SU1047969A1 - Модификатор ковкого чугуна - Google Patents
Модификатор ковкого чугуна Download PDFInfo
- Publication number
- SU1047969A1 SU1047969A1 SU792791984A SU2791984A SU1047969A1 SU 1047969 A1 SU1047969 A1 SU 1047969A1 SU 792791984 A SU792791984 A SU 792791984A SU 2791984 A SU2791984 A SU 2791984A SU 1047969 A1 SU1047969 A1 SU 1047969A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- bismuth
- sulfur
- modifier
- iron
- ductile iron
- Prior art date
Abstract
I. МОДИФИКАТОР КОВКОГО ЧУГУНА , содержащий висмут, отличающийс тем, что, с целью повышени технологичности ввода/ эффективности действи и экономии вис- мута , в его состав дополнительно введена сера при следующем соотношении компонентов, мас.%: Висмут80-85 Сера15-25 2. Модификатор по п. 1, отличающийс тем, что в качестве серу-висмутсодержащего вещества использован сульфид висмута или серу-висмутсодержаща руда.
Description
СО СП Изобретение относитс к литейном производству, в частности, к получе нию ковкого чугуна. Известно использование висмута в качестве модификатора ковкого чугуна. Высока отбеливающа способность висмута сочетаетс с незначительным замедлением как первой, так и второ стадий графитизации, что положитель но отличает действие висмута от дей стви других модификаторов 1. Однако применение висмута в качестве модификатора имеет р д существенных недостатков. Плоха смешиваемость жидкого чугуна и висмута вызывает повышенное испарение и угар-последнего, достигающий 60-70%, и, как следствие загр знение цеховой атмосферы летучими соединени ми висмута. Цель изобретени - повышение те нелогичности ввода, эффективности действи и экономии висмута. Поставленна , цель достигаетс тем, что в модификатор ковкого чу:гуна , содержащий висмут, дополнител но введена сера при следующем соотношении компонентов, мас.%: Висмут80-85 Сера15-20 В качестве серу-висмутсодержащего вещества возможно использовать сульфид висмута или серу-висмутсодержащую руду. Применение модификатора указанного состава обусловлено тем, что в нем образуетс соединение , ,т:емпература плавлени которого составл ет 775С, что зка-:--;тельно выше, чем у висмута () . Тем самым обеспечиваетс резкое снижение упругости пара висмута, меньшее его испарение и, следовательно, лучшее усвоение, повышение эффективности действи модификатора и упроьчаетс технологи ввода модификатора s жидкий чугун. Дл проверки эффективно:.,;/.-; действи модификатора и оцену.и ..пнчины его угара в сравнении с чистым висмутом провод т опытное модифицирование ваграночного чугуна сплавами висмута с серой и чистым висмутом, Исходный чугун содержит 2,-90-2,99% углерода и 1,45-1,52% кремни , Результаты испытаний приведены в табл. 1 и 2в При использовании предлагаемого модификатора угар висмута уменьшаетс в 2 раза (табл, l), а степень отбела отливок значительно выше, чем при модифицировании чугуна только висмутом (табл, 2), Применение изобретени позвол ет уменьшить расход модификатора и затраты на производство ковкого чугуна, Таблица 1
0,004
Висмут
Количество вводит МОго модификатора,
Модификатор в %
0,001
Висмут 0,002
67,5
0,0013
Таблица 2
Степень отбела пробы
Серый чугун
Поверхностный слой - полный отбел . Переходна зона - половинчатый чугун, сердцевина сера 80% Bi-0,001 20% S 0,002 85% BI0,001 15% S 0,002 83% ,001 17%.S 0,002
10479694
Продолжек е гебл, 2 Поверхностный слой - от бел. Переходна зона - половинчатый чугун, сердцевина сера . Сквозной отвел с редкими отдельными п тнами графита в центре пробы Наружный слой - сквозной отбел. Сердцевина - половинчатый чуСквозной отбел с небольшими п тнами половинчатого чугуна в центре . . Поверхностный отбел. Переходна зона-со структурой половинчатого чугуна, сердцевина сера . Сквозной отбел.
Claims (2)
1. МОДИФИКАТОР КОВКОГО ЧУГУНА, содержащий висмут, отличающий ся тем, что, с целью повышения технологичности ввода, эффективности действия и экономии вис·? мута, в его состав дополнительно введена сера при следующем соотношении компонентов, мас.%:
Висмут 80-85
Сера 15-25
2. Модификатор по π. 1, отличающийся тем, что в качестве серу-висмутсодержащего вещества использован сульфид висмута 9 или серу-висмутсодержащая руда.
О se ω
10^7969