JP2024121407A - リン含有（メタ）アクリロイル化合物、その製造方法、これを含む難燃性樹脂組成物および電子回路基板用積層板 - Google Patents
リン含有（メタ）アクリロイル化合物、その製造方法、これを含む難燃性樹脂組成物および電子回路基板用積層板 Download PDFInfo
- Publication number
- JP2024121407A JP2024121407A JP2023028498A JP2023028498A JP2024121407A JP 2024121407 A JP2024121407 A JP 2024121407A JP 2023028498 A JP2023028498 A JP 2023028498A JP 2023028498 A JP2023028498 A JP 2023028498A JP 2024121407 A JP2024121407 A JP 2024121407A
- Authority
- JP
- Japan
- Prior art keywords
- meth
- phosphorus
- general formula
- compound
- acryloyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】反応型リン系難燃剤として有用であり、硬化物における耐熱性と誘電特性に優れるリン含有化合物、これを含む硬性樹脂組成物、およびその硬化物を提供する。【解決手段】一般式（１）で表されるリン含有（メタ）アクリロイル化合物。TIFF2024121407000023.tif13122一般式（１）において、Ａｒは置換基を有しても良い炭素原子数６～３０の芳香族環基であり、Ｒ１はそれぞれ独立に下記一般式（２）で表される置換基または（メタ）アクリロイル基であるが、化合物中に一般式（２）で表される置換基と（メタ）アクリロイル基をそれぞれ少なくとも１つ含む。ｍは、３～６の整数である。TIFF2024121407000024.tif30128【選択図】なし
Description
本発明は反応型リン化合物、特にリン含有（メタ）アクリロイル化合物に関し、プラスチック材料の反応型難燃剤として有用である。
プラスチック材料は、優れた機械的特性、成形加工性から、建材や電気電子機器まで幅広い用途に使用されている。しかしながら、大抵のプラスチック材料は、燃えやすいため、使用される用途、例えば電気・電子製品やＯＡ機器、通信機器等では、発熱発火、火災に対する安全性のため難燃化が必須となっている。
プラスチック材料の難燃化技術としては、ハロゲン系難燃剤、無機系難燃剤、リン系難燃剤等の添加型難燃剤の添加が樹脂種、用途に限らず一般的となっている。しかしながら、これらの中で臭素系を主とするハロゲン系難燃剤は、発がん性の高いダイオキシンの発生源となる可能性が指摘されており、昨今の環境負荷物質低減の動きに対応して使用を制限する方向に進んでいる。また、水酸化マグネシウム、水酸化アルミニウム等無機系難燃剤は、吸熱による難燃化効果があるものの、十分な難燃化を達成するためには大量に添加する必要があり、プラスチック成形品の各種特性を低下させる原因となっている。
そのため、有害物質を発生させず、比較的少量の添加で難燃化が可能なリン系難燃剤が多く使用されているが、それでもブリードアウト等による加工性の低下や、ガラス転移温度の低下等、特性への影響は避けられない。
そのため、有害物質を発生させず、比較的少量の添加で難燃化が可能なリン系難燃剤が多く使用されているが、それでもブリードアウト等による加工性の低下や、ガラス転移温度の低下等、特性への影響は避けられない。
これら添加型難燃剤の問題を解決するために、難燃成分であるリン原子を含み、且つ反応性基を持つ反応型難燃剤が開発され、広く使用されてきた。電子・電機分野で多用されるエポキシ樹脂組成物に適用可能な反応型難燃剤としては、例えば、特許文献１には、エポキシ樹脂用の硬化剤として、ビスフェノールＡとホルムアルデヒドを反応させ、ヒドロキシメチルビスフェノールＡを得た後に９，１０－ジヒドロ－９－オキサ－１０－ホスファフェナントレン－１０－オキサイド（以下、「ＤＯＰＯ」と略記する。）を反応させる事で得られるフェノール樹脂が開示され、特許文献２には、ＤＯＰＯとキノン類を反応させた後にエポキシ樹脂と反応する事で得られるリン含有エポキシ樹脂が開示されている。これらの樹脂では、難燃剤のブリードアウト等加工性の問題は解決され、耐熱性等熱特性の悪化は見られない。この様に、添加型難燃剤に比較し、反応性の難燃剤を使用することで、一般的に添加型難燃剤の欠点を補うことが可能となることから、多くの難燃性エポキシ樹脂等が開発されている。
一方で近年、難燃性が必須となる電子・電気材料分野では、スマートフォンに代表される電子機器の急激な進化により、難燃剤を含む樹脂成分に対する要求は高度なものへと変化している。特に情報・通信分野では情報処理量の増大に伴い信号の高周波化が進行、伝送損失低減のために、この分野に使用される樹脂成分には低誘電率、低誘電正接が強く求められている。そこで、回路基板に代表される電子・電気材料分野では、エポキシ樹脂に変わって、より低誘電率・低誘電正接化が可能なラジカル重合性の樹脂が広く使用されるようになっている。そのため、反応性基がエポキシ基やエポキシ樹脂と反応性を有する難燃剤だけでなく、ラジカル重合性の樹脂と反応が可能な低誘電率・低誘電正接なハロゲンフリー難燃剤が求められている。
ラジカル重合性の官能基を持つハロゲンフリー難燃剤としては、特許文献３および特許文献４にＤＯＰＯ骨格を含むビニルベンジルエーテル化合物が開示されている。また特許文献５には、リン酸エステル構造を含む（メタ）アクリロイル化合物が開示されているが、低誘電率・低誘電正接の点で十分な特性とは言えない。また難燃性も十分とは言えず、難燃性を発現するためには多量の難燃剤を配合する必要があり、使用方法が限られる等の問題があった。そのため、ハロゲンフリー難燃性、耐熱性等の熱特性および誘電特性を満足するラジカル重合性基を含む難燃剤は未だ無い。
ラジカル重合性の官能基を持つハロゲンフリー難燃剤としては、特許文献３および特許文献４にＤＯＰＯ骨格を含むビニルベンジルエーテル化合物が開示されている。また特許文献５には、リン酸エステル構造を含む（メタ）アクリロイル化合物が開示されているが、低誘電率・低誘電正接の点で十分な特性とは言えない。また難燃性も十分とは言えず、難燃性を発現するためには多量の難燃剤を配合する必要があり、使用方法が限られる等の問題があった。そのため、ハロゲンフリー難燃性、耐熱性等の熱特性および誘電特性を満足するラジカル重合性基を含む難燃剤は未だ無い。
従って、本発明が解決しようとする課題は、反応型リン系難燃剤として有用であり、硬化物における耐熱性と誘電特性、および難燃性に優れるリン含有化合物、これを含む硬性樹脂組成物、およびその硬化物を提供することにある。
本発明者は前記課題を鋭意検討した結果、特定の構造を持ったリン含有（メタ）アクリロイル化合物が、耐熱性、誘電特性に優れることを見出し、本発明に至った。
すなわち、本発明は一般式（１）で表されることを特徴とするリン含有（メタ）アクリロイル化合物である。
一般式（１）において、Ａｒは置換基を有しても良い炭素原子数６～３０の芳香族環基であり、Ｒ１はそれぞれ独立に下記一般式（２）または（３）で表される置換基であるが、化合物中に一般式（２）で表される置換基と一般式（３）で表される置換基をそれぞれ少なくとも１つ含む。ｍは、３～６の整数である。
一般式（２）において、Ｒ２およびＲ３は、それぞれ独立して炭素原子数１～５の直鎖または分岐鎖のアルキル基であり、ｎ２、ｎ３はそれぞれ独立に０～５の整数である。
ここで、Ｒ４は、水素またはメチル基である。
本発明は、Ａｒが置換基を有していても良いベンゼン環、ナフタレン環、ビフェニル環およびアントラセン環から選択される芳香族環基である上記のリン含有（メタ）アクリロイル化合物である。
本発明は、Ａｒがベンゼン環である上記のリン含有（メタ）アクリロイル化合物である。
本発明は、ｍが３である上記のリン含有（メタ）アクリロイル化合物である。
本発明は、Ｒ１の２つが一般式（３）で表される置換基であり、１つが一般式（２）で表される置換基である化合物を１０～８０モル％、Ｒ１の１つが一般式（３）で表される置換基であり、２つが一般式（２）で表される置換基である化合物を５～５０モル％、およびＲ１の３つが一般式（２）で表される置換基である化合物を１～５０モル％含むことを特徴とする上記のリン含有（メタ）アクリロイル化合物である。
本発明は、下記一般式（４）で表されるリン含有フェノール化合物と（メタ）アクリル酸、ハロゲン化（メタ）アクリロイルまたは（メタ）アクリル酸無水物の一種以上を反応させることを特徴とする上記のリン含有（メタ）アクリロイル化合物の製造方法である。
一般式（４）において、Ａｒ、ｍは一般式（１）と同義であり、Ｒ５はそれぞれ独立に水素または下記一般式（２）で表される置換基であるが、少なくとも１つのＲ５は一般式（２）で表される置換基を含む。
一般式（２）において、Ｒ２、Ｒ３、ｎ２およびｎ３は上記と同じである。
