JP2832119B2 - 化粧料 - Google Patents
化粧料Info
- Publication number
- JP2832119B2 JP2832119B2 JP4306751A JP30675192A JP2832119B2 JP 2832119 B2 JP2832119 B2 JP 2832119B2 JP 4306751 A JP4306751 A JP 4306751A JP 30675192 A JP30675192 A JP 30675192A JP 2832119 B2 JP2832119 B2 JP 2832119B2
- Authority
- JP
- Japan
- Prior art keywords
- skin
- polymer
- hair
- water
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】
【産業上の利用分野】本発明は化粧料に関し、詳しくは
皮膚に対しては保湿効果や肌荒れ改善効果に優れ、一
方、毛髪に対しては皮膜形成作用に基づく保護効果に優
れた化粧料を提供せんとするものである。
皮膚に対しては保湿効果や肌荒れ改善効果に優れ、一
方、毛髪に対しては皮膜形成作用に基づく保護効果に優
れた化粧料を提供せんとするものである。
【0002】
【従来の技術】一般に皮膚の乾燥は、皮膚分泌物の量、
特に皮脂分泌量の減退、細胞間脂質やアミノ酸などの天
然保湿因子の減少により、角層のバリア機能が低下し、
経表皮性水分損失(以下、TEWLと略す)が大きくな
ったときにおこる。従って冬季や、過剰な皮膚洗浄、年
齢、体質などによる皮膚分泌物の減少により皮膚乾燥が
増悪し、角層水分量が10%程度以下に低下した状態を
特にドライスキンと称している。このように皮膚が乾燥
状態になると皮膚のつやは低下し、小じわが目だつなど
の弊害がでてくる。同様に、毛髪についても毛髪中の水
分量が減少することにより髪はなめらかさを失ない、ま
たつやが低下するなどの弊害を生じる。
特に皮脂分泌量の減退、細胞間脂質やアミノ酸などの天
然保湿因子の減少により、角層のバリア機能が低下し、
経表皮性水分損失(以下、TEWLと略す)が大きくな
ったときにおこる。従って冬季や、過剰な皮膚洗浄、年
齢、体質などによる皮膚分泌物の減少により皮膚乾燥が
増悪し、角層水分量が10%程度以下に低下した状態を
特にドライスキンと称している。このように皮膚が乾燥
状態になると皮膚のつやは低下し、小じわが目だつなど
の弊害がでてくる。同様に、毛髪についても毛髪中の水
分量が減少することにより髪はなめらかさを失ない、ま
たつやが低下するなどの弊害を生じる。
【0003】従来、これらの皮膚状態や毛髪状態を改善
するためには、角層や毛髪の水分含有量の低下を防止
し、正常な機能を維持することが必要であり、これまで
各種の方法が研究されてきた。その結果、提案された方
法としては、皮膚との密着性が良く、疎水性を有するワ
セリン軟膏や油中水型乳化物などの閉塞剤を用いてTE
WLを抑制する方法と、吸湿力、保湿力を有する例えば
ヒアルロン酸、キチンなどの多糖類、コラーゲン、エラ
スチンなどの蛋白質類、ソルビトール、エチレングリコ
ール、グリセリンなどの多価アルコール類、およびピロ
リドンカルボン酸ソーダ、乳酸ソーダなどの有機酸塩類
等の吸湿剤、保湿剤を皮膚料基剤中や毛髪料基剤中に配
合することにより、水和効果を高める方法とがあった。
また、最近は角層などの細胞間脂質の一成分であるセラ
ミドやスフィンゴ脂質が水分の保持に重要な働きをして
いることが解明され、合成や天然抽出のセラミドなどを
配合することも行なわれつつある。
するためには、角層や毛髪の水分含有量の低下を防止
し、正常な機能を維持することが必要であり、これまで
各種の方法が研究されてきた。その結果、提案された方
法としては、皮膚との密着性が良く、疎水性を有するワ
セリン軟膏や油中水型乳化物などの閉塞剤を用いてTE
