JP2018199803A - 水溶性シリコーンマクロマー、シリコーンハイドロゲル組成物、シリコーンハイドロゲルコンタクトレンズ及びその製造方法 - Google Patents
水溶性シリコーンマクロマー、シリコーンハイドロゲル組成物、シリコーンハイドロゲルコンタクトレンズ及びその製造方法 Download PDFInfo
- Publication number
- JP2018199803A JP2018199803A JP2017183598A JP2017183598A JP2018199803A JP 2018199803 A JP2018199803 A JP 2018199803A JP 2017183598 A JP2017183598 A JP 2017183598A JP 2017183598 A JP2017183598 A JP 2017183598A JP 2018199803 A JP2018199803 A JP 2018199803A
- Authority
- JP
- Japan
- Prior art keywords
- trimethylsiloxy
- silane
- water
- macromer
- silicone hydrogel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
E−(M1)x−(M2)y 式(1)
ただし、M1はケイ素含有モノマーから誘導された繰り返し単位であり、水溶性シリコーンマクロマーの総重量に対する含有量が30〜60wt%であり、M2は第一親水性モノマーから誘導された繰り返し単位であり、水溶性シリコーンマクロマーの総重量に対する含有量が40〜70wt%であり、Eはビニル系不飽和化合物から誘導された基であり、xは1〜20の整数であり、yは1〜20の整数であり、且つ水溶性シリコーンマクロマーの数平均分子量は2000〜5000の範囲にある水溶性シリコーンマクロマーを提供する。
E−(M1)x−(M2)y 式(1)
還流コンデンサ及び窒素導入管付きの250mlの三口丸底フラスコに、8.4gの(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン((3−methacryloxy−2−hydroxypropoxy)propylbis(trimethylsiloxy)methylsilane;SiGMA)、19.9gのポリエチレングリコールメタクリル酸メチルエーテル(polyethylene glycol methacrylate monomethyl ether;数平均分子量500(EO9))、0.78gのメルカプトエタノール(mercaptoethanol)及び30mlのテトラヒドロフラン(THF)を添加した。窒素環境で30分間還流した後、溶液を磁石で攪拌しながら80℃まで加熱した。その後、0.0283gの熱開始剤Vazo 64(AIBN)を混合物に添加し、且つ持続的に攪拌して40時間還流し、混合物が冷却された後、溶剤を除去して、更に粗生成物を浄化して乾燥した。ゲル透過クロマトグラフィー(GPC)によって数平均分子量(Mn)が3789であることが判明され、核磁気共鳴スペクトル(NMR)でその構造を確認した。
還流コンデンサ及び窒素導入管付きの250mlの三口丸底フラスコに、7.4gのヒドロキシ末端コポリマー1、0.04gのジブチルスズジラウレート(dibutyltin dilaurate)、0.0008gのメチルハイドロキノン(methyl hydroquinone)及び8mlのTHFを添加した。窒素環境で30分間還流した後、0.326gのメタクリル酸2−イソシアナトエチル(isocyanatoethyl methacrylate)を混合物にゆっくり滴下して混合物を磁石で攪拌し、この工程で10分間反応させた。20時間後、反応が終止した。溶剤を除去し、更に粗生成物を浄化して乾燥した。最後、ゲル透過クロマトグラフィー(GPC)によって数平均分子量(Mn)が3850であることが判明され、且つ核磁気共鳴スペクトル(NMR)でその構造を確認した。ヒドロキシ末端コポリマー1において、SiGMA/EO9の重量比が30/70であった。
ヒドロキシ末端コポリマー2の調製方法は、SiGMA/EO9の重量比が35/65であること以外、上記ヒドロキシ末端コポリマー1の調製方法と同様であった。
