JP2014189651A - エネルギー線硬化型樹脂組成物 - Google Patents
エネルギー線硬化型樹脂組成物 Download PDFInfo
- Publication number
- JP2014189651A JP2014189651A JP2013066868A JP2013066868A JP2014189651A JP 2014189651 A JP2014189651 A JP 2014189651A JP 2013066868 A JP2013066868 A JP 2013066868A JP 2013066868 A JP2013066868 A JP 2013066868A JP 2014189651 A JP2014189651 A JP 2014189651A
- Authority
- JP
- Japan
- Prior art keywords
- meth
- acrylate
- polyol
- polyether polyol
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】
(A1)ポリカプロラクトンジオールと、
(A2−1)芳香族構造を有する芳香族系ポリエーテルポリオールと、
(A2−2)3官能以上のポリオールを出発化合物とするポリエーテルポリオールと、
(A3)芳香族ポリイソシアネート、または、芳香族ポリイソシアネートと非芳香族ポリイソシアネートとの混合物であるポリイソシアネートと、
(A4)1以上の水酸基を有する(メタ)アクリレートモノマーと
を反応させて得られるウレタン(メタ)アクリレート、及び
(B)ガラス転移点が50℃以上のモノ(メタ)アクリレートモノマーまたはモノ(メタ)アクリルアミドモノマーを含有する。
【選択図】なし
Description
ポリカプロラクトン系ポリオール(A1)は、ジオールまたはトリオールにε−カプロラクトンを反応させて得られたものであり、好ましくは分子量150以下、より好ましくは分子量100以下のジオールまたはトリオールから得られたものである。特には、エチレングリコール、ジエチレングリコール、1,4−ブタンジオール等のジオールにε−カプロラクトンを反応させて得られたものである。分子量は500〜4000が好ましく、500〜2000がより好ましく、500〜800が更に好ましい。ここで、分子量は、水酸基価から算出される数平均分子量である。また、ジオールとトリオールを併用する場合、トリオールは好ましくは10モル%以下である。ポリカプロラクトンジオールの市販品としては、(株)ダイセルの「プラクセル205」(分子量530)や「プラクセル208」(分子量830)及びこれらの変形品種などを挙げることができる。
ポリエーテルポリオール(A2)は、2個以上のヒドロキシ基を持つ化合物(特にはポリオールまたはポリフェノール)にエチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド等のアルキレンオキサイドを付加重合させた化合物である。ポリエーテルポリオール(A2)の分子量は250〜2000が好ましく、300〜1500がより好ましく、300〜800が更に好ましい。ここでも、分子量は、水酸基価から算出される数平均分子量である。
ポリイソシアネート(A3)としては、2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート、1,3-キシレンジイソシアネート、1,4-キシレンジイソシアネート、キシリレンジイソシアネート、1,5-ナフタレンジイソシアネート、m−フェニレンジイソシアネート、p−フェニレンジイソシアネート、ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、4,4’-ジベンジルジイソシアネート、イソホロンジイソシアネート、ヘキサメチレンジイソシアネート、ジシクロヘキシルメタンジイソシアネート、2,2,4-トリメチルヘキサメチレンジイソシアネート、2,4,4-トリメチルヘキサメチレンジイソシアネートあるいはこれらジイソシアネート化合物のうち芳香族のイソシアネート類を水添して得られるジイソシアネート化合物(例えば水添キシリレンジイソシアネート、水添ジフェニルメタンジイソシアネートなどのジイソシアネート化合物)、トリフェニルメタントリイソシアネート、ジメチレントリフェニルトリイソシアネートなどのような2価あるいは3価のジイソシアネート化合物あるいはポリイソシアネート化合物や、これらを多量化させて得られる多量化ポリイソシアネート化合物等のイソシアネート基含有化合物が挙げられる。
ウレタン(メタ)アクリレートを得るのに用いられる1以上の水酸基を有する(メタ)アクリレート化合物(A4)としては、2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート、エチレングリコールモノ(メタ)アクリレート、プロピレングリコールモノ(メタ)アクリレート、2-ヒドロキシ-3-メトキシプロピルアクリレートもしくはメタクリレート、ペンタエリスリトールトリアクリレートもしくはメタクリレート、N−メチロールアクリルアミドもしくはメタクリルアミド、N−ヒドロキシアクリルアミドもしくはメタクリルアミド等が挙げられる。すなわち、本願において、水酸基含有(メタ)アクリレート化合物の語は、(メタ)アクリルアミド化合物を含むものとする。水酸基含有(メタ)アクリレート化合物は、典型的には、モノマーであり、水酸基を1〜2個、好ましくは1個含み、(メタ)アクリル基を1個だけ含み、分子量が1000以下、特には500以下である。水酸基含有(メタ)アクリレート化合物は、好ましくはヒドロキシアルキル(メタ)アクリレートであり、特に、ヒドロキシアルキル基のアルキル鎖の炭素数が、好ましくは2〜6、より好ましくは2〜5、さらに好ましくは2〜4のものである。
公知の方法で合成することが可能である。例えば、所定量のポリカプロラクトン系ポリオール(A1)及びポリエーテルポリオール(A2)を過剰量のポリイソシアネート(A3)に投入し、80℃で所定の遊離イソシアネート量になるまで反応させることでポリウレタンを得て、更に70〜80℃でさらにハイドロキノンモノメチルエーテル等の重合禁止剤の存在下、水酸基含有(メタ)アクリレート(A4)を一括で仕込み、70〜80℃で遊離イソシアネートが無くなるまで加温・攪拌することで合成可能である。この時、反応を促進させるために、ジブチルチンジラウレート等のスズ系触媒を添加することもできる。好ましい一実施形態においては、以下のようにして、ウレタン(メタ)アクリレートを得ることができる。まず、ポリカプロラクトン系ポリオール(A1)、芳香族系ポリエーテルポリオール(A2−1)及び水酸基含有(メタ)アクリレート(A4)を、過剰量のポリイソシアネート(A3)に投入し攪拌する。そして、遊離イソシアネート量と、仕込み比からのイソシアネートの理論過剰量が、例えば±10%以内になるまで反応させる。ついで、多官能ポリオール系ポリエーテルポリオール(A2−2)を加えて、残存イソシアネートが、例えば0.1%未満となるまで反応させる。
本願のエネルギー線硬化型樹脂組成物中にウレタン(メタ)アクリレートとともに含まれる(メタ)アクリレート化合物は、ホモポリマーのガラス転移点が50℃以上の単官能(メタ)アクリレートモノマー(B)である。好ましい具体例としては、アクリロイルモルホリン(145℃)、イソボルニルアクリレート(97℃)、N,N−ジメチルアクリルアミド(119℃)等が挙げられる。すなわち、ここでも、モノ(メタ)アクリレートモノマーの語は、(メタ)アクリルアミド化合物を含むものとする。