JP4808855B2 - 潤滑剤組成物 - Google Patents
潤滑剤組成物 Download PDFInfo
- Publication number
- JP4808855B2 JP4808855B2 JP2001084443A JP2001084443A JP4808855B2 JP 4808855 B2 JP4808855 B2 JP 4808855B2 JP 2001084443 A JP2001084443 A JP 2001084443A JP 2001084443 A JP2001084443 A JP 2001084443A JP 4808855 B2 JP4808855 B2 JP 4808855B2
- Authority
- JP
- Japan
- Prior art keywords
- acid
- lubricant composition
- group
- composition according
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の属する技術分野】
本発明は、切削加工、研削加工、塑性加工などの金属加工に広く適用できる潤滑剤組成物に関する。
【0002】
【従来の技術】
切削、研削加工分野に広く使用される切削油剤には鉱油をベ−スにした、不水溶性切削油剤と、鉱油、界面活性剤、有機アミン等を含有し、水に希釈して使用する水溶性切削油剤とがある。
【0003】
近年の地球資源の節約、地球環境悪化防止の観点から、切削油剤においては、従来と比較し、一層の地球環境に優しい油剤、更にはできるだけ長期間使用に耐えうる油剤の開発が求められてきている。
【0004】
その一例として、作業環境のクリーン化を目的とし、鉱油を含まない、シンセティック型の金属加工油剤も使用されている。シンセティック型金属加工油剤は水に希釈した場合にも透明感を保ち、腐敗に対しても強いという長所を有する。従来の水溶性金属加工油としては例えば、ヒドロキシカルボン酸オキシアルキレン付加物を用いる潤滑剤組成物(特開平6−100875号公報)、水溶性切削油剤組成物(特開平8−239683号公報)等が知られている。
しかしながら、従来のシンセティック型金属加工油剤は、一般的に転造タップ、深穴加工といった極端に潤滑性を必要とする加工には適さない。
【0005】
【発明が解決しようとする課題】
本発明の目的は、切削、研削をはじめとする金属加工の潤滑剤として用いた場合に、優れた加工性能を示し、水で希釈しても安定で透明性を維持し、耐腐敗性に優れ、かつ、環境にも悪影響を及ぼしにくい潤滑剤組成物を提供することである。
【0006】
【課題を解決するための手段】
本発明者は、鋭意検討の結果、特定のカルボン酸又はその塩と特定の合成油を含有させることにより、腐敗に対して強く、転造タップ、深穴加工などに適する潤滑剤が得られることを見出し、本発明を完成するに至った。
本発明は、(1)ヒドロキシカルボン酸のヒドロキシル基にオキシアルキレン基を付加したカルボン酸化合物、そのアルカリ金属塩及びそのアミン塩からなる群から選ばれる少なくとも1種の化合物、及び(2)アルキルベンゼン、ノルマルパラフィン、イソパラフィン、及びα−オレフィンからなる群から選ばれる少なくとも1種の基油を含有する潤滑剤組成物を提供するものである。
【0007】
【発明の実施の形態】
本発明の潤滑剤組成物に使用する成分(1)の化合物は、少なくとも1個のヒドロキシル基と少なくとも1個のカルボキシル基を有するヒドロキシカルボン酸のヒドロキシル基にオキシアルキレン基を付加したカルボン酸化合物、そのアルカリ金属塩及びそのアミン塩から選ばれる。
本発明に使用されるヒドロキシカルボン酸は、飽和であっても、不飽和であっても良く、炭素原子数7〜26のものが好ましい。ヒドロキシカルボン酸としては、脂肪族ヒドロキシカルボン酸、芳香族ヒドロキシカルボン酸が挙げられる。
【0008】
