JP4413080B2 - 難燃性ポリスチレン系樹脂押出発泡板 - Google Patents
難燃性ポリスチレン系樹脂押出発泡板 Download PDFInfo
- Publication number
- JP4413080B2 JP4413080B2 JP2004156771A JP2004156771A JP4413080B2 JP 4413080 B2 JP4413080 B2 JP 4413080B2 JP 2004156771 A JP2004156771 A JP 2004156771A JP 2004156771 A JP2004156771 A JP 2004156771A JP 4413080 B2 JP4413080 B2 JP 4413080B2
- Authority
- JP
- Japan
- Prior art keywords
- flame
- polystyrene resin
- extruded foam
- flame retardant
- resin extruded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
40℃<T1 −T0 <100℃・・・式1
40℃<T1 −T0 <100℃・・・式1
50℃<T1 −T0 <80℃ ・・・式2
(小径気泡及び大径気泡の占める総面積の比率〔%〕)
=100×(小径気泡の占める総面積+大径気泡の占める総面積)
/測定部分の面積
(小径気泡及び大径気泡の占める総面積に対する小径気泡の占める総面積の比率〔%〕)=100×小径気泡の占める総面積
/(小径気泡の占める総面積+大径気泡の占める総面積)
(難燃性ポリスチレン系樹脂押出発泡板の厚み方向の気泡径が0.3mm以上である気泡の占める総面積の比率〔%〕)
=100×難燃性ポリスチレン系樹脂押出発泡板の厚み方向の気泡径が0.3mm 以上である気泡の占める総面積/測定部分の面積
押出機として、口径が50mmの第一押出機の先端に口径が65mmの第二押出機が接続されてなるタンデム型押出機を用い、上記第一押出機に、ポリスチレン(東洋スチレン社製 商品名「HRM−18」)100重量部に対して、臭素化ビスフェノールとしてテトラブロモビスフェノールAビス(2,3−ジブロモプロピルエーテル)(分解開始温度:291℃)を、含ハロゲン化燐酸エステルとしてトリス(トリブロモネオペンチル)ホスフェート(分解開始温度:282℃)を、臭素化イソシアヌレートとしてトリス(2,3−ジブロモプロピル)イソシアヌレートを、難燃助剤としてトリフェニルホスフェート(TPP)及びイソシアヌル酸を、分解温度調整剤として2,3−ジメチル−2,3−ジフェニルブタンを、発泡剤として塩化メチル、ジメチルエーテル、ブタン(イソブタン:ノルマルブタン(重量比)=4:6)水及び二酸化炭素を、気泡調整剤として合成雲母(平均粒径:3μm)及びタルクを、表1〜3に示した所定量づつ供給して210℃で溶融混練した後、この溶融樹脂を第二押出機に連続的に供給して溶融混練しつつ、実施例1〜3に記載した樹脂温度(表1〜3では「樹脂冷却温度」と表記した)に冷却した上で、第二押出機の先端部に取り付けたTダイ(幅:70mm、厚み:1.2mm)から35kg/時間の吐出量で押出発泡して断面が横長長方形状の難燃性ポリスチレン系樹脂押出発泡板を連続的に製造した。但し、表1〜3において、ブロモ系難燃剤及び2,3−ジメチル−2,3−ジフェニルブタンについては、難燃剤組成物中における重量%を示すと共に、テトラブロモビスフェノールAビス(2,3−ジブロモプロピルエーテル)、トリス(トリブロモネオペンチル)ホスフェート及びトリス(2,3−ジブロモプロピル)イソシアヌレートについては、ブロモ系難燃剤中における重量%を示した。
難燃剤組成物の代わりに、ヘキサブロモシクロドデカン(HBCD)3.0重量部を用いたこと以外は、実施例9と同様にして難燃性ポリスチレン系樹脂押出発泡板を得ようとしたが、ヘキサブロモシクロドデカンが水によって分解し、良好な難燃性ポリスチレン系樹脂押出発泡板を得ることができなかった。
難燃性ポリスチレン系樹脂押出発泡板の密度をJIS K7222に準拠して測定した。
押出発泡後30日が経過した難燃性ポリスチレン系樹脂押出発泡板から、該難燃性ポリスチレン系樹脂押出発泡板の両面と、この両面のそれぞれから厚み方向に内側に2mmだけ入った部分との間にある表層部分を除外し、この表層部分が除外されたスチレン系樹脂発泡板から、押出方向に200mm、スチレン系樹脂発泡板の表面に沿い且つ押出方向に直交する方向に150mm、厚み方向に25mmの大きさを有する試験片を切り出した。
難燃性ポリスチレン系樹脂押出発泡板から5個の試験片を切り出した。そして、この5個の試験片についてJIS A9511-1995 に規定された測定方法Aの燃焼性試験に準拠して測定し、下記の基準にて判断した。
○・・・上記測定方法Aの燃焼性を満足する。即ち、5個の試験片の全てについて炎が 3秒以内に消えると共に残じんがなく、燃焼限界支持線を越えて燃焼しなかっ た。
△・・・自消性は有するものの、○の基準を満足しなかった。
×・・・自消性は認められなかった。
難燃性ポリスチレン系樹脂押出発泡板における厚み方向の平均気泡径は、ASTM D2842−69の試験方法に準拠して測定された平均弦長に基づいて算出されたものをいう。
平均弦長(t)=60/(気泡数×写真の倍率)・・・式a
平均気泡径=t/0.616・・・式b
Claims (5)
- ポリスチレン系樹脂を炭素数が3〜5である飽和炭化水素から選ばれた一種以上の飽和炭化水素を含有する発泡剤を用いて押出発泡させて得られたポリスチレン系樹脂発泡板であって、このポリスチレン系樹脂発泡板は、臭素化ビスフェノール及び含ハロゲン燐酸エステルを含有するハロゲン系難燃剤と、ジフェニルアルカン又はジフェニルアルケンである分解温度調整剤とからなる難燃剤組成物をポリスチレン系樹脂100重量部に対して1〜10重量部含有し、上記難燃剤組成物の分解開始温度T0 が210〜260℃であると共に、上記難燃剤組成物の分解開始温度T0 と上記難燃剤組成物が5重量%分解する温度T1 とが式1を満たすことを特徴とする難燃性ポリスチレン系樹脂押出発泡板。
40℃<T1 −T0 <100℃・・・式1 - 難燃剤組成物中、ハロゲン系難燃剤が60〜98重量%含有されていることを特徴とする請求項1に記載の難燃性ポリスチレン系樹脂押出発泡板。
- 臭素化ビスフェノールがテトラブロモビスフェノールAビス(2,3−ジブロモプロピルエーテル)であると共に、含ハロゲン燐酸エステルがトリス(トリブロモネオペンチル)ホスフェートであることを特徴とする請求項1又は請求項2に記載の難燃性ポリスチレン系樹脂押出発泡板。
- 炭素数が3〜5の飽和炭化水素が、ノルマルブタン、イソブタン、ノルマルペンタン及びイソペンタンからなる群から選ばれた一種以上の飽和炭化水素であることを特徴とする請求項1乃至請求項3の何れか1項に記載の難燃性ポリスチレン系樹脂発泡板。
- 非フロン系発泡剤が、ジメチルエーテル、水及び二酸化炭素からなることを特徴とする請求項1乃至請求項4の何れか1項に記載の難燃性ポリスチレン系樹脂押出発泡板。