JP2015523430A - ジシクロペンタジエンベース樹脂組成物及びそれらから製造される物品 - Google Patents
ジシクロペンタジエンベース樹脂組成物及びそれらから製造される物品 Download PDFInfo
- Publication number
- JP2015523430A JP2015523430A JP2015513997A JP2015513997A JP2015523430A JP 2015523430 A JP2015523430 A JP 2015523430A JP 2015513997 A JP2015513997 A JP 2015513997A JP 2015513997 A JP2015513997 A JP 2015513997A JP 2015523430 A JP2015523430 A JP 2015523430A
- Authority
- JP
- Japan
- Prior art keywords
- hydrocarbon polymer
- polymer additive
- composition
- weight
- mole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、エラストマーと、ジシクロペンタジエン、シクロペンタジエン及びメチルシクロペンタジエン由来含有量を有する炭化水素ポリマー添加剤とを含む、ジシクロペンタジエンベース樹脂組成物に関する。本発明は、さらに、このようなジシクロペンタジエンベース樹脂組成物から製造される物品に関する。
別の態様において、タイヤが提供される。このタイヤは、少なくとも1種のエラストマーと、炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量、約100g/モル〜約800g/モルの重量平均分子量、及び、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点を有する炭化水素ポリマー添加剤とを含む組成物を含む。
さらに別の態様において、タイヤトレッドが提供される。このタイヤトレッドは、少なくとも1種のエラストマーと、炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量、約100g/モル〜約800g/モルの重量平均分子量、及び、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点を有する炭化水素ポリマー添加剤とを含む組成物を含む。
本明細書で用いられる場合、「ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量」は、ポリマーを生成する挙げられたモノマー成分の総含有量を表す。この用語は、挙げられた成分の各々がポリマーに存在すること、又は、挙げられた成分の全てからポリマーが誘導されることを必要とする又は意味することを意図するものではない。本発明のどの実施形態においても、挙げられた成分の1つ又は2つは、存在していない、又は最低限の量においてのみ存在しているということがあり得る。
炭化水素ポリマー添加剤を含む加硫組成物は、ウェットトラクションと転がり抵抗性能特性の利点のある組合せを有し得る。
ある実施形態において、組成物は、少なくとも1種のエラストマーを含む。組成物に含まれ得る典型的なエラストマーには、ブチルゴム、分岐(「星型分岐」)ブチルゴム、星形分岐ポリイソブチレンゴム、イソブチレンとパラ−メチルスチレンとのランダムコポリマー(ポリ(イソブチレン−co−p−メチルスチレン))、ポリブタジエンゴム(「BR」)、高シス−ポリブタジエン、ポリイソプレンゴム、イソプレン−ブタジエンゴム(「IBR」)、スチレン−イソプレン−ブタジエンゴム(「SIBR)、スチレン−ブタジエンゴム(SBR)、溶液重合−スチレン−ブタジエンゴム(「sSBR」)、乳化重合−スチレン−ブタジエンゴム、ニトリルゴム、エチレンプロピレンゴム(「EP」)、エチレン−プロピレン−ジエンゴム(「EPDM」)、合成ポリイソプレン、汎用ゴム、天然ゴム、及びこれらのエラストマーのハロゲン化対応物、並びにこれらの混合物が含まれる。有用なエラストマーは、当技術分野において知られている適切な手段のどれかによって製造でき、本発明は、エラストマーの製造方法によっては限定されない。