本発明は、上記のリン含有（メタ）アクリロイル化合物に熱硬化性樹脂又は熱可塑性樹脂の一種以上を配合してなることを特徴とする難燃性樹脂組成物である。
上記の難燃性樹脂組成物を使用して得られる電子回路基板用積層板である。
本発明のリン含有（メタ）アクリロイル化合物は、従来にない、低い誘電率・誘電正接を示し、耐熱性の低下が少なく、電子機器の情報処理量増大に伴う高周波化における伝送損失を低減する反応型リン系難燃剤として非常に有用である。
以下、本発明を詳細に説明する。
本発明の説明においては、アクリル樹脂や、アクリル化合物、アクリレート化合物等の呼称に関し、通例に従って、例えば「アクリロイル」と「メタクリロイル」の両者を総称して「（メタ）アクリロイル」と云い、「アクリル」と「メタクリル」の両者を総称して「（メタ）アクリル」と云い、「アクリレート」と「メタクリレート」の両者を総称して「（メタ）アクリレート」と云うことがある。
リン含有（メタ）アクリロイル化合物又はリン含有フェノール化合物は、単一化合物だけでなく、混合物（樹脂）を包含する。
本発明の説明においては、アクリル樹脂や、アクリル化合物、アクリレート化合物等の呼称に関し、通例に従って、例えば「アクリロイル」と「メタクリロイル」の両者を総称して「（メタ）アクリロイル」と云い、「アクリル」と「メタクリル」の両者を総称して「（メタ）アクリル」と云い、「アクリレート」と「メタクリレート」の両者を総称して「（メタ）アクリレート」と云うことがある。
リン含有（メタ）アクリロイル化合物又はリン含有フェノール化合物は、単一化合物だけでなく、混合物（樹脂）を包含する。
本発明のリン含有（メタ）アクリロイル化合物は、下記一般式（１）で表される。
一般式（１）において、Ａｒは置換基を有しても良い炭素原子数６～３０の芳香族環基である。芳香族環基としては、特に制限されないが、ベンゼン、フラン、ピロール、チオフェン、イミダゾール、ピラゾール、オキサゾール、イソキサゾール、チアゾール、イソチアゾール、ピリジン、ピリミジン、ピリダジン、ピラジン、トリアジン等の単環芳香族化合物から水素原子がｍ個除かれたもの；ナフタレン、アントラセン、フェナレン、フェナントレン、キノリン、イソキノリン、キナゾリン、フタラジン、プテリジン、クマリン、インドール、ベンゾイミダゾール、ベンゾフラン、アクリジン等の縮環芳香族化合物から水素原子がｍ個除かれたもの等が挙げられる。また、これらの芳香族化合物を複数組み合わせたものであってもよく、例えば、ビフェニル、ビナフタレン、ビピリジン、ビチオフェン、フェニルピリジン、フェニルチオフェン、テルフェニル、ジフェニルチオフェン、クアテルフェニル等の環集合芳香族化合物から水素原子がｍ個除かれたもの等が挙げられる。好ましくは、ベンゼン、ナフタレン、ビフェニルおよびアントラセンである。さらに好ましくは、ベンゼンである。
Ａｒで表される芳香環上には、－ＯＲ１以外の置換基を含んでいても良い。置換基としては、炭素原子数１～１０のアルキル基および炭素原子数１～１０のアルコキシ基を、好ましくは炭素原子数１～１０のアルキル基を挙げることができる。
炭素原子数１～１０のアルキル基としては、特に制限されないが、メチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基、ｎ－ペンチル基、イソペンチル基、ｔｅｒｔ－ペンチル基、ネオペンチル基、１，２－ジメチルプロピル基、ｎ－ヘキシル基、イソヘキシル基、ｎ－ノニル基、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、シクロノニル基が挙げられ、好ましくはメチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基であり、さらに好ましくはメチル基、エチル基である。
炭素原子数１～１０のアルコキシ基としては、特に制限されないが、メトキシ基、エトキシ基、プロポキシ基、イソプロポキシ基、ブトキシ基、ペンチルオキシ基、ヘキシルオキシ基、２－エチルヘキシルオキシ基、オクチルオキシ基、ノニルオキシ基等が挙げられる。これらの置換基を単独でも、２種以上を組み合わせても良い。
一般式（１）において、ｍは３～６の整数で、３または４が好ましく、３がより好ましい。Ｒ１はそれぞれ独立に下記一般式（２）または下記一般式（３）で表される置換基であるが、化合物中に一般式（２）で表される置換基と一般式（３）で表される置換基をそれぞれ少なくとも１つ含む。
一般式（１）のＲ１は、化合物中に一般式（２）で表されるリン含有基を少なくとも１つ含む。
一般式（２）において、Ｒ２およびＲ３は、それぞれ独立して炭素原子数１～５の直鎖または分岐鎖のアルキル基である。
炭素原子数１～５のアルキル基の具体例としては、メチル、エチル、プロピル、イソプロピルｎ－ブチル、イソブチル、ｔｅｒｔ－ブチル、ｎ－ペンチル、イソペンチル、ネオペンチル等が挙げられる。これらの中でも、製造面での反応性および入手のし易さの観点からメチル、エチル、プロピル、イソプロピルが好ましく、メチル基が特に好ましい。
ｎ２、ｎ３はそれぞれ独立に０～５の整数で、好ましくは０または２以上の整数であり、より好ましくは２である。ｎ２、ｎ３が１以上である場合、Ｒ２、Ｒ３のベンゼン環上での置換位置は、特に限定されないが、それぞれ独立して、リン酸エステル結合に対して、オルト位またはメタ位に存在することが好ましい。オルト位にアルキル基がある事で、リン酸エステルが疎水的に遮断され、吸水率を低減、加水分解を抑制するため本発明のリン含有（メタ）アクリロイル化合物の特性を更に向上する事ができる。そのため、リン酸エステル結合に対し２つのオルト位にアルキル基が置換されている事が特に好ましく、ｎ２、ｎ３は２以上が好ましい。
一般式（１）のＲ１は、化合物中に一般式（３）で表される（メタ）アクリロイル基を少なくとも１つ含む。
ここで、Ｒ４は、水素またはメチル基を表す。
本発明のリン含有（メタ）アクリロイル化合物は、単一化合物で用いる必要は無く、一般式（２）で表される置換基の個数が異なる化合物を複数含んだ混合物であっても良い。一般式（２）で表される置換基の個数が増えるほど、難燃性、誘電特性が向上し、一般式（２）の構造が減少するほど反応性基である一般式（３）で表される（メタ）アクリロイル基が増えるため、耐熱性が向上するとともに、難燃剤のブリードアウトを防止する事ができる。そのため、一般式（２）で表される置換基の個数が異なる化合物を複数含むことにより、バランスの良い特性とすることができる。そのため、本発明のリン含有（メタ）アクリロイル化合物は、すべてのＲ１が一般式（２）である構造や、すべてのＲ１が一般式（３）で表される置換基である構造を含んでも良いが、難燃性と耐熱性をバランス良く発現するためには、下記のリン含有率を満たす必要がある。すなわち本発明のリン含有（メタ）アクリロイル化合物のリン含有率は１．５～１２．０重量％であり、好ましくは２．０～１１重量％であり、更に好ましくは３．０～１０重量％である。
なお、本発明のリン含有（メタ）アクリロイル化合物（混合物）は、効果を阻害しない限り、反応原料の多価ヒドロキシ化合物を含んでもよい。
なお、本発明のリン含有（メタ）アクリロイル化合物（混合物）は、効果を阻害しない限り、反応原料の多価ヒドロキシ化合物を含んでもよい。
本発明のリン含有（メタ）アクリロイル化合物は、Ａｒがベンゼンで、ｍが３である事が、原料入手の点から好ましい。更に好ましくは、Ｒ１の１つが一般式（２）で表される置換基であり、Ｒ１の２つが一般式（３）である化合物（リン含有基の１置換体、（メタ）アクリロイル基の２置換体）を１０～８０モル％、Ｒ１の２つが一般式（２）で表される置換基であり、Ｒ１の１つが一般式（３）で表される化合物（リン含有基の２置換体、（メタ）アクリロイル基の１置換体）を５～５０モル％、Ｒ１の３つが一般式（２）で表される置換基である化合物（リン含有基の３置換体）を１～５０モル％含むことで、難燃性、耐熱性及び誘電特性のバランスに優れる硬化物を得ることができる。より好ましくは、一般式（２）で表されるリン含有基の１置換体（（メタ）アクリロイル基の２置換体）２０～７０モル％、リン含有基の２置換体（（メタ）アクリロイル基の１置換体）１０～４０モル％、リン含有基の３置換体２～４０モル％である。なお、すべてのＲ１が一般式（３）で表される（メタ）アクリロイル基である化合物（（メタ）アクリロイル基の３置換体）を含んでも良いが、その割合は３０モル％未満であることが望ましい。
本発明のリン含有（メタ）アクリロイル化合物（樹脂）は、平均分子量（Ｍｗ）が好ましくは２００～３０００、より好ましくは３００～１５００の範囲である。
本発明のリン含有（メタ）アクリロイル化合物（樹脂）は、平均分子量（Ｍｗ）が好ましくは２００～３０００、より好ましくは３００～１５００の範囲である。
上記の１置換体、２置換体、３置換体などの組成は、液体クロマトグラフィー、サイズ排除クロマトグラフィー等で確認する事ができる。
次に、本発明のリン含有（メタ）アクリロイル化合物の製造方法について説明する。本発明のリン含有（メタ）アクリロイル化合物は、一般式（４）で表されるリン含有フェノール化合物と（メタ）アクリル酸、ハロゲン化（メタ）アクリロイルまたは（メタ）アクリル酸無水物を反応させることで得られる。
