JP2019151762A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2019151762A5 JP2019151762A5 JP2018038816A JP2018038816A JP2019151762A5 JP 2019151762 A5 JP2019151762 A5 JP 2019151762A5 JP 2018038816 A JP2018038816 A JP 2018038816A JP 2018038816 A JP2018038816 A JP 2018038816A JP 2019151762 A5 JP2019151762 A5 JP 2019151762A5
- Authority
- JP
- Japan
- Prior art keywords
- sodium
- heat storage
- storage material
- material composition
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Description
本発明の第1の態様に係る蓄熱材組成物は、硫酸ナトリウム10水和物、炭酸ナトリウム10水和物、及びリン酸水素二ナトリウム12水和物からなる主剤を含み、前記主剤100質量%中に、前記硫酸ナトリウム10水和物が15〜30質量%、前記炭酸ナトリウム10水和物が17〜35質量%、及び前記リン酸水素二ナトリウム12水和物が35〜61質量%含まれ、融解潜熱を発現する温度が20℃以上30℃未満にあり、前記融解潜熱が170J/g以上である。
本発明の第2の態様に係る蓄熱材組成物は、第1の態様に係る蓄熱材組成物において、前記主剤中の、前記硫酸ナトリウム10水和物の含有量をX質量%、前記炭酸ナトリウム10水和物の含有量をY質量%、及び前記リン酸水素二ナトリウム12水和物の含有量をZ質量%としたとき、X、Y及びZが下記式(1)〜(4)を満たす。
X+Y+Z=100 (1)
15≦X≦31 (2)
X−7.264Y+223.464≧0 (3)
X+3.711Y−94.888≧0 (4)。
X+Y+Z=100 (1)
15≦X≦31 (2)
X−7.264Y+223.464≧0 (3)
X+3.711Y−94.888≧0 (4)。
本発明の第3の態様に係る蓄熱材組成物は、第1又は第2の態様に係る蓄熱材組成物において、余剰水をさらに含み、前記余剰水は、前記主剤100質量部に対して9質量部以下含まれる。
本発明の第4の態様に係る蓄熱材組成物は、第1〜第3のいずれかの態様に係る蓄熱材組成物において、有機不飽和カルボン酸、有機不飽和スルホン酸、有機不飽和リン酸、有機不飽和アミド、有機不飽和アルコール、有機不飽和カルボン酸塩、有機不飽和スルホン酸塩、及び有機不飽和リン酸塩からなる群より選択される少なくとも1種の単量体と、多官能性単量体と、を重合させて得られる相分離抑制剤をさらに含む。
本発明の第5の態様に係る蓄熱材組成物は、第1〜第4のいずれかの態様に係る蓄熱材組成物において、塩化ナトリウム、塩化カリウム、硝酸ナトリウム、臭化ナトリウム、塩化アンモニウム、臭化アンモニウム、硫酸アンモニウム、硝酸アンモニウム、リン酸アンモニウム、及び尿素からなる群より選択される少なくとも1種の融点降下剤をさらに含む。
本発明の第6の態様に係る蓄熱材組成物は、第1〜第5のいずれかの態様に係る蓄熱材組成物において、ホウ砂Na2B4O5(OH)4・8H2O、プロピレングリコール、エチレングリコール、グリセリン、エチレンジアミン四酢酸、アルキル硫酸ナトリウム、アルキルリン酸ナトリウム、アルキル硫酸カリウム、及びアルキルリン酸カリウムからなる群より選択される少なくとも1種の過冷却抑制剤をさらに含む。