エラストマーは、ハロゲン化されていることも、されていないこともある。好ましいハロゲン化エラストマーは、ハロゲン化ブチルゴム、ブロモブチルゴム、クロロブチルゴム、ハロゲン化分岐(「星型分岐」)ブチルゴム、及びイソブチレンとパラ−メチルスチレンのハロゲン化ランダムコポリマーからなる群から選択され得る。
ある実施形態において、エラストマー組成物は、また、エチレン及びプロピレン由来単位のゴム、例えば、エチレン−プロピレンゴム(「EP」)及びエチレン−プロピレン−ジエンゴム(「EPDM」)、並びにこれらの混合物を含み得る。EP及びEPDMも、また、汎用エラストマーであると見なされ得る。EPDMの製造における適切なターモノマーの例は、エチリデンノルボルネン、1,4−ヘキサジエン、ジシクロペンタジエン、さらには他のモノマーである。
ある実施形態において、エラストマーは、ポリイソプレン(IR)ゴムを含み得る。100℃で測定したポリイソプレンゴムのムーニー粘度(ML 1+4、ASTM D1646)は、35〜70、若しくは40〜約65、又は、別の実施形態では、45〜60の範囲にあり得る。
本発明において有用なエラストマーは、様々な他のゴム又はプラスチックと、特に、ナイロン又はポリオレフィン(例えば、ポリプロピレン又はポリプロピレンのコポリマー)のような熱可塑性樹脂とブレンドされてもよい。これらの組成物は、ブラダーのような空気バリア、タイヤのインナーチューブ、タイヤのインナーライナー、エアースリーブ(例えば、エアーショックにおける)、ダイヤフラム、さらには高い空気又は酸素保持が望まれる他の用途に有用である。
ある実施形態において、エラストマーは、スチレンブタジエンゴム(「SBR」)(例えば、乳化重合−SBR(「E−SBR」)、溶液重合SBR(S−SBR)、高スチレンゴム(「HSR」)など)のようなスチレンゴムを含み得る。SBRの望ましい実施形態は、JSR Corporationから入手可能なE−SBRエラストマー(これには、JSR 1500(25重量%のスチレン)、JSR 1502(25重量%のスチレン)、JSR 1503(25重量%のスチレン)、JSR 1507(25重量%のスチレン)、JSR 0202(45重量%のスチレン)、JSR SL552(25重量%のスチレン)、JSR SL574(15重量%のスチレン)、JSR SL563(20重量%のスチレン)、JSR 0051、JSR 0061などが含まれる)のように、10〜60重量%のスチレン含有量を有し得る。好ましいSBRは、30〜120、又は、より好ましくは40〜80の100℃でのムーニー粘度(ML 1+4、ASTM D1646)を有する。
本発明の組成物は、また、炭化水素ポリマー添加剤を含む。炭化水素ポリマー添加剤は、炭化水素ポリマー添加剤の全重量の40〜80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量を有する。ある実施形態において、炭化水素ポリマー添加剤は、炭化水素ポリマー添加剤の全重量の50〜80重量%、又は60〜80重量%、又は70〜80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量を有し得る。ある実施形態において、炭化水素ポリマー添加剤は、ジシクロペンタジエン由来単位を主要な部分として含む、炭化水素樹脂であり得る。用語「ジシクロペンタジエン由来単位」、「ジシクロペンタジエン由来含有量」などは、ポリマーを生成するために用いられるジシクロペンタジエンモノマー、すなわち、重合前の状態の未反応化合物を表し、また、それがポリマー(これは、通常、重合反応のせいで、それが重合反応の前にもっているより少数の水素原子を有する)に組み入れられた後のモノマーも表すことができる。