水溶性シリコーンマクロマー2の調製方法は、ヒドロキシ末端コポリマー2でヒドロキシ末端コポリマー1を代替すること以外、上記水溶性シリコーンマクロマー1の調製方法と同様であった。
ヒドロキシ末端コポリマー3の調製方法は、SiGMA/EO9の重量比が40/60であること以外、上記ヒドロキシ末端コポリマー1の調製方法と同様であった。
水溶性シリコーンマクロマー3の調製方法は、ヒドロキシ末端コポリマー1をヒドロキシ末端コポリマー3で代替すること以外、上記水溶性シリコーンマクロマー1の調製方法と同様であった。
ヒドロキシ末端コポリマー4の調製方法は、SiGMA/EO9の重量比が45/55であること以外、上記ヒドロキシ末端コポリマー3の調製方法と同様であった。
水溶性シリコーンマクロマー4の調製方法は、ヒドロキシ末端コポリマー3をヒドロキシ末端コポリマー4で代替すること以外、上記水溶性シリコーンマクロマー3の調製方法と同様であった。
ヒドロキシ末端コポリマー5の調製方法は、目標とする数平均分子量が5000であること以外、上記ヒドロキシ末端コポリマー3の調製方法と同様であった。
水溶性シリコーンマクロマー5の調製方法は、ヒドロキシ末端コポリマー3をヒドロキシ末端コポリマー5で代替すること及びメタクリル酸2−イソシアナトエチル(isocyanatoethyl methacrylate)の添加量以外、上記水溶性シリコーンマクロマー3の調製方法と同様であった。
ヒドロキシ末端コポリマー6の調製方法は、SiGMAをTRISで代替し、且つTRIS/EO9の重量比が30/70であり、目標とする数平均分子量が3000であること以外、上記ヒドロキシ末端コポリマー1の調製方法と同様であった。
水溶性シリコーンマクロマー6の調製方法は、ヒドロキシ末端コポリマー1をヒドロキシ末端コポリマー6で代替すること以外、上記水溶性シリコーンマクロマー1の調製方法と同様であった。
ヒドロキシ末端コポリマー7の調製方法は、TRIS/EO9の重量比が35/65であること以外、上記ヒドロキシ末端コポリマー6の調製方法と同様であった。
水溶性シリコーンマクロマー7の調製方法は、ヒドロキシ末端コポリマー6をヒドロキシ末端コポリマー7で代替すること以外、上記水溶性シリコーンマクロマー6の調製方法と同様であった。
ヒドロキシ末端コポリマー8の調製方法は、TRIS/EO9の重量比が40/60であること以外、上記ヒドロキシ末端コポリマー6の調製方法と同様であった。
水溶性シリコーンマクロマー8の調製方法は、ヒドロキシ末端コポリマー6をヒドロキシ末端コポリマー8で代替すること以外、上記水溶性シリコーンマクロマー6の調製方法と同様であった。
ヒドロキシ末端コポリマー9の調製方法は、TRIS/EO9の重量比が45/55であること以外、上記ヒドロキシ末端コポリマー6の調製方法と同様であった。
水溶性シリコーンマクロマー9の調製方法は、ヒドロキシ末端コポリマー6をヒドロキシ末端コポリマー9で代替すること以外、上記水溶性シリコーンマクロマー6の調製方法と同様であった。
ヒドロキシ末端コポリマー10の調製方法は、目標とする数平均分子量が5000であること以外、上記ヒドロキシ末端コポリマー6の調製方法と同様であった。
水溶性シリコーンマクロマー10の調製方法は、ヒドロキシ末端コポリマー6をヒドロキシ末端コポリマー10で代替すること以外、上記水溶性シリコーンマクロマー6の調製方法と同様であった。
ヒドロキシ末端コポリマー11の調製方法は、目標とする数平均分子量が5000であること以外、上記ヒドロキシ末端コポリマー7の調製方法と同様であった。
水溶性シリコーンマクロマー11の調製方法は、ヒドロキシ末端コポリマー7をヒドロキシ末端コポリマー11で代替すること以外、上記水溶性シリコーンマクロマー7の調製方法と同様であった。
ヒドロキシ末端コポリマー12の調製方法は、EO9をN,N−ジメチルアクリルアミド(N,N−dimethyl acrylamide)で代替すること以外、上記ヒドロキシ末端コポリマー3の調製方法と同様であった。
水溶性シリコーンマクロマー12の調製方法は、ヒドロキシ末端コポリマー3をヒドロキシ末端コポリマー12で代替すること以外、上記水溶性シリコーンマクロマー3の調製方法と同様であった。
ヒドロキシ末端コポリマー13の調製方法は、SiGMAを化学式(10)の単官能性ポリジメチルシロキサンマクロマーで代替し、且つ化学式(10)の単官能性ポリジメチルシロキサンマクロマー/N,N−ジメチルアクリルアミド(N,N−dimethyl acrylamide)の重量比が35/65であること以外、上記ヒドロキシ末端コポリマー12の調製方法と同様であった。
