JP4448681B2 - 反射防止フィルム、偏光板、及び液晶表示装置 - Google Patents
反射防止フィルム、偏光板、及び液晶表示装置 Download PDFInfo
- Publication number
- JP4448681B2 JP4448681B2 JP2003392272A JP2003392272A JP4448681B2 JP 4448681 B2 JP4448681 B2 JP 4448681B2 JP 2003392272 A JP2003392272 A JP 2003392272A JP 2003392272 A JP2003392272 A JP 2003392272A JP 4448681 B2 JP4448681 B2 JP 4448681B2
- Authority
- JP
- Japan
- Prior art keywords
- particles
- group
- film
- layer
- hard coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
防眩性の質感を高めるために(見た目のざらつき感を無くすために)、防眩性を付与する粒子は、その粒度分布をできるだけシャープにすることが望ましく、また、表面散乱による黒の締まりの低下を防ぐ為に、防眩性の低い反射防止フィルム(内部散乱性を有するものの防眩性のないものも含む)が望まれてくるようになり、防眩性を付与する粒子の大きさと防眩層の厚みの差は、従来以上に小さくなってきており、粗大粒子の存在に対する欠陥検出の感度はますます高まってしまう背景が生まれつつある。
また、液晶テレビの大サイズ化(21インチ以上)、ワイド化(アスペクト比9:16)に対応するには、今まで以上に欠陥発生率を下げなければ対応できない背景もあった。
本発明の他の目的は、そのような反射防止フィルムを用いた偏光板を提供することにある。
本発明のさらなる他の目的は、上記反射防止フィルムや偏光板を装備した液晶表示装置などの表示装置を提供することにある。
数式(1):0μm≦dMAX−dAV≦7μm
dMAX:大サイズ粒子の最大粒径(単位μm)
dAV :大サイズ粒子の平均粒径(単位μm)
1.透明支持体上に、少なくとも1層のハードコート層と、最外層に位置する低屈折率層からなる光学フィルムにおいて、(a)上記光学フィルム表面のRa(中心線平均粗さ)が0.15μm以下であり、
(b)上記ハードコート層が粒子径の異なる2種以上の粒子を含有し、しかも
(c)前記粒子の少なくとも1種類が、平均粒径がハードコート層の厚みの80%以上の大きさを有する粒子であって、かつ該粒子が下記数式(1)を満たし、
前記粒子の少なくとも1種類が、内部散乱性を付与する粒子であり、該内部散乱性を付与する粒子の平均粒径が該ハードコート層の厚みの80%未満であって、かつ該内部散乱性を付与する粒子が下記数式(2)を満たし、
少なくとも1層のハードコート層が光拡散層であり、該光拡散層のゴニオフォトメーターで測定される散乱光プロファイルの出射角0°の光強度に対する30°の散乱光強度が、0.01〜0.2%の範囲にある、
ことを特徴とする反射防止フィルム。
式(1):0μm≦dMAX−dAV≦7μm
式(2):0μm≦d MAX −d AV ≦1μm
dMAX:粒子の最大粒径(単位μm)
dAV :粒子の平均粒径(単位μm)
2.前記内部散乱性を付与する粒子の平均粒径が1〜5μmであることを特徴とする上記1に記載の反射防止フィルム。
3.フィルム表面のRa(中心線平均粗さ)が0.10μm以下であることを特徴とする上記1又は2に記載の反射防止フィルム。
4.櫛幅0.5mmで測定したときの透過画像鮮明性の値が、40%以上97%未満であることを特徴とする上記1〜3のいずれかに記載の反射防止フィルム。
5.上記1〜4のいずれかに記載の反射防止フィルムを偏光板における偏光子の2枚の保護フィルムのうちの一方に用いたことを特徴とする偏光板。
6.2枚の保護フィルムのうち反射防止フィルムが用いられていない保護フィルムが、光学異方性層を含んでなる光学補償層を有する光学補償フィルムであり、該光学異方性層がディスコティック構造単位を有する化合物からなる負の複屈折率を有する層であり、該ディスコティック構造単位の円盤面が該表面保護フィルム面に対して傾いており、かつ該ディスコティック構造単位の円盤面と該表面保護フィルム面とのなす角度が、光学異方層の深さ方法に変化していることを特徴とする上記5に記載の偏光板。
7.上記1〜4のいずれかに記載の反射防止フィルムあるいは上記5または6に記載の偏光板をディスプレイの最表面に用いたことを特徴とする液晶表示装置。
8.液晶表示装置が、2 1 インチサイズ以上の液晶大型テレビ、またはアスペクト比が9対16の液晶ワイドテレビであることを特徴とする上記7に記載の液晶表示装置。