一般式（４）において、Ａｒ、ｍは一般式（１）と同義であり、Ｒ５は水素または上記一般式（２）で表される置換基である。
一般式（４）で表されるリン含有フェノール化合物のリン含有率は、好ましくは１．５～１５．０質量％であり、より好ましくは３．０～１２．０質量％、さらに好ましくは５．０～１０．０質量％であり、水酸基当量としては、好ましくは８０～８００ｇ／ｅｑであり、より好ましくは１００～６００ｇ／ｅｑである。上記の範囲のリン含有フェノール化合物を用いることで、好ましいリン含有率をもつ本発明のリン含有（メタ）アクリロイル化合物を得ることができる。
一般式（４）で表されるリン含有フェノール化合物は、原料として一般式（５）で表される多価ヒドロキシ化合物を使用し、リン酸エステル化反応によって得ることができる。
一般式（５）において、Ａｒ、ｍは、一般式（１）と同義である。
ここで、ｍは３～６の数であり、水酸基を３個以上有する多価ヒドロキシ芳香族化合物を使用することが必要である。
ここで、ｍは３～６の数であり、水酸基を３個以上有する多価ヒドロキシ芳香族化合物を使用することが必要である。
一般式（４）で表されるリン含有フェノール化合物は、一般的な芳香族リン酸エステルの製造方法に準じて得ることができ、反応形態の一例としては、オキシハロゲン化リン（ハロゲン化ホスホリル）とフェノール類を原料とするエステル化反応であり、脱ハロゲン化水素反応により、対応するリン酸エステルを得ることが出来る。
本発明の一般式（１）で表されるリン含有（メタ）アクリロイル化合物は、一般式（４）で表されるリン含有フェノール化合物と（メタ）アクリル酸、ハロゲン化（メタ）アクリロイルまたは（メタ）アクリル酸無水物とを反応させて得ることができ、その反応は、特に制約は無く、フェノール化合物の通常の（メタ）アクリロイル化反応と同様に実施できる。
例えば、（メタ）アクリル酸を使用する場合は、式（４）で表されるリン含有フェノール化合物を、硫酸、ｐ－トルエンスルホン酸、メタンスルホン酸等の強酸触媒の存在下、水酸基に対して１～１０倍の（ メタ）アクリル酸と縮合反応することで製造することができる。この反応は、副生する縮合水を系外に除去しながら進める必要があることから、反応溶媒にはトルエン等の水と共沸する炭化水素系の溶剤を使用し、反応液を７０～１４０ ℃ 程度に加熱することで行う。
また、式（４）で表されるリン含有フェノール化合物とハロゲン化（メタ）アクリロイルまたは（メタ）アクリル酸無水物との反応で本発明のリン含有（メタ）アクリロイル化合物を得ることができる。使用することができるハロゲン化（メタ）アクリロイルとしては、フッ化アクリロイル、塩化アクリロイル、臭化アクリロイル、ヨウ化アクリロイル等のハロゲン化アクリロイル、フッ化メタクリロイル、塩化メタクリロイル、臭化メタクリロイル、ヨウ化メタクリロイル等のハロゲン化メタクリロイルが挙げられる。
本発明の実施においては、ハロゲン化（メタ）アクリロイル、（メタ）アクリル酸無水物として、１種または２種以上の混合物を使用してもよい。本発明においては、なかでも、入手が容易な点から、塩化（メタ）アクリルまたは／および（メタ）アクリル酸無水物を使用することが好ましい。
本発明の実施においては、ハロゲン化（メタ）アクリロイル、（メタ）アクリル酸無水物として、１種または２種以上の混合物を使用してもよい。本発明においては、なかでも、入手が容易な点から、塩化（メタ）アクリルまたは／および（メタ）アクリル酸無水物を使用することが好ましい。
ハロゲン化（メタ）アクリロイルまたは／および（メタ）アクリル酸無水物の使用量としては、原料として用いるリン含有フェノール化合物の水酸基１モルに対して、０．８～５モル、好ましくは０．９５～４モルである。（メタ）アクリル酸ハライドまたは／および（メタ）アクリル酸無水物の使用量が上記範囲を下回ると、得られるリン含有（メタ）アクリロイル化合物の耐熱性が低下し、また水酸基の残存量が増えるため誘電特性が悪化するため好ましくなく、使用量が上記範囲を上まわると釜効率が下がりコストが高くなるため好ましくない。
ハロゲン化（メタ）アクリロイルを使用する場合においては、使用する（メタ）アクリル酸ハライドに対応したハロゲン化水素が副生物として生成することから、塩基性化合物を併用して、発生したハロゲン化水素をトラップしつつ反応を行うことが好ましい。塩基性化合物としては特に限定されず、トリメチルアミン、トリエチルアミン、ジイソプロピルエチルアミン、トリ－ｎ－プロピルアミン、トリイソプロピルアミン、トリブチルアミン、Ｎ－メチル－ジエチルアミン、Ｎ－エチル－ジメチルアミン、Ｎ－エチル－ジアミルアミン等の脂肪族アミン；Ｎ，Ｎ－ジメチルアニリン、ジエチルアニリン等の芳香族アミン；Ｎ，Ｎ－ジメチル－シクロヘキシルアミン、Ｎ，Ｎ－ジエチル－シクロヘキシルアミン等の脂環式アミン；Ｎ，Ｎ－ジメチルアミノピリジン、Ｎ－メチルモルホリン、ジアザビシクロウンデセン（ＤＢＵ）、ジアザビシクロノネン（ＤＢＮ）、Ｎ－メチルピリジン、Ｎ－メチルピロリジン等の複素環アミン；テトラメチルエチレンジアミン、トリエチレンジアミン等のジアミン等を挙げることができる。特に、トリメチルアミン、トリエチルアミン等の脂肪族アミン、ピリジンが、入手の容易さから好ましい。
塩基性化合物の使用量としては、原料として用いるリン含有フェノール化合物の水酸基１モルに対して、例えば０．８～７モル、好ましくは０．９５～５モル程度である。第３級アミンの使用量が上記範囲を下回ると、ハロゲン化水素を完全にトラップすることができず、反応装置の腐食が起こってしまい、上記範囲を上回ると、コスト高となる傾向がある。
（メタ）アクリル酸無水物で反応を行う際には、触媒を使用しなくても良いが、反応が進み難い場合には、エステル触媒、酸触媒、塩基触媒、ルイス酸触媒を用いることができる。ここで、エステル触媒としては、酢酸ナトリウム、プロピオン酸カリウム、（メタ）アクリル酸ナトリウム等の、低級カルボン酸のナトリウム、カリウム等のアルカリ金属塩が例示できる。また、酸触媒としては、硫酸、ホウ酸等の無機酸；メタンスルホン酸、パラトルエンスルホン酸等の有機酸等が例示できる。また、塩基触媒としては、有機塩基であれば、トリエチルアミン、トリエチレンジアミン等の含窒素脂肪族化合物；、ピリジン、４－（ジメチルアミノ）ピリジン、等の含窒素芳香族複素環化合物等が例示できる。また、ルイス酸触媒としては、塩化アルミニウム、塩化亜鉛等が例示できる。
触媒の使用量としては、使用する（メタ）アクリル酸無水物に対して、１０％以下が好ましく、５％以下が更に好ましい。触媒を使用する場合に上記範囲を上回ると、触媒の除去に時間がかかり、また製品中に触媒が残存しやすく、特性の悪化を招く。
式（４）で表されるリン含有フェノール化合物とハロゲン化（メタ）アクリロイルまたは／および（メタ）アクリル酸無水物の反応においては、反応溶媒として有機溶媒を使用し、溶液中での反応を行うことが好ましい。使用することができる溶媒としては、フェノール化合物および（メタ）アクリル酸ハライドまたは／および（メタ）アクリル酸無水物との反応性を有さないものであれば特に限定されず、テトラヒドロフラン、ジオキサン、酢酸エチル、アセトニトリル、ベンゼン、トルエン、キシレン、ジクロロメタン、クロロホルム、四塩化炭素、ジメチルホルムアミド、ジメチルアセトアミド、ジメチルスルホキシド、ヘキサメチルリン酸トリアミド、水等の溶剤が挙げられ、必要によりこれらを組み合わせて使用することができる。
式（４）で表されるリン含有フェノール化合物と（メタ）アクリル酸ハライドまたは／および（メタ）アクリル酸無水物の反応においては、反応温度は－５０～１５０℃であることが好ましく、高温で反応させると重合反応が生じる可能性が高くなるので、－２５～１００℃であることがより好ましい。また、反応時間は、設定した反応温度に応じて適宜設定されるが、１～４８時間の範囲に設定することが好ましい。
式（４）で表されるリン含有フェノール化合物と（メタ）アクリル酸、ハロゲン化（メタ）アクリロイルまたは（メタ）アクリル酸無水物の反応は、重合禁止剤の存在下で行ってもよい。重合禁止剤を添加することにより、反応に供する（メタ）アクリル酸、ハロゲン化（メタ）アクリロイルまたは（メタ）アクリル酸無水物や、目的生成物である（メタ）アクリル酸エステルが重合してオリゴマーを副生することを防止することができる。 重合禁止剤には公知のものを制限なく用いることができ、ヒドロキノン、ヒドロキシモノメチルエーテル、ｔ － ブチルカテコール、ｔ － ブチルハイドロキノン、４－メトキシフェノール、４－メトキシ－１－ナフトール、フェノチアジン等の有機化合物の他、塩化銅、硫化銅等の銅化合物等が挙げられ、これらを組み合わせて使用してもよい。
この反応の終了後、得られた反応液（反応混合物）を必要により、反応溶媒の留去、溶媒置換等を実施し、水等による洗浄や、活性炭処理、シリカゲルクロマトグラフィー等の手段を利用して精製し、目的物である本発明の（メタ）アクリロイル化合物を取り出すことができる。
次に、本発明のリン含有（メタ）アクリロイル化合物を必須成分とし、硬化性樹脂又は熱可塑性樹脂を配合してなる難燃性樹脂組成物について説明する。
