JP2020169302A - 防湿コート用組成物 - Google Patents
防湿コート用組成物 Download PDFInfo
- Publication number
- JP2020169302A JP2020169302A JP2019072956A JP2019072956A JP2020169302A JP 2020169302 A JP2020169302 A JP 2020169302A JP 2019072956 A JP2019072956 A JP 2019072956A JP 2019072956 A JP2019072956 A JP 2019072956A JP 2020169302 A JP2020169302 A JP 2020169302A
- Authority
- JP
- Japan
- Prior art keywords
- moisture
- styrene
- proof coating
- coating composition
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
スチレン系エラストマーと、粘着付与樹脂とを含み、
前記粘着付与樹脂は、α−メチルスチレンの構造単位又はその水素添加体の構造単位を分子中に有する炭化水素樹脂を含むことを特徴とする。
上記の防湿コート用組成物によれば、電子基板に形成されたコート被膜が高温下でひび割れることを抑制できる。
これにより、上記のコート被膜が高温下でひび割れることをより抑制できるという利点がある。
これにより、上記のコート被膜が高温下でひび割れることをより抑制できるという利点がある。
これにより、上記のコート被膜が高温下でひび割れることをより抑制できるという利点がある。
これにより、上記のコート被膜が高温下でひび割れることをより抑制できるという利点がある。
これにより、上記のコート被膜が高温下でひび割れることをより抑制できるという利点がある。
本実施形態の防湿コート用組成物は、ヒンダードフェノール構造を分子中に有する酸化防止剤をさらに含む。
本実施形態の防湿コート用組成物は、該組成物からコート被膜を形成させるときに、溶媒をさらに含んでもよい。溶媒をさらに含むことによって、上記組成物が流動性を有することができる。一方、本実施形態の防湿コート用組成物は、被コート対象物に塗布された後に溶媒が揮発して作製された、被膜の状態であってもよい。
スチレン系エラストマーを含む防湿コート用組成物によって形成されたコート被膜は、防湿性を有することができる。
スチレン系モノマーの構成単位は、上記の1種が単独でブロックを構成してもよく、2種以上がブロックを構成してもよい。
オレフィン系モノマーの構成単位は、上記の1種が単独でブロックを構成してもよく、2種以上がブロックを構成してもよい。
水素添加体としては、完全水素添加体又は部分水素添加体が挙げられ、完全水素添加体が好ましい。
なお、スチレン系エラストマーでは、通常、上記の構成単位が分子中において100を超える数で連なっている。従って、スチレン系エラストマーの質量平均分子量は、通常、数万〜数十万程度である。
これにより、本実施形態の防湿コート用組成物から形成されたコート被膜が高温下でひび割れることをより抑制できるという利点がある。
斯かる炭化水素樹脂は、さらに、インデンの構造単位を分子中に有してもよい。
上記の測定は、例えば、自動軟化点試験器「asp−6」(田中科学機器製作 社製)を用いて実施できる。測定条件は、下記の通りである。
・環球式2個がけ
・グリセリン浴+撹拌モード
・マグネチックスターラ80〜300rpm
これにより、本実施形態の防湿コート用組成物から形成されたコート被膜が高温下でひび割れることをより抑制できるという利点がある。
ヒンダードフェノール構造の具体例としては、下記の構造が挙げられる。なお、下記式中のR2は、メチル基であり、無くてもよい。式中のR2は、ベンゼン環の複数の炭素原子にそれぞれ結合していてもよい。ヒンダードフェノール構造において、水酸基(−OH)が結合している部位は、通常、パラ位であるが、メタ位やオルト位であってもよい。
また、分子中にヒンダードフェノール構造を2つ有する、6,6’−ジ−tert−ブチル−4,4’−ブチリデンジ−m−クレゾール、3,9−ビス{2−[3−(3−tert−ブチル−4−ヒドロキシ−5−メチルフェニル)プロピオニルオキシ]−1,1−ジメチルエチル}−2,4,8,10−テトラオキサスピロ[5.5]ウンデカンなどが挙げられる。
また、分子中にヒンダードフェノール構造を3つ有する、1,3,5−トリス(3,5−ジ−tert−ブチル−4−ヒドロキシベンジル)−1,3,5−トリアジン−2,4,6(1H、3H、5H)−トリオン、4,4’、4”−(1−メチルプロパニル−3−イリデン)トリス(6−tert−ブチル−m−クレゾール)、1,3,5−トリス(3,5−ジ−tert−ブチル−4−ヒドロキシフェニルメチル)−2,4,6−トリメチルベンゼンなどが挙げられる。
また、分子中にヒンダードフェノール構造を4つ有する、ペンタエリトリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]などが挙げられる。
上記の酸化防止剤としては、コート被膜が高温下でひび割れることをより抑制できるというという点で、分子中にヒンダードフェノール構造を4つ有する、ペンタエリトリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]が好ましい。
