JP2021059040A - ハードコートフィルム - Google Patents
ハードコートフィルム Download PDFInfo
- Publication number
- JP2021059040A JP2021059040A JP2019183890A JP2019183890A JP2021059040A JP 2021059040 A JP2021059040 A JP 2021059040A JP 2019183890 A JP2019183890 A JP 2019183890A JP 2019183890 A JP2019183890 A JP 2019183890A JP 2021059040 A JP2021059040 A JP 2021059040A
- Authority
- JP
- Japan
- Prior art keywords
- hard coat
- film
- acrylate
- meth
- coat layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記第一のハードコート層は6官能未満のEO変性(メタ)アクリレート(A)と、反応性ナノシリカ(B)と、光重合開始剤(C)を含み、
前記第二のハードコート層は多官能ウレタン(メタ)アクリレート(D)と、光重合開始剤(C)を含むことを特徴とするハードコートフィルムを提供する。
(式(1)のa+b+c+d=N)
ジグリセリン166g(1モル)にエチレンオキサイド246g(6モル)を付加した化合物に対し、アクリル酸317g(4.4モル)を85℃で10時間反応し、次いでトルエン及び多量の水及び未反応のアクリル酸を中和する量の苛性を加え、分液ロートで有機層を取り出しエバポレータにてトルエンを留去し、EO変性ジグリセリンテトラアクリレートを得た。また反応物の式(1)におけるN数は6が主体であった。
(A)として上記で合成したEO変性ジグリセリンテトラアクリレートを、(B)としてPGM−AC−2140Y(商品名:日産化学社製、平均粒子径10〜15nmナノシリカ、固形分40%、PGM分散品)及びPGM−AC−4130Y(商品名:日産化学社製、平均粒子径40〜50nmナノシリカ、固形分32%、PGM分散品)を、(C)としてOmnirad2959(商品名:IGM Resins社製、α−ヒドロキシアセトフェノン系)を、6官能アクリレートとしてA−DPH−6E(商品名:新中村化学社製、ジペンタエリスリトールEO変性ヘキサアクリレート)を、4官能ウレタンアクリレートとしてRUA−062S(商品名:亜細亜工業社製)を、レベリング剤としてBYK−UV3576(商品名:ビックケミー社製、有効成分40%、ポリジメチルシロキサン変性多官能アクリレート、トリプロピレングリコールジアクリレート希釈)を、溶剤としてPGMを用い、表1記載の配合で均一に溶解分散するまで撹拌し、配合1〜8のHC樹脂組成物を調製した。
配合1〜8で使用した材料に加え、(D)として6官能ウレタンアクリレート(PETA-HDI-PETA)を、(E)としてKY−1203(商品名:信越化学工業社製)を、(F)としてMEK−AC−5140Z(商品名:日産化学社製、平均粒子径80nm、ナノシリカ、固形分32%、MEK分散品)及びALMIBK30WT%−M47(商品名:CIKナノテック社製、平均粒子径30nm、酸化アルミニウム、表面処理あり、固形分30%、MIBK分散品)及びEN−2400I(商品名:CHEM-MAT社製、平均粒子径50nm、酸化アルミニウム、表面処理なし、固形分40%、IPA分散品)を、6官能アクリレートとしてDPHA(ジペンタエリスリトールヘキサアクリレート)を用い、表2記載の配合で均一に溶解分散するまで撹拌し、配合A〜HのHC樹脂組成物を調製した。
表3及び4に示す構成で、PETフィルムU403(商品名:東レ社製、厚さ125μm)に第一のHC樹脂組成物を乾燥膜厚が4μmとなるように塗工し、恒温槽で80℃×1分乾燥後、無電極ランプで出力1,200mW/cm2、積算光量が200mJとなる様に紫外線照射して第一のHC層を形成後、その上に第二のHC樹脂を乾燥膜厚が2μmとなるように塗工し、恒温槽で80℃×1分乾燥後、無電極ランプで出力1,200mW/cm2、積算光量が200mJとなる様に紫外線照射して第二のHC層を形成し実施例1〜11、比較例1〜5の試験フィルムを作成した。
Claims (6)
- 透明基材フィルムの少なくとも一方の面に第一のハードコート層を有し、更にその上に第二のハードコート層を有するハードコートフィルムであり、
前記第一のハードコート層は6官能未満のEO変性(メタ)アクリレート(A)と、反応性ナノシリカ(B)と、光重合開始剤(C)を含み、
前記第二のハードコート層は多官能ウレタン(メタ)アクリレート(D)と、光重合開始剤(C)を含むことを特徴とするハードコートフィルム。 - 前記(A)がEO変性ジグリセリンテトラアクリレートであることを特徴とする請求項1記載のハードコートフィルム。
- 前記第二のハードコート層が、更に撥水剤(E)を含むことを特徴とする請求項1又は2いずれか記載のハードコートフィルム。
- 前記第二のハードコート層が、更に無機微粒子(F)を含むことを特徴とする請求項1〜3いずれか記載のハードコートフィルム。
- 前記透明基材フィルムがポリイミドフィルムであることを特徴とする請求項1〜4いずれか記載のハードコートフィルム。
- フォルダブルディスプレイ用途のタッチパネルに用いることを特徴とする請求項1〜5いずれか記載のハードコートフィルム。