本発明の難燃性樹脂組成物において、配合割合は特に限定されるものではないが、例えば、硬化性樹脂及び熱可塑性樹脂の合計量１００重量部に対して、リン含有（メタ）アクリロイル化合物を１０～３００重量部配合するとよい。好ましくは２０～２００重量部、より好ましくは５０～１５０重量部である。
硬化性樹脂としては、例えば、不飽和ポリエステル樹脂、硬化型マレイミド樹脂、エポキシ樹脂、ポリシアナート樹脂、フェノール樹脂、分子中に１個以上の重合性不飽和炭化水素基を有する１種以上のビニル化合物類等を挙げることができ、好ましくは、エポキシ樹脂、分子中に１個以上の重合性不飽和炭化水素基を有する１種以上のビニル化合物類である。
硬化性樹脂がエポキシ樹脂である場合、１分子中に２以上のエポキシ基を有するエポキシ樹脂から選ばれる１種以上のエポキシ樹脂であることが好ましい。かかるエポキシ樹脂としては、クレゾールノボラック型エポキシ樹脂、トリフェニルメタン型エポキシ樹脂、ビフェニルエポキシ樹脂、ナフタレン型エポキシ樹脂、ビスフェノールＡ型エポキシ樹脂及びビスフェノールＦ型エポキシ樹脂等が挙げられる。これらは、単独で用いても、２種以上を組み合わせて用いてもよい。このようなエポキシ樹脂を用いることによって、本発明の硬化性樹脂組成物の有する、優れた誘電特性と流動性への影響を最小限に留め、硬化物の耐熱性と密着性を充分に高められると考えられる。
また、エポキシ樹脂を含む場合には、エポキシ樹脂の他に硬化剤を使用しても良い。硬化剤としては、特に制限されるものではなく、例えばフェノール系硬化剤、アミン系化合物、アミド系化合物、酸無水物系化合物、ナフトール系硬化剤、活性エステル系硬化剤、ベンゾオキサジン系硬化剤、シアネートエステル系硬化剤等が挙げられる。これらは１種又は２種以上組み合わせて使用してもよい。
更に、エポキシ樹脂を配合する場合には、必要に応じて硬化促進剤を用いることができる。例えば、アミン類、イミダゾール類、有機ホスフィン類、ルイス酸等である。添加量は、通常、エポキシ樹脂１００重量部に対して、０．２～５重量部の範囲である。
硬化性樹脂として、分子中に１個以上の重合性不飽和炭化水素基を有する１種以上のビニル化合物類（以下、ビニル化合物類ともいう。）である場合、その種類は特に限定されない。すなわち、ビニル化合物類は、本発明のリン含有（メタ）アクリロイル化合物と反応させることによって、架橋を形成させて、硬化させることができるものであればよい。重合性不飽和炭化水素基が炭素－炭素不飽和二重結合であるものがより好ましく、炭素－炭素不飽和二重結合を分子中に２個以上有する化合物がより好ましい。
硬化性樹脂としてのビニル化合物類の１分子当たりの炭素－炭素不飽和二重結合の平均個数（ビニル基（置換ビニル基を含む）の数。末端二重結合数ともいう。）は、ビニル化合物類のＭｗによって異なるが、例えば、１～２０個であることが好ましく、２～１８個であることがより好ましい。この末端二重結合数が少なすぎると、硬化物の耐熱性としては充分なものが得られにくい傾向がある。また、末端二重結合数が多すぎると、反応性が高くなりすぎ、例えば、硬化性樹脂組成物の保存安定性が低下したり、硬化性樹脂組成物の流動性が低下したりする等の不具合が発生するおそれがある。
ビニル化合物類としては、トリアリルイソシアヌレート（ＴＡＩＣ）等のトリアルケニルイソシアヌレート化合物、末端が（メタ）アクリロイル基やスチリル基で変性された変性ポリフェニレンエーテル（ＰＰＥ）、分子中に（メタ）アクリロイル基を２個以上有する多官能（メタ）アクリレート化合物、ポリブタジエン等のように分子中にビニル基を２個以上有するビニル化合物（多官能ビニル化合物）、及びスチレン、ジビニルベンゼン等のビニルベンジル化合物等が挙げられる。この中でも、炭素－炭素二重結合を分子中に２個以上有するものが好ましく、具体的には、ＴＡＩＣ、多官能（メタ）アクリレート化合物、変性ＰＰＥ樹脂、多官能ビニル化合物、及びジビニルベンゼン化合物等が挙げられる。これらを用いると、硬化反応により架橋がより好適に形成されると考えられ、硬化性樹脂組成物の硬化物の耐熱性をより高めることができる。また、これらを単独で用いてもよいし、２種以上を組み合わせて用いてもよい。また、炭素－炭素不飽和二重結合を分子中に１個有する化合物を併用してもよい。炭素－炭素不飽和二重結合を分子中に１個有する化合物としては、分子中にビニル基を１個有する化合物（モノビニル化合物）等が挙げられる。
熱可塑性樹脂としては、例えば、ポリスチレン、ポリフェニレンエーテル樹脂、ポリエーテルイミド樹脂、ポリエーテルサルホン樹脂、ＰＰＳ樹脂、ポリシクロペンタジエン樹脂、ポリシクロオレフィン樹脂等や、既知の熱可塑性エラストマー（例えば、スチレン－エチレン－プロピレン共重合体、スチレン－エチレン－ブチレン共重合体、スチレン－ブタジエン共重合体、スチレン‐イソプレン共重合体、水添スチレン－ブタジエン共重合体、水添スチレン－イソプレン共重合体等）や、あるいはゴム類（例えばポリブタジエン、ポリイソプレン）を挙げることができる。好ましくは、未変性または変性ポリフェニレンエーテル樹脂、水添スチレン－ブタジエン共重合体を挙げることができる。
本発明の難燃性樹脂組成物には、光または／および熱でラジカルを生じるラジカル重合開始剤（重合触媒ないし架橋剤）を配合しても良い。光重合開始剤としては、例えばべンゾイン、べンゾインメチルエーテル、べンゾインエチルエーテル、べンゾインプロピルエーテル、べンゾインイソブチルエーテル等のべンゾイン類；アセトフェノン、2,2－ジエトキシ－2－フェニルアセトフェノン、2,2－ジエトキシ－2－フェニルアセトフェノン、1,1－ジクロロアセトフェノン、2－ヒドロキシ－2－メチル－フェニルプロパン－1－オン、ジエトキシアセトフェノン、1－ヒドロキシシクロへキシルフェニルケトン、2－メチル－1－[4－（メチルチオ）フェニル]－2－モルホリノプロパン－1－オンなどのアセトフェノン類；2－エチルアントラキノン、2－ターシャリーブチルアントラキノン、2－クロロアントラキノン、2－アミルアントラキノンなどのアントラキノン類；2,4－ジエチルチオキサントン、2－イソプロピルチオキサントン、2－クロロチオキサントンなどのチオキサントン類；アセトフェノンジメチルケタール、べンジルジメチルケタールなどのケタール類；べンゾフエノン、4－べンゾイル－4’－メチルジフェニルサルファイド、4,4’－ビスメチルアミノべンゾフェノンなどのべンゾフェノン類；2,4,6－トリメチルべンゾイルジフェニルホスフィンオキサイド、ビス（2,4,6－トリメチルべンゾイル）－フェニルホスフィンオキサイド等のホスフィンオキサイド類等が挙げられる。
熱ラジカル開始剤としては、ベンゾイルパーオキサイド、クメンハイドロパーオキサイド、２，５－ジメチルヘキサン－２，５－ジハイドロパーオキサイド、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシ）ヘキシン－３、ジ－ｔ－ブチルパーオキサイド、ｔ－ブチルクミルパーオキサイド、１，３－ビス（ブチルパーオキシイソプロピル）ベンゼン、α，α’－ビス（ｔ－ブチルパーオキシ－ｍ－イソプロピル）ベンゼン、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシ）ヘキサン、ジクミルパーオキサイド、ジ－ｔ－ブチルパーオキシイソフタレート、ｔ－ブチルパーオキシベンゾエート、２，２－ビス（ｔ－ブチルパーオキシ）ブタン、２，２－ビス（ｔ－ブチルパーオキシ）オクタン、２，５－ジメチル－２，５－ジ（ベンゾイルパーオキシ）ヘキサン、ジ（トリメチルシリル）パーオキサイド、トリメチルシリルトリフェニルシリルパーオキサイド等の過酸化物があるがこれらに限定されない。また過酸化物ではないが、２，３－ジメチル－２，３－ジフェニルブタンも、ラジカル重合開始剤として使用できる。しかし、これらの例に限定されるものではなく、ラジカル開始剤２種以上を組み合わせて用いてもよい。
ラジカル重合開始剤の配合量は、リン含有リン含有（メタ）アクリロイル化合物１００重量部に対して、好ましくは０．０１～１０重量部、より好ましくは０．１～５重量部である。
熱ラジカル開始剤としては、ベンゾイルパーオキサイド、クメンハイドロパーオキサイド、２，５－ジメチルヘキサン－２，５－ジハイドロパーオキサイド、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシ）ヘキシン－３、ジ－ｔ－ブチルパーオキサイド、ｔ－ブチルクミルパーオキサイド、１，３－ビス（ブチルパーオキシイソプロピル）ベンゼン、α，α’－ビス（ｔ－ブチルパーオキシ－ｍ－イソプロピル）ベンゼン、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシ）ヘキサン、ジクミルパーオキサイド、ジ－ｔ－ブチルパーオキシイソフタレート、ｔ－ブチルパーオキシベンゾエート、２，２－ビス（ｔ－ブチルパーオキシ）ブタン、２，２－ビス（ｔ－ブチルパーオキシ）オクタン、２，５－ジメチル－２，５－ジ（ベンゾイルパーオキシ）ヘキサン、ジ（トリメチルシリル）パーオキサイド、トリメチルシリルトリフェニルシリルパーオキサイド等の過酸化物があるがこれらに限定されない。また過酸化物ではないが、２，３－ジメチル－２，３－ジフェニルブタンも、ラジカル重合開始剤として使用できる。しかし、これらの例に限定されるものではなく、ラジカル開始剤２種以上を組み合わせて用いてもよい。