WLを抑制する方法と、吸湿力、保湿力を有する例えば
ヒアルロン酸、キチンなどの多糖類、コラーゲン、エラ
スチンなどの蛋白質類、ソルビトール、エチレングリコ
ール、グリセリンなどの多価アルコール類、およびピロ
リドンカルボン酸ソーダ、乳酸ソーダなどの有機酸塩類
等の吸湿剤、保湿剤を皮膚料基剤中や毛髪料基剤中に配
合することにより、水和効果を高める方法とがあった。
また、最近は角層などの細胞間脂質の一成分であるセラ
ミドやスフィンゴ脂質が水分の保持に重要な働きをして
いることが解明され、合成や天然抽出のセラミドなどを
配合することも行なわれつつある。
【0004】
【発明が解決しようとする課題】ところが、前記の従来
知られている方法はいずれも水分保持能力が充分なもの
とは言えないばかりか、閉塞剤を用いた場合は油っぽ
く、ベタベタするなどの不快な感触を与える欠点があ
り、一方、吸湿剤、保湿剤を用いた場合にも効果を高め
る為には多量に配合しなければならず、その結果として
ベタベタ感やヌメリ感等の不快な感触を与えるという問
題があり、実際には処方系では多量に配合することが不
可能である。更には経時や微生物に対する安定性に劣る
という欠点もあった。また、一物質で角層の吸保湿機能
を助ける、HAのような吸保湿作用と、セラミド等
の細胞間脂質ラメラ層の形成促進・安定化作用、を併せ
もつものはいまだ存在しない。
知られている方法はいずれも水分保持能力が充分なもの
とは言えないばかりか、閉塞剤を用いた場合は油っぽ
く、ベタベタするなどの不快な感触を与える欠点があ
り、一方、吸湿剤、保湿剤を用いた場合にも効果を高め
る為には多量に配合しなければならず、その結果として
ベタベタ感やヌメリ感等の不快な感触を与えるという問
題があり、実際には処方系では多量に配合することが不
可能である。更には経時や微生物に対する安定性に劣る
という欠点もあった。また、一物質で角層の吸保湿機能
を助ける、HAのような吸保湿作用と、セラミド等
の細胞間脂質ラメラ層の形成促進・安定化作用、を併せ
もつものはいまだ存在しない。
【0005】本発明は斯かる実情に鑑みてなされたもの
であって、肌あれ、つや不足等の乾燥に起因する皮膚及
び毛髪状態を改善し、充分な水分保持により潤いを与え
る、いわゆる美肌及び美髪効果を有するとともに、感触
的にも問題の殆んどない化粧料を提供することを課題と
する。
であって、肌あれ、つや不足等の乾燥に起因する皮膚及
び毛髪状態を改善し、充分な水分保持により潤いを与え
る、いわゆる美肌及び美髪効果を有するとともに、感触
的にも問題の殆んどない化粧料を提供することを課題と
する。
【0006】
【課題を解決するための手段】本発明者は、上記課題を
解決するため鋭意研究を行なった結果、生体膜の主成分
であるリン脂質(ホスファチジルコリン)の極性基と同
一の構造を有する2−メタクリロイルオキシエチルホス
ホリルコリンを構成単位とするポリマー物質が吸湿、保
湿作用に基づく水分保持機能が高く、またラメラ形成促
進・安定化作用や皮膜形成能に優れていることを見い出
し、これに基づいて本発明を完成した。
解決するため鋭意研究を行なった結果、生体膜の主成分
であるリン脂質(ホスファチジルコリン)の極性基と同
一の構造を有する2−メタクリロイルオキシエチルホス
ホリルコリンを構成単位とするポリマー物質が吸湿、保
湿作用に基づく水分保持機能が高く、またラメラ形成促
進・安定化作用や皮膜形成能に優れていることを見い出
し、これに基づいて本発明を完成した。
【0007】すなわち、本発明は、2−メタクリロイル
オキシエチルホスホリルコリンのホモ重合体を含有する
ことを特徴とする化粧料である。または重合体の分子量
が5,000以上であり、または重合体の含有量が化粧料
全体に対して0.001〜10重量%である化粧料に関す
るものである。
オキシエチルホスホリルコリンのホモ重合体を含有する
ことを特徴とする化粧料である。または重合体の分子量
