JP4700463B2 - 保護層熱転写フィルムおよび印画物 - Google Patents
保護層熱転写フィルムおよび印画物 Download PDFInfo
- Publication number
- JP4700463B2 JP4700463B2 JP2005281657A JP2005281657A JP4700463B2 JP 4700463 B2 JP4700463 B2 JP 4700463B2 JP 2005281657 A JP2005281657 A JP 2005281657A JP 2005281657 A JP2005281657 A JP 2005281657A JP 4700463 B2 JP4700463 B2 JP 4700463B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- protective layer
- thermal transfer
- weight
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
保護層熱転写フィルムの他の例としては、基材フィルムの一方面に、熱転写性保護層と熱昇華性色材層及び熱溶融性色材層からなる群より選ばれた少なくとも1つの色材層が面順次に設けられている保護層熱転写フィルム等を挙げることができる。
固形分50%
セルトップ227:シリコーン変性アクリル系樹脂、ダイセル化学工業(株)製、
固形分50%
ダイヤナールBR-87:アクリル系樹脂、三菱レイヨン(株)製、
Mw:25000
セルトップCAT-A:硬化剤、ダイセル化学工業(株)製、固形分10%
KF-6011:ポリエーテル変性シリコーンオイル、信越化学工業(株)製、
粘度 130mm2/s(25℃)
KF-355A:ポリエーテル変性シリコーンオイル、信越化学工業(株)製、
粘度 130mm2/s(25℃)
X-22-4741:エポキシ、ポリエーテル変性シリコーンオイル、信越化学工業(株)製、
粘度 400mm2/s(25℃)
X-22-4742:ポリエーテル変性シリコーンオイル、信越化学工業(株)製、
粘度 300mm2/s(25℃)
X-22-4952:ポリエーテル変性シリコーンオイル、信越化学工業(株)製、
粘度 90mm2/s(25℃)
X-22-6266:ポリエーテル変性シリコーンオイル、信越化学工業(株)製、
粘度 420mm2/s(25℃)
X-22-162C:カルボキシル変性シリコーンオイル、信越化学工業(株)製、
粘度 230mm2/s(25℃)
KF-6003:カルビノール変性シリコーンオイル、信越化学工業(株)製、
粘度 110mm2/s(25℃)
X-22-1821:フェノール変性シリコーンオイル、信越化学工業(株)製、
粘度 100mm2/s(25℃)
KF-8001:アミノ・アルコキシ変性シリコーンオイル、信越化学工業(株)製、
粘度 250mm2/s(25℃)
KF-410:メチルスチリル変性シリコーンオイル、信越化学工業(株)製、
粘度 900mm2/s(25℃)
KF-413:アルキル変性シリコーンオイル、信越化学工業(株)製、
粘度 190mm2/s(25℃)
X-22-715:高級脂肪酸エステル変性シリコーンオイル、信越化学工業(株)製、
粘度 15000mm2/s(25℃)
KF96-100:ジメチルシリコーンオイル、信越化学工業(株)製、
粘度 100mm2/s(25℃)
KF965-100:ジメチルシリコーンオイル、信越化学工業(株)製、
粘度 100mm2/s(25℃)
鹸化度95%、Mn:80000
PVP‐K90:ポリビニルピロリドン、ISPジャパン(株)製、
Mn:1570000 (K=90)
スノーテックス20L:コロイダルシリカ、日産化学(株)製、
平均粒径40nm
C318:ポリビニルアルコール、クラレ(株)製、
鹸化度80%、Mn:80000
スノーテックスOL-40:コロイダルシリカ、日産化学(株)製、
平均粒径40nm
バイロナールMD-1500:ポリエステル、東洋紡績(株)製、
スミレーズレジン5004:硬化剤、住友化学(株)製
Mn:130000
ダイヤナールBR-87:ポリメチルメタクリル酸(PMMA)、三菱レイヨン(株)製、
Mw:25000
サンプレンIB-114B:ウレタンポリオール、三洋化成(株)製、
ダイヤナールLR-209:アクリルポリオール、三菱レイヨン(株)製、
Mn:9000
PUVA-50M-40TM:(UVA)含有アクリル樹脂、大塚化学(株)製、
Mn:30000
チヌビン900:UVA化合物、チバ・スペシャルティ・ケミカルズ(株)製
サイリシア310P:シリカフィラー、富士シリシア(株)製、
平均粒径3μm、
UVAは「ULTRA-VIOLET LIGHT ABSORBER」の略である。
第1層(離型層)