9.上記1〜4のいずれかに記載の反射防止フィルムあるいは上記5または6に記載の偏光板を少なくとも1枚有するTN、STN、VA、IPS、またはOCBのモードの透過型、反射型、または半透過型の液晶表示装置。
また、本発明の反射防止フィルムを装備した表示装置あるいは本発明の反射防止フィルムを用いた偏光板を装備した表示装置は、視認性に優れると共に視野角が非常に広い。
ハードコート層はハードコート性を付与するためのバインダー、大サイズ粒子、内部散乱性を付与するための粒子、および高屈折率化、架橋収縮防止、高強度化のための無機フィラー、から形成される。本発明で言及する粒子と、無機フィラーとは区別される。
バインダーとしては、飽和炭化水素鎖またはポリエーテル鎖を主鎖として有するポリマーであることが好ましく、飽和炭化水素鎖を主鎖として有するポリマーであることがさらに好ましい。
また、バインダーポリマーは架橋構造を有することが好ましい。
飽和炭化水素鎖を主鎖として有するバインダーポリマーとしては、エチレン性不飽和モノマーの重合体が好ましい。飽和炭化水素鎖を主鎖として有し、かつ架橋構造を有するバインダーポリマーとしては、二個以上のエチレン性不飽和基を有するモノマーの(共)重合体が好ましい。
高屈折率にするには、このモノマーの構造中に芳香族環や、フッ素以外のハロゲン原子、硫黄原子、リン原子、及び窒素原子から選ばれた少なくとも1種の原子を含むことが好ましい。
従って、エチレン性不飽和基を有するモノマー、光ラジカル開始剤、あるいは熱ラジカル開始剤、大サイズ粒子(防眩性を付与する粒子であってもよい)、内部散乱性を付与する粒子、および無機フィラーを含有する塗液を調製し、該塗液を透明支持体上に塗布・乾燥後、電離放射線または熱による重合反応により硬化して、更に必要に応じて、硬化の前後に、残留溶剤低減を目的とした後加熱乾燥によって、ハードコート層を形成することができる。
アセトフェノン類の例には、2,2−ジエトキシアセトフェノン、p−ジメチルアセトフェノン、1−ヒドロキシジメチルフェニルケトン、1−ヒドロキシシクロヘキシルフェニルケトン、2−メチル−4−メチルチオ−2−モルフォリノプロピオフェノンおよび2−ベンジル−2−ジメチルアミノ−1−(4−モルフォリノフェニル)−ブタノンが含まれる。
ベンゾイン類の例には、ベンゾインベンゼンスルホン酸エステル、ベンゾイントルエンスルホン酸エステル、ベンゾインメチルエーテル、ベンゾインエチルエーテルおよびベンゾインイソプロピルエーテルが含まれる。
ベンゾフェノン類の例には、ベンゾフェノン、2,4−ジクロロベンゾフェノン、4,4−ジクロロベンゾフェノンおよびp−クロロベンゾフェノンが含まれる。
ホスフィンオキシド類の例には、2,4,6−トリメチルベンゾイルジフェニルフォスフィンオキシドが含まれる。
最新UV硬化技術(P.159,発行人;高薄一弘,発行所;(株)技術情報協会,1991年発行)にも種々の例が記載されており本発明に有用である。
市販の光開裂型の光ラジカル重合開始剤としては、日本チバガイギー(株)製のイルガキュア(651,184,907)等が好ましい例として挙げられる。
光重合開始剤は、多官能モノマー100質量部に対して、0.1〜15質量部の範囲で使用することが好ましく、より好ましくは1〜10質量部の範囲である。
光重合開始剤に加えて、光増感剤を用いてもよい。光増感剤の具体例として、n−ブチルアミン、トリエチルアミン、トリ−n−ブチルホスフィン、ミヒラーのケトンおよびチオキサントンを挙げることができる。
具体的には、有機過酸化物として過酸化ベンゾイル、過酸化ハロゲンベンゾイル、過酸化ラウロイル、過酸化アセチル、過酸化ジブチル、クメンヒドロぺルオキシド、ブチルヒドロぺルオキシド、無機過酸化物として、過酸化水素、過硫酸アンモニウム、過硫酸カリウム等、アゾ化合物として2−アゾービスーイソブチロニトリル、2−アゾービスープロピオニトリル、2−アゾ−ビスーシクロヘキサンジニトリル等、ジアゾ化合物としてジアゾアミノベンゼン、p−ニトロベンゼンジアゾニウム等を挙げることができる。
従って、多官能エポシキシ化合物、光酸発生剤あるいは熱酸発生剤、マット粒子および無機フィラーを含有する塗液を調製し、該塗液を透明支持体上に塗布後電離放射線または熱による重合反応により硬化して反射防止フィルムを形成することができる。
架橋性官能基の例には、イソシアナート基、エポキシ基、アジリジン基、オキサゾリン基、アルデヒド基、カルボニル基、ヒドラジン基、カルボキシル基、メチロール基および活性メチレン基が含まれる。ビニルスルホン酸、酸無水物、シアノアクリレート誘導体、メラミン、エーテル化メチロール、エステルおよびウレタン、テトラメトキシシランのような金属アルコキシドも、架橋構造を導入するためのモノマーとして利用できる。ブロックイソシアナート基のように、分解反応の結果として架橋性を示す官能基を用いてもよい。すなわち、本発明において架橋性官能基は、すぐには反応を示すものではなくとも、分解した結果反応性を示すものであってもよい。
