JP4754818B2 - 継目無鋼管熱間圧延用潤滑剤 - Google Patents
継目無鋼管熱間圧延用潤滑剤 Download PDFInfo
- Publication number
- JP4754818B2 JP4754818B2 JP2004378722A JP2004378722A JP4754818B2 JP 4754818 B2 JP4754818 B2 JP 4754818B2 JP 2004378722 A JP2004378722 A JP 2004378722A JP 2004378722 A JP2004378722 A JP 2004378722A JP 4754818 B2 JP4754818 B2 JP 4754818B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- alkali metal
- lubricant
- hot rolling
- seamless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[5]炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%からなり、
マンネスマン方式によるプラグミル圧延において、中空素間を延伸圧延する際に、中空素間内に投入し使用することを特徴とする継目無鋼管熱間圧延用潤滑剤。
[6]脂肪酸のアルカリ金属塩0〜40質量%、脂肪酸のアルカリ土類金属塩0〜40質量%、炭酸ナトリウム0〜30質量%、アルカリ金属の硫酸塩0〜20質量%のうちの1種または2種以上を含むことを特徴とする前記[5]に記載の継目無鋼管熱間圧延用潤滑剤。
[7]炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%を含み、かつ、炭酸ナトリウム0〜30質量%、アルカリ金属の硫酸塩0〜20質量%のうちの1種または2種を含むことを特徴とする継目無鋼管熱間圧延用潤滑剤。
[8]炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%を含み、かつ、炭酸ナトリウム20〜30質量%、アルカリ金属の硫酸塩5〜20質量%の1種または2種、および、脂肪酸のアルカリ金属塩0〜40質量%、脂肪酸のアルカリ土類金属塩0〜40質量%の1種または2種を含むことを特徴とする継目無鋼管熱間圧延用潤滑剤。
[9]炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%を含み、かつ、脂肪酸のアルカリ金属塩0〜40質量%、脂肪酸のアルカリ土類金属塩0〜40質量%の1種または2種を含む(但し、脂肪酸Na塩またはCa塩のいずれか1種または2種を5〜30質量%で混合してなる場合を除く)ことを特徴とする継目無鋼管熱間圧延用潤滑剤。
[10]マンネスマン方式の穿孔圧延機で穿孔された中空素管を延伸圧延する際に、中空素管内に投入し使用することを特徴とする前記[7]〜[9]のいずれかに記載の継目無鋼管熱間圧延用潤滑剤。
各物質の酸化鉄への反応性(スラグ化)と広がり性:
アルカリ金属硼酸塩の高温粘度及び素管内面での広がり性を改善させる各物質について酸化鉄(スケール)への反応性(スラグ化)と広がり性について調査した。
試験片SPCC冷間圧延鋼鈑(80×60×1mm)を1150℃電気炉内に5分間放置し表面にスケールを発生させた後、表1.に示す各物質0.5gを試験片の中央部に載せ電気炉内に20秒間放置後取り出しスケールへの反応性(スラグ化)及び広がり性について評価した。
スケールへの反応性(スラグ化): まったく反応性の無い無添加を0とし、最も反応性の高い塩化ナトリウム10として10段階にて評価した。
表1に示すとおり炭酸リチウムのみが酸化鉄への反応性(スラグ化)が極端に低く、広がり性が良い事が解る。
ワークプラグ先端ノズルより素管内面に黒鉛を噴射しながら延伸圧延を行う方法での使用を想定し、黒鉛を配合していない本発明の潤滑剤について下記試験方法により評価した。
空気雰囲気中の電気炉で5分間加熱しスケールを発生た試片を取り出し、試片表面上に黒鉛Bを振り掛け更に潤滑剤を直ちに振り掛け、再度電気炉内に入れ4秒後に上下のダイスで圧縮させた場合のダイスへの焼付性、潤滑性として摩擦係数、及び粗度測定、スケールの展着(堆積)性を測定した。
ダイス:SKD−61 HRC=55
ダイス加熱温度:300℃
リング材質:SS−400
リング形状:30φ×15φ×10mm
リング加熱温度:1150℃×5min
荷重:40t
落下高さ:45mm
圧縮率:60%
潤滑剤塗布量:60mg(120g/m2)
評価方法:
ダイスへの焼付性:圧縮後の上部ダイスへの焼付程度を下記A〜Eの5段階とし評価した。
D:焼付き多い E:焼付き極めて多い
摩擦係数:リング試片の圧縮率、内径変化率を計測しを算出した。
フコム574A)にてスケールが押し込まれた深さを平均粗さRa(μm)として測定した。
C:スケールの展着多い D:スケールの展着極めて多い
但し、表1〜表6に於いて使用した各成分は以下のものである。
四硼酸カリウム K2B4O7・4H2O (平均粒径100μm,純度99%)
炭酸リチウム Li2CO3 (平均粒径40μm,純度99%)
炭酸ナトリウム Na2CO3 (平均粒径80μm,純度98%)
炭酸カリウム K2CO3 (平均粒径80μm,純度98%)
炭酸カルシウム CaCO3 (平均粒径40μm,純度99%)
硫酸ナトリウム NaSO4 (平均粒径40μm,純度98%)