脂肪族ヒドロキシカルボン酸としては、例えば、モノヒドロキシモノカルボン酸として、ヒドロキシペラルゴン酸、ヒドロキシカプリン酸、ヒドロキシラウリル酸、ヒドロキシミリスチン酸、ヒドロキシパルミチン酸、ヒドロキシステアリン酸、ヒドロキシアラキン酸、ヒドロキシベヘン酸、リシノレイン酸、ヒドロキシオクタデセン酸、モノヒドロキシジカルボン酸として、ヒドロキシセバシン酸、ヒドロキシオクチルデカン二酸、モノヒドロキシトリカルボン酸として、ノルカペラート酸、アガリチン酸、ジヒドロキシモノカルボン酸として、イプロール酸、ジヒドロキシヘキサデカン酸、ジヒドロキシステアリン酸、ジヒドロキシオクタデセン酸、ジヒドロキシオクタデカンジエン酸、ジヒドロキシジカルボン酸として、ジヒドロキシドデカン二酸、ジヒドロキシヘキサデカン二酸、フロイオン酸、ジヒドロキシヘキサコ二酸、トリヒドロキシモノカルボン酸として、トリヒドロキシヘキサデカン酸(ウスチル酸−B)、トリヒドロキシオクタデカン酸、テトラヒドロキシモノカルボン酸として、テトラヒドロキシオクタデカン酸などが挙げられる。また、天然油脂より採取したひまし油脂肪酸や、硬化ひまし油脂肪酸も挙げられる。
【0009】
芳香族ヒドロキシカルボン酸としては、ヒドロキシ安息香酸、ジヒドロキシ安息香酸、トリヒドロキシ安息香酸、ヒドロキシメチル安息香酸、ヒドロキシジメチル安息香酸、ヒドロキシイソプロピル安息香酸、ヒドロキシイソプロピルメチル安息香酸、ジヒドロキシメチル安息香酸、ヒドロキシフタル酸、ジヒドロキシフタル酸、トリヒドロキシフタル酸、ヒドロキシイソフタル酸、ジヒドロキシイソフタル酸、トリヒドロキシイソフタル酸、ヒドロキシメチルイソフタル酸、ヒドロキシテレフタル酸、ジヒドロキシテレフタル酸、ジバール酸、オリベトールカルボン酸、スフェルホルロカルボン酸などが挙げられる。
【0010】
オキシアルキレン基として好ましいものは、オキシエチレン基、オキシプロピレン基、又はオキシエチレン基とオキシプロピレン基との混合基であり、それらの付加モル数は好ましくは1〜200、さらに好ましくは、1〜50が適当である。
アルカリ金属塩としては、ナトリウム塩、カリウム塩、リチウム塩等が挙げられる。例えば、ひまし油のオキシアルキレン付加物のけん化反応によって得られるカルボン酸化合物の塩であっても良い。
アミン塩を構成するアミンとしては、ジエタノールアミン、トリエタノールアミン、モノイソプロパノールアミン、トリイソプロパノールアミン、メチルジエタノールアミン、ジメチルエタノールアミン、2−アミノ2−メチル−1−プロパノール、2−(2−アミノエトキシ)エタノール、ジエチルモノイソプロパノールアミン、N,N−ジブチルアミノエタノール、N,N−ジ−n−ブチルアミノイソプロパノール、N,N−ジ−n−プロピルアミノイソプロパノール、N,N−ジターシャリーブチルジエタノールアミン、N,N−エチレンジアミン(ジイソプロパノール)、N,N−エチレンジアミン(ジエタノール)、モノ−n−ブチルジエタノールアミン、モノエチルジイソプロパノールアミン、2−アミノ−2−メチルエタノール等が挙げられる。
【0011】
本発明の潤滑剤組成物の成分(2)のアルキルベンゼンとしては、炭素原子数10〜14(約12)のアルキル基を有するモノアルキルベンゼン(分子量218〜274)、ジアルキルベンゼン(分子量358〜470)が挙げられ、具体例としては、デシルベンゼン、ウンデシルベンゼン、ドデシルベンゼン、トリデシルベンゼン、ジデシルベンゼン、ジウンデシルベンゼン、ジドデシルベンゼン、ジトリデシルベンゼン等が挙げられる。
【0012】
ノルマルパラフィンとしては、炭素原子数12〜14程度のもの(分子量170〜198)が挙げられ、具体例としては、デカン、ウンデカン、ドデカン、トリデカン、テトラデカン等が挙げられる。イソパラフィンとしては、炭素原子数12〜14程度のもの(分子量170〜198)が挙げられ、具体例としては、イソデカン、イソウンデカン、イソドデカン、イソトリデカン、イソテトラデカン等が挙げられる。α−オレフィンとしては、炭素原子数12〜14程度のもの(分子量168〜196)が挙げられ、具体例としては、デセン、ウンデセン、ドデセン、トリデセン、テトラデセン等が挙げられる。
【0013】
本発明の潤滑剤組成物において成分(1)対成分(2)の質量比率は好ましくは1:20〜20:1である。成分(1)の比率がこれより少ないと硬水希釈安定性が不充分となることがあり、多いと安定な潤滑剤組成物を構成できず、液がゲル状となることがある。
