JP2017214459A - ポリメチルペンテン樹脂組成物 - Google Patents
ポリメチルペンテン樹脂組成物 Download PDFInfo
- Publication number
- JP2017214459A JP2017214459A JP2016107679A JP2016107679A JP2017214459A JP 2017214459 A JP2017214459 A JP 2017214459A JP 2016107679 A JP2016107679 A JP 2016107679A JP 2016107679 A JP2016107679 A JP 2016107679A JP 2017214459 A JP2017214459 A JP 2017214459A
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- polymethylpentene resin
- resin composition
- polymethylpentene
- crystal polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
〈結晶融解温度〉
示差走査熱量計(セイコーインスツルメンツ株式会社製Exstar6000)を用いて、試料を室温から20℃/分の昇温条件で測定した際に観測される吸熱ピーク温度(Tm1)を測定した後、Tm1より50℃高い温度で10分間保持する。次いで、20℃/分の降温条件で室温まで試料を冷却し、さらに再度20℃/分の昇温条件で測定した際の吸熱ピークを観測し、そのピークトップを示す温度を結晶融解温度(Tm)とした。
射出成形機(日精樹脂工業株式会社製 UH1000−110)にて、厚み0.5mm、幅12.7mmのバーフロー流動長測定金型を用いて、シリンダー温度300℃、射出圧力75MPaにて成形したときの流動長で評価した。
溶融粘度測定装置(東洋精機(株)製キャピログラフ1D)により、0.7mmφ×10mmのキャピラリーレオメーターを用いて、300℃にて溶融粘度を測定した。
射出成形機(日精樹脂工業(株)製UH1000−110)を用いて、結晶融解温度+20〜40℃のシリンダー温度、金型温度70℃にて、短冊状試験片(長さ127mm×幅12.7mm×厚さ3.2mm)を射出成形し、これを用いてASTM D648に準拠し、荷重0.46MPa、昇温速度2℃/分で所定たわみ量(0.254mm)になる温度を測定した。
射出成形機(日精樹脂工業(株)製UH1000−110)を用いて、結晶融解温度+20〜40℃のシリンダー温度、金型温度70℃にて、円板状試験片(直径50mm×厚さ3mm)を射出成形し、これを用いてASTM D792に準拠して測定した。
射出成形機(日精樹脂工業(株)製UH1000−110)を用いて、結晶融解温度+20〜40℃のシリンダー温度、金型温度70℃にて、ダンベル状引張試験片(長さ115mm×幅6mm×厚さ3.2mm)を射出成形した。INSTRON5567(インストロンジャパン カンパニイリミテッド社製万能試験機)を用いて、ASTM D638に準拠し、チャック間距離64.0mm、引張速度5mm/minで測定した。
引張強度および引張弾性率測定に用いた成形片と同条件にし、短冊状曲げ試験片(長さ127mm×幅12.7mm×厚さ3.2mm)を射出成形した。曲げ試験は、3点曲げ試験をINSTRON5567(インストロンジャパン カンパニイリミテッド社製万能試験機)を用いて、ASTM D790に準拠し、スパン間距離50.0mm、圧縮速度1.3mm/minで行った。
PMP:ポリメチルペンテン
LCP:液晶ポリエステル
POB:4−ヒドロキシ安息香酸
BON6:6−ヒドロキシ−2−ナフトエ酸
HQ:ハイドロキノン
BP:4,4’−ビフェノール
TPA:テレフタル酸
実施例において、ポリメチルペンテン樹脂として以下のものを使用した。
PMP:三井化学社製TPX(MX004)
[合成例1(LCP1)]
トルクメーター付き攪拌装置および留出管を備えた2Lの反応容器に、POB、BON6を表1に示す組成比で、総量6.5molとなるように仕込み、全モノマーの水酸基量(モル)に対して1.03倍モルの無水酢酸を仕込み、次の条件で脱酢酸重合を行った。
トルクメーター付き攪拌装置および留出管を備えた2Lの反応容器に、POB、BON6、HQ、BPおよびTPAを表2に示す組成比にて、総量6.5molとなるように仕込み、さらに全モノマーの水酸基量(モル)に対して1.03倍モルの無水酢酸を仕込み、次の条件で脱酢酸重合を行った。
ポリメチルペンテンおよびLCP1を、表3に記載の重量比となるようにブレンドし、二軸押出機TEX−30(日本製鋼所株式会社製)を用いて、300℃にて溶融混練を行い、LCPが均一に分散されたポリメチルペンテン樹脂組成物のペレットを得た。その後、流動性、溶融粘度、荷重たわみ温度、比重、引張強度、引張弾性率、曲げ強度および曲げ弾性率を測定した。
ポリメチルペンテン樹脂、LCP1をそれぞれ単独で、実施例1と同様に流動性、溶融粘度、荷重たわみ温度、比重、引張強度、引張弾性率、曲げ強度および曲げ弾性率を測定した。結果を表3に示す。
ポリメチルペンテン樹脂、LCP1を表3に示すような比率に変更した以外は、実施例1と同様にしてポリメチルペンテン樹脂組成物のペレットを作製し、流動性、溶融粘度、荷重たわみ温度、比重、引張強度、引張弾性率、曲げ強度および曲げ弾性率を測定した。結果を表3に示す。
ポリメチルペンテンおよびLCP2を、表3に記載の重量比となるようにブレンドし、二軸押出機TEX−30(日本製鋼所株式会社製)を用いて、355℃にて溶融混練を試みたが、混練開始直後からPMPの分解に伴うガスが大量に発生したため、溶融混練を中止した。
Claims (6)
- ポリメチルペンテン樹脂100重量部に対して、結晶融解温度が300℃以下である液晶ポリマー0.1〜100重量部を含有するポリメチルペンテン樹脂組成物。
- 比重が1.00g/cm3以下である、請求項1〜4の何れかに記載のポリメチルペンテン樹脂組成物。
- 請求項1〜5の何れかに記載のポリメチルペンテン樹脂組成物から構成される成形品。