食塩 NaCl (平均粒径80μm,純度99%)
トリポリ燐酸ナトリウム Na5P3O10 (平均粒径80μm,純度99%)
脂肪酸ナトリウム 脂肪酸がC12〜C18の混合脂肪酸Na
(平均粒径500μm,純度98%)
ステアリン酸ナトリウム C17H35COONa
(平均粒径40μm,純度99%)
ステアリン酸カリウム C17H35COOK
(平均粒径40μm,純度99%)
ステアリン酸カルシウム (C17H35COO)2Ca
(平均粒径100μm,純度99%)
三酸化二鉄 Fe2O3 (平均粒径0.4μm,純度98%)
合成雲母 (ナトリウム四ケイ素雲母)(NaMg2.5(Si4O10)F2)
(平均粒径50μm,純度99%)
黒鉛A 天然鱗片状黒鉛 (平均粒径35μm,純度97%)
黒鉛B 天然鱗片状黒鉛 (平均粒径10μm,純度86%)
ワークプラグ先端ノズルより素管内面に黒鉛を噴射せずに延伸圧延を行う方法での使用を想定し、黒鉛を所定量配合した本発明の潤滑剤について下記試験方法により評価した。
空気雰囲気中の電気炉で5分間加熱しスケールを発生た試片を取り出し、試片表面上に潤滑剤を振り掛け、再度電気炉内に入れ4秒後に上下のダイスで圧縮させた場合のダイスへの焼付性、潤滑性として摩擦係数、及び粗度測定、スケールの展着(堆積)性を測定した。
黒鉛を所定量配合した本発明の潤滑剤についての実機での評価として、マンネスマン方式によるプラグミル工程において、材質SCM435の丸ビレットを加熱炉で約1250℃に加熱し、ビアサーにて穿孔しエロンゲーターで傾斜圧延されて得られた長さ10,000mm、外径250mm、肉厚15mm、表面温度約1150℃の中空素管をプラグミルにて延伸圧延する際、工具が挿入される直前に圧縮空気にて表6.に示す各潤滑剤約250gを投入し、 長さ14,000mm、外径240mm、肉厚11mm、の中空素管とし、後のリーラーで磨管し再加熱後サイジングミルで長さ13,700mm、外径244.5mm、肉厚11mm、に圧延して得られた継目無管の内面すじ疵及びプラグミル工具の摩耗、寿命を調査した。
内面すじ疵:上記プラグミルにて各潤滑剤に対し同一工具を用いて中空素管を200本づつ延伸圧延を行い内面すじ疵の深さが0.1〜0.5mmのものについては手入れを加えれば良しとし、0.5mm以上のものについては手入れが不可能であり格落品とし、内面すり疵不合格率を算出し評価した。
格落品率 =(格落本数/圧延本数) ×100
工具の寿命:上記プラグミル工程にて各潤滑剤に対し同一工具を用いて中空素管を延伸圧延し、工具表面の高さ0.5mm以上の焼付き疵あるいは深さ0.5mm以上のえぐれ疵発生までの圧延パス回数で評価した。
Claims (10)
- 炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%、黒鉛10〜60質量%からなることを特徴とする粉体状の継目無鋼管熱間圧延用潤滑剤。
- 脂肪酸のアルカリ金属塩0〜40質量%、脂肪酸のアルカリ土類金属塩0〜40質量%、炭酸ナトリウム0〜30質量%、アルカリ金属の硫酸塩0〜20質量%のうちの1種または2種以上を含むことを特徴とする請求項1に記載の粉体状の継目無鋼管熱間圧延用潤滑剤。
- マンネスマン方式の穿孔圧延機で穿孔された中空素管を延伸圧延する際に、中空素管内に投入して使用することを特徴とする請求項1または2に記載の継目無鋼管熱間圧延用潤滑剤。
- マンネスマン方式によるプラグミル圧延において、中空素管を延伸圧延する際に、中空素管内に投入して使用することを特徴とする請求項1〜3のいずれかに記載の継目無鋼管熱間圧延用潤滑剤。
- 炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%からなり、
マンネスマン方式によるプラグミル圧延において、中空素間を延伸圧延する際に、中空素間内に投入し使用することを特徴とする継目無鋼管熱間圧延用潤滑剤。 - 脂肪酸のアルカリ金属塩0〜40質量%、脂肪酸のアルカリ土類金属塩0〜40質量%、炭酸ナトリウム0〜30質量%、アルカリ金属の硫酸塩0〜20質量%のうちの1種または2種以上を含むことを特徴とする請求項5に記載の継目無鋼管熱間圧延用潤滑剤。
- 炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%を含み、かつ、炭酸ナトリウム0〜30質量%、アルカリ金属の硫酸塩0〜20質量%のうちの1種または2種を含むことを特徴とする継目無鋼管熱間圧延用潤滑剤。
- 炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%を含み、かつ、炭酸ナトリウム20〜30質量%、アルカリ金属の硫酸塩5〜20質量%の1種または2種、および、脂肪酸のアルカリ金属塩0〜40質量%、脂肪酸のアルカリ土類金属塩0〜40質量%の1種または2種を含むことを特徴とする継目無鋼管熱間圧延用潤滑剤。
- 炭酸リチウム5〜40質量%及びアルカリ金属硼酸塩10〜70質量%を含み、かつ、脂肪酸のアルカリ金属塩0〜40質量%、脂肪酸のアルカリ土類金属塩0〜40質量%の1種または2種を含む(但し、脂肪酸Na塩またはCa塩のいずれか1種または2種を5〜30質量%で混合してなる場合を除く)ことを特徴とする継目無鋼管熱間圧延用潤滑剤。
- マンネスマン方式の穿孔圧延機で穿孔された中空素管を延伸圧延する際に、中空素管内に投入し使用することを特徴とする請求項7〜9のいずれかに記載の継目無鋼管熱間圧延用潤滑剤。