- 高速増殖炉使用済み燃料の再処理システムから与えられる、硝酸プルトニウム溶液と硝酸ウラニル溶液を溶液のまま混合し、プルトニウム(Pu)対ウラン(U)の比率が予め定められた割合になるように調整し、
プルトニウム富化度が調整された硝酸Pu-U混合溶液を容器に移し、マイクロ波照射によって脱硝して脱硝粉体とした後、前記脱硝粉体を前記容器内で焙焼還元し、
焙焼還元された粉体にバインダを加えて、前記容器内で造粒し、MOX造粒粉末を作製し、
ペレット化に必要な一定量のMOX造粒粉末を、予め定められた核燃料ペレットの形状に成型し、
最後に成型された核燃料ペレットをそのまま一定時間焼結し、O/M比を調整するための熱処理を行うことを特徴とする高速増殖炉用核燃料ペレットの製造方法において、焼結終了時に、熱処理温度の降温速度を1000℃/hで急速降温させることを特徴とする高速増殖炉用核燃料ペレットの製造方法。