ある実施形態において、炭化水素ポリマー添加剤は、ASTM D6090で求めて、約100℃〜約160℃、又は約110℃〜約150℃、又は約110℃〜約140℃、又は約115℃〜約140℃、又は約120℃〜約140℃の環球式軟化点を有し得る。
通常、ピペリレンは、C5ジオレフィンの留分又は合成混合物であり、これは、これらに限らないが、シス−1,3−ペンタジエン、トランス−1,3−ペンタジエン、及び混合1,3−ペンタジエンを含む。通常、ピペリレンは、イソプレンのような分岐C5ジオレフィンを含まない。
炭化水素ポリマー添加剤に存在し得る好ましい芳香族化合物には、スチレン、インデン、スチレン誘導体、及びインデン誘導体からの1種又は複数が含まれる。特に好ましい芳香族オレフィンには、スチレン、α−メチルスチレン、β−メチルスチレン、インデン、及びメチルインデン、並びにビニルトルエンが含まれる。
スチレン系成分には、スチレン、スチレン誘導体、及び置換スチレンが含まれる。通常、スチレン系成分は、縮合環、例えばインデンを含まない。
ある実施形態において、炭化水素ポリマー添加剤は水素化され得る。炭化水素ポリマー添加剤の水素化は、当技術分野において知られている方法のどれかによって実施でき、本発明は、水素化の方法によっては限定されない。例えば、炭化水素ポリマー添加剤の水素化は、バッチ式又は連続プロセスのいずれかであり得る。好ましくは、炭化水素ポリマー添加剤は触媒を用いて水素化される。炭化水素ポリマー添加剤の水素化に用いられる触媒は、通常、元素の周期表の6、8、9、10、又は11族からの元素に基づく担持一元金属及び二元金属触媒系である。
ある実施形態において、本発明の組成物は、ゴムコンパウンドに常用される他の成分及び添加剤、例えば、有効量の他の加工助剤、顔料、促進剤、架橋剤及び加硫剤、酸化防止剤、オゾン劣化防止剤、フィラー、及び/又はクレーを含み得る。ある実施形態において、エラストマー組成物は、他の有用な加工助剤、例えば、プラストマー、ポリブテン、又はこれらの混合物を含み得る。
ある実施形態において、本発明の組成物は、また、少なくとも1種のフィラー、例えば、炭酸カルシウム、クレー、マイカ、シリカ、シリケート、タルク、二酸化チタン、酸化アルミニウム、酸化亜鉛、デンプン、木粉、カーボンブラック、又はこれらの混合物も含み得る。フィラーは、任意の大きさであってよいが、通常は、例えばタイヤ業界では、約0.0001μm〜約100μmの範囲であり得る。
シリケートは、膨張性結晶格子を有するクレー鉱物の一般分類を表す、「スメクタイト」又は「スメクタイト型クレー」の少なくとも1種を含み得る。例えば、これは、モンモリロナイト、バイデライト、及びノントロナイトからなる2八面体スメクタイト、並びに、サポナイト、ヘクトライト、及びソーコナイトを含む3八面体スメクタイトを含み得る。やはり含まれるのは、合成により調製されるスメクタイトクレーである。
シリケートには、天然又は合成フィロシリケート、例えば、モンモリロナイト、ノントロナイト、バイデライト、ベントナイト、ボルコンスコイト、ラポナイト、ヘクトライト、サポナイト、ソーコナイト、マガダイト、ケニヤアイト、ステベンサイトなど、さらにはバーミキュライト、ハロイサイト、アルミネート酸化物、ハイドロタルサイトなども含まれ得る。上で論じられたシリケートの任意の組合せもまた想定される。
ある実施形態において、フィラーは、カーボンブラック又は改質カーボンブラックであり得る。フィラーは、また、カーボンブラックとシリカのブレンドであってもよい。ある実施形態において、エラストマー組成物は、タイヤのトレッド又はサイドウォールであり得、強化グレードのカーボンブラックを、ブレンドの10〜100phr、別の実施形態において、より好ましくは30〜80phr、又は50〜80phrのレベルで含む。カーボンブラックの有用なグレードは、N110〜N990の範囲を含む。
本発明の組成物及びこれらの組成物から製造される物品は、通常、少なくとも1種の加硫パッケージ、少なくとも1つの加硫剤、少なくとも1種の架橋剤の助けにより製造され、及び/又は、エラストマー組成物を加硫するプロセスを経る。本明細書で用いられる場合、少なくとも1つの加硫性パッケージは、業界によって一般に理解されている加硫後特性をゴムに付与できる任意の物質又は方法を表す。