【0014】
本発明の潤滑剤組成物は、脂肪酸、アミン、水、鉱油、乳化剤などと合わせて切削油剤、研削油剤などの金属加工油剤として使用することができる。本発明の潤滑剤組成物は、そのままで金属加工油剤として使用してもよく、また、水で5〜200倍程度に希釈して使用しても良い。
本発明の潤滑剤組成物を希釈して使用する場合には、有効成分(1)及び(2)の合計の含有量は希釈した状態で0.5〜10質量%が適当である。
【0015】
本発明の潤滑剤組成物は、必要に応じて抗菌剤を含んでも良い。抗菌剤としては、例えば、ジエタノールアミン、トリエタノールアミン、モノイソプロパノールアミン、トリイソプロパノールアミン、メチルジエタノールアミン、ジメチルエタノールアミン、2−アミノ2−メチル−1−プロパノール、2−(2−アミノエトキシ)エタノール、ジエチルモノイソプロパノールアミン、N,N−ジブチルアミノエタノール、N,N−ジ−n−ブチルアミノイソプロパノール、N,N−ジ−n−プロピルアミノイソプロパノール、N,N−ジターシャリーブチルジエタノールアミン、N,N−エチレンジアミン(ジイソプロパノール)、N,N−エチレンジアミン(ジエタノール)、モノ−n−ブチルジエタノールアミン、モノエチルジイソプロパノールアミン、2−アミノ−2−メチルエタノール、シクロヘキシルアミン、ジシクロヘキシルアミン、1,3−ビスアミノメチルシクロヘキサン、メタキシレンジアミン、モルホリンなどのアミン、ラウリルアミン、オレイルアミンなどに代表されるアルキルアミン及びそれらのオキシエチレン付加物などが挙げられる。
【0016】
また、本発明の潤滑剤組成物は、必要に応じて防錆剤を含んでいても良い。防錆剤としては、カプロン酸、エナント酸、カプリン酸、ペラルゴン酸、カプリル酸、ウンデカン酸、ウンデシレン酸、ドデカン酸、トリデカン酸、ペンタデカン酸、ヘプタデカン酸、ノナデカン酸、ラウリル酸、ミリスチン酸、パルミチン酸、ステアリン酸、アラキン酸、ベヘン酸、イソステアリン酸、エライジン酸、オレイン酸、リノール酸、リノレイン酸、エルカ酸、アゼライン酸、ヒドロキシラウリル酸、ヒドロキシミリスチン酸、ヒドロキシパルミチン酸、ヒドロキシステアリン酸、ヒドロキシアラキン酸、ヒドロキシベヘン酸、リシノレイン酸、ヒドロキシオクタデセン酸、セバシン酸、ドデカン二酸、ドデシルコハク酸、ラウリルコハク酸、ステアリルコハク酸、イソステアリルコハク酸、ダイマー酸、リノール酸メタアクリル酸縮合物(商品名:ハリマ化成製 DA-1550)などの脂肪酸;石油スルホン酸ナトリウムなどのスルホン酸塩;カルボン酸アミド;アルケニルコハク酸、カルボン酸ザルコシド等が挙げられる。
【0017】
また、その他の任意の添加剤として、シリコーン系消泡剤、アルコール系消泡剤、トリアジン系防腐剤、アルキルベンゾイミダゾール系防腐剤又は金属防食剤、ベンゾチアゾール系金属防食剤、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテル、カルボン酸アルカノールアミドなどのノニオン系界面活性剤、多価アルコール類、グリコール類、水などのカップリング剤、燐酸塩、炭酸塩、ほう酸塩、珪酸塩などの無機塩、EDTAなどのイオン封鎖剤、酸化ワックス、天然油脂、合成油脂、合成エステル、高分子ポリマーなどの油性剤などを含有していても良い。
これら添加剤の合計量は一般に上記有効成分に対して、水を除いた質量比で1:20〜20:1である。
【0018】
【実施例】
以下、本発明を実施例、比較例によってさらに詳細に説明する。
実施例1〜9及び比較例1〜3
けん化物Iの調製
ひまし油オキシエチレン付加物(オキシエチレン1モル付加)750gに水酸化カリウム250g及び水250gを添加し、80℃で3時間撹拌し、ひまし油オキシエチレン付加物のけん化物Iを調製した。
けん化物IIの調製
ひまし油オキシエチレン付加物(オキシエチレン10モル付加)750gに水酸化カリウム125g及び水250gを添加し、80℃で3時間撹拌し、ひまし油オキシエチレン付加物のけん化物IIを調製した。
【0019】
