JP2021066995A - 冷感生地、それを有する紡織品、及び冷感生地の製造方法 - Google Patents
冷感生地、それを有する紡織品、及び冷感生地の製造方法 Download PDFInfo
- Publication number
- JP2021066995A JP2021066995A JP2020194328A JP2020194328A JP2021066995A JP 2021066995 A JP2021066995 A JP 2021066995A JP 2020194328 A JP2020194328 A JP 2020194328A JP 2020194328 A JP2020194328 A JP 2020194328A JP 2021066995 A JP2021066995 A JP 2021066995A
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- cooling sensation
- material layer
- cold
- woven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
前記冷感材料層は、融点が20〜39℃である相転移物質を含有するマイクロカプセルと、接触冷感材料と、有機バインダとを含有し、
前記接触冷感材料は、吸水性樹脂、ジェル状物質、及びシリコン樹脂から選ばれた少なくとも1種を含有し、
前記有機バインダは、アクリル樹脂、及びポリウレタン樹脂から選ばれた少なくとも1種を含有することを特徴とする。
前記塗布された混合液を乾燥させて、前記生地に付着した冷感材料層を形成する乾燥工程とを含み、
前記接触冷感材料は、吸水性樹脂、ジェル状物質、及びシリコン樹脂から選ばれた少なくとも1種を含有し、
前記有機バインダは、アクリル樹脂、及びポリウレタン樹脂から選ばれた少なくとも1種を含有することを特徴とする。
(1)有機バインダを、調整桶にいれて、300〜500回転/分ぐらいのスピードでかき混ぜる。
(2)相転移物質を含有する、マイクロカプセルを調整桶にゆっくり入れて、10分間ぐらいかき混ぜる。
(3)接触冷感材料を調整桶に入れて5分間くらいかき混ぜる。
(4)消臭剤と防カビ剤と柔軟剤を調整桶に入れて、3分間ぐらいかき混ぜる。
(5)必要により、水や増粘剤や網詰り防止剤を適量添加する。
材料層14を比較的多量に塗布形成しても、相転移物質の表生地11表面への染み出しなどを抑制できる。
[実施例1]
生地として、綿の布帛(番手 60S*40S 打込み数172*120)を用い、この生地の片面に、融点30℃の相転移物質を含有するマイクロカプセル(PCM)34質量%、セルロース・プロプリン・グラフト・コポリマー(吸水性樹脂、接触冷感材料)15質量%、ポリウレタンバインダ45質量%、消臭剤3質量%、柔軟剤2質量%、防カビ剤1質量%に、適量の水と増粘剤とを加えて形成した混合液を、スクリーン印刷によって塗布し、乾燥することにより、冷感材料層を形成した。冷感材料層の塗布面積は50%、塗布量は20g/m2、乾燥温度は150℃1〜3分間とした。こうして実施例1の冷感生地を得た。
実施例1において、接触冷感材料としてのセルロース・プロプリン・グラフト・コポリマー(吸水性樹脂)を添加しない混合液を塗布して、その他は実施例1と同様にして、比較例1の冷感生地を得た。
[実施例2]
生地として、レーヨン不織布(目付量50g/m2)を用い、この生地の片面に、融点28℃の相転移物質を含有するマイクロカプセル(PCM)30質量%、ジェルとポリアクリル酸の混合物(吸水性樹脂、接触冷感材料)15質量%、ポリウレタンバインダ50質量%、消臭剤3質量%、柔軟剤2質量%、防カビ剤1質量%に、適量の水と増粘剤とを加えて形成した混合液を、コーティング加工装置を用いて塗布し、乾燥することにより、冷感材料層を形成した。冷感材料層の塗布面積は50%、塗布量は20g/m2、乾燥温度は150℃1〜3分間とした。こうして実施例2の冷感生地を得た。
実施例2において、冷感材料層を形成しないレーヨン不織布(目付量50g/m2)の生地を比較例2とした。実施例2及び比較例2の生地を用いて、下記の方法より、持続冷感を試験した。
[実施例3]
前記実施例2と同様にして、レーヨン不織布に冷感材料層を形成した冷感生地を作成した。この冷感生地を用いて、下記層構成の枕カバーを製造した。
1層:表生地:ナイロン65%、レーヨン30%、ポリウレタン5%
2層:冷感材料層+レーヨン不織布
3層:吸水性中綿(ポリエステル100%)
4層:ポリエステルのニット生地。
[比較例3]
市販品の枕カバー(N社製品)を、比較例3とした。この枕カバーは、下記層構成からなっている。
1層:表生地:ナイロン100%
2層:ポリエチレン不織布
3層:中綿(ポリエステル80%、アクリレート20%)
4層:シンカーパイル(パイル:80%ポリエステル+20%コットン;地糸:ポリエステル100%)。
市販品の枕カバー(I社製品)を、比較例4とした。この枕カバーは、下記層構成からなっている。
1層:表生地:複合繊維(PE60%+ナイロン40%)