本発明の第7の態様に係る蓄熱材組成物は、第1〜第6のいずれかの態様に係る蓄熱材組成物において、ケイ酸ナトリウム、水ガラス、ポリアクリル酸、ポリアクリル酸ナトリウム、ポリカルボキシレートポリエーテルポリマー、アクリル酸・マイレン酸共重合体ナトリウム、アクリル酸・スルホン酸系モノマー共重合体ナトリウム、アクリルアミド・ジメチルアミノエチルメタクリラートジメチル硫酸塩共重合物、アクリルアミド・アクリル酸ソーダ共重合物、ポリエチレングリコール、ポリプロピレングリコール、高吸水樹脂(SAP)、カルボキシメチルセルロース(CMC)、CMCの誘導体、カラギーナン、カラギーナンの誘導体、キサンタンガム、キサンタンガムの誘導体、ペクチン、ペクチンの誘導体、デンプン、デンプンの誘導体、コンニャク、寒天、層状ケイ酸塩、及び上記物質の複合物質からなる群より選択される少なくとも1種の相分離抑制剤をさらに含む。
本発明の第8の態様に係る建築物の冷暖房用の蓄熱システムは、第1〜第7のいずれかの態様に係る蓄熱材組成物を用いた蓄熱材モジュールを具備する。
Claims (8)
- 硫酸ナトリウム10水和物、炭酸ナトリウム10水和物、及びリン酸水素二ナトリウム12水和物からなる主剤を含み、
前記主剤100質量%中に、
前記硫酸ナトリウム10水和物が15〜30質量%、
前記炭酸ナトリウム10水和物が17〜35質量%、及び
前記リン酸水素二ナトリウム12水和物が35〜61質量%含まれ、
融解潜熱を発現する温度が20℃以上30℃未満にあり、
前記融解潜熱が170J/g以上であることを特徴とする蓄熱材組成物。 - 前記主剤中の、前記硫酸ナトリウム10水和物の含有量をX質量%、前記炭酸ナトリウム10水和物の含有量をY質量%、及び前記リン酸水素二ナトリウム12水和物の含有量をZ質量%としたとき、X、Y及びZが下記式(1)〜(4)を満たすことを特徴とする請求項1に記載の蓄熱材組成物。
X+Y+Z=100 (1)
15≦X≦31 (2)
X−7.264Y+223.464≧0 (3)
X+3.711Y−94.888≧0 (4) - 余剰水をさらに含み、
前記余剰水は、前記主剤100質量部に対して9質量部以下含まれることを特徴とする請求項1又は2に記載の蓄熱材組成物。 - 有機不飽和カルボン酸、有機不飽和スルホン酸、有機不飽和リン酸、有機不飽和アミド、有機不飽和アルコール、有機不飽和カルボン酸塩、有機不飽和スルホン酸塩、及び有機不飽和リン酸塩からなる群より選択される少なくとも1種の単量体と、
多官能性単量体と、
を重合させて得られる相分離抑制剤をさらに含むことを特徴とする請求項1〜3のいずれか1項に記載の蓄熱材組成物。 - 塩化ナトリウム、塩化カリウム、硝酸ナトリウム、臭化ナトリウム、塩化アンモニウム、臭化アンモニウム、硫酸アンモニウム、硝酸アンモニウム、リン酸アンモニウム、及び尿素からなる群より選択される少なくとも1種の融点降下剤をさらに含むことを特徴とする請求項1〜4のいずれか1項に記載の蓄熱材組成物。
- ホウ砂Na2B4O5(OH)4・8H2O、プロピレングリコール、エチレングリコール、グリセリン、エチレンジアミン四酢酸、アルキル硫酸ナトリウム、アルキルリン酸ナトリウム、アルキル硫酸カリウム、及びアルキルリン酸カリウムからなる群より選択される少なくとも1種の過冷却抑制剤をさらに含むことを特徴とする請求項1〜5のいずれか1項に記載の蓄熱材組成物。
- ケイ酸ナトリウム、水ガラス、ポリアクリル酸、ポリアクリル酸ナトリウム、ポリカルボキシレートポリエーテルポリマー、アクリル酸・マイレン酸共重合体ナトリウム、アクリル酸・スルホン酸系モノマー共重合体ナトリウム、アクリルアミド・ジメチルアミノエチルメタクリラートジメチル硫酸塩共重合物、アクリルアミド・アクリル酸ソーダ共重合物、ポリエチレングリコール、ポリプロピレングリコール、高吸水樹脂(SAP)、カルボキシメチルセルロース(CMC)、CMCの誘導体、カラギーナン、カラギーナンの誘導体、キサンタンガム、キサンタンガムの誘導体、ペクチン、ペクチンの誘導体、デンプン、デンプンの誘導体、コンニャク、寒天、層状ケイ酸塩、及び上記物質の複合物質からなる群より選択される少なくとも1種の相分離抑制剤をさらに含むことを特徴とする請求項1〜6のいずれか1項に記載の蓄熱材組成物。
- 請求項1〜7のいずれか1項に記載の蓄熱材組成物を用いた蓄熱材モジュールを具備することを特徴とする建築物の冷暖房用の蓄熱システム。