JP2020193149A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2020193149A5 JP2020193149A5 JP2020148201A JP2020148201A JP2020193149A5 JP 2020193149 A5 JP2020193149 A5 JP 2020193149A5 JP 2020148201 A JP2020148201 A JP 2020148201A JP 2020148201 A JP2020148201 A JP 2020148201A JP 2020193149 A5 JP2020193149 A5 JP 2020193149A5
- Authority
- JP
- Japan
- Prior art keywords
- mol
- glass article
- less
- glass
- composition according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000011521 glass Substances 0.000 claims 54
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 22
- 229910018068 Li 2 O Inorganic materials 0.000 claims 19
- 239000000203 mixture Substances 0.000 claims 16
- 229910004298 SiO 2 Inorganic materials 0.000 claims 6
- ODINCKMPIJJUCX-UHFFFAOYSA-N calcium monoxide Chemical compound [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 claims 6
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N iron oxide Chemical compound [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 claims 6
- CPLXHLVBOLITMK-UHFFFAOYSA-N magnesium oxide Chemical compound [Mg]=O CPLXHLVBOLITMK-UHFFFAOYSA-N 0.000 claims 6
- XLOMVQKBTHCTTD-UHFFFAOYSA-N zinc monoxide Chemical compound [Zn]=O XLOMVQKBTHCTTD-UHFFFAOYSA-N 0.000 claims 6
- 239000000758 substrate Substances 0.000 claims 4
- 229910000272 alkali metal oxide Inorganic materials 0.000 claims 3
- QVQLCTNNEUAWMS-UHFFFAOYSA-N barium oxide Inorganic materials [Ba]=O QVQLCTNNEUAWMS-UHFFFAOYSA-N 0.000 claims 3
- 229910052792 caesium Inorganic materials 0.000 claims 3
- 229910001409 divalent cation oxide Inorganic materials 0.000 claims 3
- 229910052730 francium Inorganic materials 0.000 claims 3
- 229910052700 potassium Inorganic materials 0.000 claims 3
- 229910052701 rubidium Inorganic materials 0.000 claims 3
- LIVNPJMFVYWSIS-UHFFFAOYSA-N silicon monoxide Inorganic materials [Si-]#[O+] LIVNPJMFVYWSIS-UHFFFAOYSA-N 0.000 claims 3
- 229910052708 sodium Inorganic materials 0.000 claims 3
- IATRAKWUXMZMIY-UHFFFAOYSA-N strontium oxide Inorganic materials [O-2].[Sr+2] IATRAKWUXMZMIY-UHFFFAOYSA-N 0.000 claims 3
- 239000007791 liquid phase Substances 0.000 claims 2
Claims (25)
