JP2017069197A - 光透過性導電フィルム及び光透過性導電フィルムの製造方法 - Google Patents
光透過性導電フィルム及び光透過性導電フィルムの製造方法 Download PDFInfo
- Publication number
- JP2017069197A JP2017069197A JP2016184076A JP2016184076A JP2017069197A JP 2017069197 A JP2017069197 A JP 2017069197A JP 2016184076 A JP2016184076 A JP 2016184076A JP 2016184076 A JP2016184076 A JP 2016184076A JP 2017069197 A JP2017069197 A JP 2017069197A
- Authority
- JP
- Japan
- Prior art keywords
- conductive layer
- ino
- conductive film
- light
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明に係る光透過性導電フィルムは、光透過性及び導電性を有する導電層と、前記導電層の一方の表面側に配置されている基材とを備え、前記導電層のXRD測定を行い、前記導電層の面方向において360°にわたりInO2(222)の回折パターンを測定したときに、InO2(222)の回折強度の最大値のInO2(222)の回折強度の最小値に対する比が2以下である。
【選択図】図1
Description
基材の全体の厚みは、好ましくは23μm以上、より好ましくは50μm以上、好ましくは300μm以下、より好ましくは200μm以下である。
基材フィルムは、高い光透過性を有することが好ましい。従って、基材フィルムの材料としては、特に限定されないが、例えば、ポリオレフィン、ポリエーテルサルフォン、ポリスルホン、ポリカーボネート、シクロオレフィンポリマー、ポリアリレート、ポリアミド、ポリメチルメタクリレート、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、トリアセチルセルロース、及びセルロースナノファイバー等が挙げられる。上記基材フィルムの材料は、単独で用いてもよく、複数を併用してもよい。
第1及び第2のハードコート層はそれぞれ、バインダー樹脂により構成されていることが好ましい。上記バインダー樹脂は、硬化樹脂であることが好ましい。上記硬化樹脂としては、熱硬化樹脂や、活性エネルギー線硬化樹脂などを用いることができる。生産性及び経済性を良好にする観点から、上記硬化樹脂は、紫外線硬化樹脂であることが好ましい。
アンダーコート層は、例えば、屈折率調整層である。アンダーコート層を設けることで、光透過性導電フィルムの光透過性をより一層高めることができる。
導電層は、光透過性を有する導電性材料により形成されている。上記導電性材料として、インジウム・錫酸化物(ITO)が用いられている。上記導電層は、非晶質層である。
保護フィルムは、基材シート及び粘着剤層により構成されていることが好ましい。
基材フィルムとして、厚み50μmのPETフィルムを用いた。PETフィルムの一方の面にジルコニア粒子を分散したアクリル系ハードコート樹脂を塗布し、厚み1.0μmのハードコート層を得た。PETフィルムの他方の面には、アクリル系ハードコート樹脂を塗布し、厚み1.0μmのハードコート層を得た。このようにして、両面ハードコートフィルムを得た。
導電層の形成時の搬送速度及び形成温度を下記の表1に示すように設定したこと以外は実施例1と同様にして、光透過性導電フィルムを作製した。
基材フィルムとして、厚み125μmのPETフィルムを用いた。PETフィルムの一方の面にジルコニア粒子を分散したアクリル系ハードコート樹脂を塗布し、厚み0.8μmのハードコート層を得た。PETフィルムの他方の面には、アクリル系ハードコート樹脂を塗布し、厚み0.8μmのハードコート層を得た。このようにして、両面ハードコートフィルム(基材)を得た。
導電層の形成時の搬送速度及び形成温度を下記の表1に示すように設定したこと以外は実施例5と同様にして、光透過性導電フィルムを作製した。
(1)XRD測定
XRD測定には、光透過性導電フィルムを送風乾燥機内で150℃で1時間加熱処理したフィルムをサンプルとして用いた。X線回折装置としてリガク社製の薄膜評価用資料水平型X線回折装置 SmartLabを用いて、薄膜法にて両方向のロッキングカーブを測定した。具体的には、平行ビーム光学配置を用い、光源にはCuKα線(波長:1.5418Å)を40kV、30mAのパワーで用いた。入射側スリット系にはソーラスリット5.0°、高さ制御スリット10mm、入射スリット0.1mmを用い、受光側スリットにはパラレルスリットアナライザー(PSA)0.114deg.を用いた。検出器にはシンチレーションカウンターを用いた。φ軸のステップ間隔及び測定スピードはステップ間隔0.2°、測定スピード10°/minとした。
得られた光透過性導電フィルムについて、以下の基準で骨見えの評価を行った。
○○…LED光、蛍光灯及び白色灯のいずれを照射した場合においても、目視で導電層のパターンが視認されない。
○…LED光を照射した場合には、目視で導電層パターンが視認されるが、蛍光灯及び白色灯のいずれを照射した場合には、目視で導電層のパターンが視認されない。
×…LED光、蛍光灯及び白色灯のいずれを照射した場合においても、目視で導電層パターンが視認される。
2,2A…基材
2a…第1の表面
2b…第2の表面
3…導電層
4…保護フィルム
11…基材フィルム
12…第1のハードコート層
13…第2のハードコート層
14…アンダーコート層
Claims (5)
- 光透過性及び導電性を有する導電層と、
前記導電層の一方の表面側に配置されている基材とを備え、
前記導電層のXRD測定を行い、前記導電層の面方向において360°にわたりInO2(222)の回折パターンを測定したときに、InO2(222)の回折強度の最大値のInO2(222)の回折強度の最小値に対する比が2以下である、光透過性導電フィルム。 - 前記導電層のXRD測定を行い、前記導電層の面方向において360°にわたりInO2(222)の回折パターンを測定したときに、式:[(InO2(222)の回折強度の最大値−InO2(222)の回折強度の最小値)/InO2(222)の回折強度の平均値]の値が、0.7以下である、請求項1に記載の光透過性導電フィルム。
- 基材上に、光透過性及び導電性を有する導電層を形成し、光透過性導電フィルムを得る工程を備え、
前記導電層のXRD測定を行い、前記導電層の面方向において360°にわたりInO2(222)の回折パターンを測定したときに、InO2(222)の回折強度の最大値のInO2(222)の回折強度の最小値に対する比が2以下である、光透過性導電フィルムの製造方法。 - 前記導電層のXRD測定を行い、前記導電層の面方向において360°にわたりInO2(222)の回折パターンを測定したときに、式:[(InO2(222)の回折強度の最大値−InO2(222)の回折強度の最小値)/InO2(222)の回折強度の平均値]の値が、0.7以下である、請求項3に記載の光透過性導電フィルムの製造方法。
- ロールツーロール法により前記導電層を形成する、請求項3又は4に記載の光透過性導電フィルムの製造方法。