これら架橋性官能基を有するバインダーポリマーは塗布後、加熱することによって架橋構造を形成することができる。
上記粒子の具体例としては、例えばシリカ粒子、TiO2粒子等の無機化合物の粒子、架橋アクリル粒子、架橋スチレン粒子、メラミン樹脂粒子、ベンゾグアナミン樹脂、ナイロン樹脂等の樹脂粒子、あるいは無機−有機ハイブリッド粒子等が挙げられる。なかでも架橋スチレン粒子、架橋アクリル粒子、シリカ粒子が好ましい。
光耐候性の観点から、架橋アクリル粒子、シリカ粒子が特に好ましい。
粒子の形状は、真球あるいは不定形、針状、棒状、平板状のいずれも使用できるが、一般的には真球状である。
ハードコート層には、高屈折率化、架橋収縮防止、高強度化のために、上記の粒子に加えて、チタン、ジルコニウム、アルミニウム、インジウム、亜鉛、錫、アンチモンのうちより選ばれる少なくとも1種の金属の酸化物からなり、平均粒径が0.2μm以下、好ましくは0.1μm以下、より好ましくは0.06μm以下であって、ハードコート層の厚みよりも充分小さい無機フィラーが含有されることが好ましい。
これらの無機フィラーの添加量は、ハードコート層の全質量の10〜90%であることが好ましく、より好ましくは20〜80%であり、特に好ましくは30〜75%である。
なお、このようなフィラーは、粒径が光の波長よりも十分小さいために散乱が生じず、樹脂バインダーに該無機フィラーが分散した複合体は光学的に均一な物質として振舞う。分散性を充分確保することで、点欠陥の原因となる無機フィラーは含まれない。
(点欠陥個数の定義)
ランダムにサンプリングした1m×1mの反射防止フィルム端末について、透過光源下にて、点欠陥検査を行い、一般ユーザーの目で検出可能な50μm以上の輝点を点欠陥としてマーキングする。その後、マーキングした部分を光学顕微鏡にて、ひとつひとつ写真撮影し、ハードコート層に含有される粒子の粗大粒子によって、点欠陥になっている場合の個数を数える。このような検査を、ランダムにサンプリングした1m×1mの端末サンプル100枚について行い、数えた点欠陥の総数を100で割って、1m2あたりの平均の点欠陥個数とする。
製品得率を考えると1個/m2以下が必要であり、好ましくは0.3個/m2以下、更に好ましくは0.1個/m2以下、最も好ましくは0個/m2(検出感度以下)である。
数式(1):0μm≦dMAX−dAV≦7μm
ここで、dMAXは大サイズ粒子の最大粒径(単位μm)であり、dAVは大サイズ粒子の平均粒径(単位μm)である。
より好ましくは0μm≦dMAX−dAV≦5μm、更により好ましくは0μm≦dMAX−dAV≦3μm、もっと好ましくは0μm≦dMAX−dAV≦1μmを満たすことである。
粒度分布として最も好ましいのは、粒径が単一であること、すなわち、dMAX−dAV≒0μmであるが、粒子の粒度分布を極端に狭くすることは、例えば液晶スペーサー粒子のように、分級加工費が著しく上がるため、この点で好ましくはなく、製造コストを考慮すると、実質の下限は0.5μm程度である。平均粒径及び、最大粒径の測定方法については、後述の実施例に記載されている。
分級については、風力分級、メッシュ分級、沈降速度差を利用する分級、遠心分離を利用する分級などが挙げられるが、所望の粒度分布が得られれば、その方法に制限は無い。最も、高効率な分級方法として、風力分級法が挙げられる。
この測定装置、原理は、透過物体の写像性測定方法として、JIS K 7105 (プラスチックの光学特性試験方法)で広く知られており、ISO/TC79/SC1でISO技術報告書として作成することが決定している。この方法は、試料からの反射光を移動する光学クシを通して測定し、その値を計算によって求めるものである。試料がボケを生じるものの場合、光学クシ上に結像されるスリットの像は、そのボケの影響で太くなるため、透過部の位置ではスリット像の両端が不透明部にかかり、100%あった光量が減少する。また、不透明部の位置ではスリット像の両端は不透明部から光が漏れて、0%の光量が増加する。このようにして、写像性測定機による透過画像鮮明性の値は、光学クシの透明部の透過光最大値Mと、不透明部の最小値mから次式によって定義される。
透過画像鮮明性の値 C(%)=[(M−m)/(M+m)] × 100
Cの値が大きければ透過画像鮮明性が高く、小さければ"ボケ"または"歪"をもっていることを示す。(塗装技術、1985年7月号、写像性測定器、須賀・三田村)
本発明の反射防止フィルムの場合、櫛幅0.5mmの光学櫛を用いた透過画像鮮明性の値は、40%以上97%未満が好ましく、さらに好ましくは60%以上95%未満である。