- ５５．０モル％以上から７０．０モル％以下のＳｉＯ２、
１２．０モル％以上から２０．０モル％以下のＡｌ２Ｏ３、
０モル％超から７．５モル％以下のＢ ２ Ｏ ３ 、
５．０モル％以上から１５．０モル％以下のＬｉ２Ｏ、および
４．０モル％以上から１５．０モル％以下のＮａ２Ｏ、
を含み、
−８．００モル％≦Ｒ２Ｏ＋ＲＯ−Ａｌ２Ｏ３−Ｂ２Ｏ３−Ｐ２Ｏ５≦−１．７５モル％、
９．１０≦（ＳｉＯ２＋Ａｌ２Ｏ３＋Ｌｉ２Ｏ）／Ｎａ２Ｏ、
１．８０≦（Ｌｉ２Ｏ＋Ａｌ２Ｏ３＋Ｐ２Ｏ５）／（Ｎａ２Ｏ＋Ｂ２Ｏ３）≦３．５０、
Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏが２１．４モル％超であり、
ＲＯが、二価陽イオン酸化物の合計であり、ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯ、ＦｅＯ、およびＺｎＯからなる群から選択され、
Ｒ ２ Ｏが、アルカリ金属酸化物の合計であり、Ｌｉ ２ Ｏ、Ｎａ ２ Ｏ、Ｋ ２ Ｏ、Ｒｂ ２ Ｏ、Ｃｓ ２ Ｏ、およびＦｒ ２ Ｏからなる群から選択される、ガラス組成物。 - −７．５０モル％≦Ｒ ２ Ｏ＋ＲＯ−Ａｌ ２ Ｏ ３ −Ｂ ２ Ｏ ３ −Ｐ ２ Ｏ ５ ≦−２．５０モル％である、請求項１記載のガラス組成物。
- ９．１０≦（ＳｉＯ ２ ＋Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏ）／Ｎａ ２ Ｏ≦１６．００である、請求項１または２記載のガラス組成物。
- ９．２０≦（ＳｉＯ ２ ＋Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏ）／Ｎａ ２ Ｏ≦１５．５０である、請求項１から３いずれか１項記載のガラス組成物。
- １．８０≦（Ｌｉ ２ Ｏ＋Ａｌ ２ Ｏ ３ ＋Ｐ ２ Ｏ ５ ）／（Ｎａ ２ Ｏ＋Ｂ ２ Ｏ ３ ）≦３．３５である、請求項１から４いずれか１項記載のガラス組成物。
- Ｂ ２ Ｏ ３ ＋Ｐ ２ Ｏ ５ が０．０モル％超である、請求項１から５いずれか１項記載のガラス組成物。
- １．００≦（Ｌｉ ２ Ｏ＋Ａｌ ２ Ｏ ３ ）／（Ｎａ ２ Ｏ＋Ｂ ２ Ｏ ３ ＋Ｐ ２ Ｏ ５ ）≦２．７５である、請求項１から６いずれか１項記載のガラス組成物。
- Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏ＋Ｎａ ２ Ｏが２５．０モル％超である、請求項１から７いずれか１項記載のガラス組成物。
- ０．９０＜Ａｌ ２ Ｏ ３ ／（Ｒ ２ Ｏ＋ＲＯ）＜１．２０である、請求項１から８いずれか１項記載のガラス組成物。
- １．０＜（Ａｌ ２ Ｏ ３ ＋Ｂ ２ Ｏ ３ ＋Ｐ ２ Ｏ ５ ）／（Ｒ ２ Ｏ＋ＲＯ）である、請求項１から９いずれか１項記載のガラス組成物。
- ６．９６Ａｌ ２ Ｏ ３ −１．９０Ｂ ２ Ｏ ３ ＋２．１６ＣａＯ＋３．３０ＭｇＯ−１．５０Ｎａ ２ Ｏ＋１２．７４Ｌｉ ２ Ｏ−１．１０ＳｒＯ−１４．５０Ｋ ２ Ｏ−１．８７Ｌａ ２ Ｏ ３ ＋６．１３ＺｒＯ ２ −７６．４０モル％＞５０．００モル％である、請求項１から１０いずれか１項記載のガラス組成物。
- ガラス物品において、
第一面；
前記第一面と反対の第二面であって、該第一面と該第二面との間の距離として前記ガラス物品の厚さ（ｔ）が測定される、第二面；および
前記第一面と前記第二面の少なくとも一方から前記ガラス物品の厚さ（ｔ）中に延在する圧縮応力層；
を備えたガラス物品であって、
前記ガラス物品の中央張力は６０ＭＰａ以上であり、
前記圧縮応力層は０．１５ｔ以上から０．２５ｔ以下の圧縮深さを有し、
前記ガラス物品は、
５５．０モル％以上から７０．０モル％以下のＳｉＯ ２ 、
１２．０モル％以上から２０．０モル％以下のＡｌ ２ Ｏ ３ 、
０モル％超から７．５モル％以下のＢ ２ Ｏ ３ 、
５．０モル％以上から１５．０モル％以下のＬｉ ２ Ｏ、および
４．０モル％以上から１５．０モル％以下のＮａ ２ Ｏ、
を含み、
−８．００モル％≦Ｒ ２ Ｏ＋ＲＯ−Ａｌ ２ Ｏ ３ −Ｂ ２ Ｏ ３ −Ｐ ２ Ｏ ５ ≦−１．７５モル％、
９．００≦（ＳｉＯ ２ ＋Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏ）／Ｎａ ２ Ｏ、
１．８０≦（Ｌｉ ２ Ｏ＋Ａｌ ２ Ｏ ３ ＋Ｐ ２ Ｏ ５ ）／（Ｎａ ２ Ｏ＋Ｂ ２ Ｏ ３ ）≦３．５０
Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏが２１．４モル％超であり、
ＲＯが、二価陽イオン酸化物の合計であり、ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯ、ＦｅＯ、およびＺｎＯからなる群から選択され、