水溶性シリコーンマクロマー13の調製方法は、ヒドロキシ末端コポリマー12をヒドロキシ末端コポリマー13で代替すること以外、上記水溶性シリコーンマクロマー12の調製方法と同様であった。
ヒドロキシ末端コポリマー14の調製方法は、一部のEO9をN,N−ジメチルアクリルアミド(N,N−dimethyl acrylamide)で代替し、且つTRIS/EO9/N,N−ジメチルアクリルアミドの重量比が40/40/20であること以外、上記ヒドロキシ末端コポリマー8の調製方法と同様であった。
水溶性シリコーンマクロマー14の調製方法は、ヒドロキシ末端コポリマー8をヒドロキシ末端コポリマー14で代替すること以外、上記水溶性シリコーンマクロマー8の調製方法と同様であった。
UV・可視分光光度計によって濃度1%、0.5%、0.1%の水溶性シリコーンマクロマー水溶液及び濃度0.5%の水溶性シリコーンマクロマー水溶液に300ppmの界面活性剤Triton(商標) X−100が添加されたものの450nmでの光透過率を測定して判断した。上記1%の水溶性シリコーンマクロマー水溶液は、0.1gの水溶性シリコーンマクロマーを10mlの水に添加して、且つ3時間攪拌することで得られた。上記実施例の水溶性シリコーンマクロマーの水溶性測定結果は、以下の表2に示される。
水溶性シリコーンマクロマー、第二親水性モノマー、架橋剤、溶剤(5%のtert−アミルアルコール)、青色染料化合物(200ppmのRB−19)、光開始剤(0.2%のIrgacure(登録商標) 819)を含む反応混合物を調製した。
以下の表3で挙げられた異なるレシピのシリコーンハイドロゲル組成物について、上記製造方法によってシリコーンハイドロゲルコンタクトレンズを製造し、且つ含水量及び酸素透過性の測定を行った。
以下の表4で挙げられた異なるレシピのシリコーンハイドロゲル組成物について、上記製造方法によってシリコーンハイドロゲルコンタクトレンズを製造し、且つ含水量、酸素透過性及び伸び率の測定を行った。且つそれぞれ熱水及びイソプロパノールでシリコーンハイドロゲルコンタクトレンズを抽出処理し、その抽出率を比較した。
以下の表5で挙げられた異なるレシピのシリコーンハイドロゲル組成物について、上記製造方法でシリコーンハイドロゲルコンタクトレンズを製造し、且つ伸び率の測定を行った。
以下の表6で挙げられた異なるレシピのシリコーンハイドロゲル組成物について、上記製造方法でシリコーンハイドロゲルコンタクトレンズを製造して、含水量、酸素透過性及び伸び率の測定を行った。
22℃、相対湿度50%の条件で、シリコーンハイドロゲルコンタクトレンズを計量台の頂部のサンプルトレイに入れて、且つ0、5、10、15、20、25、30、60分間で計量して記録する。図1及び表7は、本発明の実施例のシリコーンハイドロゲルコンタクトレンズ34A〜34Cと市販のハイドロゲルコンタクトレンズ(Omafilcon B、Etafilcon A)及びシリコーンハイドロゲルコンタクトレンズ(Clariti)に対して水の損失テストを行った結果の比較である。
Claims (25)
- 式(1)に示す構造を有する水溶性シリコーンマクロマーであって、
E−(M1)x−(M2)y 式(1)
M1はケイ素含有モノマーから誘導された繰り返し単位であり、水溶性シリコーンマクロマーの総重量に対する含有量が30〜60wt%であり、
M2は第一親水性モノマーから誘導された繰り返し単位であり、水溶性シリコーンマクロマーの総重量に対する含有量が40〜70wt%であり、
Eはビニル系不飽和化合物から誘導された基であり、
xは1〜20の整数であり、
yは1〜20の整数であり、
且つ前記水溶性シリコーンマクロマーの数平均分子量は2000〜5000の範囲にある水溶性シリコーンマクロマー。 - 前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン、数平均分子量が1500より小さい単官能性ポリジメチルシロキサンマクロマー及びその組み合わせからなる群から選ばれ、前記単官能性ポリジメチルシロキサンマクロマーは、化学式(10)又は化学式(11)の化学構造を有し、
- 前記第一親水性モノマーは、N,N−ジメチルアクリルアミド、N,N−ジエチルアクリルアミド、N−イソプロピルアクリルアミド、N−ビニルピロリドン、N−エチル−N−メチルエチルアミド、2−ヒドロキシエチルメタクリレート、メタクリル酸グリシジル、数平均分子量が1000より小さいポリエチレングリコールメタクリル酸メチルエーテル及びその組み合わせからなる群から選ばれる請求項1に記載の水溶性シリコーンマクロマー。