ラジカル重合開始剤の配合量は、リン含有リン含有（メタ）アクリロイル化合物１００重量部に対して、好ましくは０．０１～１０重量部、より好ましくは０．１～５重量部である。
本発明の難燃性樹脂組成物には、充填剤を配合することができる。充填剤としては、硬化性樹脂組成物の硬化物の、耐熱性や難燃性を高めるために添加するもの等が挙げられ、公知の充填剤を使用することができるが、特に限定されない。また、充填剤を含有させることによって、耐熱性、寸法安定性や難燃性等をさらに高めることができる。具体的には、球状シリカ等のシリカ、アルミナ、酸化チタン、及びマイカ等の金属酸化物、水酸化アルミニウム、水酸化マグネシウム等の金属水酸化物、タルク、ホウ酸アルミニウム、硫酸バリウム、及び炭酸カルシウム等が挙げられる。水酸化アルミニウム、水酸化マグネシウムなどの金属水酸化物を用いた場合、難燃助剤として作用し、リン含有率が少なくても難燃性を確保することが出来る。この中でも、シリカ、マイカ、及びタルクが好ましく、球状シリカがより好ましい。また、これらの１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
充填剤は、そのまま用いてもよいが、エポキシシランタイプ、又はアミノシランタイプ等のシランカップリング剤で表面処理したものを用いてもよい。このシランカップリング剤としては、ラジカル重合開始剤との反応性との観点から、ビニルシランタイプ、メタクリロキシシランタイプ、アクリロキシシランタイプ、及びスチリルシランタイプのシランカップリング剤が好ましい。これにより、金属箔との接着強度や樹脂同士の層間接着強度が高まる。また、充填剤に予め表面処理する方法でなく、上記シランカップリング剤をインテグラルブレンド法で添加して用いてもよい。
充填剤の含有量は、充填剤を除く固形分（モノマー等の有機成分と難燃剤を含み、溶剤を除く。）の合計１００質量部に対して、１０～２００質量部であることが好ましく、３０～１５０質量部であることが好ましい。
本発明の難燃性樹脂組成物には、上記以外の添加剤をさらに含有してもよい。添加剤としては、例えば、シリコーン系消泡剤及びアクリル酸エステル系消泡剤等の消泡剤、熱安定剤、帯電防止剤、紫外線吸収剤、染料や顔料、滑剤、湿潤分散剤等の分散剤等が挙げられる。
本発明の難燃性樹脂組成物を硬化させて得られる硬化物は、成型物、積層物、注型物、接着剤、塗膜、フィルムとして使用できる。例えば、半導体封止材料の硬化物は注型物又は成型物であり、かかる用途の硬化物を得る方法としては、硬化性樹脂組成物を注型、或いはトランスファ－成形機、射出成形機などを用いて成形し、さらに８０～２３０℃で０．５～１０時間に加熱することにより硬化物を得ることができる。
本発明の難燃性樹脂組成物は、プリプレグとして使用することもできる。プリプレグを製造する際には、プリプレグを形成するための基材（繊維質基材）に含浸する目的、あるいは回路基板を形成する回路基板材料とする目的でワニス状に調製して、樹脂ワニスとすることができる。この樹脂ワニスは、回路基板用に適し、回路基板材料用ワニスとして使用できる。なお、ここでいう回路基板材料の用途は、具体的には、プリント配線基板、プリント回路板、フレキシブルプリント配線板、ビルドアップ配線板等が挙げられる。
上記の樹脂ワニスに用いられる有機溶媒としては、硬化反応を阻害しないものであれば、特に限定されない。例えば、アセトン、メチルエチルケトン、メチルイソブチルケトン等のケトン類；酢酸エチル、酢酸プロピル、酢酸ブチル等のエステル類；ジメチルアセトアミド、ジメチルホルムアミド等の極性溶剤類；トルエン、キシレン等の芳香族炭化水素溶剤類等が挙げられ、これらを１種または２種以上を混合して使用することも可能である。誘電特性の観点から、ベンゼン、トルエン、キシレンなどの芳香族炭化水素類が好ましい。
樹脂ワニスを作成する際に、使用する有機溶剤の量は、本発明の硬化性樹脂組成物１００重量部に対して、好ましくは５～９００重量部、より好ましくは１０～７００重量部、特に好ましくは２０～５００重量部である。
プリプレグを作成するのに用いられる基材としては、公知の材料が用いられるが、例えば、ガラス繊維、カーボン繊維、ポリエステル繊維、ポリアミド繊維、アルミナ繊維、紙などの基材がそれぞれ単独で、あるいは２種以上併せて用いられる。これら基材には、必要に応じて樹脂と基材の界面における接着性を改善する目的でカップリング剤を用いることができる。カップリング剤としては、シランカップリング剤、チタネートカップリング剤、アルミニウム系カップリング剤、ジルコアルミネートカップリング剤など一般のものが使用できる。
プリプレグを得る方法としては、上記樹脂ワニスを基材に含浸させた後、乾燥する方法が挙げられる。含浸は浸漬（ディッピング）、塗布等によって行われる。含浸は必要に応じて複数回繰り返すことも可能であり、またこの際、組成や濃度の異なる複数の溶液を用いて含浸を繰り返し、最終的に希望とする樹脂組成及び樹脂量に調整することも可能である。含浸後に、１００～１８０℃で１～３０分加熱乾燥することでプリプレグを得ることができる。ここで、プリプレグ中の樹脂量は、樹脂分３０～８０重量％とすることが好ましい。
本発明の硬化性樹脂組成物は、積層板としても使用することもできる。プリプレグを用いて積層板を形成する場合は、プリプレグを一又は複数枚積層し、片側又は両側に金属箔を配置して積層物を構成し、この積層物を加熱・加圧して積層一体化する。ここで金属箔としては、銅、アルミニウム、真鍮、ニッケル等の単独、合金、複合の金属箔を用いることができる。積層物を加熱加圧する条件としては、硬化性樹脂組成物が硬化する条件で適宜調整して加熱加圧すればよいが、加圧の圧力があまり低いと、得られる積層板の内部に気泡が残留し、電気的特性が低下する場合があるため、成形性を満足する条件で加圧することが好ましい。例えば温度を１８０～２５０℃、圧力を４９．０～４９０．３Ｎ／ｃｍ2（５～５０ｋｇｆ／ｃｍ2）、加熱加圧時間を４０～２４０分間にそれぞれ設定することができる。更にこのようにして得られた単層の積層板を内層材として、多層板を作製することができる。この場合、まず積層板にアディティブ法やサブトラクティブ法等にて回路形成を施し、形成された回路表面を酸溶液で処理して黒化処理を施して、内層材を得る。この内層材の、片側又は両側の回路形成面に、樹脂シート、樹脂付き金属箔、又はプリプレグにて絶縁層を形成すると共に、絶縁層の表面に導体層を形成して、多層板を形成するものである。
また、本発明の硬化性組成物をビルドアップフィルムに使用することもできる。本発明の樹脂組成物からビルドアップフィルムを製造する方法は、例えば、上記樹脂ワニスを、支持フィルム上に塗布、乾燥させてフィルム状の絶縁層を形成する方法が挙げられる。このようにして形成させたフィルム状の絶縁層は、多層プリント配線板用のビルドアップフィルムとして使用できる。
次に、実施例により本発明を説明するが、本発明はこれらにより限定されるものではない。各例中の部はいずれも質量部である。
なお、実施例中の各硬化物サンプルの物性測定は、以下に示す方法により行った。
なお、実施例中の各硬化物サンプルの物性測定は、以下に示す方法により行った。
（１）化合物の分子量及び分子量分布：化合物の分子量及び分子量分布測定はＧＰＣ（東ソー製、ＨＬＣ－８１２０ＧＰＣ）を使用し、溶媒にテトラヒドロフラン、流量１．０ｍｌ／ｍｉｎ、カラム温度３８℃、単分散ポリスチレンによる検量線を用いて行った。
（２）水酸基当量：１００ｍＬの共栓付フラスコに約６ｍｇ／ｅｑの試料を精秤し、無水酢酸/ピリジン＝３/１（容量比）で混合した試薬を３ｍＬ加え、冷却管を付け、ホットプレートで５分間加熱還流させ、５分間の放冷の後、１ｍＬの水を加える。その液を、０．５mol/LのＫＯＨ/ＭｅＯＨ溶液で電位差滴定する事で算出した。
（３）リン含有率：試料に硫酸、塩酸、過塩素酸を加え、加熱して湿式灰化し、全てのリン原子をオルトリン酸とした。硫酸酸性溶液中でメタバナジン酸塩及びモリブデン酸塩を反応させ、生じたリンバナードモリブデン酸錯体の４２０ｎｍにおける吸光度を測定し、予めリン酸二水素カリウムを用いて作成した検量線により、求めたリン原子含有率を質量％で表した。
（４）ガラス転移温度：株式会社日立ハイテクサイエンス製、示差走査熱量測定を用いて１０℃／分の昇温速度で、ベースラインシフトから求めた。
（５）比誘電率及び誘電正接：ＩＰＣ－ＴＭ－６５０ ２．５．５．９規格に準じてマテリアルアナライザー（ＡＧＩＬＥＮＴ Ｔｅｃｈｎｏｌｏｇｉｅｓ社製）を用い、２５℃、湿度６０％環境下で容量法により周波数１ＧＨｚにおける誘電率（Ｄｋ）及び誘電正接（Ｄｆ）を求めた。
（６）難燃性：ＵＬ９４に準じ、試験片５本を用いて垂直法により評価した。評価は、試験片５本の合計燃焼時間とＶ－０、Ｖ－１、Ｖ－２の分類で記した。