が5,000以上であり、または重合体の含有量が化粧料
全体に対して0.001〜10重量%である化粧料に関す
るものである。
【0008】以下、本発明を詳細に説明する。
【0009】本発明に適用される重合体は、下記「化
1」に示す一般式(I)で示される2−メタクリロイル
オキシエチルホスホリルコリン(以下MPCと略記)を
重合させて得られるものである。
1」に示す一般式(I)で示される2−メタクリロイル
オキシエチルホスホリルコリン(以下MPCと略記)を
重合させて得られるものである。
【0010】
【化1】
【0011】かかるMPCについては、例えば2−ブロ
モエチルホスホリルジクロリドと2−ヒドロキシエチル
ホスホリルジクロリドと2−ヒドロキシエチルメタクリ
レートとを反応させて2−メタクリロイルオキシエチル
−2′−ブロモエチルリン酸を得、更にこれをトリメチ
ルアミンとメタノール溶液中で反応させて得ることがで
きる。(高分子論文集,Vol.35,P423〜42
7,1978)
モエチルホスホリルジクロリドと2−ヒドロキシエチル
ホスホリルジクロリドと2−ヒドロキシエチルメタクリ
レートとを反応させて2−メタクリロイルオキシエチル
−2′−ブロモエチルリン酸を得、更にこれをトリメチ
ルアミンとメタノール溶液中で反応させて得ることがで
きる。(高分子論文集,Vol.35,P423〜42
7,1978)
【0012】次に、重合体の製造方法については常法に
従えば良く、MPCを溶媒中で重合開始剤の存在下、反
応させて得られる。ここで使用される溶媒としては、M
PCが溶解するものであれば良く、具体的には水、メタ
ノール、エタノール、プロパノール、t−ブタノール、
ベンゼン、トルエン、ジメチルホルムアミド、テトラヒ
ドロフラン、クロロホルムまたはこれらの混合溶媒等が
例示される。また、重合開始剤としては、通常のラジカ
ル開始剤ならば何れを用いても良く、2,2′−アゾビ
スイソブチロニトリル(AIBN)、3−カルボキシプ
ロピオニトリル、アゾビスマレノニトリル等の脂肪酸ア
ゾ化合物や過酸化ベンゾイル、過酸化ラウロイル、過硫
酸カリウム等の有機過酸化物を挙げることができる。
従えば良く、MPCを溶媒中で重合開始剤の存在下、反
応させて得られる。ここで使用される溶媒としては、M
PCが溶解するものであれば良く、具体的には水、メタ
ノール、エタノール、プロパノール、t−ブタノール、
ベンゼン、トルエン、ジメチルホルムアミド、テトラヒ
ドロフラン、クロロホルムまたはこれらの混合溶媒等が
例示される。また、重合開始剤としては、通常のラジカ
ル開始剤ならば何れを用いても良く、2,2′−アゾビ
スイソブチロニトリル(AIBN)、3−カルボキシプ
ロピオニトリル、アゾビスマレノニトリル等の脂肪酸ア
ゾ化合物や過酸化ベンゾイル、過酸化ラウロイル、過硫
酸カリウム等の有機過酸化物を挙げることができる。
【0013】以下に、本発明に係る重合体の製造例を示
す。
す。
【0014】1.Poly(MPC)の合成 MPCを0.5mol/Lになるようにエタノールに溶解
し、開始剤としてアゾビスイソブチロニトリル(AIB
N)をモノマーに対して1mol%加える。溶液をガラ
ス製反応器に入れアルゴンで充分に置換した後、封管す
る。60度にて4時間反応し、反応混合物を大量のジエ
チルエーテルに滴下してポリマーを沈澱させる。沈澱物
をろ別し、ガラスフィルター上で充分にジエチルエーテ
ルで洗浄した後、真空乾燥する。収率は約60%であ
る。
し、開始剤としてアゾビスイソブチロニトリル(AIB
N)をモノマーに対して1mol%加える。溶液をガラ
ス製反応器に入れアルゴンで充分に置換した後、封管す
る。60度にて4時間反応し、反応混合物を大量のジエ
チルエーテルに滴下してポリマーを沈澱させる。沈澱物
をろ別し、ガラスフィルター上で充分にジエチルエーテ
ルで洗浄した後、真空乾燥する。収率は約60%であ
る。
【0015】2.末端にカルボキシル基を有するPol