本発明では上記大サイズの粒子径(dAV)、粒子頻度、ハードコート層膜厚を調整することによって、中心線平均粗さRaの値を上記した範囲とすることができ、黒の締まりが良好で、外光のもとでも白けない、しかも、Raを0.03以上とすると実質的な防眩性が得られ、点欠陥故障を多発させることなく、防眩性反射防止ファイルムを製造することができる。
本発明の反射防止フィルムの低屈折率層の屈折率は、1.38〜1.49であり、好ましくは1.38〜1.44の範囲にある。さらに、低屈折率層は下記数式(2)を満たすことが低反射率化の点で好ましい。
数式(2):m/4×0.7<n1d1<m/4×1.3
上記数式(2)中、mは正の奇数であり、n1は低屈折率層の屈折率であり、そしてd1は低屈折率層の膜厚(nm)である。また、λは波長であり、500〜550nmの範囲の値である。
なお、上記数式(2)を満たすとは、上記波長の範囲において数式(2)を満たすm(正の奇数、通常1である)が存在することを意味している。
低屈折率層には、低屈折率バインダーとして、含フッ素ポリマー、あるいは含フッ素ゾルゲル素材などが含まれる。含フッ素ポリマー、あるいは含フッ素ゾルゲルとしては動摩擦係数0.03〜0.15、水に対する接触角90〜120°の、熱または電離放射線により架橋する素材が好ましい。本発明の低屈折率層には膜強度向上のための無機フィラーを用いることもできる。
低屈折率層に用いられる含フッ素ポリマーとしてはパーフルオロアルキル基含有シラン化合物(例えば(ヘプタデカフルオロ−1,1,2,2−テトラヒドロデシル)トリエトキシシラン)の加水分解、脱水縮合物の他、含フッ素モノマー単位と架橋反応性付与のための構成単位を構成成分とする含フッ素共重合体が挙げられる。
該無機フィラーは、低屈折率層に含有させることから、低屈折率であることが望ましい。
例えば、フッ化マグネシウムやシリカが挙げられる。特に、屈折率、分散安定性、コストの点で、シリカが好ましい。該シリカの粒径は、該低屈折率層の厚みの30%以上100%以下が好ましく、より好ましくは35%以上80%以下、更に好ましくは40%以上60%以下である。低屈折率層の厚みが100nmであれば、シリカの粒径は30nm以上100nmが好ましく、より好ましくは35nm以上80nm以下、更に好ましくは、40nm以上60nmである。シリカの粒径が小さすぎると、耐擦傷性の改良効果が少なくなり、大きすぎると低屈折率層表面に微細な凹凸でき、黒の締まりといった外観、積分反射率が悪化する。 シリカは、結晶質でも、アモルファスのいずれでも良く、また 単分散粒子でも、所定の粒径を満たすならば凝集粒子でも構わない。形状は、球径が最も好ましいが、不定形であっても問題無い。
用いられるオルガノシラン化合物は、下記一般式(3)で表すことができる。
一般式(3):(R10)m−Si(X)4-m
上記一般式(3)において、R10は置換もしくは無置換のアルキル基、置換もしくは無置換のアリール基を表す。
Xは加水分解可能な基を表し、例えばアルコキシ基(炭素数1〜5のアルコキシ基が好ましい。例えばメトキシ基、エトキシ基等が挙げられる)、ハロゲン(例えばCl、Br、I等)、又はR2COO(R2は水素原子または炭素数1〜5のアルキル基が好ましい。例えばCH3COO、C2H5COO等が挙げられる)が挙げられ、好ましくはアルコキシ基であり、特に好ましくはメトキシ基またはエトキシ基である。
mは1〜3の整数を表す。R10もしくはXが複数存在するとき、複数のR10もしくはXはそれぞれ同じであっても異なっていても良い。mとしては、好ましくは1または2であり、特に好ましくは1である。
R10に含まれる置換基としては特に制限はないが、ハロゲン原子(フッ素、塩素原子、臭素原子等)、水酸基、メルカプト基、カルボキシル基、エポキシ基、アルキル基(メチル基、エチル基、i−プロピル基、プロピル基、t−ブチル基等)、アリール基(フェニル基、ナフチル等基)、芳香族ヘテロ環基(フリル基、ピラゾリル基、ピリジル基等)、アルコキシ基(メトキシ基、エトキシ基、i−プロポキシ基、ヘキシルオキシ基等)、アリールオキシ基(フェノキシ基等)、アルキルチオ基(メチルチオ基、エチルチオ基等)、アリールチオ基(フェニルチオ基等)、アルケニル基(ビニル基、1−プロペニル基等)、アシルオキシ基(アセトキシ基、アクリロイルオキシ基、メタクリロイルオキシ基等)、アルコキシカルボニル基(メトキシカルボニル基、エトキシカルボニル基等)、アリールオキシカルボニル基(フェノキシカルボニル基等)、カルバモイル基(カルバモイル基、N−メチルカルバモイル基、N,N−ジメチルカルバモイル基、N−メチル−N−オクチルカルバモイル基等)、アシルアミノ基(アセチルアミノ基、ベンゾイルアミノ基、アクリルアミノ基、メタクリルアミノ基等)等が挙げられ、これら置換基は更に置換されていても良い。
一般式(4)