（２）水酸基当量：１００ｍＬの共栓付フラスコに約６ｍｇ／ｅｑの試料を精秤し、無水酢酸/ピリジン＝３/１（容量比）で混合した試薬を３ｍＬ加え、冷却管を付け、ホットプレートで５分間加熱還流させ、５分間の放冷の後、１ｍＬの水を加える。その液を、０．５mol/LのＫＯＨ/ＭｅＯＨ溶液で電位差滴定する事で算出した。
（３）リン含有率：試料に硫酸、塩酸、過塩素酸を加え、加熱して湿式灰化し、全てのリン原子をオルトリン酸とした。硫酸酸性溶液中でメタバナジン酸塩及びモリブデン酸塩を反応させ、生じたリンバナードモリブデン酸錯体の４２０ｎｍにおける吸光度を測定し、予めリン酸二水素カリウムを用いて作成した検量線により、求めたリン原子含有率を質量％で表した。
（４）ガラス転移温度：株式会社日立ハイテクサイエンス製、示差走査熱量測定を用いて１０℃／分の昇温速度で、ベースラインシフトから求めた。
（５）比誘電率及び誘電正接：ＩＰＣ－ＴＭ－６５０ ２．５．５．９規格に準じてマテリアルアナライザー（ＡＧＩＬＥＮＴ Ｔｅｃｈｎｏｌｏｇｉｅｓ社製）を用い、２５℃、湿度６０％環境下で容量法により周波数１ＧＨｚにおける誘電率（Ｄｋ）及び誘電正接（Ｄｆ）を求めた。
（６）難燃性：ＵＬ９４に準じ、試験片５本を用いて垂直法により評価した。評価は、試験片５本の合計燃焼時間とＶ－０、Ｖ－１、Ｖ－２の分類で記した。
合成例において下記の化合物を原料として用いた。
・オキシ塩化リン（東京化成工業株式会社製）
・２，６-ジメチルフェノール（東京化成工業株式会社製）
・フロログルシノール（東京化成工業株式会社製）
・オキシ塩化リン（東京化成工業株式会社製）
・２，６-ジメチルフェノール（東京化成工業株式会社製）
・フロログルシノール（東京化成工業株式会社製）
（合成例１）ジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）の合成
撹拌機、温度計および塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた２Ｌの４つ口フラスコに、オキシ塩化リン（下記構造式）７６７ｇ（５ｍｏｌ）、
２，６－ジメチルフェノール（下記構造式）１２００ｇ（９．８ｍｏｌ）、
溶剤としてのキシレン１４０ｇ、触媒として塩化マグネシウム６．２ｇ（０．０６５ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら約３時間かけて温度１６０℃まで徐々に加熱昇温して反応させ、発生する塩化水素ガスを水スクラバーで回収した。その後、同温度でフラスコ内の圧力を徐々に２０ｋＰａまで減圧し、キシレンや未反応のオキシ塩化リンおよび２，６－ジメチルフェノール、副生する塩化水素を除去し、ジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ：下記構造式）を主成分とする反応生成物１７００ｇを得た。また、反応混合物の塩素含有率は１０．９質量％であった。
撹拌機、温度計および塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた２Ｌの４つ口フラスコに、オキシ塩化リン（下記構造式）７６７ｇ（５ｍｏｌ）、
２，６－ジメチルフェノール（下記構造式）１２００ｇ（９．８ｍｏｌ）、
溶剤としてのキシレン１４０ｇ、触媒として塩化マグネシウム６．２ｇ（０．０６５ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら約３時間かけて温度１６０℃まで徐々に加熱昇温して反応させ、発生する塩化水素ガスを水スクラバーで回収した。その後、同温度でフラスコ内の圧力を徐々に２０ｋＰａまで減圧し、キシレンや未反応のオキシ塩化リンおよび２，６－ジメチルフェノール、副生する塩化水素を除去し、ジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ：下記構造式）を主成分とする反応生成物１７００ｇを得た。また、反応混合物の塩素含有率は１０．９質量％であった。
（合成例２）リン含有フェノール化合物Ａの合成
撹拌機、温度計、塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた２００ｍＬの４つ口フラスコに、メシチレン５１．６ｇ、フロログルシノール（下記構造式）
１２．６ｇ（０．１ｍｏｌ）、合成例１で得られたジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）２１．８ｇ（０．０６ｍｏｌ）、触媒として無水塩化マグネシウム０．４ｇ（０．００４ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら１５５℃まで徐々に加熱昇温し１５５℃に到達してから１８時間反応させ発生する塩化水素を捕集した。６０℃に冷却後、酢酸エチル３５ｇを加え、酸洗い、中和、２回の水洗いを行い、溶媒除去を行って化合物Ａ２６．１ｇを得た。
化合物Ａは、水酸基当量１２５ｇ／ｅｑ、リン含有率が６．４質量％であった。更に、ＧＰＣによりフロログルシノールの水酸基の１つがジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）と反応した化合物（１置換体、下記構造式）を６８モル％、水酸基の２つが反応した化合物（２置換体、下記構造式）を１０モル％、水酸基の３つと反応した化合物（３置換体、下記構造式）を２モル％、フロログルシノールを２０モル％含むことを確認した。
撹拌機、温度計、塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた２００ｍＬの４つ口フラスコに、メシチレン５１．６ｇ、フロログルシノール（下記構造式）
１２．６ｇ（０．１ｍｏｌ）、合成例１で得られたジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）２１．８ｇ（０．０６ｍｏｌ）、触媒として無水塩化マグネシウム０．４ｇ（０．００４ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら１５５℃まで徐々に加熱昇温し１５５℃に到達してから１８時間反応させ発生する塩化水素を捕集した。６０℃に冷却後、酢酸エチル３５ｇを加え、酸洗い、中和、２回の水洗いを行い、溶媒除去を行って化合物Ａ２６．１ｇを得た。
化合物Ａは、水酸基当量１２５ｇ／ｅｑ、リン含有率が６．４質量％であった。更に、ＧＰＣによりフロログルシノールの水酸基の１つがジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）と反応した化合物（１置換体、下記構造式）を６８モル％、水酸基の２つが反応した化合物（２置換体、下記構造式）を１０モル％、水酸基の３つと反応した化合物（３置換体、下記構造式）を２モル％、フロログルシノールを２０モル％含むことを確認した。
（合成例３）リン含有フェノール化合物Ｂの合成
撹拌機、温度計、塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた２００ｍＬの４つ口フラスコに、メシチレン１１０．９ｇ、フロログルシノール１２．６ｇ（０．１ｍｏｌ）、合成例１で得られたジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）５４．５ｇ（０．１５ｍｏｌ）、触媒として無水塩化マグネシウム０．８ｇ（０．００８ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら１５５℃まで徐々に加熱昇温し１５５℃に到達してから１８時間反応させ発生する塩化水素を捕集した。６０℃に冷却後、酢酸エチル６０ｇを加え、酸洗い、中和、２回の水洗いを行い、溶媒除去を行って化合物Ｂ５１．２ｇを得た。
化合物Ｂは、水酸基当量４１２ｇ／ｅｑ、リン含有率が８．４質量％であった。更に、ＧＰＣによりフロログルシノールの水酸基の１つがジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）と反応した化合物（１置換体）を３９．５モル％、水酸基の２つが反応した化合物（２置換体）を３４．０モル％、水酸基の３つと反応した化合物（３置換体）を２５．０モル％、フロログルシノールを１．５モル％含むことを確認した。
撹拌機、温度計、塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた２００ｍＬの４つ口フラスコに、メシチレン１１０．９ｇ、フロログルシノール１２．６ｇ（０．１ｍｏｌ）、合成例１で得られたジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）５４．５ｇ（０．１５ｍｏｌ）、触媒として無水塩化マグネシウム０．８ｇ（０．００８ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら１５５℃まで徐々に加熱昇温し１５５℃に到達してから１８時間反応させ発生する塩化水素を捕集した。６０℃に冷却後、酢酸エチル６０ｇを加え、酸洗い、中和、２回の水洗いを行い、溶媒除去を行って化合物Ｂ５１．２ｇを得た。
