JP2021509155A - 鋳鉄接種剤及び鋳鉄接種剤の製造方法 - Google Patents
鋳鉄接種剤及び鋳鉄接種剤の製造方法 Download PDFInfo
- Publication number
- JP2021509155A JP2021509155A JP2020536542A JP2020536542A JP2021509155A JP 2021509155 A JP2021509155 A JP 2021509155A JP 2020536542 A JP2020536542 A JP 2020536542A JP 2020536542 A JP2020536542 A JP 2020536542A JP 2021509155 A JP2021509155 A JP 2021509155A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- fine particles
- mixture
- fes
- fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
タンディッシュカバー処理レードル中の1.05重量%のMgFeSiノジュール化合金を添加することによりマグネシウムで処理した、275kgの溶融鋳鉄の1つのレードルから3回の接種試験を実施した。0.9重量%のスチールチップをカバーとして使用した。MgFeSiノジュール化合金は、以下の組成を有していた:46.2重量%のSi、5.85重量%のMg、1.02重量%のCa、0.92重量%のRE、0.7重量4%のAl、残部の通常量の鉄及び不可避不純物。
タンディッシュカバー処理レードル中の1.2〜1.25重量%のMgFeSiノジュール化合金を添加することによってマグネシウムで処理した、275kgの溶融鋳鉄の1つのレードルから2つの接種試験を実施した。0.9重量%のスチールチップをカバーとして使用した。MgFeSiノジュール化合金は、以下の組成を有していた:46重量%のSi、4.33重量%のMg、0.69重量%のCa、0.44重量%のRE、0.44重量%のAl、残部の通常量の鉄及び不可避不純物である。
タンディッシュカバー処理レードル中の1.25重量%のMgFeSiノジュール化合金を添加することによってマグネシウムで処理した、275kgの溶融鋳鉄の1つのレードルから2つの接種試験を実施した。MgFeSiノジュール化合金は、以下の組成を有していた:46重量%のSi、4.33重量%のMg、0.69重量%のCa、0.44重量%のRE、0.44重量%のAl、残部は通常量の鉄及び不可避不純物である。
溶融物275kgを製造し、タンディッシュカバーレードル中、1.20〜1.25重量%のMgFeSiノジュラライザーで処理した。MgFeSiノジュール化合金は、以下の組成を有していた:4.33重量%のMg、0.69重量%のCa、0.44重量%のRE、0.44重量%のAl、46重量%のSi、残部の通常量の鉄及び不可避不純物。0.7重量%のスチールチップをカバーとして使用した。全ての接種物の添加率は、各注ぎレードルに添加された0.2重量%であった。ノジュラライザー処理温度は1500℃であり、注ぎ温度は1373〜1353℃であった。注ぎレードルを満たしてから注ぐまでの保持時間は、全ての試験について1分であった。引張サンプルを、標準的な鋳型でΦ28mm鋳造し、標準的な実践に従って切断及び調製した後、自動画像解析ソフトウェアを用いて評価した。
Claims (19)
- 球状黒鉛を有する鋳鉄の製造のための接種剤であって、前記接種剤が、
40〜80重量%のSi、
0.02〜8重量%のCa、
0〜5重量%のSr、
0〜12重量%のBa、
0〜15重量%の希土類金属、
0〜5重量%のMg、
0.05〜5重量%のAl、
0〜10重量%のMn、
0〜10重量%のTi、
0〜10重量%のZr、
残部の通常量のFe及び不可避不純物
からなる微粒子フェロシリコン合金を含み、
前記接種剤が、更に、接種剤の総重量に基づいて、
0.1〜15重量%の微粒子Sb2O3、並びに0.1〜15重量%の微粒子Bi2O3、0.1〜5重量%の、微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、又は0.1〜5重量%の、微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つを含有する、接種剤。 - 前記フェロシリコン合金が、45〜60重量%のSiを含む、請求項1に記載の接種剤。
- 前記フェロシリコン合金が、60〜80重量%のSiを含む、請求項1に記載の接種剤。
- 前記希土類金属が、Ce、La、Y及び/又はミッシュメタルを含む、請求項1〜3のいずれか一項に記載の接種剤。
- 0.5〜8重量%の微粒子Sb2O3を含む、請求項1〜4のいずれか一項に記載の接種剤。
- 0.1〜10%の微粒子Bi2O3を含む、請求項1〜5のいずれか一項に記載の接種剤。
- 0.5〜3%の、微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は0.5〜3%の、微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物を含む、請求項1〜6のいずれか一項に記載の接種剤。
- 前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つの総量が、前記接種剤の総重量に基づいて最大で20重量%である、請求項1〜7のいずれか一項に記載の接種剤。
- 前記微粒子フェロシリコン合金及び前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つの、ブレンド又は物理的混合物の形態である、請求項1〜8のいずれか一項に記載の接種剤。
- 前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つが、微粒子フェロシリコン系合金上のコーティング化合物として存在する、請求項1〜9のいずれか一項に記載の接種剤。
- 前記微粒子フェロシリコン合金及び前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つの、混合物から作製される凝集体の形態である、請求項1〜10のいずれか一項に記載の接種剤。
- 前記微粒子フェロシリコン合金及び前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つの、混合物から作製されるブリケットの形態である、請求項1〜11のいずれか一項に記載の接種剤。
- 微粒子フェロシリコン系合金及び前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つが、別個ではあるが同時に、液体鋳鉄に添加される、請求項1〜12のいずれか一項に記載の接種剤。
- 請求項1〜13に記載の接種剤を製造する方法であって、
40〜80重量%のSi、
0.02〜8重量%のCa、
0〜5重量%のSr、
0〜12重量%のBa、
0〜15重量%の希土類金属、
0〜5重量%のMg、
0.05〜5重量%のAl、
0〜10重量%のMn、
0〜10重量%のTi、
0〜10重量%のZr、
残部の通常量のFe及び不可避不純物
からなる微粒子ベース合金を準備することと、
前記微粒子ベースに、接種剤の総重量に基づいて、0.1〜15重量%の微粒子Sb2O3、並びに0.1〜15重量%の微粒子Bi2O3、0.1〜5重量%の、微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、又は0.1〜5重量%の、微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つを添加して前記接種剤を製造することと
を含む、方法。 - 前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つが、前記微粒子ベース合金と混合又はブレンドされる、請求項14に記載の方法。
- 前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つが、前記微粒子ベース合金と混合される前に、混合される、請求項14に記載の方法。
- 球状黒鉛を有する鋳鉄の製造における請求項1〜13に記載の接種剤の、鋳造前、鋳造と同時、又は鋳型内接種剤として、前記接種剤を前記鋳鉄溶融物に添加することによる、使用。
- 微粒子フェロシリコン系合金及び前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つが、機械的混合物又はブレンドとして、前記鋳鉄溶融物に添加される、請求項17に記載の使用。
- 微粒子フェロシリコン系合金及び前記微粒子Sb2O3、並びに微粒子Bi2O3、及び/又は微粒子Fe3O4、Fe2O3、FeOのうちの1つ以上、若しくはこれらの混合物、及び/又は微粒子FeS、FeS2、Fe3S4のうちの1つ以上、若しくはこれらの混合物のうちの少なくとも1つが、別個ではあるが同時に、前記鋳鉄溶融物に添加される、請求項17に記載の使用。