ハロゲン含有エラストマーは、金属酸化物との、それらの反応によって架橋され得る。有用な金属酸化物の例には、これらに限らないが、ZnO、CaO、及びPbOが含まれる。金属酸化物は、単独で、又は対応するその金属脂肪酸複合体(例えば、ステアリン酸亜鉛、ステアリン酸カルシウムなど)と、或いは、単独で添加される有機脂肪酸、例えば、ステアリン酸と一緒に用いることができ、他の加硫剤、例えば、硫黄若しくは硫黄化合物、アルキルペルオキシド化合物、ジアミン又はこれらの誘導体と一緒に用いられてもよい。
硫黄は、ジエン含有エラストマーに対する最も一般的な化学加硫剤である。硫黄加硫系は、硫黄を活性化するための活性剤、促進剤、及び加硫速度を制御する助けとなる遅延剤からなり得る。
促進剤は、加硫の開始及び速度、並びに生成される架橋の数及びタイプを制御する助けとなる。遅延剤は、未加硫ゴムを加工するための十分な時間があるように、加硫の初期の開始を遅らせるために使用され得る。
加硫プロセスの速度の増加は、多くの場合有機化合物である、速度を増加させる促進剤の量を調節することによって制御され得る。天然ゴム、BR、及びSBRの促進加硫のメカニズムは、加硫剤、促進剤、活性剤、及びポリマーの間の複雑な相互作用を含む。理想的には、利用できる全ての加硫剤が、2つのポリマー鎖を互いにつなぎ、ポリマーマトリックスの全体としての強度を高める、有効な架橋を生成するために消費される。多数の促進剤が当技術分野において知られており、これらに限らないが、次のものが含まれる:ステアリン酸、ジフェニルグアニジン(DPG)、テトラメチルチウラムジスルフィド(TMTD)、ベンゾチアジルジスルフィド(MBTS)、N−tert−ブチル−2−ベンゾチアゾールスルフェンアミド(TBBS)、N−シクロヘキシル−2−ベンゾチアゾール−スルフェンアミド(CBS)、及びチオウレア。
ある実施形態において、少なくとも1種の加硫剤は、0.2〜10phr、又は0.5〜5phr、又は0.75phr〜2phr、存在し得る。
ある実施形態において、本発明の組成物は、当業者に知られている通常の手段のどれかによってコンパウンディング(混合)され得る。混合は、単一ステップにおいて、又は多段階で行われ得る。例えば、成分は、通常、少なくとも2つの段階で、すなわち、少なくとも1つの非生産段階と、それに続く生産混合段階で混合される。通常、最後の加硫剤は、「生産」混合段階と通常呼ばれる最終段階において混合される。生産混合段階において、混合は、通常、先行する非生産混合段階の混合温度より低い温度、又は最終温度で行われる。エラストマー、ポリマー添加剤、シリカ及びシリカカプラー、並びにカーボンブラックは、用いられる場合、通常、1つ又は複数の非生産混合段階において混合される。用語「非生産」及び「生産」混合段階は、ゴム混合技術の技術者によく知られている。
本発明の組成物は、繊維、フィルム、ラミネート、層、自動車のパーツのような産業用パーツ、器具ハウジング、消費者製品、包装材などを含めて、様々な形状の物品に、押出、圧縮成形、ブロー成形、射出成形、及びラミネートされ得る。
特に、本発明の組成物は、トラックのタイヤ、バスのタイヤ、自動車のタイヤ、オートバイのタイヤ、オフロードタイヤ、航空機のタイヤなどのような様々なタイヤ用途のための物品に有用である。このようなタイヤは、当業者に知られていて、直ちに明らかであろう様々な方法によって、組み立てられ、形作られ、成形され、加硫され得る。本発明の組成物は、最終物品、又は、タイヤのインナーライナーのような、最終物品の構成要素のいずれかに製造され得る。物品は、空気バリア、空気膜、フィルム、層(ミクロ層及び/又は多層)、インナーライナー、インナーチューブ、エアースリーブ、サイドウォール、トレッド、タイヤ加硫ブラダーなどから選択され得る。本発明のエラストマー組成物は、タイヤトレッドに特に有用であり得る。