けん化物IIIの調製
硬化ひまし油オキシエチレン付加物(オキシエチレン10モル付加)750gに水酸化カリウム125g及び水250gを添加し、80℃で3時間撹拌し、硬化ひまし油オキシエチレン付加物のけん化物IIIを調製した。
けん化物IVの調製
ひまし油オキシエチレン/オキシプロピレン付加物(オキシエチレン34モル、オキシプロピレン8モル付加)750gに水酸化カリウム50g及び水250gを添加し、80℃で3時間撹拌し、ひまし油オキシエチレン、オキシプロピレン付加物のけん化物IVを調製した。
【0020】
下記表1に記載された配合組成で潤滑剤組成物を調製した。表中の配合量は質量%である。
【0021】
試験方法
硬水希釈安定性試験
調整した硬水(塩化カルシウム2水塩0.757gを蒸留水で希釈し1Lとした水:ドイツ硬度30°、Ca硬度540ppm、JIS K 2221切削油剤 乳化安定性試験参照)を用い、表1の組成を有する水溶性金属加工油剤の2質量%希釈液を作り、希釈直後及び、24時間後の状態を目視にて観察する。
【0022】
切削性試験
表1の組成を有する水溶性金属加工油剤を水道水で10倍に希釈して10質量%希釈液200Lを調製し、これをマシニングセンターのクーラントタンクに張り込み、下記切削条件で切削実験を行いリーマ加工後の加工面で評価判定する。
【0023】
切削諸元
実験材として、アルミニウム合金(AC8B−T6、300×200×30mm,HRB60)を用い、下穴5.45φ止まり穴をあけ、M6のタップ(OSG製:ニューロールタップ B−NRT)による切削性試験を行った。
【0024】
耐腐敗性試験
表1の組成を有する水溶性金属加工油剤を水道水で3質量%に希釈した液100mlに下記腐敗液を3質量%添加し、30℃、150rpmで7日間振盪培養後、生菌数を測定する。
【0025】
判定基準
一般細菌の数あるいは汚染度をサンアイバイオチェッカー(三愛石油株式会社製)により評価した。1ml中の菌数を、no、103個>、103個、104個、105個、106個、107個、107個<の8段階で評価。
【0026】
【表1】
【0027】
本発明の実施例1〜9の組成物は、希釈安定性、切削性及び耐腐敗性に優れている。これに対して、基油として本発明の特定の基油の代わりに鉱油を用いた比較例1では希釈安定性が低く耐腐敗性も低い。また、特定のカルボン酸化合物又は特定の基油の一方を含まない比較例2及び3では、切削性が低い。
【発明の効果】
本発明の潤滑剤組成物は、金属加工油剤として使用したとき、腐敗に対して強く、かつ転造タップ、深穴加工などの金属加工において優れた切削性を示す。また、水希釈液が透明もしくは半透明であるため作業がしやすい。
Claims (8)
- (1)ヒドロキシカルボン酸のヒドロキシル基にオキシアルキレン基を付加したカルボン酸化合物、そのアルカリ金属塩及びそのアミン塩からなる群から選ばれる少なくとも1種の化合物、及び
(2)基油を含有し、前記基油が、アルキルベンゼン、ノルマルパラフィン、イソパラフィン、及びα−オレフィンからなる群から選ばれる少なくとも1種の合成油である潤滑剤組成物。 - 前記組成物が、鉱油を含まない、シンセティック型の金属加工油剤である、請求項1記載の潤滑剤組成物。
- オキシアルキレン基が、オキシエチレン基又はオキシエチレン基とオキシプロピレン基との混合基であり、その付加モル数が1〜200であるカルボン酸化合物、そのアルカリ金属塩及びそのアミン塩からなる群から選ばれる少なくとも1種の化合物を含有する請求項1又は2記載の潤滑剤組成物。
- ヒドロキシカルボン酸が、炭素原子数7〜26のヒドロキシカルボン酸である、請求項1〜3のいずれか1項記載の潤滑剤組成物。
- ヒドロキシカルボン酸が、ひまし油脂肪酸又は硬化ひまし油脂肪酸である、請求項1〜4のいずれか1項記載の潤滑剤組成物。
- 基油がアルキルベンゼンである請求項1〜5のいずれか1項記載の潤滑剤組成物。
- 成分(1)対成分(2)の質量比率が1:20から20:1である請求項1〜6のいずれか1項記載の潤滑剤組成物。
- 請求項1〜7のいずれか1項記載の潤滑剤組成物を水で5〜200倍に希釈してなる金属加工用油剤。