y(MPC)の合成 開始剤としてAIBNの代わりにアゾビス(3−カルボ
キシプロピオニトリル)を用いた他は上記と同様の操作
で反応を行った。反応時間を3時間とし、モノマーに対
する開始剤の比率を3mol%として得られるポリマー
の分子量を調整した。収率は約30%である。
y(MPC)の合成 開始剤としてAIBNの代わりにアゾビス(3−カルボ
キシプロピオニトリル)を用いた他は上記と同様の操作
で反応を行った。反応時間を3時間とし、モノマーに対
する開始剤の比率を3mol%として得られるポリマー
の分子量を調整した。収率は約30%である。
【0016】〇IR(cm-1)測定 3200〜2900(CH2 ,CH3 )、1720(C=O) 1100〜1200(C−O−C)、1250(P=O)
【0017】〇分子量測定 ポリマーの水−エタノール{80/20(V/V)}溶
液をGPCを用いて分析測定した結果、ポリエチレング
リコール換算で37,000であった。
液をGPCを用いて分析測定した結果、ポリエチレング
リコール換算で37,000であった。
【0018】上記の如くして得られる本発明に係る重合
体の分子量は、その使用目的に応じて種々調整すること
ができるが、感触面、ゲル化能、皮膜形成能等を勘案し
た場合、通常はポリエチレングリコール(PEG)換算
で5,000以上であり、好ましくは10,000以上であ
る。すなわち、MPCの分子量がより小さくなると、水
分保持機能やラメラ形成促進安定化作用が低下して好ま
しくない。
体の分子量は、その使用目的に応じて種々調整すること
ができるが、感触面、ゲル化能、皮膜形成能等を勘案し
た場合、通常はポリエチレングリコール(PEG)換算
で5,000以上であり、好ましくは10,000以上であ
る。すなわち、MPCの分子量がより小さくなると、水
分保持機能やラメラ形成促進安定化作用が低下して好ま
しくない。
【0019】本発明の化粧料では、上記重合体が化粧料
全体に対して、通常0.001〜10重量%、好ましくは
0.01〜3重量%の範囲で含有される。
全体に対して、通常0.001〜10重量%、好ましくは
0.01〜3重量%の範囲で含有される。
【0020】また、本発明の化粧料は、化粧水、乳液、
クリーム、口紅、ファンデーションなどの形態で皮膚化
粧料として用いることができ、一方、ヘアートニック、
ヘアークリーム、ヘアーローションなどの形態で毛髪化
粧料として用いることができる。更に、重合体のゲル化
能、皮膜形成能を利用してマッサージ料やパック料とし
て用いることもできる。尚、これらの化粧料は常法に従
って製造することができる。
クリーム、口紅、ファンデーションなどの形態で皮膚化
粧料として用いることができ、一方、ヘアートニック、
ヘアークリーム、ヘアーローションなどの形態で毛髪化
粧料として用いることができる。更に、重合体のゲル化
能、皮膜形成能を利用してマッサージ料やパック料とし
て用いることもできる。尚、これらの化粧料は常法に従
って製造することができる。
【0021】更に、本発明の化粧料には重合体に加え
て、必要に応じて界面活性剤、粉体または顔料、酸化防
止剤、紫外線吸収剤、保湿剤、ビタミン類、防腐剤、香
料などを配合できる。
て、必要に応じて界面活性剤、粉体または顔料、酸化防
止剤、紫外線吸収剤、保湿剤、ビタミン類、防腐剤、香
料などを配合できる。
【0022】ここで、本発明に係る重合体が如何に優れ
た吸湿特性及び経時安定性を有するかの評価をするため
の実験を行なった。その内容を以下に示す。
た吸湿特性及び経時安定性を有するかの評価をするため
の実験を行なった。その内容を以下に示す。
【0023】実験1.MPC重合体の吸湿性 〔サンプル〕 (A)MPC重合体(分子量12,000) (B)キト
サン(比較品)
サン(比較品)
【0024】〔測定方法〕MPC重合体の50%エタノ
ール溶液(5重量%)、キトサンの酢酸水溶液(5重量