本発明の組成物は、様々な用途、特に、空気タイヤ構成部材、ホース、コンベヤーベルト若しくは自動車ベルトのようなベルト、ソリッドタイヤ、履物構成部材、グラフィックアート用途のローラー、防振デバイス、薬学デバイス、接着剤、コーキング剤、シーラント、ガラス用コンパウンド、保護コーティング剤、エアークッション、空気バネ、空気ベロー(bellow)、アキュムレーターバッグ、流体保持及び加硫プロセスのためのブラダーに有用である。それらは、また、ゴム配合物における可塑剤として;ストレッチ−ラップフィルムに製造される組成物の成分として;潤滑油のための分散剤として;並びに、ポッティング及び電気ケーブル充填及びケーブルハウジングの材料としても有用である。
エラストマー組成物は、また、成形ゴムパーツにも有用であり、自動車サスペンションバンパー、自動車排気系ハンガー、及びボディマウントに広い用途が見出され得る。さらに別の用途において、1種又は複数のエラストマーの本発明の組成物は、また、医薬品のストッパー及びクロージャ及び医療デバイスのコーティングのような医療用途にも有用である。
「PR373」は、ExxonMobil Chemical CompanyからOppera(商標)373として入手可能な炭化水素ポリマー添加剤である。それは、89℃の軟化点、約1500g/モルの重量平均分子量、及び40重量%未満の、ジシクロペンタジエン/シクロペンタジエン/メチルシクロペンタジエン含有量を有する。
「E5415」は、ExxonMobil Chemical CompanyからEscorez(商標)5415として入手可能な炭化水素ポリマー添加剤である。それは、118℃の軟化点、約430g/モルの重量平均分子量、及び40〜80重量%の、ジシクロペンタジエン/シクロペンタジエン/メチルシクロペンタジエン含有量を有する。
「E5340」は、ExxonMobil Chemical CompanyからEscorez(商標)5340として入手可能な炭化水素ポリマー添加剤である。それは、140℃の軟化点、約460g/モルの重量平均分子量、及び40〜80重量%の、ジシクロペンタジエン/シクロペンタジエン/メチルシクロペンタジエン含有量を有する。
「E5600」は、ExxonMobil Chemical CompanyからEscorez(商標)5600として入手可能な炭化水素ポリマー添加剤である。それは、103℃の軟化点、約520g/モルの重量平均分子量、及び40〜80重量%の、ジシクロペンタジエン/シクロペンタジエン/メチルシクロペンタジエン含有量を有する。
「E5615」は、ExxonMobil Chemical CompanyからEscorez(商標)5615として入手可能な炭化水素ポリマー添加剤である。それは、118℃の軟化点、約500g/モルの重量平均分子量、及び40〜80重量%の、ジシクロペンタジエン/シクロペンタジエン/メチルシクロペンタジエン含有量を有する。
「ウェットトラクション」は、ASTM D5270−01に従うARES歪み制御レオメータを用い、歪み掃引(strain sweep)を実施することによって、2回目の歪みによる3%の歪みでの、0℃及び10Hzのtanδ値を比較することによって評価した。より大きな値は、より良好なウェットトラクション値を示唆する。
「Payne効果」は、G’@45%(kPa)を、G’A0.5%(kPa)から引くことによって求められる。
[0077]少なくとも1種のエラストマーと、炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量、約100g/モル〜約800g/モルの重量平均分子量、並びに、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点を有する炭化水素ポリマー添加剤とを含む、組成物。
[0079]炭化水素ポリマー添加剤の重量平均分子量が、約300g/モル〜約500g/モルである、段落[0077]の組成物。
[0080]炭化水素ポリマー添加剤の軟化点が、約110℃〜約140℃である、段落[0076]〜[0078]のいずれかの組成物。
[0081]炭化水素ポリマー添加剤の軟化点が、約115℃〜約140℃である、段落[0079]の組成物。