表1に示した配合物(表中の%は重量%を表す)を、溶剤(トルエン/メチルエチルケトン(MEK)=1/1)で希釈し、離型層用インキを調製した。得られたインキを、ワイヤーコーターバー(#3)にて塗布量1.0g/m2(乾燥時、以下同様)となるように、厚み4.5μmのPETフィルム上に塗布した。得られた塗布フィルムを110℃のオーブンにて1分間乾燥させた。
表1に示した剥離層仕様1または2の仕様で剥離層を形成した。
RS−1717(PVA):25重量%
PVP−K90: 25重量%
スノーテックス20L: 50重量%
上記配合物を溶剤(水/イソプロピルアルコール(IPA)=1/1)で希釈し、固形分5%の剥離層用インキを調製した。得られたインキを、ワイヤーコーターバー(#3)にて塗布量0.3g/m2となるように、離型層上に塗布した。得られた塗布フィルムを110℃のオーブンにて1分間乾燥させた。
RS−1717(PVA):20重量%
スノーテックス20L: 80重量%
上記配合物を溶剤(水/イソプロピルアルコール(IPA)=1/1)で希釈し、固形分5%の剥離層用インキを調製した。得られたインキを、ワイヤーコーターバー(#3)にて塗布量0.3g/m2となるように、離型層上に塗布した。得られた塗布フィルムを110℃のオーブンにて1分間乾燥させた。
RS−1717(PVA): 20重量%
スノーテックスOL−40(コロイダルシリカ):76重量%
スミレーズレジン5004(硬化剤): 4重量%
ガントレッツAN−119(ポリ無水マレイン酸):50重量%
ダイヤナールBR−87(PMMA): 42重量%
サンプレンIB−114B(ウレタンポリオール): 8重量%
バイロン700(ポリエステル): 72重量%
PUVA−50M−40TM(UVA含有アクリル樹脂):18重量%
チヌビン900(UVA化合物): 8重量%
サイリシア310P(シリカフィラー、平均粒径3μm): 2重量%
[はじき]
剥離層用インキを離型層上に塗布したときのはじきを目視にて観察し以下のようにランク付けした
○:はじきなし
△:少しはじき気味であるが、膜作製に支障なし
×:はじきあり(膜作製に支障あり)
結果を表2にまとめた。
保護層をテストプリンタで印画し(印画条件はライン速度20ms/line、パルスデューティー65%、電圧14.5V、階調地255/255、印画幅8cm)、180度剥離するときの剥離力をロードセルにて測定した(剥離速度1000mm/min)。
剥離力は、保護層転写フィルム作成後および40℃、湿度90%の環境下に24時間保存後に測定した。
剥離力が50〜60g以下であれば、いかなるプリンタ動作環境下印画動作に支障がない。
結果を表2にまとめた。表2中、「−」ははじきなどの理由から評価に値しなかった事(未評価)を意味する。
(印画物の製造)
イエロー、マゼンタ及びシアンの各色材層が設けられた熱転写フィルムを用い、プリンタ(SONY製フォト用プリンタDPP−SV55)で、画像を形成した。次に、画像形成部に上記実施例、比較例で製造した各保護層熱転写フィルムを重ね合わせ、プリンタ(SONY製フォト用プリンタDPP−SV55)を用いて、保護層熱転写フィルムから保護層を、画像形成部を覆うように転写し、保護層で被覆した印画物を形成した。得られた印画物の表面に水性スタンプで捺印したところ実施例のものは良好に捺印できた(◎)。比較例のものは、はじきの為に評価できないものや、剥離力が重いために印画後転写面が正常ではなく捺印性を評価できたものはなかった。結果を表2にまとめた。「−」は、はじきなどの理由から評価しなかった事(未評価)を意味する。
本発明の保護層熱転写フィルムは、剥離性に優れている。
本発明保護層熱転写フィルムの保護層が転写された被転写体は、水性タイプの捺印性等、水性インクの筆記性に優れている。
2 基材フィルム
3 離型層
4 剥離層
5 多孔層
6 プライマー層
7 ヒートシール層(HS層)
8 保護層
21 保護層熱転写フィルム
22 基材フィルム
26 熱転写性保護層
27 背面層
Claims (4)
- 基材フィルムの一方の面に、該基材フィルム側から順に少なくとも離型層および保護層が設けられている保護層熱転写フィルムであって、
該離型層が少なくともシリコーン変性アクリル系樹脂とポリエーテル変性シリコーンオイルから形成され、かつ該シリコーン変性アクリル系樹脂に対する該ポリエーテル変性シリコーンオイルの添加量が3〜15重量%であり、
該保護層が、該離型層上に形成された剥離層を少なくとも含み、該剥離層が水系塗布液から形成されてなる、ことを特徴とする保護層熱転写フィルム。 - ポリエーテル変性シリコーンオイルが、500mm2/s以下(25℃)の粘度を有する、請求項1に記載の保護層熱転写フィルム。
- 剥離層が、少なくとも水系樹脂とシリカ粒子からなり、該シリカ粒子が固型分で90重量%以下である、請求項1または2に記載の保護層熱転写フィルム。
- 基材フィルムの一面に、熱転写可能な保護層と共に、熱昇華性色材層および/または熱溶融性色材層が設けられていることを特徴とする、請求項1〜3のいずれかに記載の保護層熱転写フィルム。