Ｒ ２ Ｏが、アルカリ金属酸化物の合計であり、Ｌｉ ２ Ｏ、Ｎａ ２ Ｏ、Ｋ ２ Ｏ、Ｒｂ ２ Ｏ、Ｃｓ ２ Ｏ、およびＦｒ ２ Ｏからなる群から選択されるガラスから形成される、ガラス物品。 - 前記ガラス物品の中央張力が８０ＭＰａ以上である、請求項１２記載のガラス物品。
- 前記ガラス物品の中央張力が９０ＭＰａ以上である、請求項１２または１３記載のガラス物品。
- 前記圧縮応力層が、０．１８ｔ以上から０．２２ｔ以下の圧縮深さを有する、請求項１２から１４いずれか１項記載のガラス物品。
- 前記ガラス物品が、２０ｋＰ以上から１０００ｋＰ未満の液相粘度を有する、請求項１２から１５いずれか１項記載のガラス物品。
- 前面、背面、および側面を有する筐体；
前記筐体内に少なくとも部分的に内部にある電気部品であって、少なくとも制御装置、メモリ、および前記筐体の前面に、またはその近くにあるディスプレイを含む電気部品；および
前記ディスプレイ上に配置されたカバー基板；
を備える家電製品であって、
前記筐体および前記カバー基板の少なくとも一方の少なくとも一部が、請求項１２から１６いずれか１項記載のガラス物品を含む、家電製品。 - ガラス物品において、
第一面；
前記第一面と反対の第二面であって、該第一面と該第二面との間の距離として前記ガラス物品の厚さ（ｔ）が測定される、第二面；および
前記第一面と前記第二面の少なくとも一方から前記ガラス物品の厚さ（ｔ）中に延在する圧縮応力層；
を備えたガラス物品であって、
前記ガラス物品の中央張力は６０ＭＰａ以上であり、
前記圧縮応力層は０．１５ｔ以上から０．２５ｔ以下の圧縮深さを有し、
前記ガラス物品は、
５５．０モル％以上から７０．０モル％以下のＳｉＯ ２ 、
１２．０モル％以上から２０．０モル％以下のＡｌ ２ Ｏ ３ 、
０モル％超から７．５モル％以下のＢ ２ Ｏ ３ 、
５．０モル％以上から１５．０モル％以下のＬｉ ２ Ｏ、および
４．０モル％以上から１５．０モル％以下のＮａ ２ Ｏ、
を含み、
−８．００モル％≦Ｒ ２ Ｏ＋ＲＯ−Ａｌ ２ Ｏ ３ −Ｂ ２ Ｏ ３ −Ｐ ２ Ｏ ５ ≦−１．７５モル％、
９．００≦（ＳｉＯ ２ ＋Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏ）／Ｎａ ２ Ｏ、
１．８０≦（Ｌｉ ２ Ｏ＋Ａｌ ２ Ｏ ３ ＋Ｐ ２ Ｏ ５ ）／（Ｎａ ２ Ｏ＋Ｂ ２ Ｏ ３ ）≦３．５０、
Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏが２１．４モル％超であり、
ＲＯが、二価陽イオン酸化物の合計であり、ＭｇＯ、ＣａＯ、ＳｒＯ、ＢａＯ、ＦｅＯ、およびＺｎＯからなる群から選択され、
Ｒ ２ Ｏが、アルカリ金属酸化物の合計であり、Ｌｉ ２ Ｏ、Ｎａ ２ Ｏ、Ｋ ２ Ｏ、Ｒｂ ２ Ｏ、Ｃｓ ２ Ｏ、およびＦｒ ２ Ｏからなる群から選択される
組成を前記ガラス物品の中心深さで有する、ガラス物品。 - ガラス組成物において、
６０．０モル％以上から７０．０モル％以下のＳｉＯ ２ 、
１２．０モル％以上から１８．０モル％以下のＡｌ ２ Ｏ ３ 、
０モル％超から７．５モル％以下のＢ ２ Ｏ ３ 、
５．０モル％以上から１０．０モル％以下のＬｉ ２ Ｏ、
４．０モル％以上から１０．０モル％以下のＮａ ２ Ｏ、および
０．７５モル％以上のＰ ２ Ｏ ５ 、
を含み、
Ｌｉ ２ Ｏ／Ｎａ ２ Ｏは１．００以上であり、
Ａｌ ２ Ｏ ３ ＋Ｌｉ ２ Ｏは２１．４モル％超かつ２５．２５モル％以下である、ガラス組成物。 - ガラス物品において、
第一面；
前記第一面と反対の第二面であって、該第一面と該第二面との間の距離として前記ガラス物品の厚さ（ｔ）が測定される、第二面；および
前記第一面と前記第二面の少なくとも一方から前記ガラス物品の厚さ（ｔ）中に延在する圧縮応力層；
を備えたガラス物品であって、
前記ガラス物品の中央張力は６０ＭＰａ以上であり、
前記圧縮応力層は０．１５ｔ以上から０．２５ｔ以下の圧縮深さを有し、
前記ガラス物品は、請求項１９記載のガラス組成物から形成される、ガラス物品。 - 前記ガラス物品の中央張力が８０ＭＰａ以上である、請求項２０記載のガラス物品。
- 前記ガラス物品の中央張力が９０ＭＰａ以上である、請求項２０または２１記載のガラス物品。
- 前記圧縮応力層が、０．１８ｔ以上から０．２２ｔ以下の圧縮深さを有する、請求項２０から２２いずれか１項記載のガラス物品。
- 前記ガラス物品が、２０ｋＰ以上から１０００ｋＰ未満の液相粘度を有する、請求項２０から２３いずれか１項記載のガラス物品。
- 前面、背面、および側面を有する筐体；
前記筐体内に少なくとも部分的に内部にある電気部品であって、少なくとも制御装置、メモリ、および前記筐体の前面に、またはその近くにあるディスプレイを含む電気部品；および
前記ディスプレイ上に配置されたカバー基板；
を備える家電製品であって、
前記筐体および前記カバー基板の少なくとも一方の少なくとも一部が、請求項２０から２４いずれか１項記載のガラス物品を含む、家電製品。