- 前記ビニル系不飽和化合物は、塩化アクリル、アクリル酸、メタクリル酸、メタクリル酸グリシジル、メタクリル酸2−イソシアナトエチル及びアクリル酸2−イソシアナトエチルからなる群から選ばれる請求項1に記載の水溶性シリコーンマクロマー。
- 前記第一親水性モノマーは、数平均分子量が1000より小さいポリエチレングリコールメタクリル酸メチルエーテルであり、
前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン及びその組み合わせからなる群から選ばれる請求項1に記載の水溶性シリコーンマクロマー。 - 前記第一親水性モノマーは、数平均分子量が500より小さいポリエチレングリコールメタクリル酸メチルエーテルであり、
前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン及びその組み合わせからなる群から選ばれる請求項1に記載の水溶性シリコーンマクロマー。 - 前記第一親水性モノマーは、N,N−ジメチルアクリルアミドであり、
前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン、数平均分子量が1500より小さい単官能性ポリジメチルシロキサンマクロマー及びその組み合わせからなる群から選ばれ、前記単官能性ポリジメチルシロキサンマクロマーは、化学式(10)又は化学式(11)の化学構造を有し、
- 前記第一親水性モノマーは、N−ビニルピロリドンであり、
前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン、数平均分子量が1500より小さい単官能性ポリジメチルシロキサンマクロマー及びその組み合わせからなる群から選ばれ、前記単官能性ポリジメチルシロキサンマクロマーは、化学式(10)又は化学式(11)の化学構造を有し、
- 前記第一親水性モノマーは、N−イソプロピルアクリルアミドであり、
前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン、数平均分子量が1500より小さい単官能性ポリジメチルシロキサンマクロマー及びその組み合わせからなる群から選ばれ、前記単官能性ポリジメチルシロキサンマクロマーは、化学式(10)又は化学式(11)の化学構造を有し、
- 前記第一親水性モノマーは、N,N−ジエチルアクリルアミドであり、
前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン、数平均分子量が1500より小さい単官能性ポリジメチルシロキサンマクロマー及びその組み合わせからなる群から選ばれ、前記単官能性ポリジメチルシロキサンマクロマーは、化学式(10)又は化学式(11)の化学構造を有し、
- 前記第一親水性モノマーは、数平均分子量が500より小さいポリエチレングリコールメタクリル酸メチルエーテル及びN,N−ジメチルアクリルアミドの組み合わせであり、
前記ケイ素含有モノマーは、3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン、3−アクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−メタアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、3−ビニルアクリルアミドプロピルトリス(トリメチルシロキシ)シラン、(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシラン及びその組み合わせからなる群から選ばれる請求項1に記載の水溶性シリコーンマクロマー。 - 前記第一親水性モノマーは、N,N−ジメチルアクリルアミド、N,N−ジエチルアクリルアミド、N−イソプロピルアクリルアミド、N−ビニルピロリドン、N−エチル−N−メチルエチルアミド、2−ヒドロキシエチルメタクリレート、メタクリル酸グリシジル及びその組み合わせからなる群から選ばれ、
前記ケイ素含有モノマーは数平均分子量が1500より小さい単官能性ポリジメチルシロキサンマクロマーと3−メタアクリロイルオキシプロピルトリス(トリメチルシロキシ)シラン又は(3−メタアクリロイルオキシ−2−ヒドロキシプロポキシ)プロピルビス(トリメチルシロキシ)メタシランとの組成物を含み、前記単官能性ポリジメチルシロキサンマクロマーは、化学式(10)又は化学式(11)の化学構造を有し、
