JP4755485B2 - 管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法及びこの方法を実施するための装置 - Google Patents
管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法及びこの方法を実施するための装置 Download PDFInfo
- Publication number
- JP4755485B2 JP4755485B2 JP2005323790A JP2005323790A JP4755485B2 JP 4755485 B2 JP4755485 B2 JP 4755485B2 JP 2005323790 A JP2005323790 A JP 2005323790A JP 2005323790 A JP2005323790 A JP 2005323790A JP 4755485 B2 JP4755485 B2 JP 4755485B2
- Authority
- JP
- Japan
- Prior art keywords
- mandrel
- fibrous material
- curable resin
- film
- multilayer hose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(I)外側マンドレルの内部に内側マンドレルを挿入した二重構造のマンドレルの内側マンドレル内に、筒状のインナ−フィルムをマンドレル導入口から連続的に挿通し、マンドレル導出口から引き出すように配置し、
(II)少なくとも1つの繊維状材料繰出装置から繰出される帯状の繊維状材料及びアウタ−フィルム繰出装置から繰出されるアウタ−フィルムを、外側マンドレルに繊維状材料、アウタ−フィルムの順に重ね合わせて筒形状に巻き付けるに際して、少なくとも2つのリングをマンドレルの軸線方向に相互に間隔をおいて且つ外側マンドレルの外周面との間に間隙をおいて外側マンドレルに嵌装し、
前記各リングには外側マンドレルの外周面に対してらせん状に且つマンドレル導出口方向へ延びるらせん状支持体を延設し、
前記のように嵌装した各リングの内、マンドレルの導入口側に位置する前記リングに対して前記繊維状材料繰出装置から繰出される前記帯状繊維状材料を当該リング内周面に接するように且つ外側マンドレルに巻き付いて両縁部が互いに重なり合うように導き、その際、前記らせん状支持部材により、重なり合った前記両縁部を前記外側マンドレルに押し付けて当該両縁部の重畳関係を維持し、且つ
前記各リングの内、マンドレル導出口側に位置する前記リングに対して前記アウタ−フィルム繰出装置から繰出されるアウタ−フィルムを当該リング内周面に接するように且つ外側マンドレルに巻き付けられた帯状繊維状材料上に巻き付いて両縁部が互いに重なり合うように導き、その際、当該リングのらせん状支持部材により、重なり合ったアウタ−フィルムの両縁部を前記巻付き帯状繊維状材料に押し付けて当該アウターフィルム両縁部の重畳関係を維持する工程、
(III)前記アウタ−フィルムの重畳縁部を熱融着ゾ−ンで溶着して前記筒状繊維状材料を被覆するアウターフィルム筒体を形成し、前記インナーフィルム、前記繊維状材料、及び前記アウターフィルムから成る多層ホースを前記マンドレルから送出する工程、
(IV)前記マンドレルから送出された後の前記多層ホ−スの略半円部に周方向に切れ目を入れ、筒状インナ−フィルムの内部に多層ホース拡幅部材を樹脂含浸区間を含む範囲に収容する工程、
(V)予め前記外側マンドレルと内側マンドレルとの間に挿通されている硬化性樹脂組成物送液導管及び増粘剤送液導管をこれら導管で送られる液体を混合するための混合器に接続し、該混合器を前記マンドレルから送出される多層ホースの前記インナ−フィルム層と前記繊維状材料層の間に介在させ、該混合器で両送液導管からの材料を均一に混合して硬化性樹脂を製造する工程、
(VI)前記混合器端部に接続され、前記インナ−フィルム層と前記繊維状材料層の間に位置している導管を水平方向から所定の角度下降傾斜するように方向転換させ、下降傾斜した前記導管の先端吐出口から前記硬化性樹脂を吐出し、この硬化性樹脂を多層ホ−スの繊維状材料に含浸させる工程、