また、スチレン系エラストマーの100質量部に対して、上記の酸化防止剤が15質量部以下含まれることが好ましい。これにより、本実施形態の防湿コート用組成物が有機溶媒を含んだ場合における、上記の酸化防止剤の溶解性を良好に確保できるという利点がある。また、防湿コート用組成物で形成されたコート被膜において酸化防止剤が析出(ブリードアウト)することをより確実に抑制できる。
なお、スチレン系エラストマーは、水素添加体となって炭素間の不飽和結合がほとんどなくなっていたとしても、酸化劣化され得る。
炭化水素系の有機溶媒としては、飽和環状炭化水素、飽和鎖状炭化水素、芳香族炭化水素などが挙げられる。
飽和鎖状炭化水素としては、ヘプタン、ペンタンなどが挙げられる。
芳香族炭化水素としては、ベンゼン、トルエン、キシレン、ペンタメチルベンゼンなどが挙げられる。
その他の添加剤としては、例えば、難燃剤、耐候剤、防錆剤、充填剤、改質剤、顔料などが挙げられる。
即ち、一般的な防湿コート用組成物において用いられる種々の形態が、本発明の効果を損ねない範囲において、採用され得る。
また、これら防湿コート用組成物によって電子基板上に形成したコート被膜について、高温でのひび割れの発生の有無を評価した。
(A)スチレン系エラストマー(水素添加体)
スチレン−エチレン−ブチレン−スチレン(SEBS)ブロック共重合体
(製品名「クレイトン G1650MU」:クレイトン(KRATON)社製)
(B)粘着付与樹脂(炭化水素樹脂)
分子中にα−メチルスチレン構造単位、スチレン構造単位、及びインデン構造単位を有する(水素添加体)
軟化点−100℃
(製品名「アルコン M100」:荒川化学工業社製)
(C−1)酸化防止剤
化学名:ペンタエリトリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート](ヒンダードフェノール構造4つ)
(製品名「イルガノックス1010」:BASFジャパン社製)
(C−2)酸化防止剤
化学名:3,9−ビス{2−[3−(3−tert−ブチル−4−ヒドロキシ−5−メチルフェニル)プロピオニルオキシ]−1,1−ジメチルエチル}−2,4,8,10−テトラオキサスピロ[5.5]ウンデカン(ヒンダードフェノール構造2つ)
(製品名「アデカスタブAO−80」:ADEKA社製)
(C−3)酸化防止剤
化学名:2,6−ジ−tert−ブチル−4―メチルフェノール(ヒンダードフェノール構造1つ)
(製品名「ノクラック200」:大内新興化学工業社製)
(D)溶媒
メチルシクロヘキサン
表1に示す配合組成で各原料を60℃で混合して、その後室温まで冷却し、液状の防湿コート用組成物を製造した。
表1に示す配合組成に変更した点以外は、実施例と同様にして、液状の防湿コート用組成物を製造した。
各防湿コート用組成物で形成したコート被膜について、以下のようにして、高温条件下で放置したあとのひび割れ(クラック)の有無を目視評価した。
整面処理を施した銅板を用意した。整面処理は、次のようにして行った。イオン交換水にペルオキソ二硫酸ナトリウムを50g/Lとなるように加えて溶解し、さらに硫酸濃度が2%となるように硫酸を添加して水溶液を調製した。調整した水溶液を恒温機に入れて50℃に加温した後、銅板を6分間浸漬し、整面処理した。
整面処理した銅板上に、液状の防湿コート用組成物を塗布した。120℃で10分間の乾燥処理を行い、厚さが約100μmのコート被膜を作製した。コート被膜を銅板ごと、165℃の恒温機に所定時間入れた。その後、恒温機から取り出して常温に冷却した被膜にクラック(ひび割れ)が発生したかどうか目視で確認した。
評価結果を表1に示す。
酸化防止剤の相溶性の評価として、下記の2試験を行った。
実施例及び比較例の各樹脂組成物がメチルシクロヘキサンを含んだ液状の状態において、それぞれの酸化防止剤が溶解しているかどうかを目視によって確認した。
また、各組成物で形成されたコート被膜における酸化防止剤の析出(ブリードアウト)を目視によって評価した。
評価結果を表1に示す。
一方、比較例の防湿コート用組成物で形成したコート被膜では、高温下で長期間放置した後、ひび割れ(クラック)が発生した。
なお、アルミニウム板を用いて同様にして評価した結果、実施例及び比較例の全てにおいて、コート被膜のクラックが発生しなかった。このことから、コート被膜のクラックは、銅の触媒作用等によって引き起こされやすいといえる。
Claims (6)
- スチレン系エラストマーと、粘着付与樹脂とを含み、
前記粘着付与樹脂は、α−メチルスチレンの構造単位又はその水素添加体の構造単位を分子中に有する炭化水素樹脂を含む、防湿コート用組成物。 - ヒンダードフェノール構造を分子中に有する酸化防止剤をさらに含む、請求項1に記載の防湿コート用組成物。
- 前記スチレン系エラストマーの100質量部に対して、前記酸化防止剤を5質量部以上20質量部以下含む、請求項2に記載の防湿コート用組成物。
- 前記スチレン系エラストマーの100質量部に対して、前記炭化水素樹脂を30質量部以上150質量部以下含む、請求項1〜3のいずれか1項に記載の防湿コート用組成物。
- 前記炭化水素樹脂の軟化点が70℃以上150℃以下である、請求項1〜4のいずれか1項に記載の防湿コート用組成物。
- 前記スチレン系エラストマーは、スチレン−エチレン−ブチレン−スチレンブロック共重合体である、請求項1〜5のいずれか1項に記載の防湿コート用組成物。