[0082]炭化水素ポリマー添加剤が、炭化水素ポリマー添加剤の全重量の約60重量%〜約100重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量を有する、段落[0076]〜[0080]のいずれかの組成物。
[0084]組成物が、加硫組成物である、段落[0076]〜[0084]のいずれかの組成物。
[0085]エラストマーが、組成物の全重量に対して約33重量%〜約75重量%の範囲で、組成物中に存在する、段落[0076]〜[0083]のいずれかの組成物。
[0087]段落[0076]〜[0085]のいずれかの組成物を含むタイヤ。
[0088]段落[0076]〜[0085]のいずれかの組成物を含むタイヤトレッド。
特定の実施形態及び特徴が、1組の上限値及び1組の下限値を用い、記載された。特に断らなければ、任意の下限から任意の上限までの範囲が想定されていることが理解されるべきである。特定の下限、上限及び範囲は、下の特許請求の範囲の1つ又は複数に現れる。全ての数値は、「約」又は「ほぼ」示された値であり、当業者によって予想され得る実験誤差及び変動が考慮されている。
また、本発明は以下の態様であり得る。
〔1〕少なくとも1種のエラストマー、及び
炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量と、約100g/モル〜約800g/モルの重量平均分子量と、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点とを有する炭化水素ポリマー添加剤
を含む組成物。
〔2〕炭化水素ポリマー添加剤の重量平均分子量が、約200g/モル〜約600g/モルである、前記〔1〕に記載の組成物。
〔3〕炭化水素ポリマー添加剤の重量平均分子量が、約300g/モル〜約500g/モルである、前記〔2〕に記載の組成物。
〔4〕炭化水素ポリマー添加剤の軟化点が、約110℃〜約140℃である、前記〔1〕から〔3〕のいずれかに記載の組成物。
〔5〕炭化水素ポリマー添加剤の軟化点が、約115℃〜約140℃である、前記〔4〕に記載の組成物。
〔6〕炭化水素ポリマー添加剤が、炭化水素ポリマー添加剤の全重量の約60重量%〜約80重量%の、ジシクロペンタジエン由来含有量を有する、前記〔1〕に記載の組成物。
〔7〕炭化水素ポリマー添加剤が、炭化水素ポリマー添加剤の全重量の約70重量%〜約
90重量%の、ジシクロペンタジエン由来含有量を有する、前記〔6〕に記載の組成物。
〔8〕組成物が、加硫組成物である、前記〔1〕に記載の組成物。
〔9〕エラストマーが、組成物の全重量に対して、約33重量%〜約75重量%の範囲で、組成物中に存在する、前記〔1〕に記載の組成物。
〔10〕炭化水素ポリマー添加剤が、組成物の全重量に対して、約3重量%〜約10重量%の範囲で、組成物中に存在する、前記〔1〕に記載の組成物。
〔11〕少なくとも1種のエラストマー、及び
炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量と、約100g/モル〜約800g/モルの重量平均分子量と、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点とを有する炭化水素ポリマー添加剤
を含む組成物を含むタイヤ。
〔12〕炭化水素ポリマー添加剤の重量平均分子量が、約200g/モル〜約600g/モルである、前記〔11〕に記載のタイヤ。
〔13〕炭化水素ポリマー添加剤の重量平均分子量が、約300g/モル〜約500g/モルである、前記〔12〕に記載のタイヤ。
〔14〕炭化水素ポリマー添加剤の軟化点が、約110℃〜約140℃である、前記〔11〕から〔13〕のいずれかに記載のタイヤ。
〔15〕炭化水素ポリマー添加剤の軟化点が、約115℃〜約140℃である、前記〔14〕に記載のタイヤ。
〔16〕少なくとも1種のエラストマー、及び
炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量と、約100g/モル〜約800g/モルの重量平均分子量と、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点とを有する炭化水素ポリマー添加剤