を有すること特徴とする。
上記前記含浸区間における多層ホースの外周面から所定の距離に配置され、硬化性樹脂の充填量の大小により変位する多層ホースの外径の状態を検知するセンサーと、
上記センサーから送信される計測距離情報を受けて前記硬化性樹脂組成物送液導管と増粘剤送液導管とに給送する材料の量を調整する装置と、
を有することを特徴とする。
B 混合調整セクション
C 含浸セクション
1 外側マンドレル
2 内側マンドレル
3 筒状インナ−フィルム
4 樹脂組成物送液導管
5 増粘剤送液導管
6 樹脂組成物送液ポンプ
7 増粘剤送液ポンプ
8 樹脂組成物タンク
9 増粘剤タンク
11,12 繊維状材料繰出装置
13a,13b,13c 巻付けリング
14 アウタ−フィルム繰出装置
15a,15b,15c リング支持枠
17 上部溶着バンド
18 下部溶着バンド
20,22 繊維状材料
21 繊維状材料重複部
23 繊維状材料重複部
24 アウタ−フィルム
25 フィルム溶着部
26 拡幅部材
27 引張紐
29 静止型管内混合器
30 方向転換ロ−ラ−
31 樹脂混合物吐出口
36 樹脂混合物導管
39 樹脂含浸層
40 樹脂組成物吐出量制御弁
41 増粘剤吐出量制御弁
42 反射光センサー
43 上部キャタピラー
44 下部キャタピラー
45 多層ホ−ス含浸プリプレグ
46 収納箱
48,49 プリプレグ膜厚調整ロ−ラ
50a,50b,50c らせん状支持体
Claims (13)
- 筒状多層ホ−ス内に先端吐出口型導管を挿入し、硬化性樹脂混合物を前記吐出口から吐出させ、多層ホ−ス内の繊維状材料に含浸し、管ライニング用硬化性樹脂含浸多層ホ−スを製造する方法であって、
(I)外側マンドレルの内部に内側マンドレルを挿入した二重構造のマンドレルの内側マンドレル内に、筒状のインナ−フィルムをマンドレル導入口から連続的に挿通し、マンドレル導出口から引き出すように配置し、
(II)少なくとも1つの繊維状材料繰出装置から繰出される帯状の繊維状材料及びアウタ−フィルム繰出装置から繰出されるアウタ−フィルムを、外側マンドレルに繊維状材料、アウタ−フィルムの順に重ね合わせて筒形状に巻き付けるに際して、少なくとも2つのリングをマンドレルの軸線方向に相互に間隔をおいて且つ外側マンドレルの外周面との間に間隙をおいて外側マンドレルに嵌装し、
前記各リングには外側マンドレルの外周面に対してらせん状に且つマンドレル導出口方向へ延びるらせん状支持体を延設し、
前記のように嵌装した各リングの内、マンドレルの導入口側に位置する前記リングに対して前記繊維状材料繰出装置から繰出される前記帯状繊維状材料を当該リング内周面に接するように且つ外側マンドレルに巻き付いて両縁部が互いに重なり合うように導き、その際、前記らせん状支持部材により、重なり合った前記両縁部を前記外側マンドレルに押し付けて当該両縁部の重畳関係を維持し、且つ
前記各リングの内、マンドレル導出口側に位置する前記リングに対して前記アウタ−フィルム繰出装置から繰出されるアウタ−フィルムを当該リング内周面に接するように且つ外側マンドレルに巻き付けられた帯状繊維状材料上に巻き付いて両縁部が互いに重なり合うように導き、その際、当該リングのらせん状支持部材により、重なり合ったアウタ−フィルムの両縁部を前記巻付き帯状繊維状材料に押し付けて当該アウターフィルム両縁部の重畳関係を維持する工程、
(III)前記アウタ−フィルムの重畳縁部を熱融着ゾ−ンで溶着して前記筒状繊維状材料を被覆するアウターフィルム筒体を形成し、前記インナーフィルム、前記繊維状材料、及び前記アウターフィルムから成る多層ホースを前記マンドレルから送出する工程、
(IV)前記マンドレルから送出された後の前記多層ホ−スの略半円部に周方向に切れ目を入れ、筒状インナ−フィルムの内部に多層ホース拡幅部材を樹脂含浸区間を含む範囲に収容する工程、
(V)予め前記外側マンドレルと内側マンドレルとの間に挿通されている硬化性樹脂組成物送液導管及び増粘剤送液導管をこれら導管で送られる液体を混合するための混合器に接続し、該混合器を前記マンドレルから送出される多層ホースの前記インナ−フィルム層と前記繊維状材料層の間に介在させ、該混合器で両送液導管からの材料を均一に混合して硬化性樹脂を製造する工程、
