JP2021155230A - コンクリート組成物及びモルタルコンクリート - Google Patents
コンクリート組成物及びモルタルコンクリート Download PDFInfo
- Publication number
- JP2021155230A JP2021155230A JP2020054092A JP2020054092A JP2021155230A JP 2021155230 A JP2021155230 A JP 2021155230A JP 2020054092 A JP2020054092 A JP 2020054092A JP 2020054092 A JP2020054092 A JP 2020054092A JP 2021155230 A JP2021155230 A JP 2021155230A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- aggregate
- parts
- cement
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
[1]セメント、ポゾラン物質、粒径2.5mm未満の骨材A及び粒径2.5mm以上10mm以下の骨材Bを含み、ポゾラン物質の含有量が、セメント100質量部に対し、3〜34質量部であり、骨材A及び骨材Bの合計の含有量が、セメント100質量部に対し、110〜390質量部であり、骨材A及び骨材Bの合計の含有量に対する骨材Bの含有量の質量比([骨材Bの含有量(質量部)]/[骨材A及び骨材Bの合計の含有量(質量部)])が、0.03〜0.44である、コンクリート組成物。
[2]骨材Aの含有量が、セメント100質量部に対し、100〜340質量部である、[1]に記載のコンクリート組成物。
[3]骨材Bの含有量が、セメント100質量部に対し、10〜140質量部である、[1]又は[2]に記載のコンクリート組成物。
[4]膨張材を更に含む、[1]〜[3]のいずれかに記載のコンクリート組成物。
[5][1]〜[4]のいずれかに記載のコンクリート組成物と水とを含み、水の含有量が、セメント100質量部に対し、25〜45質量部である、モルタルコンクリート。
セメント:速硬性セメント(略号C)
骨材:珪砂(最大粒径2.5mm未満、粗粒率2.4、略号S)
骨材:豆砂利(粒径2.5mm以上8mm以下、粗粒率5.9、略号G1)
骨材:砕石(粒径5mm以上20mm以下、粗粒率6.6、略号G2)
ポゾラン物質:シリカフューム(BET比表面積10.2m2/g、略号SF)
膨張材:生石灰系膨張材
減水剤:ナフタレンスルホン酸系減水剤
凝結遅延剤:クエン酸塩
セメント100質量部に対し、骨材及びポゾラン物質を表1に示す割合とし、膨張材を2質量部、減水剤を1質量部、凝結遅延剤を1質量部として配合設計した。
20℃環境下において、セメント100質量部に対し、上水道水36質量部を10Lの円筒容器に添加し、表1で配合設計したコンクリート組成物の各材料を添加し、ハンドミキサーで60秒混練してモルタルコンクリートを約3L作製した。
各項目について、以下の方法で評価した。評価結果を表1に示す。
1)圧縮強度
土木学会基準JSCE−G 5050−2010「円柱供試体を用いたモルタルまたはセメントペーストの圧縮強度試験方法(案)」に準じて、材齢3時間及び56日における圧縮強度を測定した。供試体の寸法は、直径50mm、高さ100mmとした。材齢56日の供試体は翌日に脱型した後、材齢日まで水中で養生した。養生は常に20℃の恒温槽内で行った。
2)施工性
a)軟度
JIS R 5201:2015「セメントの物理試験方法」12.フロー試験に準じて、20℃環境下で測定した。15打フロー値が120〜180mmとなる場合を良好(○)と評価し、それ以外は不良(×)と評価した。
b)ダレ性
型枠(30cm×30cm×3cm)を勾配5%の状態に設置し、モルタルコンクリートを施工した後、コテで均し、モルタルコンクリートのダレ性状を目視観察した。ダレが生じたものを不良(×)と評価し、ダレが生じなかったものを良好(○)と評価した。
c)コテ性状
型枠(30cm×30cm×3cm)にモルタルコンクリートを施工した後、コテで均し、モルタルコンクリートのコテ性状の評価を行った。モルタルコンクリートの施工からコテ均しの仕上げまで時間を要した場合を不良(×)と評価し、時間を要しなかった場合を良好(○)と評価した。
d)薄層性
型枠(30cm×30cm×3cm)にモルタルコンクリートを施工した際、モルタルコンクリート厚さを20mmで施工できる場合を良好(○)と評価し、施工が困難な場合を不良(×)と評価した。
Claims (5)
- セメント、ポゾラン物質、粒径2.5mm未満の骨材A及び粒径2.5mm以上10mm以下の骨材Bを含み、
前記ポゾラン物質の含有量が、前記セメント100質量部に対し、3〜34質量部であり、
前記骨材A及び前記骨材Bの合計の含有量が、前記セメント100質量部に対し、110〜390質量部であり、
前記骨材A及び前記骨材Bの合計の含有量に対する前記骨材Bの含有量の質量比([前記骨材Bの含有量(質量部)]/[前記骨材A及び前記骨材Bの合計の含有量(質量部)])が、0.03〜0.44である、コンクリート組成物。 - 前記骨材Aの含有量が、前記セメント100質量部に対し、100〜340質量部である、請求項1に記載のコンクリート組成物。
- 前記骨材Bの含有量が、前記セメント100質量部に対し、10〜140質量部である、請求項1又は2に記載のコンクリート組成物。
- 膨張材を更に含む、請求項1〜3のいずれか一項に記載のコンクリート組成物。
- 請求項1〜4のいずれか一項に記載のコンクリート組成物と水とを含み、
前記水の含有量が、前記セメント100質量部に対し、25〜45質量部である、モルタルコンクリート。