JP2021130742A - 塩化ビニル樹脂フィルム及び粘着シート - Google Patents
塩化ビニル樹脂フィルム及び粘着シート Download PDFInfo
- Publication number
- JP2021130742A JP2021130742A JP2020025380A JP2020025380A JP2021130742A JP 2021130742 A JP2021130742 A JP 2021130742A JP 2020025380 A JP2020025380 A JP 2020025380A JP 2020025380 A JP2020025380 A JP 2020025380A JP 2021130742 A JP2021130742 A JP 2021130742A
- Authority
- JP
- Japan
- Prior art keywords
- chloride resin
- vinyl chloride
- resin film
- weight
- epoxy group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
上記塩化ビニル樹脂としては、例えば、塩化ビニルの単独重合体、塩化ビニルと共重合可能な他の単量体と塩化ビニルとの共重合体等が挙げられる。上記塩化ビニル樹脂は、印刷適性や視認性、寸法安定性に優れる点から、塩化ビニルの単独重合体が好ましい。
上記エポキシ基含有アクリル樹脂は、エポキシ当量が140以上、170以下であり、かつ重量平均分子量が4万以上、6万以下である。上記エポキシ当量とは、1当量のエポキシ基を含む樹脂の質量である。上記エポキシ当量は、JIS K7236:2001に準拠した方法により測定することができる。エポキシ当量が小さいほど、樹脂に含まれるエポキシ基の量が多いことを表す。本実施形態に係る塩化ビニル樹脂フィルムに含まれるエポキシ基含有アクリル樹脂は、エポキシ当量が170以下と少ない。すなわち、上記エポキシ基含有アクリル樹脂に含まれるエポキシ基の量が多い。そのため、塩素等の塩化ビニル樹脂の分解物をより多くトラップでき、塩化ビニル樹脂フィルムの熱安定性を高めることができる。また、上記エポキシ基含有アクリル樹脂は、熱安定化効果が高いため、添加量が少なくても充分な熱安定性が得られる。例えば、上記エポキシ当量が300程度では、充分な熱安定性を得るために必要なエポキシ基含有アクリル樹脂の添加量が多くなり、塩化ビニル樹脂フィルムの表面にエポキシ基含有アクリル樹脂やその他の配合成分が溶出する噴き出しが発生する。なお、上記エポキシ当量の下限値140は、エポキシ基が一つである場合のエポキシ基含有アクリル樹脂の分子量を基準に設定した値である。
装置:東ソー社製「HLC−8220」
カラム:ミックスカラム(2本連結)
東ソー社製「TSKguardcolumn HHR−H」及び「東ソー社製「TSKgel GMHHR−HHHR−」
移動相:クロロホルム
流速:1.0ml/min
測定温度:40℃
検出器:示差屈折計(RI)
標準サンプル:東ソー社製TSKgel標準ポリスチレン(A−500、A−1000、A−2500、A−5000、F−1、F−2、F−4、F−10、F−20、F−40、F−80、F−128)
上記可塑剤の含有量は、上記塩化ビニル樹脂100重量部に対して、10重量部以上、75重量部以下である。上記可塑剤の含有量が10重量部未満であると、得られる塩化ビニル樹脂フィルムが硬くなり、被着体に貼り付けた際に被着体の表面形状に追従することが困難となる。また、得られる塩化ビニル樹脂フィルムの風合いが悪くなる。上記可塑剤の含有量が75重量部を超えると、得られる塩化ビニル樹脂フィルムが柔らかくなり過ぎ、カレンダー成形した場合にカレンダーロールからの巻き取りが困難となる。上記塩化ビニル樹脂100質量部に対する、上記可塑剤の含有量の好ましい下限は20重量部、好ましい上限は60重量部であり、より好ましい下限は30重量部、より好ましい上限は50重量部である。
本実施形態の粘着シートは、本実施形態の塩化ビニル樹脂フィルムと、粘着剤層とを有する。上記粘着剤層は、特に限定されないが、例えば、アクリル系粘着剤、天然ゴム系粘着剤、シリコーン系粘着剤、ビニルエーテル系粘着剤等を含有するものが挙げられる。上記粘着シートを後述する皮膚貼付用として用いる場合には、皮膚への刺激が少ないことから、上記粘着剤層はアクリル系粘着剤を含有することが好ましい。
平均重合度が1300の塩化ビニル樹脂100重量部に対して、下記表3に示したように、熱安定化剤としてエポキシ基含有アクリル樹脂Aを3重量部、ポリエステル系可塑剤を54重量部、加工助剤、金属石ケン及びポリエステル系オリゴマーを添加し、塩化ビニル樹脂組成物を得た。得られた塩化ビニル樹脂組成物をバンバリーミキサーで溶融混練後、カレンダー成形により、塩化ビニル樹脂フィルムを作製した。
下記表3に示したように塩化ビニル樹脂組成物の材料を変更したことを除いて実施例1と同様にして、実施例2及び3、比較例1〜7に係る塩化ビニル樹脂フィルムをそれぞれ作製した。
実施例及び比較例で調整した塩化ビニル樹脂組成物について、下記の方法により分解時間を測定し、実施例及び比較例で作製した塩化ビニル樹脂フィルムについて、下記の方法により噴き出しの有無を確認した。
混錬・押出成形評価試験装置(株式会社東洋精機製作所製、ラボプラストミル)の測定容器に実施例及び比較例で用いた塩化ビニル樹脂組成物の材料を投入し、190℃、60rpmで装置を回転させ、上記材料が溶解してトルク値が上昇し始めるまでの時間を分解時間とした。上記分解時間が19分以上である場合を適合とした。結果を表3及び図1に示した。図1は、実施例及び比較例に係る塩化ビニル樹脂フィルムの分解時間を表したグラフである。
上記カレンダー成形により、実施例及び比較例に係る塩化ビニル樹脂フィルムを作製し、得られた塩化ビニル樹脂フィルムをカレンダーロールから巻き取った後に、カレンダーロールの表面を目視にて確認した。カレンダーロールの表面に付着物が観察されなかった場合を○(噴き出し無し)とし、カレンダーロールの表面が白くなっていた場合を×(噴き出し有り)とした。結果を下記表3に示した。
Claims (3)
- 塩化ビニル樹脂と、エポキシ基含有アクリル樹脂と、可塑剤とを含有し、
前記エポキシ基含有アクリル樹脂は、エポキシ当量が140以上、170以下であり、かつ重量平均分子量が4万以上、6万以下であり、
前記可塑剤の含有量は、前記塩化ビニル樹脂100重量部に対して、10重量部以上、75重量部以下であることを特徴とする塩化ビニル樹脂フィルム。 - 厚みは、25μm以上、300μm以下であることを特徴とする請求項1に記載の塩化ビニル樹脂フィルム。
- 請求項1又は2に記載の塩化ビニル樹脂フィルムと、粘着剤層とを有することを特徴とする粘着シート。