- 濃度0.5wt%の前記水溶性シリコーンマクロマーの水溶液の450nmでの光透過率が20%より大きい請求項1に記載の水溶性シリコーンマクロマー。
- シリコーンハイドロゲル組成物であって、
前記シリコーンハイドロゲル組成物の総重量に対する含有量が50〜80wt%である、請求項1〜13の何れか1項に記載の水溶性シリコーンマクロマーと、
前記シリコーンハイドロゲル組成物の総重量に対する含有量が19〜50wt%である第二親水性モノマーと、
前記シリコーンハイドロゲル組成物の総重量に対する含有量が0.1〜1.5wt%である架橋剤と;
前記シリコーンハイドロゲル組成物の総重量に対する含有量が0.1〜1wt%である開始剤と、
有機溶剤と、
を含むシリコーンハイドロゲル組成物。 - 前記第二親水性モノマーは、N,N−ジメチルアクリルアミド(DMA)、N,N−ジエチルアクリルアミド(DEA)、N−イソプロピルアクリルアミド(NIPAM)、N−ビニルピロリドン(NVP)、N−エチル−N−メチルエチルアミド(VMA)、2−ヒドロキシエチルメタクリレート(HEMA)、3−ヒドロキシプロピルメタクリレート(HPMA)、メタクリル酸グリシジル、メタクリル酸(MAA)、アクリル酸(AA)、アクリロイルモルホリン(ACMO)、2−メタアクリロイルオキシエチルホスホリルコリン(MPC)及びその組み合わせからなる群から選ばれる請求項14に記載のシリコーンハイドロゲル組成物。
- 前記架橋剤は、エチレングリコールジメタクリレート(EGDMA)、トリエチレングリコールジメタクリレート、テトラエチレングリコールジメタクリレート(TEGDMA)、トリメチロールプロパントリメタクリレート(TMPTMA)、ネオペンタエリトリトールテトラメタクリレート(TMAPMA)、ビスフェノールAジメタクリレート、メチレンビスメタアクリルアミド、ジビニルエーテル、ジビニルスルホン、ジビニルベンゼン、トリビニルベンゼン、トリアリルイソシアヌレート(TAIC)、フタル酸トリアリル、フタル酸ジアリル、メタクリル酸アリル(AMA)及びその組み合わせからなる群から選ばれる請求項14に記載のシリコーンハイドロゲル組成物。
- 前記開始剤は、光開始剤又は熱開始剤である請求項14に記載のシリコーンハイドロゲル組成物。
- 前記有機溶剤は、n−ブタノール、tert−ブタノール、n−ペンタノール、tert−アミルアルコール、n−ヘキサノール、3−メトキシ−1−ブタノール、メチルカルビトール、エチルカルビトール、プロピルカルビトール、ブチルカルビトール及びその組み合わせからなる群から選ばれる請求項14に記載のシリコーンハイドロゲル組成物。
- 着色モノマー又は着色化合物を更に含む請求項14に記載のシリコーンハイドロゲル組成物。
- ベンゾトリアゾール(benzotriazole)基を有するUV遮断モノマーを更に含む請求項14に記載のシリコーンハイドロゲル組成物。
- 請求項14〜20の何れか1項に記載のシリコーンハイドロゲル組成物に架橋硬化反応を行うことによって製造されるシリコーンハイドロゲルコンタクトレンズ。
- シリコーンハイドロゲルコンタクトレンズであって、請求項1〜13の何れか1項に記載の水溶性シリコーンマクロマーから製造されて、前記コンタクトレンズの含水量は52〜72%であり、酸素透過性は50〜75DKであるシリコーンハイドロゲルコンタクトレンズ。
- 請求項1〜13の何れか1項に記載の水溶性シリコーンマクロマーに光重合反応を行うことで製造され、且つ前記光重合反応を行った後、有機溶剤で抽出処理されないシリコーンハイドロゲルコンタクトレンズ。
- 請求項14〜20の何れかの一項に記載のシリコーンハイドロゲル組成物を提供する工程と、
前記シリコーンハイドロゲル組成物を架橋硬化反応させ、シリコーンハイドロゲルコンタクトレンズを形成する工程と、
水を含有する液体によって前記シリコーンハイドロゲルコンタクトレンズを抽出処理することで、前記シリコーンハイドロゲルコンタクトレンズにおける前記架橋硬化反応をしなかった水溶性シリコーンマクロマーを除去する工程と、
を備えるシリコーンハイドロゲルコンタクトレンズの製造方法。 - 前記水を含有する液体は、HLB値が13〜17の界面活性剤を更に含む請求項24に記載のシリコーンハイドロゲルコンタクトレンズの製造方法。