使用可能なモノ(メタ)アクリレート化合物の他の具体例としては、2−アクリロイルオキシエチルフタレート(Tg130℃)、2−アクリロイルオキシプロピルフタレート(Tg158℃)、ジシクロペンタニルアクリレート(Tg120℃)、ジシクロペンタニルメタクリレート(Tg175℃)、ジシクロペンテニルアクリレート(Tg120℃)、イソボルニルメタクリレート(Tg180℃)、アダマンチルアクリレート(Tg153℃)、アダマンチルメタクリレート(Tg250℃)が挙げられる。例えば、興人フィルム&ケミカルズ(株)の「アクリロイルモルホリン」及び「ジメチルアクリルアミド」、並びに、ダイセル・サイテック(株)の「イソボルニルアクリレート」を、そのまま用いることができる。モノ(メタ)アクリレートモノマー(B)は、典型的には、分子量が1000以下、特には500以下のモノマーである。
使用可能な重合開始剤には、光重合開始剤と紫外線等の活性エネルギー線による重合開始剤との双方が含まれる。
本発明の硬化性樹脂組成物には、前記有機溶剤又はモノマー類、各種開始剤以外に各種添加剤を必要に応じて添加することができる。添加剤の例としては、光安定剤、紫外線吸収剤、触媒、レベリング剤、消泡剤、重合促進剤、酸化防止剤、難燃剤、赤外線吸収剤、帯電防止剤、スリップ剤、可塑剤、分散剤等が挙げられる。
・製造例1
フラスコに、イソホロンジイソシアネート1333.7g(6モル)キシレンジイソシアネート1129.6g(6モル)を入れ、撹拌しつつポリカプロラクトンポリオール(製品名:プラクセル205、株式会社ダイセル製、分子量530)を3180g(6モル)、ビスフェノールAエチレンオキサイド4モル付加物(製品名:ニューポールBPE‐40、三洋化成工業株式会社製)1213g(3モル)、さらにハイドロキノンモノメチルエーテルを加えてから2-ヒドロキシエチルアクリレート(HEA)383.2g(3.3モル)を仕込み、80℃に昇温し、所定の遊離イソシアネート含量になるまで反応させた。ついで、ポリエーテルポリオール(製品名:DKポリオールG‐480、第一工業製薬株式会社製)372g(1モル)を仕込み、70〜80℃で残存イソシアネート濃度が0.1%未満となるまで反応を行いウレタン(メタ)アクリレート1を製造した。
フラスコに、トリレンジイソシアネート2089.9g(12モル)を入れ、撹拌しつつポリカプロラクトンポリオール(製品名:プラクセル205、株式会社ダイセル製、分子量530)を3180g(6モル)、ビスフェノールAエチレンオキサイド4モル付加物(製品名:ニューポールBPE‐40、三洋化成工業株式会社製)1213g(3モル)、さらにハイドロキノンモノメチルエーテルを加えてから2-ヒドロキシエチルアクリレート(HEA)383.2g(3.3モル)を仕込み、80℃に昇温し、所定の遊離イソシアネート含量になるまで反応させた。ついで、ポリエーテルポリオール(製品名:DKポリオールG‐480、第一工業製薬株式会社製)372g(1モル)を仕込み、70〜80℃で残存イソシアネート濃度が0.1%未満となるまで反応を行いウレタン(メタ)アクリレート2を製造した。
フラスコに、イソホロンジイソシアネート2667.4g(12モル)を入れ、撹拌しつつビスフェノールAエチレンオキサイド4モル付加物(製品名:ニューポールBPE‐40、三洋化成工業株式会社製)3639g(9モル)、さらにハイドロキノンモノメチルエーテルを加えてから2-ヒドロキシエチルアクリレート(HEA)383.2g(3.3モル)を仕込み、80℃に昇温し、所定の遊離イソシアネート含量になるまで反応させた。ついで、ポリエーテルポリオール(製品名:DKポリオールG‐480、第一工業製薬株式会社製)372g(1モル)を仕込み、70〜80℃で残存イソシアネート濃度が0.1%未満となるまで反応を行いウレタン(メタ)アクリレート3を製造した。