化合物Ｂは、水酸基当量４１２ｇ／ｅｑ、リン含有率が８．４質量％であった。更に、ＧＰＣによりフロログルシノールの水酸基の１つがジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）と反応した化合物（１置換体）を３９．５モル％、水酸基の２つが反応した化合物（２置換体）を３４．０モル％、水酸基の３つと反応した化合物（３置換体）を２５．０モル％、フロログルシノールを１．５モル％含むことを確認した。
（合成例４）リン含有フェノール化合物Ｃの合成
撹拌機、温度計、塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた３００ｍＬの４つ口フラスコに、メシチレン２４９．５ｇ、フロログルシノール１２．６ｇ（０．１ｍｏｌ）、合成例１で得られたジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）８７．２ｇ（０．２４ｍｏｌ）、触媒として無水塩化マグネシウム１．２ｇ（０．０１２ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら１５５℃まで徐々に加熱昇温し１５５℃に到達してから１８時間反応させ発生する塩化水素を捕集した。６０℃に冷却後、酢酸エチル６０ｇを加え、酸洗い、中和、２回の水洗いを行い、溶媒除去を行って化合物Ｃ５１．２ｇを得た。
化合物Ｃは、水酸基当量５８７ｇ／ｅｑ、リン含有率が９．０質量％であった。更に、ＧＰＣによりフロログルシノールの水酸基の１つがジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）と反応した化合物（１置換体）を２５モル％、水酸基の２つが反応した化合物（２置換体）を３５モル％、水酸基の３つと反応した化合物（３置換体）を４０モル％含むことを確認した。
撹拌機、温度計、塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた３００ｍＬの４つ口フラスコに、メシチレン２４９．５ｇ、フロログルシノール１２．６ｇ（０．１ｍｏｌ）、合成例１で得られたジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）８７．２ｇ（０．２４ｍｏｌ）、触媒として無水塩化マグネシウム１．２ｇ（０．０１２ｍｏｌ）を充填した。得られた混合溶液を撹拌しながら１５５℃まで徐々に加熱昇温し１５５℃に到達してから１８時間反応させ発生する塩化水素を捕集した。６０℃に冷却後、酢酸エチル６０ｇを加え、酸洗い、中和、２回の水洗いを行い、溶媒除去を行って化合物Ｃ５１．２ｇを得た。
化合物Ｃは、水酸基当量５８７ｇ／ｅｑ、リン含有率が９．０質量％であった。更に、ＧＰＣによりフロログルシノールの水酸基の１つがジ２，６－キシリルホスホロクロリデート（ＤＸＰＣ）と反応した化合物（１置換体）を２５モル％、水酸基の２つが反応した化合物（２置換体）を３５モル％、水酸基の３つと反応した化合物（３置換体）を４０モル％含むことを確認した。
（実施例１）リン含有メタクリロイル化合物Ａの合成
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ａ１００．０ｇ、テトラヒドロフラン１５０．０ｇ、トリエチルアミン１６１．９ｇ、４－ジメチルアミノピリジン６．０ｇを仕込み、室温で溶解した。窒素雰囲気化で、メタクリル酸無水物（下記構造式）１５１．０ｇ
を１時間かけて滴下し、更に５０℃で６時間反応を継続した。
続いて、反応液を濃縮し、トルエン３６０．４ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ａの５０％トルエン溶液２４７．１ｇを得た。
リン含有メタクリロイル化合物Ａのリン含有率は５．０％であった。更に、ＧＰＣによりリン含有フェノール化合物Ａの１置換体の２つの水酸基がメタクリロイルオキシ基に置換された成分を６９モル％、２置換体の１つの水酸基がメタクリロイルオキシ基に置換された成分を１０モル％、３置換体の成分を３モル％、フロログルシノールの３つの水酸基がメタクリロイルオキシ基に置換された成分を１８モル％含むことを確認した。
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ａ１００．０ｇ、テトラヒドロフラン１５０．０ｇ、トリエチルアミン１６１．９ｇ、４－ジメチルアミノピリジン６．０ｇを仕込み、室温で溶解した。窒素雰囲気化で、メタクリル酸無水物（下記構造式）１５１．０ｇ
続いて、反応液を濃縮し、トルエン３６０．４ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ａの５０％トルエン溶液２４７．１ｇを得た。
リン含有メタクリロイル化合物Ａのリン含有率は５．０％であった。更に、ＧＰＣによりリン含有フェノール化合物Ａの１置換体の２つの水酸基がメタクリロイルオキシ基に置換された成分を６９モル％、２置換体の１つの水酸基がメタクリロイルオキシ基に置換された成分を１０モル％、３置換体の成分を３モル％、フロログルシノールの３つの水酸基がメタクリロイルオキシ基に置換された成分を１８モル％含むことを確認した。
（実施例２）リン含有メタクリロイル化合物Ｂの合成
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ｂ１００．０ｇ、テトラヒドロフラン１５０．０ｇ、トリエチルアミン３４．５ｇ、４－ジメチルアミノピリジン１．３ｇを仕込み、室温で溶解した。窒素雰囲気化で、メタクリル酸無水物３２．２ｇを１時間かけて滴下し、更に５０℃で６時間反応を継続した。
続いて、反応液を濃縮し、トルエン３６０．４ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ｂの５０％トルエン溶液１８６．４ｇを得た。
リン含有メタクリロイル化合物Ｂのリン含有率は７．２％であった。更に、ＧＰＣによりリン含有フェノール化合物Ｂの１置換体の２つの水酸基がメタクリロイルオキシ基に置換された成分を４０モル％、２置換体の１つの水酸基がメタクリロイルオキシ基に置換された成分を３４モル％、３置換体の成分を２４％、フロログルシノールの３つの水酸基がメタクリロイルオキシ基に置換された成分を２モル％含むことを確認した。
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ｂ１００．０ｇ、テトラヒドロフラン１５０．０ｇ、トリエチルアミン３４．５ｇ、４－ジメチルアミノピリジン１．３ｇを仕込み、室温で溶解した。窒素雰囲気化で、メタクリル酸無水物３２．２ｇを１時間かけて滴下し、更に５０℃で６時間反応を継続した。
続いて、反応液を濃縮し、トルエン３６０．４ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ｂの５０％トルエン溶液１８６．４ｇを得た。
リン含有メタクリロイル化合物Ｂのリン含有率は７．２％であった。更に、ＧＰＣによりリン含有フェノール化合物Ｂの１置換体の２つの水酸基がメタクリロイルオキシ基に置換された成分を４０モル％、２置換体の１つの水酸基がメタクリロイルオキシ基に置換された成分を３４モル％、３置換体の成分を２４％、フロログルシノールの３つの水酸基がメタクリロイルオキシ基に置換された成分を２モル％含むことを確認した。
（実施例３）リン含有メタクリロイル化合物Ｃの合成
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ｃ１００．０ｇ、テトラヒドロフラン１５０．０ｇ、トリエチルアミン４９．１ｇ、４－ジメチルアミノピリジン１．８ｇを仕込み、室温で溶解した。窒素雰囲気化で、メタクリル酸無水物４５．８ｇを１時間かけて滴下し、更に５０℃で６時間反応を継続した。
続いて、反応液を濃縮し、トルエン２６０．４ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ｃの５０％トルエン溶液１７８．６ｇを得た。
リン含有メタクリロイル化合物Ｃのリン含有率は８．２％であった。更に、ＧＰＣによりリン含有フェノール化合物Ｃの１置換体の２つの水酸基がメタクリロイルオキシ基に置換された成分を２５モル％、２置換体の１つの水酸基がメタクリロイルオキシ基に置換された成分を３５モル％、３置換体の成分を４０モル％含むことを確認した。
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ｃ１００．０ｇ、テトラヒドロフラン１５０．０ｇ、トリエチルアミン４９．１ｇ、４－ジメチルアミノピリジン１．８ｇを仕込み、室温で溶解した。窒素雰囲気化で、メタクリル酸無水物４５．８ｇを１時間かけて滴下し、更に５０℃で６時間反応を継続した。
続いて、反応液を濃縮し、トルエン２６０．４ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ｃの５０％トルエン溶液１７８．６ｇを得た。