%)を調製し、各溶液5mlを25cm2 のテフロン板上
に流延した後、室温にて溶媒を揮散させ、厚さ約100
μmの膜を作成した。これを、飽和塩溶液により各相対
湿度(60%、80%、95%)に調整したデシケータ
ー中に入れ、20℃以下、48時間後の重量増加率を測
定した。その結果を図1に示す。 重量増加率(%)=〔(48hr後の重量−初期重量)
/初期重量〕×100
ール溶液(5重量%)、キトサンの酢酸水溶液(5重量
%)を調製し、各溶液5mlを25cm2 のテフロン板上
に流延した後、室温にて溶媒を揮散させ、厚さ約100
μmの膜を作成した。これを、飽和塩溶液により各相対
湿度(60%、80%、95%)に調整したデシケータ
ー中に入れ、20℃以下、48時間後の重量増加率を測
定した。その結果を図1に示す。 重量増加率(%)=〔(48hr後の重量−初期重量)
/初期重量〕×100
【0025】〔結果〕図1の結果から明らかな如く、本
発明に係るMPC重合体は、比較品であるキトサンに比
べて高い吸湿性を有していることが示された。
発明に係るMPC重合体は、比較品であるキトサンに比
べて高い吸湿性を有していることが示された。
【0026】実験2.MPC重合体の安定性 〔サンプル〕 MPC重合体(分子量15000)
【0027】〔測定方法〕各種バッファーによりpH4.
0、6.0、8.0、9.0に調整した10%エタノール水溶
液中に、夫々、サンプルを2重量%濃度で溶解し、40
℃下で3ヶ月間放置してその状態を観察した。尚、スタ
ート時には着色、沈殿は認められず透明であった。その
結果を表1に示す。
0、6.0、8.0、9.0に調整した10%エタノール水溶
液中に、夫々、サンプルを2重量%濃度で溶解し、40
℃下で3ヶ月間放置してその状態を観察した。尚、スタ
ート時には着色、沈殿は認められず透明であった。その
結果を表1に示す。
【0028】
【表1】
【0029】表1の結果に示された如く、本発明に係る
MPC重合体は、広いpH領域で経時安定性が優れてい
ることが明らかとなった。
MPC重合体は、広いpH領域で経時安定性が優れてい
ることが明らかとなった。
【0030】
【実施例】以下に、本発明の化粧料の実施例を示す。
尚、配合割合は重量%である。
尚、配合割合は重量%である。
【0031】実施例1.o/w型乳液 ステアリン酸 1 ミツロウ 2 マイクロクリスタリンワックス 1 MPC重合体3%水溶液(分子量35,000) 30 プロピレングリコール 5 グリセリン 2 エチルアルコール 5 防腐剤 0.3 香 料 0.3 精製水 53.4
【0032】実施例2.化粧水 MPC重合体2%水溶液(分子量20,000) 25 グリセリン 1.5 エタノール 6 プロピレングリコール 1.5 クエン酸 0.01 クエン酸ナトリウム 0.1 香 料 0.05 精製水 65.84
【0033】実施例3.クリーム スクワラン 5 2−エチルヘキサン酸トリグリセライド 1 ワセリン 0.5 MPC重合体 3%水溶液(分子量20,000) 50 グリセリン 3 1,3−ブタンジオール 4 ポリグリセリンポリオキシブチレンステアリルエーテル 2.5 香 料 0.2 精製水 33.8
【0034】実施例4.ヘアーローション MPC重合体2%水溶液(分子量45,000) 5 エタノール 10 グリセリン 3 カルボキシメチルキチン 0.01 ビタミンE 0.1 色 素 0.02 精製水 81.87
【0035】実施例5.ヘアークリーム スクワラン 30.0 ワセリン 3.0 ミツロウ 4.0 ステアリン酸 4.0 オリーブ油 2.0 ソルビタンモノステアレート 2.5 ポリオキシエチレンソルビタンモノステアレート 2.5 ブチルパラベン 0.1 MPC重合体10%水溶液(分子量40,000) 30 1,3−ブタンジオール 2.5 ポリエチレングリコール200 1.5 トリエタノールアミン 1.0 メチルパラベン 0.1 香 料 0.2 精製水 16.6