2層:ポリエチレン不織布
3層:中綿(レーヨン30%+ポリエステル70%)
4層:ポリメッシュ(ポリエステル100%)。
生地として、綿の布帛(番手 60S*40S 打込み数172*120)を用い、この生地の片面に、融点30℃の相転移物質を含有するマイクロカプセル(PCM)34質量%、セルロース・プロプリン・グラフト・コポリマー(吸水性樹脂、接触冷感材料)15質量%、ポリウレタンバインダ45質量%、消臭剤3質量%、柔軟剤2質量%、防カビ剤1質量%に、適量の水と増粘剤とを加えて形成した混合液を、スクリーン印刷によって塗布し、乾燥することにより、冷感材料層を形成した。冷感材料層の塗布面積は50%、塗布量は20g/m2、乾燥温度は150℃1〜3分間とした。こうして実施例4の冷感生地を得た。
生地として、レーヨン不織布(目付量50g/m2)を用い、この生地の片面に、融点28℃の相転移物質を含有するマイクロカプセル(PCM)30質量%、ジェルとポリアクリル酸の混合物(接触冷感材料)15質量%、ポリウレタンバインダ50質量%、消臭剤3質量%、柔軟剤2質量%、防カビ剤1質量%に、適量の水と増粘剤とを加えて形成した混合液を、コーティング加工装置を用いて塗布し、乾燥することにより、冷感材料層を形成した。冷感材料層の塗布面積は50%、塗布量は20g/m2、乾燥温度は150℃1〜3分間とした。こうして実施例5の冷感生地を得た。
生地として、ナイロン50%、レーヨン45%、ポリウレタン5%の繊維からなるニット天竺生地(目付量200g/m2)を用い、この生地の片面に、融点28℃の相転移物質を含有するマイクロカプセル(PCM)40質量%、メチルビニルポリシロキサン(接触冷感材料)10質量%、ポリウレタンバインダ44質量%、消臭剤2質量%、柔軟剤2質量%、防カビ剤2質量%に、適量の水と増粘剤とを加えて形成した混合液を、プリント装置を用いて塗布し、乾燥することにより、冷感材料層を形成した。冷感材料層の塗布面積は60%、塗布量は30g/m2とした。こうして実施例6の冷感生地を得た。
11 表生地
12 裏生地
13 中わた
14 冷感材料層
15 不織布
Claims (12)
- 織布又は不織布からなる生地と、該生地の片面又は両面に塗布された冷感材料層とを有する冷感生地において、
前記冷感材料層は、融点が20〜39℃である相転移物質を含有するマイクロカプセルと、接触冷感材料と、有機バインダとを含有し、
前記接触冷感材料は、吸水性樹脂、ジェル状物質、及びシリコン樹脂から選ばれた少なくとも1種を含有し、
前記有機バインダは、アクリル樹脂、及びポリウレタン樹脂から選ばれた少なくとも1種を含有することを特徴とする冷感生地。 - 前記吸水性樹脂は、ポリアクリル酸ナトリウム、メチルセルロース、エチルセルロース、セルロース・プロピレン・グラフト・コポリマー、澱粉・アクリル酸・グラフト・コポリマーから選ばれたものからなり、
前記ジェル状物質は、キサンタンガム、寒天、ペクチンから選ばれたものからなり、
前記シリコン樹脂は、熱伝導性シリコン樹脂から選ばれたものからなる、請求項1記載の冷感生地。 - 前記冷感材料層は、更に消臭剤、柔軟剤、及び防カビ剤から選ばれた少なくとも1種を含有する、請求項1又は2記載の冷感生地。
- 前記生地が織布からなり、前記冷感材料層は、5〜200g/m2の量で塗布されている、請求項1〜3のいずれか1項に記載の冷感生地。
- 前記生地が不織布からなり、前記冷感材料層は、5〜300g/m2の量で塗布されている、請求項1〜3のいずれか1項に記載の冷感生地。
- 請求項1〜5のいずれか1項に記載された冷感生地を有する紡織品。
- 前記紡織品は、寝具用カバー、シーツ、布団、敷きパッド、枕、ラグ、クッション、ソファーカバー、タオル、カーテン、帽子、襟巻き、靴底シート、靴下、鉢巻、手首巻き、椅子シート、椅子カバー及び衣服から選ばれた1種である、請求項6記載の紡織品。
- 前記冷感生地は、前記紡織品の表生地として使用されており、前記冷感材料層は、前記表生地の裏面に塗布されている、請求項6又は7記載の紡織品。
- 前記冷感生地は、前記紡織品の表生地の内側に配置されており、前記冷感材料層は、前記表生地に接する面に塗布されている、請求項6又は7記載の紡織品。
- 織布又は不織布からなる生地の片面又は両面に、融点が20〜39℃である相転移物質を含有するマイクロカプセルと、接触冷感材料と、有機バインダとを含有する混合液を塗布する塗布工程と、
前記塗布された混合液を乾燥させて、前記生地に付着した冷感材料層を形成する乾燥工程とを含み、
前記接触冷感材料は、吸水性樹脂、ジェル状物質、及びシリコン樹脂から選ばれた少なくとも1種を含有し、
前記有機バインダは、アクリル樹脂、及びポリウレタン樹脂から選ばれた少なくとも1種を含有することを特徴とする冷感生地の製造方法。 - 前記混合液は、前記マイクロカプセルを10〜90質量%、前記接触冷感材料を1〜50質量%、前記有機バインダを8〜89質量%含有する、請求項10記載の冷感生地の製造方法。
- 前記塗布工程は、前記乾燥工程後の前記冷感材料層の塗布量が5〜300g/m2となる量で、前記混合液を塗布する、請求項10又は11記載の冷感生地の製造方法。