フラスコに、イソホロンジイソシアネート2667.4g(12モル)を入れ、撹拌しつつポリカプロラクトンポリオール(製品名:プラクセル205、株式会社ダイセル製、分子量530)を3180g(6モル)、ビスフェノールAエチレンオキサイド4モル付加物(製品名:ニューポールBPE‐40、三洋化成工業株式会社製)1213g(3モル)、さらにハイドロキノンモノメチルエーテルを加えてから2-ヒドロキシエチルアクリレート(HEA)383.2g(3.3モル)を仕込み、80℃に昇温し、所定の遊離イソシアネート含量になるまで反応させた。ついで、ポリエーテルポリオール(製品名:DKポリオールG‐480、第一工業製薬株式会社製)372g(1モル)を仕込み、70〜80℃で残存イソシアネート濃度が0.1%未満となるまで反応を行いウレタン(メタ)アクリレート4を製造した。
実施例及び比較例で用いた、混合用の(メタ)アクリレートモノマーは下記のとおりである。混合用の各モノマーの分子量などについて、表1にまとめて示す。
・アクリロイルモルホリン:興人フィルム&ケミカルズ(株)の同名の製品。
・イソボルニルアクリレート:日本触媒(株)の同名の製品。
・N,N−ジメチルアクリルアミド:興人フィルム&ケミカルズ(株)の「ジメチルアクリルアミド」。
・ジシクロペンテニルオキシエチルアクリレート:日立化成工業(株)の「FA-512AS」。
・ノナンジオールジアクリレート:第一工業製薬(株)の「ニューフロンティアL-C9A」、1,9-ノナンジオールジアクリレート。
得られたウレタン(メタ)アクリレートを冷却後、表2中に示すとおり、所定の(メタ)アクリレートモノマー(B)と、所定の比率で混ぜ合わせた。この後、E型粘度計にて25℃の粘度を測定した。
このようにして得られたエネルギー硬化性樹脂液に、下記のとおり、重合開始剤を添加して均一に混合した後、ガラス板上にアプリケーターバーで塗布してから、紫外線照射を行った。
エネルギー硬化性樹脂液(固形分=オリゴマー+モノマー) 100重量部、
重合開始剤 Irgacure 184 3重量部、
膜厚:約100μm、
紫外線照射条件
ランプ:高圧水銀灯80W/cm、積算照度:250mJ/cm2、
ラインスピード:5m/min.、電力2kW、雰囲気:N2(O2濃度0.3%)。
・硬化物のガラス移転点:JIS K 7244−4 に準拠し、動的粘弾性測定装置(「レオログラフ・ソリッド」、東洋精機製作所製)を使用して、周波数10Hz、昇温速度2℃/minで測定されたtanδの極大点から求めた。
・引っ張り強度及び伸び:JIS-C-2151に準拠して、短冊形試験片を所定温度に30分以上放置後、速度200mm/minで引張試験を行った。
・鉛筆硬度:JIS K 5600−5−4に従い、ガラス板上での皮膜硬度を測定した。
・動摩擦係数:JIS K 7125に準拠し、約80×200mmの硬化フィルム試験片に、接触面積 40cm2(一辺の長さ 63mm)のすべり片を介して200gの荷重を印加した状態で、試験速度100mm/minにて、100Nのロードセルを用いて測定した。
Claims (3)
- (A1)ポリカプロラクトン系ポリオールと、
(A2)ポリエーテルポリオールと、
(A3)ポリイソシアネートと、
(A4)1以上の水酸基を有する(メタ)アクリレートモノマーと
を反応させて得られるウレタン(メタ)アクリレート、及び
(B)ガラス転移点が50℃以上のモノ(メタ)アクリレートモノマーまたはモノ(メタ)アクリルアミドモノマーを含有することを特徴とするエネルギー線硬化型樹脂組成物。 - (A2)のポリエーテルポリオールが、芳香族構造を有する芳香族系ポリエーテルポリオール(A2−1)、及び/又は、3官能以上のポリオールを出発化合物とする多官能ポリオール系ポリエーテルポリオール(A2−2)であることを特徴とする請求項1に記載のエネルギー線硬化型樹脂組成物。
- (A2)のポリエーテルポリオールが、芳香族系ポリエーテルポリオール(A2−1)と、前記多官能ポリオール系ポリエーテルポリオール(A2−2)との両者を含み、ポリエーテルポリオール(A2)の総重量に対する多官能ポリオール系ポリエーテルポリオールの重量比率が10〜40重量%であることを特徴とする請求項2に記載のエネルギー線硬化型樹脂組成物。