リン含有メタクリロイル化合物Ｃのリン含有率は８．２％であった。更に、ＧＰＣによりリン含有フェノール化合物Ｃの１置換体の２つの水酸基がメタクリロイルオキシ基に置換された成分を２５モル％、２置換体の１つの水酸基がメタクリロイルオキシ基に置換された成分を３５モル％、３置換体の成分を４０モル％含むことを確認した。
（比較合成例）リン含有メタクリロイル化合物Ｄの合成
特開２０２２－１６４２２に記載の方法に従って合成した。具体的には、撹拌機、温度計および塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた容量２リットルの４つ口フラスコに、オキシ塩化リン１５００ｇ、２，６-ジメチルフェノール６１１ｇ、触媒としての塩化マグネシウム１．２ｇ充填した。
得られた混合溶液を撹拌しながら約３時間かけて温度１１０℃まで徐々に加熱昇温して反応させ、発生する塩化水素（塩酸ガス）を水スクラバーで回収した。その後、１２０℃でフラスコ内の圧力を徐々に１２ｋＰａまで減圧し、未反応のオキシ塩化リンおよびフェノール、副生する塩化水素を除去し、モノ２，６-ジメチルフェニルホスホロジクロリデート１２００ｇを得た。
撹拌機、温度計、滴下ロートおよびコンデンサーを備えた容量２リットルの４つ口フラスコに、２，３，５－トリメチルハイドロキノン３２０ｇ、塩化水素捕捉剤としてピリジン１３５ｇ、溶剤としてトルエン２００ｇを充填した。また、滴下ロートに上記モノ２，６-ジメチルフェニルホスホロジクロリデート２０３ｇを充填した。
４つ口フラスコ中の混合溶液を撹拌しながら温度２０℃まで加熱し、同温度（２０℃）で維持しながら、滴下ロート中のモノ２，６-ジメチルフェニルホスホロジクロリデートを２時間かけて滴下した。滴下終了後、６５℃まで加熱し、５時間撹拌し反応生成物を得た。得られた反応生成物を希塩酸および水で洗浄後、温度１５０℃まで加熱し、２ｋＰａまで減圧して水、トルエン、低沸分を留去し、常温まで冷却することで黒褐色固体のリン含有フェノール化合物Ｄ ３３０ｇを得た。
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ｄ２００ｇ、テトラヒドロフラン１３３．２ｇ、トリエチルアミン１９．５ｇ、を仕込み、溶解後に５℃以下に氷浴で冷却した。窒素雰囲気化で塩化メタクリロイル７８．０ｇを１時間かけて滴下し、更に２時間反応を継続した。
続いて、反応液を濃縮し、トルエン６０１．６ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ｄのトルエン溶液２２７．６ｇを得た。
得られたリン含有メタクリロイル化合物Ｄのリン含有率は、５．２％であった。
特開２０２２－１６４２２に記載の方法に従って合成した。具体的には、撹拌機、温度計および塩酸回収装置（水スクラバーを連結したコンデンサー）を備えた容量２リットルの４つ口フラスコに、オキシ塩化リン１５００ｇ、２，６-ジメチルフェノール６１１ｇ、触媒としての塩化マグネシウム１．２ｇ充填した。
得られた混合溶液を撹拌しながら約３時間かけて温度１１０℃まで徐々に加熱昇温して反応させ、発生する塩化水素（塩酸ガス）を水スクラバーで回収した。その後、１２０℃でフラスコ内の圧力を徐々に１２ｋＰａまで減圧し、未反応のオキシ塩化リンおよびフェノール、副生する塩化水素を除去し、モノ２，６-ジメチルフェニルホスホロジクロリデート１２００ｇを得た。
撹拌機、温度計、滴下ロートおよびコンデンサーを備えた容量２リットルの４つ口フラスコに、２，３，５－トリメチルハイドロキノン３２０ｇ、塩化水素捕捉剤としてピリジン１３５ｇ、溶剤としてトルエン２００ｇを充填した。また、滴下ロートに上記モノ２，６-ジメチルフェニルホスホロジクロリデート２０３ｇを充填した。
４つ口フラスコ中の混合溶液を撹拌しながら温度２０℃まで加熱し、同温度（２０℃）で維持しながら、滴下ロート中のモノ２，６-ジメチルフェニルホスホロジクロリデートを２時間かけて滴下した。滴下終了後、６５℃まで加熱し、５時間撹拌し反応生成物を得た。得られた反応生成物を希塩酸および水で洗浄後、温度１５０℃まで加熱し、２ｋＰａまで減圧して水、トルエン、低沸分を留去し、常温まで冷却することで黒褐色固体のリン含有フェノール化合物Ｄ ３３０ｇを得た。
攪拌装置、温度計、冷却管、滴下ロートを備えたガラス製セパラブルフラスコに、リン含有フェノール化合物Ｄ２００ｇ、テトラヒドロフラン１３３．２ｇ、トリエチルアミン１９．５ｇ、を仕込み、溶解後に５℃以下に氷浴で冷却した。窒素雰囲気化で塩化メタクリロイル７８．０ｇを１時間かけて滴下し、更に２時間反応を継続した。
続いて、反応液を濃縮し、トルエン６０１．６ｇに溶解後、塩酸、炭酸ナトリウム水溶液、水の順で洗浄した。水による洗浄後、脱水して、ろ過、更に溶媒を濃縮することで、リン含有メタクリロイル化合物Ｄのトルエン溶液２２７．６ｇを得た。
得られたリン含有メタクリロイル化合物Ｄのリン含有率は、５．２％であった。
実施例４～９、比較例１～５
＜硬化性樹脂組成物の調整及び硬化物の作成＞
各種成分を表１の割合で配合することでワニスを作成し、ペットフィルム上に塗布、１３０℃オーブンで５分乾燥させ樹脂組成物のフィルムを作成した。次に、このフィルムを粉砕することで、樹脂組成物の粉末を得た。更に、この粉末をステンレス製の鏡面板にスペーサーと伴に挟み、真空オーブンを用いて２１０℃９０分間で成形することで硬化物のサンプルを得た。
＜難燃試験片の作成＞
各種成分を表１の割合で配合することでワニスを作成し、この樹脂ワニスをガラスクロス（日東紡績株式会社製；７６２８タイプ；品番 Ｈ２５８）に含浸させた後、１３０℃で５分間加熱することにより乾燥し、プリプレグを得た。
得られたプリプレグ８枚と、上下に銅箔（三井金属鉱業株式会社製、３ＥＣ－ＩＩＩ、厚み３５μｍ）を重ね、１３０℃×１５分＋１９０℃×８０分の温度条件で２ＭＰａの真空プレスを行い、１．６ｍｍ厚の積層板を得た。銅箔をエッチングし、カットすることで、難燃性試験片を得た。
＜硬化性樹脂組成物の調整及び硬化物の作成＞
各種成分を表１の割合で配合することでワニスを作成し、ペットフィルム上に塗布、１３０℃オーブンで５分乾燥させ樹脂組成物のフィルムを作成した。次に、このフィルムを粉砕することで、樹脂組成物の粉末を得た。更に、この粉末をステンレス製の鏡面板にスペーサーと伴に挟み、真空オーブンを用いて２１０℃９０分間で成形することで硬化物のサンプルを得た。
＜難燃試験片の作成＞
各種成分を表１の割合で配合することでワニスを作成し、この樹脂ワニスをガラスクロス（日東紡績株式会社製；７６２８タイプ；品番 Ｈ２５８）に含浸させた後、１３０℃で５分間加熱することにより乾燥し、プリプレグを得た。
得られたプリプレグ８枚と、上下に銅箔（三井金属鉱業株式会社製、３ＥＣ－ＩＩＩ、厚み３５μｍ）を重ね、１３０℃×１５分＋１９０℃×８０分の温度条件で２ＭＰａの真空プレスを行い、１．６ｍｍ厚の積層板を得た。銅箔をエッチングし、カットすることで、難燃性試験片を得た。
ＯＰＥ－２Ｓｔ：三菱ガス化学製株式会社製 末端スチリル変性ポリフェニレンエーテル樹脂
ＰＸ－２００：大八化学工業株式会社製 芳香族縮合リン酸エステル、リン含有率９．０％
パーブチルＰ：日油社製１，３－ビス（ブチルパーオキシイソプロピル）ベンゼン
ＰＸ－２００：大八化学工業株式会社製 芳香族縮合リン酸エステル、リン含有率９．０％
パーブチルＰ：日油社製１，３－ビス（ブチルパーオキシイソプロピル）ベンゼン
その結果を表１に示した。
本発明のリン含有（メタ）アクリロイル化合物は、電気・電子製品やOA機器、通信機器、建材等に使用されるプラスチック材料の難燃化に有用であり、特に電子機器の情報処理量増大に伴う高周波化における伝送損失低減の反応型リン系難燃剤として有用である。
Claims (8)
- 一般式（１）で表されるリン含有（メタ）アクリロイル化合物。
- Ａｒが置換基を有していても良いベンゼン環、ナフタレン環、ビフェニル環およびアントラセン環から選択される芳香族環基である請求項１に記載のリン含有（メタ）アクリロイル化合物。
- Ａｒがベンゼン環である請求項１に記載のリン含有（メタ）アクリロイル化合物。
- ｍが３である請求項１に記載のリン含有（メタ）アクリロイル化合物。
- Ｒ１の２つが一般式（３）で表される置換基であり、１つが一般式（２）で表される置換基である化合物を１０～８０モル％、Ｒ１の１つが一般式（３）で表される置換基であり、２つが一般式（２）で表される置換基である化合物を５～５０モル％、およびＲ１の３つが一般式（２）で表される置換基である化合物を１～５０モル％含むことを特徴とする請求項１に記載のリン含有（メタ）アクリロイル化合物。
- 一般式（４）で表されるリン含有フェノール化合物と（メタ）アクリル酸、ハロゲン化（メタ）アクリロイルまたは（メタ）アクリル酸無水物の一種以上を反応させることを特徴とする請求項１～５のいずれか１項に記載のリン含有（メタ）アクリロイル化合物の製造方法。
- 請求項１～５のいずれか１項に記載のリン含有（メタ）アクリロイル化合物に熱硬化性樹脂又は熱可塑性樹脂の一種以上を配合してなることを特徴とする難燃性樹脂組成物。
- 請求項７に記載の難燃性樹脂組成物を使用して得られる電子回路基板用積層板。