JP2022010754A - ウレタン粘着剤組成物及びこれを塗布した粘着フィルム - Google Patents
ウレタン粘着剤組成物及びこれを塗布した粘着フィルム Download PDFInfo
- Publication number
- JP2022010754A JP2022010754A JP2020111470A JP2020111470A JP2022010754A JP 2022010754 A JP2022010754 A JP 2022010754A JP 2020111470 A JP2020111470 A JP 2020111470A JP 2020111470 A JP2020111470 A JP 2020111470A JP 2022010754 A JP2022010754 A JP 2022010754A
- Authority
- JP
- Japan
- Prior art keywords
- sensitive adhesive
- pressure
- urethane
- adhesive composition
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(a-1)としてPTMG2000(商品名:三菱ケミカル社製、Mn2,000)を、(a-2)としてAM302(商品名:ADEKA社製、Mn3,000、プロピレンオキシ基含有)を、(b-1)としてHDIを、触媒としてジメチル[ビス(ネオデカノイルオキシ)]スタンナンを表1に記載した配合量用い、窒素還流下で75℃4時間反応させて(C)を調製した。なお触媒の配合量はは(A)に対し0.03重量%とした。その後(C)にコロネートHX(商品名:東ソー社製、HDIのイソシアヌレート体)を表1記載の配合量で混合し、実施例1のウレタン粘着剤組成物を調製した。
実施例1で用いた材料の他、(a-1)としてPTMG3000(商品名:三菱ケミカル社製、Mn3,000)及びPTMG650(商品名:三菱ケミカル社製、Mn650)を、(a-2)としてG3000B(商品名:ADEKA社製、Mn3,000、プロピレンオキシ基含有)を、(a-3)としてPR3007(商品名:ADEKA社製、Mn3,000、プロピレンオキシ基含有)及びP3000(商品名:ADEKA社製、Mn3,000、プロピレンオキシ基含有)を表1に記載した配合量用い、実施例1と同様に実施例2~9のウレタン粘着剤組成物を調製した。
実施例で用いた材料の他、(a-2)としてG3308(商品名:ADEKA社製、Mn3,400、プロピレンオキシ基含有)及びプレミノール7001K(商品名:AGC社製、Mn6,000、プロピレンオキシ基含有)を、(a-3)としてPEG2000(商品名:三洋化成社製、Mn2,000、ポリエチレングリコール、プロピレンオキシ基非含有)及びプレミノール4013F(商品名:AGC社製、Mn12,000、プロピレンオキシ基含有)を表2に記載した配合量用い、実施例1と同様に比較例1~9のウレタン粘着剤組成物を調製した。
上記ウレタン粘着剤組成物100重量部に酢酸エチル100重量部を配合して塗工液とし、PETフィルムTA063(商品名:東洋紡社製、厚さ50μm)に、乾燥後の層厚が25μmとなるように塗布し、120℃で180秒乾燥して溶剤を揮発させ、その後離型フィルムSPPET5001BU(商品名:パナック社製、厚み50μm)を貼着し、40℃で72時間養生して粘着フィルムを作成した。
Claims (5)
- ポリテトラメチレングリコール(a-1)と3官能ポリエーテルポリオール(a-2)を少なくとも含むポリエーテルポリオール(A)と2官能イソシアネート(b-1)との反応物であるポリウレタンポリオール(C)と、多官能イソシアネート(b-2)から成り、ポリエーテルポリオール(A)のOH基と、(b-1)と(b-2)のNCO基モル数合計の比がNCO基/OH基=1.1~1.8であることを特徴とするウレタン粘着剤組成物。
- 前記(A)における(a-1)の比率が5~60重量%であり、(a-2)の比率が20~60重量%であることを特徴とする請求項1記載のウレタン粘着剤組成物。
- 前記(A)が更に2官能ポリエーテルポリオール(a-3)を含む(但し(a-1)を除く)ことを特徴とする請求項1又は2いずれか記載のウレタン粘着剤組成物。
- 前記(b-2)が2官能イソシアネートのイソシアヌレート体であることを特徴とする請求項1~3いずれか記載のウレタン粘着剤組成物。
- 前記請求項1~4いずれか記載のウレタン粘着剤からなるウレタン粘着層をベースフィルムの少なくとも片面に有する粘着フィルム。