Yは、単結合、エステル基、アミド基、エーテル基、またはウレア基を表す。なかでも、単結合、エステル基、およびアミド基が好ましく、単結合およびエステル基が更に好ましく、エステル基が特に好ましい。
R10は、一般式(3)と同義であり、置換もしくは無置換のアルキル基、無置換のアリール基が好ましく、無置換のアルキル基、無置換のアリール基が更に好ましい。
Xは、一般式(3)と同義であり、ハロゲン、水酸基、および無置換のアルコキシ基が好ましく、塩素原子、水酸基、および無置換の炭素数1〜6のアルコキシ基が更に好ましく、水酸基、および炭素数1〜3のアルコキシ基が更に好ましく、メトキシ基が特に好ましい。
これらの有機溶媒は、1種単独であるいは2種以上を組み合わせて使用することもできる。
該反応における固形分の濃度は特に限定されるものではないが通常1%〜90%の範囲であり、好ましくは20%〜70%の範囲である。
加水分解性基がアルコキシドで触媒が有機酸の場合には、有機酸のカルボキシル基やスルホ基がプロトンを供給するために、水の添加量を減らすことができ、オルガノシランのアルコキシド基1モルに対する水の添加量は、0〜2モル、好ましくは0〜1.5モル、より好ましくは、0〜1モル、特に好ましくは、0〜0.5モルである。アルコールを溶媒に用いた場合には、実質的に水を添加しない場合も好適である。
反応は25〜100℃で撹拌することにより行われるが、オルガノシランの反応性により適宜調節されることが好ましい。
ジクロロメタン等のハロゲン化炭化水素を実質的に含まないセルロースアセテートフィルムおよびその製造法については発明協会公開技報(公技番号2001−1745、2001年3月15日発行、以下公開技報2001−1745号と略す)に記載されている。
鹸化処理することにより、最外層を有する側とは反対側の透明支持体の表面が親水化される。
親水化された表面は、ポリビニルアルコールを主成分とする偏向膜との接着性を改良するのに特に有効である。また、親水化された表面は、空気中の塵埃が付着しにくくなるため、偏向膜と接着させる際に偏向膜と反射防止フィルムの間に塵埃が入りにくく、塵埃による点欠陥を防止するのに有効である。
鹸化処理は、最外層を有する側とは反対側の透明支持体の表面の水に対する接触角が40゜以下になるように実施することが好ましい。更に好ましくは30゜以下、特に好ましくは20゜以下である。
(1)透明支持体上に反射防止層を形成後に、アルカリ液中に少なくとも1回浸漬することで、該フィルムの裏面を鹸化処理する。
(2)透明支持体上に反射防止層を形成する前または後に、アルカリ液を該反射防止フィルムの反射防止フィルムを形成する面とは反対側の面に塗布し、加熱、水洗および/または中和することで、該フィルムの裏面だけを鹸化処理する。
まず、各層を形成するための成分を含有した塗布液が調製される。次に、ハードコート層を形成するための塗布液を、ディップコート法、エアーナイフコート法、カーテンコート法、ローラーコート法、ワイヤーバーコート法、グラビアコート法やエクストルージョンコート法(米国特許2681294号明細書参照)により透明支持体上に塗布し、加熱・乾燥するが、マイクログラビアコート法が特に好ましい。その後、光照射あるいは加熱して、ハードコート層を形成するためのモノマーを重合して硬化する。これによりハードコート層が形成される。
ここで、必要であればハードコート層を複数層とし、ハードコート層塗布の前に同様な方法で平滑なハードコート層塗布および硬化を行うことができる。
次に、同様にして低屈折率層を形成するための塗布液をハードコート層上、例えば防眩性ハードコート層上に塗布し、光照射あるいは加熱し低屈折率層が形成される。このようにして、本発明の反射防止フィルムが得られる。
攪拌機、還流冷却器を備えた反応器、アクリロイルオキシプロピルトリメトキシシラン161部、シュウ酸123部、エタノール415部を加え混合したのち、70℃で5時間反応させた後、室温まで冷却しオルガノシランのゾル組成物aを得た。
市販ジルコニア含有UV硬化型ハードコート液(デソライトZ7404、JSR(株)製、固形分濃度61.2%、固形分中ジルコニア含率69.6%、重合性モノマー、重合開始剤含有)47600質量部、ジペンタエリスリトールペンタアクリレートとジペンタエリスリトールヘキサアクリレートの混合物(DPHA、日本化薬(株)製)14400質量部、メチルエチルケトン2700質量部を混合、攪拌し、更にこの溶液中に、平均粒径1.5μmのシリカ粒子(シーホスターKE−P150、屈折率1.45、日本触媒(株)製)を分散液中の固形分が30%となるように、分散媒をメチルイソブチルケトンとして、ポリトロン分散機にて10000rpmで40分間分散し、作製した分散液14800質量部加え、攪拌し、次いで、シランカップリング剤KBM−5103(信越化学(株)製)4800質量部加え、攪拌し、ハードコート層中間液(α)を作製した。尚、このシリカ粒子は、追加の分級工程を施さずして、dMAX−dAV≦1μmの範囲に入る、シャープな粒度分布を有する粒子であった。