(VI)前記混合器端部に接続され、前記インナ−フィルム層と前記繊維状材料層の間に位置している導管を水平方向から所定の角度下降傾斜するように方向転換させ、下降傾斜した前記導管の先端吐出口から前記硬化性樹脂を吐出し、この硬化性樹脂を多層ホ−スの繊維状材料に含浸させる工程、
を有すること特徴とする管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。 - 前記外側マンドレルと内側マンドレルとの間の空間に硬化性樹脂組成物送液導管と増粘剤送液導管をマンドレル導入口側から挿入することを特徴とする請求項1に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記アウタ−フィルムが、同質組成複層フィルム及び/又は異質組成複層フィルムであることを特徴とする請求項1または2に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記アウタ−フィルムがその内面にポリエステル不織布を積層した複合フィルムであることを特徴とする請求項1〜3の何れか1項に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記熱融着ゾ−ンでの熱融着を、前記アウターフィルムの移送方向で重なり合う両縁部を合掌状態に突合せて行うか、または、前記両縁部を互いに重ね合わせて行うことを特徴とする請求項1〜4の何れか1項に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記硬化性樹脂組成物が、光硬化性樹脂組成物または熱硬化性樹脂組成物であることを特徴とする請求項1〜5の何れか1項に記載の管ライニング用硬化性樹脂組成物含浸多層ホ−スの連続的製造方法。
- 前記繊維状材料が、ガラス繊維及び/又はフェルト及び/又は不織布であることを特徴とする請求項1〜6の何れか1項に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記拡幅部材は長手方向にU字型に形成されており、樹脂含浸区間前の水平部分並びに樹脂含浸区間での下降傾斜部分は硬質性材料で製作され、前記水平部分と含浸区間の間の方向転換部分は可撓性材料で製作され、横断面形状は方形状、円形状または楕円状であることを特徴とする請求項1〜7の何れか1項に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記混合器が、静止型管内混合器であることを特徴とする請求項1〜8の何れか1項に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記混合器は、多層ホ−スの移送方向と同じ水平方向に設置し、この混合器に接続した前記導管は水平の前記未含浸区間と、この未含浸区間から30度以上、90度未満の角度で傾斜して下降する含浸区間とを有するように構成し、前記含浸区間で前記樹脂混合物を前記先端吐出口から吐出して前記繊維状材料に含浸させることを特徴とする請求項1〜9の何れか1項に記載の管ライニング用硬化性樹脂含浸多層ホ−スの連続的製造方法。
- 前記導管の前記先端吐出口の断面形状は、方形状、円形状または楕円状であることを特徴とする請求項1〜10の何れか1項に記載の管ライニング用樹脂含浸多層ホ−スの連続的製造方法。
- 請求項1〜11の何れか1つに記載の方法を実施するための管ライニング用樹脂含浸多層ホ−スの製造装置において、
前記含浸区間における多層ホースの外周面から所定の距離に配置され、硬化性樹脂の充填量の大小により変位する多層ホースの外径の状態を検知するセンサーと、
前記センサーから送信される計測距離情報を受けて前記硬化性樹脂組成物送液導管と増粘剤送液導管とに給送する材料の量を調整する装置と、
を有することを特徴とする管ライニング用樹脂含浸多層ホ−スの製造装置。 - 前記多層ホ−スを移送方向に移動するため、該多層ホ−スを直径方向の両側から挟むように可動の2つのキャタピラー駆動装置が含浸区間の前方及び/又は後方に設けてあることを特徴とする請求項12に記載の管ライニング用樹脂含浸多層ホースの製造装置。