【0036】(比較実験)本発明により得られた化粧料
と従来の化粧料とを肌荒れ改善効果及び毛髪保護効果に
より比較した。
と従来の化粧料とを肌荒れ改善効果及び毛髪保護効果に
より比較した。
【0037】実験3.人工的な肌荒れの改善効果 〔サンプル〕 (ア)本発明の実施例1の乳液 (イ)本発明の実施例1の乳液からMPC重合体を除去
(水を増量)した従来の乳液
(水を増量)した従来の乳液
【0038】〔実験方法〕邦人女性10人(年令20〜
37才)を被験者として、界面活性剤による人工的な肌
荒れに対する改善効果を角層水分量の測定及び皮疹の判
定により行なった。すなわち、前腕内側部の皮膚を対象
とし、これに直径3cmのガラスコップを密着させ、そこ
へ10mlの5%ドデシル硫酸ナトリウム(SDS)を
入れ軽く揺らしながら10分間放置した後処理液を回収
し、さらに同一部位に次の20分間同一の処理液で放置
した後処理液を回収して肌荒れを惹起させた。このSD
S処理の1日後から、処理部位に1日2回当りサンプル
(ア)または(イ)の乳液を塗布した。実験前後の角層
水分量を下記測定法に従い皮表コンダクタンス値として
測定した結果および皮疹を下記判定基準に従って判定し
た結果(平均値)を図2及び図3に示す。
37才)を被験者として、界面活性剤による人工的な肌
荒れに対する改善効果を角層水分量の測定及び皮疹の判
定により行なった。すなわち、前腕内側部の皮膚を対象
とし、これに直径3cmのガラスコップを密着させ、そこ
へ10mlの5%ドデシル硫酸ナトリウム(SDS)を
入れ軽く揺らしながら10分間放置した後処理液を回収
し、さらに同一部位に次の20分間同一の処理液で放置
した後処理液を回収して肌荒れを惹起させた。このSD
S処理の1日後から、処理部位に1日2回当りサンプル
(ア)または(イ)の乳液を塗布した。実験前後の角層
水分量を下記測定法に従い皮表コンダクタンス値として
測定した結果および皮疹を下記判定基準に従って判定し
た結果(平均値)を図2及び図3に示す。
【0039】1)角層水分量の測定 角層の水分量は田上らの方法に従い Capacitance condu
ctance meter(IBM社MODEL IB−354)を
用いて測定する。測定に際しては測定部位皮膚を37℃
の温水で30秒間洗浄後、20℃,50%相対湿度下、
5回測定してその平均を測定値とする。
ctance meter(IBM社MODEL IB−354)を
用いて測定する。測定に際しては測定部位皮膚を37℃
の温水で30秒間洗浄後、20℃,50%相対湿度下、
5回測定してその平均を測定値とする。
【0040】2)皮疹判定基準 0:乾燥性落屑性変化を認めない。 1:かすかな乾燥性落屑性変化を認める。(かすかな落
屑または光沢) 2:明瞭な乾燥性落屑性変化を認める。(処理部の境界
が明瞭で、明瞭な落屑に一部光沢、亀裂) 3:著しい乾燥性落屑性変化を認める。(明瞭な落屑に
明瞭な光沢、亀裂)
屑または光沢) 2:明瞭な乾燥性落屑性変化を認める。(処理部の境界
が明瞭で、明瞭な落屑に一部光沢、亀裂) 3:著しい乾燥性落屑性変化を認める。(明瞭な落屑に
明瞭な光沢、亀裂)
【0041】図2及び図3の結果に示された如く、本発
明品の乳液であるサンプル(ア)は、従来品の乳液であ
るサンプル(イ)に比し、角層水分量の回復(皮表コン
ダクタンス値の上昇)や乾燥性皮疹に対して著しい効果
のあることが実証された。
明品の乳液であるサンプル(ア)は、従来品の乳液であ
るサンプル(イ)に比し、角層水分量の回復(皮表コン
ダクタンス値の上昇)や乾燥性皮疹に対して著しい効果
のあることが実証された。
【0042】実験4.実使用テスト 〔サンプル〕実験3で使用したサンプル(ア)及び
(イ)の乳液と同一のものを用いた。
(イ)の乳液と同一のものを用いた。
【0043】〔実験方法〕日頃から肌荒れ、乾燥性の症
状を訴える邦人女性40人(年令20〜49才)を無作