屈折率1.42の熱架橋性含フッ素ポリマー(JN−7228、固形分濃度6%、JSR(株)製)15kg、MEK−ST(平均粒径15nmコロイダルシリカのメチルエチルケトン分散液、固形分濃度30%、日産化学(株)製)0.7kg、MEK−ST−L(平均粒径45nmコロイダルシリカのメチルエチルケトン分散液、固形分濃度30%、日産化学(株)製)0.7kg、オルガノシランのゾル組成物a 0.4kgおよびメチルエチルケトン3kg、シクロヘキサノン0.6kgを添加、攪拌の後、孔径1μmのポリプロピレン製フィルターでろ過して、低屈折率層用塗布液Aを調製した。
(1)ハードコート層の塗設
80μmの厚さのトリアセチルセルロースフイルム(TAC−TD80U、富士写真フイルム(株)製)をロール形態で巻き出して、上記のハードコート層用塗布液Aを線数135本/インチ、深度40μmのグラビアパターンを有する直径50mmのマイクログラビアロールとドクターブレードを用いて、グラビアロール回転数30rpm、搬送速度10m/分の条件で塗布し、60℃で150秒乾燥の後、さらに窒素パージ下で160W/cmの空冷メタルハライドランプ(アイグラフィックス(株)製)を用いて、照度400mW/cm2、照射量300mJ/cm2の紫外線を照射して塗布層を硬化させ、厚さ2.9μmのハードコート層を形成し、巻き取った。
ハードコート層を塗設したトリアセチルセルロースフイルムを再び巻き出して、上記低屈折率層用塗布液Aを線数200本/インチ、深度40μmのグラビアパターンを有する直径50mmのマイクログラビアロールとドクターブレードを用いて、グラビアロール回転数30rpm、搬送速度15m/分の条件で塗布し、120℃で150秒乾燥の後、更に140℃で8分乾燥させてから窒素パージ下で240W/cmの空冷メタルハライドランプ(アイグラフィックス(株)製)を用いて、照度400mW/cm2、照射量600mJ/cm2の紫外線を照射し、厚さ100nmの低屈折率層を形成し、巻き取った。
製膜後、前記試料1について、以下の処理を行った。
1.5Nの水酸化ナトリウム水溶液を調製し、55℃に保温した。0.01Nの希硫酸水溶液を調製した。作製した反射防止フィルムを上記の水酸化ナトリウム水溶液に2分間浸漬した後、水に浸漬し水酸化ナトリウム水溶液を十分に洗い流した。次いで、上記の希硫酸水溶液に1分間浸漬した後、水に浸漬し希硫酸水溶液を十分に洗い流した。 最後に試料を120℃で十分に乾燥させた。
このようにして、鹸化処理済み反射防止フィルムを作製した。
これを実施例試料1とする。
得られた反射防止フィルムについて、以下の項目の評価を行った。
自動変角光度計GP−5型((株) 村上色彩技術研究所製)を用いて、入射光に対してフィルムを垂直に配置し、全方位に渡って散乱光プロファイルを測定した。このプロファイルより、出射角0°に対する30°散乱光強度を求めた。
各粒子の粒度分布を測定するための測定用粒子分散液を、分散媒にIPA(イソプロピルアルコール)を用いて調整し、シスメックス(株)製フロー式粒子像分析装置FPIA−2100を用いて測定した(測定時のフロー液もIPAとした。)。測定粒子数は100万個とした。この測定結果から、粒子の平均粒径と、粒径の最大粒径を求めた。分散液処方は、IPA40gに対し、粒子粉体0.05gとし、超音波分散及び粒子分散用界面活性剤の使用にて分散液を作製することを標準とした。
スガ試験機(株)製の写像性測定器(ICM−2D型)を用いて、0.5mmの光学櫛にて、透過画像鮮明性の値を測定した。
1.5規定、55℃のNaOH水溶液中に2分間浸漬したあと中和、水洗した80μmの厚さのトリアセチルセルロースフイルム(TAC−TD80UL、富士写真フイルム(株)製)と、実施例試料1の裏面鹸化済みトリアセチルセルロースフィルムに、ポリビニルアルコールにヨウ素を吸着させ、延伸して作製した偏光子の両面を接着、保護して偏光板を作製した。このようにして作製した偏光板を、反射防止膜側が最表面となるように透過型TN液晶表示装置搭載の23インチ液晶テレビ(偏光選択層を有する偏光分離フィルムである住友3M(株)製のD−BEFをバックライトと液晶セルとの間に有する)の視認側の偏光板と貼り代えて実装し、黒表示させて、室内の蛍光灯下で防眩性を下記のように評価した。
1)防眩性が弱すぎて、蛍光灯の写り込みが大きい。・・・×
2)防眩性が強くなり、黒の締まりが低下し始める。・・・△
3)防眩性は弱い。・・・△
4)防眩性がほどよくあり、視認性は良好。・・・○
5)防眩性がほどよくあり、視認性は良好。黒の締まりも非常に優れで好適。
・・・◎