を含む組成物を含むタイヤトレッド。
〔17〕炭化水素ポリマー添加剤の重量平均分子量が、約200g/モル〜約600g/モルである、前記〔16〕に記載のタイヤ。
〔18〕炭化水素ポリマー添加剤の重量平均分子量が、約300g/モル〜約500g/モルである、前記〔17〕に記載のタイヤ。
〔19〕炭化水素ポリマー添加剤の軟化点が、約110℃〜約140℃である、前記〔16〕から〔18〕のいずれかに記載のタイヤ。
〔20〕炭化水素ポリマー添加剤の軟化点が、約115℃〜約140℃である、前記〔19〕に記載のタイヤ。
Claims (20)
- 少なくとも1種のエラストマー、及び
炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量と、約100g/モル〜約800g/モルの重量平均分子量と、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点とを有する炭化水素ポリマー添加剤
を含む組成物。 - 炭化水素ポリマー添加剤の重量平均分子量が、約200g/モル〜約600g/モルである、請求項1に記載の組成物。
- 炭化水素ポリマー添加剤の重量平均分子量が、約300g/モル〜約500g/モルである、請求項2に記載の組成物。
- 炭化水素ポリマー添加剤の軟化点が、約110℃〜約140℃である、請求項1から3のいずれかに記載の組成物。
- 炭化水素ポリマー添加剤の軟化点が、約115℃〜約140℃である、請求項4に記載の組成物。
- 炭化水素ポリマー添加剤が、炭化水素ポリマー添加剤の全重量の約60重量%〜約80重量%の、ジシクロペンタジエン由来含有量を有する、請求項1に記載の組成物。
- 炭化水素ポリマー添加剤が、炭化水素ポリマー添加剤の全重量の約70重量%〜約
90重量%の、ジシクロペンタジエン由来含有量を有する、請求項6に記載の組成物。 - 組成物が、加硫組成物である、請求項1に記載の組成物。
- エラストマーが、組成物の全重量に対して、約33重量%〜約75重量%の範囲で、組成物中に存在する、請求項1に記載の組成物。
- 炭化水素ポリマー添加剤が、組成物の全重量に対して、約3重量%〜約10重量%の範囲で、組成物中に存在する、請求項1に記載の組成物。
- 少なくとも1種のエラストマー、及び
炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量と、約100g/モル〜約800g/モルの重量平均分子量と、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点とを有する炭化水素ポリマー添加剤
を含む組成物を含むタイヤ。 - 炭化水素ポリマー添加剤の重量平均分子量が、約200g/モル〜約600g/モルである、請求項11に記載のタイヤ。
- 炭化水素ポリマー添加剤の重量平均分子量が、約300g/モル〜約500g/モルである、請求項12に記載のタイヤ。
- 炭化水素ポリマー添加剤の軟化点が、約110℃〜約140℃である、請求項11から13のいずれかに記載のタイヤ。
- 炭化水素ポリマー添加剤の軟化点が、約115℃〜約140℃である、請求項14に記載のタイヤ。
- 少なくとも1種のエラストマー、及び
炭化水素ポリマー添加剤の全重量の約40重量%〜約80重量%の、ジシクロペンタジエン、シクロペンタジエン、及びメチルシクロペンタジエン由来含有量と、約100g/モル〜約800g/モルの重量平均分子量と、ASTM D6090に従って求めて、約110℃〜約150℃の軟化点とを有する炭化水素ポリマー添加剤
を含む組成物を含むタイヤトレッド。 - 炭化水素ポリマー添加剤の重量平均分子量が、約200g/モル〜約600g/モルである、請求項16に記載のタイヤ。
- 炭化水素ポリマー添加剤の重量平均分子量が、約300g/モル〜約500g/モルである、請求項17に記載のタイヤ。
- 炭化水素ポリマー添加剤の軟化点が、約110℃〜約140℃である、請求項16から18のいずれかに記載のタイヤ。
- 炭化水素ポリマー添加剤の軟化点が、約115℃〜約140℃である、請求項19に記載のタイヤ。