JP2016223001A - アルミニウム合金クラッド材およびろう付け方法 - Google Patents
アルミニウム合金クラッド材およびろう付け方法 Download PDFInfo
- Publication number
- JP2016223001A JP2016223001A JP2015113635A JP2015113635A JP2016223001A JP 2016223001 A JP2016223001 A JP 2016223001A JP 2015113635 A JP2015113635 A JP 2015113635A JP 2015113635 A JP2015113635 A JP 2015113635A JP 2016223001 A JP2016223001 A JP 2016223001A
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- brazing
- aluminum
- clad
- surface layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【構成】Mg:0.2〜2.0%(質量%、以下同じ)を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の心材の片面または両面に、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とする。また、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とする。
【選択図】なし
Description
(1)材料の製造段階で表面に強固な酸化皮膜が形成されないこと。
(2)ろう材の溶融前から酸化皮膜の破壊あるいは脆弱化が進行すること。
(3)フィレット形成の開始後に、酸化皮膜の破壊がさらに速やかに進行すること。
これらのうち、(1)については、材料表面における酸化性元素の量が制限されている必要がある。酸化性元素のうち、一般のアルミニウム合金の添加元素として頻繁に使用されるのはMgであり、材料表面のMg量が制限されていることが重要である。その他のBe、Li、Ca、Ba等については、特殊な場合を除き、一般的には使用されない元素であるが、何かの理由で添加される場合は、添加量を厳しく制限する必要がある。
ろう付け試験評価用に表1に示す組成、厚さ、クラッド率を有する2種類のブレージングシートを準備した。ろう材と心材をそれぞれ連続鋳造により造塊し、心材については、得られた鋳塊を縦163mm、横163mm、厚さ27mmのサイズに面削した。ろう材については、得られた鋳塊を厚さ3mmあるいは1.5mmまで熱間圧延し、縦163mm、横163mmの寸法に切断した。心材とろう材を積層し、熱間圧延により3mm厚さまでクラッド圧延し、その後、1回の中間焼鈍を挟んで0.4mmまで冷間圧延し、最終焼鈍を施して調質をO材とした。
すき間充填長さは次の4段階で評価した(小数第一位は四捨五入)。
◎:≧19mm
〇:14〜18mm
△:6〜13mm
×:≦5mm
〇以上を合格とし、△と×は不合格と判定した。
◎:完全に均一なフィレットを形成
〇:長手方向にやや不均一な部分もあるが、左右に均等なフィレットを形成
△:左右に均等でないフィレットを形成
×:フィレットが極小あるいは左右のいずれかがフィレットを未形成
〇以上を合格とし、△と×は不合格と判定した。
Claims (18)
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、Mg:0.2〜2.0%(質量%、以下同じ)を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の心材の片面または両面に、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、Mg:0.2〜2.0%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の心材の片面または両面に、Zn:0.05〜4%、Si:0.05〜2%の1種または2種を含有し、Mgを0.1%未満に制限したアルミニウム合金の表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、Mg:0.2〜2.0%、Mn:0.05〜1.8%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の心材の片面または両面に、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、Mg:0.2〜2.0%、Mn:0.05〜1.8%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の心材の片面または両面に、Zn:0.05〜4%、Si:0.05〜2%のうちの1種または2種を含有し、Mgを0.1%未満に制限したアルミニウム合金の表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 前記心材が、さらにCu:0.05〜2%、Si:0.05〜1.0%の1種または2種を含有することを特徴とする請求項1〜4のいずれかに記載のアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Zn:0.05〜4%、Si:0.05〜2%のうちの1種または2種を含有し、Mgを0.1%未満に制限したアルミニウム合金の表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%を含有し、さらにLi:0.01〜0.2%、Be:0.01〜0.3%の1種または2種を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%を含有し、さらにLi:0.01〜0.2%、Be:0.01〜0.3%の1種または2種を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Zn:0.05〜4%、Si:0.05〜2%のうちの1種または2種を含有し、Mgを0.1%未満に制限したアルミニウム合金の表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%、Cu:0.05〜2%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%、Cu:0.05〜2%を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Zn:0.05〜4%、Si:0.05〜2%のうちの1種または2種を含有し、Mgを0.1%未満に制限したアルミニウム合金の表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%、Cu:0.05〜2%を含有し、さらにLi:0.01〜0.2%、Be:0.01〜0.3%の1種または2種を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Mgを0.1%未満に制限した純アルミニウムの表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 不活性ガス雰囲気中でフラックスを塗布せずにろう付けするためのアルミニウム合金クラッド材であって、アルミニウムあるいはアルミニウム合金の心材の片面または両面に、Mg:0.3〜2.0%、Cu:0.05〜2%を含有し、さらにLi:0.01〜0.2%、Be:0.01〜0.3%の1種または2種を含有し、残部Alおよび不可避的不純物からなるアルミニウム合金の中間材を介して、Zn:0.05〜4%、Si:0.05〜2%のうちの1種または2種を含有し、Mgを0.1%未満に制限したアルミニウム合金の表層材をクラッドしてなることを特徴とするアルミニウム合金クラッド材。
- 前記アルミニウムの心材が、Mg:0.2〜2.0%を含有し、残部Alおよび不可避的不純物からなることを特徴とする請求項6〜13のいずれかに記載のアルミニウム合金クラッド材。
- 前記アルミニウム合金の心材が、Mg:0.2〜2.0%、Mn:0.05〜1.8%を含有し、残部Alおよび不可避的不純物からなることを特徴とする請求項6〜13のいずれかに記載のアルミニウム合金クラッド材。
- 前記アルミニウム合金の心材が、さらにCu:0.05〜2%を含有することを特徴とする請求項14または15に記載のアルミニウム合金クラッド材。
- 前記表層材の厚さが0.1mm以下であることを特徴とする請求項1〜16のいずれかに記載のアルミニウム合金クラッド材。
- 請求項1〜17のいずれかに記載のアルミニウム合金クラッド材を組み付けてろう付けする方法であって、アルミニウム合金クラッド材をろう付け前に酸溶液あるいはアルカリ溶液によってエッチング処理することを特徴とするろう付け方法。