作製した反射防止フィルムを用い、後述する実施例1−Bのように作製した偏光板を、23インチ液晶TVに実装し、視野角改良効果の有無、文字ボケの有無を目視確認した。この時の評価基準は、当社防眩性反射防止フィルム「富士フイルム CV FILM CV L 01A」を用いた以外全く同様にして作製した偏光板を同じく23インチ液晶TVに実装したものとし、比較判定した。尚、CV FILM CV L 01Aでは、階調反転しない視野角範囲は十分なものではなかった。
作製した反射防止フィルムについて、小坂研究所(株)製の表面粗さ計AY22を用いて、中心線平均粗さ(Ra)の値を測定した。
ランダムにサンプリングした1m×1mの反射防止フィルム端末について、透過光源下にて、点欠陥検査を行い、一般ユーザーの目で検出可能な50μm以上の輝点を点欠陥としてマーキングし、その後、マーキングした部分を光学顕微鏡にて、ひとつひとつ写真撮影し、ハードコート層に含有される粒子の粗大粒子によって、点欠陥になっている場合の個数を数えた。このような検査を、ランダムにサンプリングした1m×1mの端末サンプル100枚について行い、数えた点欠陥の総数を100で割って、1m2あたりの点欠陥個数とした。製品得率を考えると1個/m2以下が必要であり、好ましくは0.3個/m2以下、更に好ましくは0.1個/m2以下、最も好ましくは0個/m2(検出感度以下)である。
実施例試料1において、架橋PMMA粒子(MX−300、平均粒径3μm、綜研化学(株)製)に対し、表1に記載の通り、追加の風力分級を全く行なわず、そのまま用いるか、あるいは、追加の風力分級工程を入れ、この条件を変えて、表1に記載の粒度分布にした粒子を用いた以外は、全く実施例試料1と同じく反射防止フィルムを作製した。これを実施例試料2〜7、比較例試料1〜2とする。
実施例試料2において、内部散乱性を付与する粒子を、シリカ粒子から、架橋PMMA粒子(MX−150、平均粒径1.5μm、綜研化学(株)製)に変え、そのまま用いるか、あるいは、追加の風力分級工程を入れ、この条件を変えて、表1に記載した粒度分布にした粒子を用いた以外は、全く実施例試料2と同じく反射防止フィルムを作製した。これを実施例試料8〜14とする。
実施例試料1において、3μmの架橋PMMA粒子から、5μmの架橋PMMA粒子(MX−500、平均粒径5μm、綜研化学(株)製)に変え、そのまま用いるか、あるいは、追加の風力分級工程を入れ、この条件を変えて、表1に記載した粒度分布にした粒子を用い、加えて、全てのハードコート層の厚みを4.9μmにする以外は、全く実施例試料1と同じく反射防止フィルムを作製した。これを実施例試料15〜21、比較例試料3〜4とする。
実施例試料2において、内部散乱性を付与するシリカ粒子の塗設量を変え、透過光の散乱強度比(I30°/I0°)を表1に記載の通りに変える以外は、全く実施例試料2と同じく反射防止フィルムを作製した。これを実施例試料22〜30とする。
実施例試料2において、ハードコート層の厚みを精度良く調整(薄膜化、厚膜化)し、表1に記載の中心線平均粗さ(Ra)、透過画像鮮明性にする以外は、全く実施例試料2と同じく反射防止フィルムを作製した。これを実施例試料31〜35、比較例試料5〜6とする。
数式(1):0μm≦dMAX−dAV≦7μm(dMAX、dAVの定義は既述の通りである)
また、各粒子は、より好ましくは、0μm≦dMAX−dAV≦5μm、更により好ましくは、0μm≦dMAX−dAV≦3μm、特に好ましくは、0μm≦dMAX−dAV≦1μmを満たすことであることも表1〜4から分かる。
PVAフィルムをヨウ素2.0g/l、ヨウ化カリウム4.0g/lの水溶液に25℃にて240秒浸漬し、さらにホウ酸10g/lの水溶液に25℃にて60秒浸漬後、特開2002−86554号公報の図2の形態のテンター延伸機に導入し、5.3倍に延伸し、テンターを延伸方向に対し図2の如く屈曲させ、以降幅を一定に保った。80℃雰囲気で乾燥させた後テンターから離脱した。左右のテンタークリップの搬送速度差は、0.05%未満であり、導入されるフィルムの中心線と次工程に送られるフィルムの中心線のなす角は、46゜であった。ここで|L1−L2|は0.7m、Wは0.7mであり、|L1−L2|=Wの関係にあった。テンター出口における実質延伸方向Ax−Cxは、次工程へ送られるフィルムの中心線22に対し45゜傾斜していた。テンター出口におけるシワ、フィルム変形は観察されなかった。
さらに、PVA((株)クラレ製PVA−117H)3%水溶液を接着剤としてケン化処理した富士写真フィルム(株)製フジタック(セルローストリアセテート、レターデーション値3.0nm)と貼り合わせ、さらに80℃で乾燥して有効幅650mmの偏光板を得た。得られた偏光板の吸収軸方向は、長手方向に対し45゜傾斜していた。この偏光板の550nmにおける透過率は43.7%、偏光度は99.97%であった。さらに図2の如く310×233mmサイズに裁断したところ、91.5%の面積効率で辺に対し45゜吸収軸が傾斜した偏光板を得た。