為にA群、B群(各20人)に分け、A群にはサンプル
(ア)の乳液を、またB群にはサンプル(イ)の乳液を
それぞれ1ヶ月間使用してもらった。1ヶ月後のしっと
り感(保水効果)、肌のはりの改善(賦活効果)などの
美肌効果と使用中の感触(ベたつき感)について群間比
較を行なった。その結果を表2に示す。
状を訴える邦人女性40人(年令20〜49才)を無作
為にA群、B群(各20人)に分け、A群にはサンプル
(ア)の乳液を、またB群にはサンプル(イ)の乳液を
それぞれ1ヶ月間使用してもらった。1ヶ月後のしっと
り感(保水効果)、肌のはりの改善(賦活効果)などの
美肌効果と使用中の感触(ベたつき感)について群間比
較を行なった。その結果を表2に示す。
【0044】
【表2】
【0045】表2の結果から明らかなように、本発明品
の乳液であるサンプル(ア)は、従来品の乳液であるサ
ンプル(イ)と同様に感触的な問題もなく、一方、保水
効果や賦活効果等の美肌効果については格段に優れてい
ることが実証された。
の乳液であるサンプル(ア)は、従来品の乳液であるサ
ンプル(イ)と同様に感触的な問題もなく、一方、保水
効果や賦活効果等の美肌効果については格段に優れてい
ることが実証された。
【0046】実験5.毛髪保護効果 〔サンプル〕 (ウ)本発明の実施例4のヘアーローション (エ)本発明の実施例4のヘアーローションからMPC
重合体を除去(水を増量)した従来のヘアーローション
重合体を除去(水を増量)した従来のヘアーローション
【0047】〔実験方法〕これまでパーマ、ブリーチ等
の処理を行なったことのない邦人女性の毛髪10g(長
さ10cm)を束ね、これにサンプル(ウ)または(エ)
のヘアーローションの所定量を塗布した後、風乾した。
評価は、専門パネラー5名により下記表3に示す基準に
従って官能評価し、その平均点を表4に示した。尚、評
価項目は毛髪の平滑性、つやならびにしっとり感(保湿
性)について行なった。
の処理を行なったことのない邦人女性の毛髪10g(長
さ10cm)を束ね、これにサンプル(ウ)または(エ)
のヘアーローションの所定量を塗布した後、風乾した。
評価は、専門パネラー5名により下記表3に示す基準に
従って官能評価し、その平均点を表4に示した。尚、評
価項目は毛髪の平滑性、つやならびにしっとり感(保湿
性)について行なった。
【0048】
【表3】
【0049】
【表4】
【0050】表4の結果に示された如く、本発明品のヘ
アーローションであるサンプル(ウ)は、従来品のヘア
ーローションであるサンプル(エ)に比し、毛髪の平滑
性、つやならびにしっとり感の何れにおいても優れてい
ることが明らかとなった。
アーローションであるサンプル(ウ)は、従来品のヘア
ーローションであるサンプル(エ)に比し、毛髪の平滑
性、つやならびにしっとり感の何れにおいても優れてい
ることが明らかとなった。
【0051】実験6.ラメラ層の安定化 細胞間脂質類似物質であるレシチン(EPC)にてラメ
ラを作り、MPC重合体が、レシチンからなるラメラ構
造の配列を規則的にし、分子間をタイト(ラメラ層の安
定化・形成促進)による作用があるかをX線小角散乱で
検討した。
ラを作り、MPC重合体が、レシチンからなるラメラ構
造の配列を規則的にし、分子間をタイト(ラメラ層の安
定化・形成促進)による作用があるかをX線小角散乱で
検討した。
【0052】〔実験方法〕レシチンと水とを90〜6
5:10〜35の重量比で混合し、対照品のラメラ相を
調製した。一方、対照品の水の一部をMPC重合体で置
換、混合してラメラ相を調製した。得られたラメラ相に
ついてX線回析装置(日本電子製JDX−3500)を
用いて、ラメラ相の面間隔を測定した。その結果を図4
に示した。
5:10〜35の重量比で混合し、対照品のラメラ相を
調製した。一方、対照品の水の一部をMPC重合体で置
換、混合してラメラ相を調製した。得られたラメラ相に
ついてX線回析装置(日本電子製JDX−3500)を