次に、実施例1試料(鹸化処理済み)フィルムを上記偏光板と貼り合わせて反射防止付き偏光板を作製した。この偏光板を用いて反射防止層を最表層に配置した液晶表示装置を作製したところ、外光の映り込みがないために優れたコントラストが得られ、防眩性により反射像が目立たず優れた視認性を有していた。
前述(4)「防眩性の評価」で記載した、実施例1試料を貼りつけた透過型TN液晶セルの視認側の偏光板の液晶セル側の保護フィルム、およびバックライト側の偏光板の液晶セル側の保護フィルムに、ディスコティック構造単位の円盤面が透明支持体面に対して傾いており、且つ該ディスコティック構造単位の円盤面と透明支持体面とのなす角度が、光学異方層の深さ方向において変化している光学補償層を有する視野角拡大フィルム(ワイドビューフィルムSA−12B、富士写真フイルム(株)製)を用いたところ、上下左右の視野角が非常に広く、極めて視認性に優れ、表示品位の高い液晶表示装置が得られた。出射角0°に対する30°の散乱光強度比(I30°/I0°)を0.01%〜0.20%の範囲にすることで、好ましくは、0.02%〜0.15%、更に好ましくは、0.03%〜0.1%にすることで、文字ボケが問題とならず、液晶ディスプレイの視野角改良効果のある優れた反射防止フィルムが、点欠陥の発生の問題なく製造できることが、表1〜4の実施例試料1、22〜30の結果よりわかる。
全く同様にして、アスペクト比9:16の液晶ワイドテレビに実装して視野角改良効果を確認したところ、同様の優れた効果を得ることができ、実施例試料は視角依存性のない、大型液晶テレビ、液晶ワイドテレビで特に有効な反射防止フィルムであった。
実施例1試料を、有機EL表示装置の表面のガラス板に粘着剤を介して貼り合わせたところ、ガラス表面での反射が抑えられ、視認性の高い表示装置が得られえた。
実施例1試料を用いて、片面反射防止フィルム付き偏光板を作製し、偏光板の反射防止膜を有している側の反対面にλ/4板を張り合わせ、有機EL表示装置の表面のガラス板に貼り付けたところ、表面反射および、表面ガラスの内部からの反射がカットされ、極めて視認性の高い表示が得られた。
2 透明支持体
3 ハードコート層
4 ハードコート層
5 低屈折率層
6 大サイズ粒子
Claims (7)
- 透明支持体上に、少なくとも1層のハードコート層と、最外層に位置する低屈折率層からなる光学フィルムにおいて、
(a)上記光学フィルム表面のRa(中心線平均粗さ)が0.15μm以下であり、
(b)上記ハードコート層が粒子径の異なる2種以上の粒子を含有し、しかも
(c)前記粒子の少なくとも1種類が、平均粒径がハードコート層の厚みの80%以上の大きさを有する粒子であって、かつ該粒子が下記数式(1)を満たし、
前記粒子の少なくとも1種類が、内部散乱性を付与する粒子であり、該内部散乱性を付与する粒子の平均粒径が該ハードコート層の厚みの80%未満であって、かつ該内部散乱性を付与する粒子が下記数式(2)を満たし、
少なくとも1層のハードコート層が光拡散層であり、該光拡散層のゴニオフォトメーターで測定される散乱光プロファイルの出射角0°の光強度に対する30°の散乱光強度が、0.01〜0.2%の範囲にある、
ことを特徴とする反射防止フィルム。
式(1):0μm≦dMAX−dAV≦7μm
式(2):0μm≦d MAX −d AV ≦1μm
dMAX:粒子の最大粒径(単位μm)
dAV :粒子の平均粒径(単位μm) - 前記内部散乱性を付与する粒子の平均粒径が1〜5μmであることを特徴とする請求項1に記載の反射防止フィルム。
- フィルム表面のRa(中心線平均粗さ)が0.10μm以下であることを特徴とする請求項1又は2に記載の反射防止フィルム。
- 櫛幅0.5mmで測定したときの透過画像鮮明性の値が、40%以上97%未満であることを特徴とする請求項1〜3のいずれかに記載の反射防止フィルム。
- 請求項1〜4のいずれかに記載の反射防止フィルムを偏光板における偏光子の2枚の保護フィルムのうちの一方に用いたことを特徴とする偏光板。
- 2枚の保護フィルムのうち反射防止フィルムが用いられていない保護フィルムが、光学異方性層を含んでなる光学補償層を有する光学補償フィルムであり、該光学異方性層がディスコティック構造単位を有する化合物からなる負の複屈折率を有する層であり、該ディスコティック構造単位の円盤面が該表面保護フィルム面に対して傾いており、かつ該ディスコティック構造単位の円盤面と該表面保護フィルム面とのなす角度が、光学異方層の深さ方法に変化していることを特徴とする請求項5に記載の偏光板。
- 請求項1〜4のいずれかに記載の反射防止フィルムあるいは請求項5または6に記載の偏光板をディスプレイの最表面に用いたことを特徴とする液晶表示装置。