用いて、ラメラ相の面間隔を測定した。その結果を図4
に示した。
【0053】〔測定条件〕 ・小角散乱装置:日本電子製DX−LSV3 ・ディテクター:シンチレーションカウンター ・線源 :Cu線 ・電圧 :45KV ・電流 :200mA ・測定温度 :22〜24℃ ・試料はセルホルダーに4μmのマイラーの間にはさん
で測定
で測定
【0054】〔結果〕図4に示したとおり、レシチン/
水=90〜65/10〜35重量比の混合物は面間隔3
9〜58Åの範囲で層状構造を持つラメラ相を形成す
る。水をMPC重合体溶液に置換していくとd値は低下
した。又、小角散乱ピーク(図略)をみると、MPC重
合体添加により水添加系よりもレシチンの分子の方向性
や配列が整っていることが判明した。このことは、以下
のことを反映していると考られる。ラメラ液晶相の面間
隔dは疎水性部分(レシチン層)daと水層部分dwと
から出来ているので、水をMPC重合体で置換した場合
にd値が低下したのは、MPC重合体がレシチン層に入
り込んだ結果と考られる。又、レシチン層にMPC重合
体が入りこむことによりレシチン層の分子の配列・規則
性が増したと考られる。以上のことから、MPC重合体
はヒト角層間脂質によるラメラ層を安定化し肌荒れ抑制
に効果があることが判明した。
水=90〜65/10〜35重量比の混合物は面間隔3
9〜58Åの範囲で層状構造を持つラメラ相を形成す
る。水をMPC重合体溶液に置換していくとd値は低下
した。又、小角散乱ピーク(図略)をみると、MPC重
合体添加により水添加系よりもレシチンの分子の方向性
や配列が整っていることが判明した。このことは、以下
のことを反映していると考られる。ラメラ液晶相の面間
隔dは疎水性部分(レシチン層)daと水層部分dwと
から出来ているので、水をMPC重合体で置換した場合
にd値が低下したのは、MPC重合体がレシチン層に入
り込んだ結果と考られる。又、レシチン層にMPC重合
体が入りこむことによりレシチン層の分子の配列・規則
性が増したと考られる。以上のことから、MPC重合体
はヒト角層間脂質によるラメラ層を安定化し肌荒れ抑制
に効果があることが判明した。
【0055】
【発明の効果】本発明によれば、水分保持機能、ラメラ
形成促進・安定化作用ならびに皮膜形成能等に基づく皮
膚に対する美肌効果、また毛髪に対する美髪効果が格段
に優れていることは勿論のこと、安定性上の問題もなく
使用することができる。
形成促進・安定化作用ならびに皮膜形成能等に基づく皮
膚に対する美肌効果、また毛髪に対する美髪効果が格段
に優れていることは勿論のこと、安定性上の問題もなく
使用することができる。
【図1】相対湿度と重量増加率の関係を示す図である。
【図2】日数と皮表コンダクタンス値の関係を示す図で
ある。
ある。
【図3】日数と皮疹との関係を示す図である。
【図4】水相/油相比と面間隔の関係を示す図である。
───────────────────────────────────────────────────── フロントページの続き (72)発明者 黒田 秀夫 神奈川県横浜市戸塚区柏尾町560 ポー ラ化成工業株式会社 戸塚研究所内 (72)発明者 狩野 愛 神奈川県横浜市戸塚区柏尾町560 ポー ラ化成工業株式会社 戸塚研究所内 (72)発明者 中林 宣男 千葉県松戸市小金原5−6−20 (56)参考文献 特開 昭62−126108(JP,A) 特開 昭59−116206(JP,A) (58)調査した分野(Int.Cl.6,DB名) A61K 7/00 - 7/50
Claims (3)
- 【請求項1】 2−メタクリロイルオキシエチルホスホ
リルコリンのホモ重合体を含有することを特徴とする化
粧料。 - 【請求項2】 重合体の分子量が5,000以上である請
求項1の記載の化粧料。 - 【請求項3】 重合体の含有量が化粧料全体に対して0.
001〜10重量%である請求項1または2に記載の化
粧料。